• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.18 no.1
• /
• pp.715-723
• /
• 2017

This study investigates the properties of a high-performance cementitious composite with partial substitution of stone dust for fine aggregate. The relationship between the properties and particle size distribution was analyzed using several analytical models. Experiments were carried out to examine the flowability, rheology, and strength of cement mortars with different stone-dust replacement ratios of 0-30 wt.%. The results showed improved flowability, lower rheological parameters (yield stress and plastic viscosity), and improved strength as the amount of stone dust increased. These results are closely related to the packing density of the solid particles in the mortar. The effect was therefore estimated by introducing an optimum particle size distribution (PSD) model for maximum packing density. The PSD with a higher amount of stone dust was closer to the optimum PSD, and the optimization was quantified using RMSE. The improvement in the PSD by the stone dust was proven to affect the flowability, strength, and plastic viscosity based on several relevant analytical models. The reduction in yield stress is related to the increase of the average particle diameter when using stone dust.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.19 no.1
• /
• pp.35-44
• /
• 2015

Two main parameters were examined such as CSA content and polymer-binder ratio to find effects on the strength, water absorption, chloride ion penetration depth, carbonation depth, length change and chemical resistance of polymer-modified mortar with CSA and EVA polymer powder (EVAPP). As results, compressive, flexural, tensile, adhesive strengths, and length change of the polymer-modified mortar with CSA and EVAPP increases with increasing CSA content and polymer-binder ratio, although the water absorption, chloride ion penetration depth, and carbonation depth decrease with increasing polymer-binder ratio and CSA content, and also the chemical resistance decreases. Such strength and durability development is attributed to the high tensile strength of EVA polymer and the improved bond between cement hydrates and aggregates because of the addition of EVAPP and CSA.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.05a
• /
• pp.811-815
• /
• 2003

The effects of high-range water-reducing agent (WRA) content and polymer-cement ratio on the strength properties of autoclaved SBR-modified mortars with WRA are examined. As a result, the flexural strength of the autoclaved SBR-modified mortars with WRAs tends to increase with increasing WRA content and polymer-cement ratio, and reaches a maximum at a WRA content of 2.0%. The compressive strength of the autoclaved SBR-modified mortars with WRAs is inclined to increase with increasing WRA content and polymer-cement ratio, and reaches a maximum at a WRA content of 2.0% and a polymer-cement ratio of 10%. From the test results, the addition of the WRAs is effective for improving strength properties of the autoclaved SBR-modified mortars.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.1
• /
• pp.23-29
• /
• 2022

This study was conducted to confirm the applicability of recycled aggregates as aggregates for structural concrete as a way to respond to the shortage of natural aggregates. The two-stage mixing approach developed by Tam et al. is known to be a method that can improve the mechanical performance of recycled aggregate concrete without the installation of new additional facilities. In this work, modified version of two stage mixing approach, which was used in our earlier work, was introduced to prepare mortar specimens with recycled fine aggregate, and the compressive strength and fire resistance were compared to mortar mixed with normal mixing approach. According to the experimental results from mortar with recycled fine aggregate, the use of two-stage mixing approach was found to be more effective than normal mixing approach for compressive strength development. In addition, the residual strengths of the mortar with two-stage mixing approach was higher than mortar made of normal mixing approach after exposure to 600 and 900 ℃. It is possible to manufacture high-performance cement composites with recycled fine aggregates through the active use of the two-stage mixing approach.

• Magazine of the Korea Concrete Institute
• /
• v.8 no.4
• /
• pp.161-169
• /
• 1996

Styrene-maleic anhydride copolymers with different composition (1:1SMA. 5:1SMA) were synthesized and further reacted with sulfuric acid to obtain water soluble copolymers (1:1SSMA, 5:1SSM.4). In the flow experiments of cement mortar mixed with copolymers, 5:1SSMA showed higher fluidity than 1:1SSMA. The cement mortar mixed with 1% 5:1SSMA maintained 95% of original flow after 60 min. On the other hand, the compressive strength of the hardened cement mortars containing 0.5% copolymers after 28 days curing was also examined. The compressive strength of hardened cement mortar containing 5:1SSMA was increased up to 41% compared to the plain while 1:1SSMA was increased up to 29%. As the results, the 5:1SSMA used in this study are greatly expected as a new high range water reducers for the concrete.

• Journal of the Korea Concrete Institute
• /
• v.17 no.5 s.89
• /
• pp.709-716
• /
• 2005

The objective of this study is to develop a high ductile fiber reinforced mortar, ECC(Engineered Cementitious Composite) with using raw material commercially available in Korea. A single fiber pullout test and a wedge splitting test were employed to measure the bond properties in a matrix and the fracture toughness of mortar matrix respectively, which are used for designing mix proportion suitable for achieving strain-hardening behavior at a composite level. Test results showed that the properties tended to increase with decreasing water-cement ratio. A high ductile fiber reinforced mortar has been developed by employing micromechanics-based design procedure. Micromechanical analysis was initially peformed to properly select water-cement ratio, and then basic mixture proportion range was determined based on workability considerations, including desirable fiber dispersion without segregation. Subsequent direct tensile tests were performed on the composites with W/C's of 47.5% and 60% at 28 days that the fiber reinforced mortar exhibited high ductile uniaxial tension property, represented by a maximum strain capacity of 2.2%, which is around 100 times the strain capacity of normal concrete. Also, compressive tests were performed to examine high ductile fiber reinforced mortar under the compression. The test results showed that the measured value of compressive strength was from 26MPa to 34 MPa which comes under the strength of normal concrete at 28 days.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.05a
• /
• pp.312-315
• /
• 2004

The effects of polymer-cement ratio, antifoamer content and shrinkage-reducing agent content on the strength of high-fluidity polymer-modified mortars using redispersible polymer powder are examined. As a result, the flexural and tensile strengths of the high-fluidity polymer-modified mortars using redispersible polymer powder tend to increase with increasing polymer-cement ratio, and tend to decrease with increasing shrinkage-reducing agent content, regardless of the antifoamer content. However, the compressive strength of the high-fluidity polymer-modified mortars using redispersible polymer powder decrease with increasing polymer-cement ratio and shrinkage-reducing agent content.

• Journal of the Korea Institute of Building Construction
• /
• v.4 no.2
• /
• pp.81-88
• /
• 2004

The purpose of this study is to investigate the chemical shrinkage and autogenous shrinkage of high strength cement paste and silica fume and fly ash and sand to cement ratio by the method of volumetric tests, and also investigate the autogenous shrinkage of high measurement method, and compare the results of volumetric test and linear length measurement test. A series of cement paste which have W/C ratio of 25%, 35%, 45% respectively were planed to study the effect of the W/C ratio to the shrinkages, and a series of cement paste which were replaced the cement by the silica fume and fly ash with 5%, 10%, 15% as the mass of cement respectively were planed to investigate the effects of poazolana to the shrinkages. A series of mortar which have a C/S ratio of 1:1, 1:1.5, 1:2 respectively were planed to investigate the shrinkage resistant effect of aggregate.

• Carbon letters
• /
• v.20
• /
• pp.72-75
• /
• 2016

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.485-488
• /
• 2008

Recycled fine aggregate has low quality because it contains large amount of old mortar. So, its usage is limited to a lower value-add, such as the roadbed material etc. Also, alkaline water occurred from treatment process of the waste concrete is becoming the cause of environmental problem. Accordingly, this study is to develop on the high quality recycled fine aggregate produced by low speed wet abraser using sulphuric. We investigated the properties of compressive strength of the mortar which was manufactured using recycled fine aggregate containing calcined gypsum produced by earlier mentioned process. Test results indicate that mortar using recycled fine aggregate containing calcined gypsum has lowest compressive strength. It seems that low compressive strength is closely associated with the expansion of the specimen by excessive formation of ettringite.