• Resources Recycling
• /
• v.19 no.6
• /
• pp.86-92
• /
• 2010

In the many kind of construct-material, the concrete which has the high-strength and a durability is sufficient to use with structure-material. but the color of concrete is very monotony, so generally concrete isn't used the out surface. although color concrete is a method of expressing surface, the combination of pigment and cement cause many physical problem such as efflorescence phenomenon, strength degradation and so on. In this study, It attempt to develop the black mortar using the industrial granulated blast furnace slag and to evaluate basic physical properties compare with general color concrete to solve the color concrete problem. The result of experiment showed that the flow dropped mixing of pigment. but flow increased in proportion to the mixing rate in occasion of mortar that mix granulated blast furnace sla and black mortar which was made granulated blast furnace slag has more visible black color than any mortar.

• Journal of the Korea Institute of Building Construction
• /
• v.13 no.1
• /
• pp.58-65
• /
• 2013

Currently, many high-rise buildings are built in Korea for land-efficient utilization and vista. In high-rise buildings this tall, the use of high-strength concrete is essential to reduce the cross-section of structure members and secure axial load. However, this high strength concrete is vulnerable to spalling by fire, due to the water vapor pressure caused by the very high temperature in fire. To prevent this, the main method used is to reinforce the concrete with fiber. However, there has been little research on the pumpability of fiber reinforced high strength concrete. For this reason, this study features a performance review based on the properties and pumpability of fiber reinforced high strength concrete. In addition, the parameter of rheology was measured by extracting mortar from the concrete, and friction factor was measured through a 400 m horizontal pipe pumping test using the fiber reinforced high strength concrete. The basic information on fiber reinforced high strength concrete that we obtain through the experiments and review will contribute to the field.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.2
• /
• pp.92-98
• /
• 2019

In general, high strength and high performance fiber reinforced cement composites exclude coarse aggregates basically in order to have homogeneous distributions of material properties. However, these fiber-reinforced cement mortar without coarse aggregate have a tenancy that the modulus of elasticity is low and the unit weight of cement is high, resulting in low economic efficiency. Therefore, in this study, the development of high ductile fiber - reinforced concrete was conducted, which has the adequate level of coarse aggregate but still retains the high flexural toughness and strength and also has the crack - distributing performance. Experimental study was carried out by using the amount of coarse aggregate as an experimental parameter. The results showed that the best flexural toughness and crack dispersion characteristics was obtained when the coarse aggregate was added at 25% by weight of the fine aggregate to the typical mixtures of high ductile cement mortar. PVA fiber was effective in crack distribution and ductility enhancement, and steel fiber was effective in strengthening flexural strength rather than crack distribution.

• Journal of the Korea Concrete Institute
• /
• v.24 no.6
• /
• pp.753-760
• /
• 2012

In this study, experimental research was carried out to evaluate and improve the constructability and seismic performance of high strength R/C interior beam-column joints regions, with or without the shear reinforcement, using high ductile fiber-reinforced mortar. Six specimens of retrofitted the beam-column joint regions using high ductile fiber-reinforced mortar are constructed and tested for their retrofit performances. Specimens designed by retrofitting the interior beam-column joint regions (IJNS series) of existing reinforced concrete building showed a stable mode of failure and an increase in load-carrying capacity due to the enhancement of crack dispersion by fiber bridging from using new high ductile materials for retrofitting. Specimens of IJNS series, designed by the retrofitting of high ductile fiber-reinforced mortar in beam-column joint regions increased its maximum load carrying capacity by 96~102.8% and its energy dissipation capacity by 0.99~1.11 folds when compared to standard specimen of SIJC with a displacement ductility of 5.

• Journal of the Korea Concrete Institute
• /
• v.23 no.4
• /
• pp.487-494
• /
• 2011

In this research, the possibility of using bottom ash as a binder for the alkali-activated cement mortar is studied. Several experiments were performed to investigate the variation of the material properties according to the mix proportion. In the experimental program, the flowability and compressive strength were evaluated for various values of water/ash ratio, activator/ash ratio, sodium silicate to sodium hydroxide ratio, curing temperature, and the fineness of bottom ash as the main variables. The experimental results showed that high strength of 40 MPa or greater could be achieved in $60^{\circ}C$ high temperature curing condition with proper flowability. For $20^{\circ}C$ ambient temperature curing, the 28 days compressive strength of approximately 30MPa could be obtained although the early-age strength development was very slow. Based on the results, the range of optimized mix design of bottom-ash based alkali-activated cement mortar was suggested. In addition, using the artificial neural network analysis, the flowability and compressive strength were predicted with the difference in the mix proportion of the bottom-ash based alkali-activated cement mortar.

• Journal of the Korea Concrete Institute
• /
• v.13 no.5
• /
• pp.516-524
• /
• 2001

Among many connection methods of reinforcing bar, the grout-filled splice sleeve system is very effective method of precast concrete construction due to its superior construction efficiency, such as large allowable limit to arrangement of reinforcing bars, good application of large sized reinforcing bars. In this study, totally 20 full-sited specimens were made and tested under monotonic and cyclic loading in order to extend the usage range of grout-filled splice sleeve system. The experimental variables adopted in this study are size of reinforcing bars embedded in upper and lower part of sleeve and compressive strength of filled mortar etc. After test was performed, the results were compared and analyzed with respect to previous test of author. Following main conclusions are obtained : 1) The structural performance of splice sleeve system is improved with increasing compressive strength of filled mortar. And also it was verified that the splice sleeve system with over 700 kgf/㎠ mortar compressive strength and over 6.54 development length of reinforcing bar retains the structural performance of over A class(AIJ Criteria). 2) In the case of using different size of reinforcing bars embedded in upper and lower part of sleeve, the result show that splice sleeve matching with large sized reinforcing bar must be used. And also up to 2 level smaller size of reinforcing bar compared to large reinforcing bar embedded in sleeve can be used.

• Journal of the Korea Concrete Institute
• /
• v.25 no.2
• /
• pp.233-240
• /
• 2013

In this study, experimental research was carried out to evaluate and improve the seismic performance of high strength R/C interior beam-column joints regions using advanced reinforcing detailings and high ductile fiber-reinforced mortar. Five specimens of retrofitted the beam-column joint regions using advanced reinforcing detailings and high ductile fiber-reinforced mortar were constructed and tested for their retrofitring performances. Specimens designed by retrofitting the interior beam-column joint regions (IJIR series) of existing reinforced concrete building showed a stable mode of failure and an increase in load-carrying capacity. Specimens of IJIR series, designed by the retrofitting of advanced reinforcing detailings and high ductile fiber-reinforced mortar in reinforecd beam-column joint regions increased its maximum load carrying capacity by 114.2~123.5% and its energy dissipation capacity by 1.55~1.85 times in comparison with the standard specimen of SIJC with a displacement ductility of 5.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.3
• /
• pp.330-337
• /
• 2021

3D printing is not only at the fundamental study and small-scale level, but has recently been producing buildings that can be inhabited by people. Buildings require a lot of cost and labor to work on the form work, but if 3D printing is applied to the building, the construction industry is received attention from technologies using 3D printing as it can reduce the construction period and cost. 3D printing technology for buildings can be divided into structural and non-structural materials, of which 3D printing is applied to non-structural materials. Because 3D printing needs to be additive manufacturing, control such as curing speed and workability is needed. Since cement mortar has a large shrinkage due to evaporation of water, cement polymer dispersion is used to improve the hardening speed, workability, and adhesion strength. The addition of polymer dispersion to cement mortar improves the tensile strength and brittleness between the cement hydrate and the polymer film. Cement mortar using polymer materials can be additive manufacturing but it has limited height that can be additive manufacturing due to its high density. When light-weight materials are mixed with polymer cement mortar, the density of polymer cement mortar is lowered and the height of additive manufacturing, so it is essential to use light-weight materials. However, the use of EVA redispersible polymer powder and light-weight materials, additional damage such as cracks in cement mortar can occur at high temperatures such as fires. This study produced a test specimen incorporating light-weight materials and EVA redispersible polymer powder to produce exterior building materials using 3D printing, and examined flame resistance performance through water absorption rate, length change rate, and cone calorimeter test and non-flammable test. From the test result, the test specimen using silica sand and light-weight aggregate showed good flame resistance performance, and if the EVA redispersible polymer powder is applied below 5%, it shows good flame resistance performance.

• Journal of the Korean GEO-environmental Society
• /
• v.6 no.4
• /
• pp.59-64
• /
• 2005

Although high pressure discharge method is widely used for improving soft ground, it has various problems including lack of strength increase and the possibility of water pollution and soil contamination. MJM(Morta Jet Method) uses sand in addition to cement as the injection material. MJM uses triple rods with a built-in nozzle that allows easier discharge of the slime, resulting in higher replacement area ratio and more uniform formation of pillar hydrates, and thus results in significant increase in strength. MJM is expected to perform especially well as piles in marine clays. This study investigates the field applicability of the MJM through extensive laboratory and field tests.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.11 no.3
• /
• pp.210-217
• /
• 2023

Various performances of ultra-high performance concrete (UHPC) applied with microplastics and expanded polystyrene (EPS) beads were evaluated. CompressIve and flexural strength, performance after ignition, flow-down in fresh state, and effective bond strength were evaluated. Designed weight of the cement panel with these mixtures was calculated based on the flexural strength. As a result of the experiments, it was confirmed that the EPS could reduce the density of UHPC with largest range. By maximum addition of EPS beeds, the density of UHPC decreased to 1300 kg/m³, and the compressive and flexural strengths for this mixtures were in ranges of 20-30 MPa and 15-20 MPa, respectively. On the other hand, lightest cement panel could be designed with UHPC having a density ranges about 2.0 g/cm³.