• Journal of the Korean Society for Heat Treatment
• /
• v.6 no.3
• /
• pp.144-151
• /
• 1993

For the purpose of studying the influence of stress relieving on microstructures and mechanical properties of weld metal, manual arc welding, onepole and twopole submerged arc welding were accomplished on $60kg/mm^2$ quenched and tempered high strength steel. After stress relieving, a lot of carbides were precipitated, developed and subsequently coarsened at the grain boundaries and within matrix due tn multiple tempering effect in manual arc welding, resulting in deterioated toughness. Meanwhile pearlite and cementite films were spheroidized and shortened in submerged arc welding, resulting in improved considerable toughness. It was observed that main effect of stress relieving was to reduce solut supersaturation by nucleation and growth of carbide precipitates, and stress relieving led to some reduction in the yield and tensile strenath but did not significantly affect elongation.

• Transactions of Materials Processing
• /
• v.28 no.4
• /
• pp.219-225
• /
• 2019

This study deals with the effect of austempering temperature and time on the microstructures and mechanical properties of high-carbon nano-bainite steels. Although all the austempered specimens are mainly composed of bainite, martensite, and retained austenite, the specimens which are austempered at lower temperatures contain finer packets of bainite. As the duration for austempering increases, bainite packets are clearly seen due to larger amount of carbon atoms being redistributes into bainite and retained austenite during bainite transformation. As the austempering time increases, the hardness of the specimens gradually decreases as a result of lower martensite volume fraction, and later increases again due to the formation of nano-bainite structure. The Charpy impact test results indicate that the impact toughness of the austempered specimens can be improved if the formation of nano-bainite structure and the transformation induced plasticity effect of retained austenite are optimized at higher austempering temperature.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.19 no.4
• /
• pp.109-115
• /
• 2015

High performance fiber reinforced cementitious composite (HPFRCC) can provide high fracture energy absorption as well as high strength with high fiber volume fraction. The increased fracture energy helps resisting high frequency loadings, such as earthquake, impact or blast. This study investigates the flexural performance of slurry infiltrated fiber concrete (SIFCON), one of the important HPFRCC, with respect to varying fiber volume fraction. The maximum fiber volume fraction was 8.0 % and reduced to 6.0% by 0.5% and the maximum volume fraction is obtained by packing fibers with simple tapping by hands. The used fiber was a steel fiber with the length 30 mm and the diameter of 0.5 mm. The flexural strengths were 48.7 MPa at 8.0 % and 22.8 MPa at 6.0 %. The measured flexural strength is much higher compared to other cememtitious composite materials but decreased proportional to the fractions. This result implies that for SIFCON considered herein the reduced amount of steel fibers may affect its flexural performance in a negatively way. The flexural toughness, an index to represent the fracture energy absorption, also decreased with the reduced fiber amount.

• Proceedings of the KWS Conference
• /
• 2003.11a
• /
• pp.227-229
• /
• 2003

Low heat input welding methods have been investigated in order to minimize the HAZ softening of the 600MPa grade fine grained steel weldment. The welding processes of interest were a high speed FCA welding with a multi-torch welding system, laser welding with filler feeding and hybrid laser welding. No HAZ softening was found for all the weldments formed with low heat input less than 10kJ/cm. Tensile strength of the weldments was high enough to satisfy the required value. Impact toughness of the weldments was also good even at -20$^{\circ}C$.

• Proceedings of the KWS Conference
• /
• 2005.06a
• /
• pp.147-149
• /
• 2005

Effect of nitrogen content on SAW weld metal properties were investigated. Weld metal nitrogen content increased with an increase of base metal nitrogen content due to dilution. High nitrogen content in weld metal resulted in high free nitrogen content, and consequently reduced impact toughness due to, mainly, strain aging effect.

• Journal of the Korea Concrete Institute
• /
• v.17 no.4 s.88
• /
• pp.543-550
• /
• 2005

In the present work, modulus of rupture (MOR), flexural toughness properties $(I_{30}\;and\;W_{2.0})$ and workability (slump) of high performance hybrid fiber reinforced concrete (HPHFRC) mixed with micro-fiber (carbon fiber) and macro-fiber (steel fiber), and replaced with a fine mineral admixture such as silica fume (SF) are characterized through the analysis of variance (ANOVA). Data of MOR, $I_{30}(or W_{2.0})$ and slump are used as the characteristic values to estimate flexural performance and workable property of HPHFRC. Specially, an experimental design was Planned according to the fractional orthogoanl nay method to reduce experimental number of times. The experimental results show that steel fiber is a considerable significant factor in MOR and I30 $(W_{2.0})$. Based on the significance of experimental factors about each characteristic factors, the following evaluation can be used: Experiment factors which reduce slump most remarkably are carbon fiber, steel fiber, silica fume order.; Those that improve MOR most significantly are silica fume $({\fallingdotseq}\;carbon\;fiber)$, steel fiber order; Those that increase flexural toughness most distinctly are silica fume, carbon fiber, steel fiber order. It is obtained that the combination of steel fiber $1.0\%$, carbon fiber $0.25\%$ and silica fume $5.0\%$ is the experimental condition that improve MOR and flexural toughness excellently with workability ensured within the experiment.

• Korean Journal of Materials Research
• /
• v.3 no.3
• /
• pp.253-260
• /
• 1993

High strength and fracture toughness of Al-Li-Cu alloy(2090 Al alloy) have been achieved by the improvement of melting and casting, extrusion and heat treatment techniques. To establish the sucessful process for semi-industrial scale ingot(20Kg) the following areas have been investigated: (1) Improvement of melting and casting techniques for ingot by introducing atmospheric modifications, vacuum and rotary degassing, and deslagging. (2) The effect of heat treatment on mechanical properties (3) Mechanical characterization by tensile test, fracture toughness test and fatigue crack propagation test. High mechanical properties were found to be intimately related with ingot soundness. Tensile strength of final products varied from 534MPa to 566MPa in peak aged condition while elongation/ductility ranged from 9.0% to 11.9%. From the fracture toughness test with using compact tensile specimen, plane strain fracture toughness($K_{Ic}$) appeared to be 39MPa${\surd}$m in peak aged condition and 23MPa${\surd}$ m in underaged condition. When load ratios of 0.1, 0.3 and 0.5 were given ${\Delta}K_{th}$ was 6.0MPa${\surd}$ m, 5.3MPa${\surd}$ m and 4.3MPa${\surd}$ m respectively.

• Journal of the Korean Society for Heat Treatment
• /
• v.28 no.2
• /
• pp.75-81
• /
• 2015

Effects of B and Cu additions on the microstructure and mechanical properties of high-strength bainitic steels were investigated in this study. Six kinds of high-strength bainitic steels with different B and Cu contents were fabricated by thermo-mechanical control process composed of controlled rolling and accelerated cooling. The microstructures of the steels were analyzed using optical and transmission microscopy, and the tensile and impact tests were conducted on them in order to investigate the correlation of microstructure with mechanical properties. Depending on the addition of B and Cu, various low-temperature transformation products such as GB (granular bainite), DUB (degenerated upper bainite), LB (lower bainite), and LM (lath martensite) were formed in the steels. The addition of B and Cu increased the yield and tensile strengths because of improved hardenability and solid solution strengthening, but decreased the ductility and low-temperature toughness. The steels containing both B and Cu had a very high strength above 1.0 GPa, but showed a worse low-temperature toughness of higher DBTT (ductile-to-brittle transition temperature) and lower absorbed energy. On the other hand, the steels having GB and DUB showed a good combination of tensile and impact properties in terms of strength, ductility, yield ratio, absorbed energy, and DBTT.

• Journal of the Korea Institute of Building Construction
• /
• v.8 no.3
• /
• pp.75-83
• /
• 2008

In this paper, concrete material tests were carried out to investigate influence of steel fiber volumn ratios on variations of workability and strength characteristics of steel fiber reinforced high-strength concrete, $50MPa{\sim}90MPa$ of compressive strength, according to increase of fiber volume. Test specimens were arranged with six levels of concrete compressive strength and fiber volumn ratios, 0.0%, 0.5%, 1.0%, 1.5%, 2.0%. The test results showed that steel fiber reinforced high-strength concrete($70MPa{\sim}90MPa$, 1.5% fiber volumn ratio) with good workability of slump 20cm could be used practically and effects of steel fiber reinforcement in improvement of concrete strength and toughness characteristics such as splitting tensile strength, flexural strength, and diagonal tensioned shear strength, were more distinguished in high-strength concrete than general strength concrete. And the test results indicated that splitting tensile strength of fiber reinforced concrete was proportioned to the product of steel fiber volumn ratios, $V_f(%)$ and sqare root of compressive strength, $\sqrt{f_{ck}}$, and the increasing rate was in contrast with that of flexural strength, and increase of diagonal tensioned shear strength was remarkable at steel fiber volumn ratio, 0.5%.

• Journal of the Korea Concrete Institute
• /
• v.27 no.4
• /
• pp.411-418
• /
• 2015

This paper investigates the effects of fiber volume fraction and panel thickness on face damage characteristics of steel fiber-reinforced concrete (SFRC) under high-velocity globular projectile impact. The target specimens were prepared with $200{\times}200mm$ prismatic panels with thickness of 30 or 50 mm. All panels were subjected to the impact of a steel projectile with a diameter of 20 mm and velocity of 350 m/s. Specifically, this paper explores the correlation between mechanical properties and face damage characteristics of SFRC panels with different fiber volume fraction and panel thickness. The mechanical properties of SFRC considered in this study included compressive strength, modulus of rupture, and toughness. Test results indicated that the addition of steel fiber significantly improve the impact resistance of conventional concrete panel. The front face damage of SFRC panels decreased with increasing the compressive toughness and rear face damage decreased as the modulus of rupture and flexural toughness increased. To evaluate the damage response of SFRC panels under high-velocity impact, finite element analysis conducted using ABAQUS/Explicit commercial program. The predicted face damage of SFRC panels based on simulation shows well agreement with the experimental result in similar failure mode.