• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2000년도 추계학술대회논문집A
• /
• pp.219-224
• /
• 2000

A research for development of composite body panel is in progress for lightening tare. Low specific weight LPMC (Low pressure molding compound) has advantages such as lightweight and resistance to dent and corrosion. In this study, tensile, bending and impact tests for the LPMC and SPRC35 (High tension steel plate) were carried out and compared. Although mechanical properties of SPRC35 are better than the LPMC, the LPMC satisfies basic requirements for car body panel. The high temperature exposed LPMC were degraded due to fiber-matrix debonding and deterioration of resin.

• 한국건설순환자원학회논문집
• /
• 제6권4호
• /
• pp.283-288
• /
• 2018

균열 자기치유 소재는 균열발생 시점부터 노출환경 조건에 따라 활성화되기 때문에 치유성능과 균열면의 노출환경 조건과의 관계 규명이 매우 중요하다. 이에 본 연구에서는 자기치유형 보수 모르타르의 치유성능에 노출환경 조건이 미치는 영향을 투수시험을 통하여 조사하였다. 균열시험체의 초기 균열폭에 대한 온도 및 습도의 영향을 조사한 결과, 양생온도의 영향은 미미하였으나, 건습변화에 의해서는 균열닫힘 현상이 발생하고 있음을 확인하였다. 그리고 자기치유형 보수 모르타르 시험체의 균열부위에서 생성된 치유물질은 calcite 광물로 확인되었다. 밀도가 높은 calcite 광물은 중력의 영향을 받아 침강하기 때문에, 균열면의 방향에 따라 치유성능에 다소 차이를 나타냈으며, 또한 대기노출 조건보다 습윤노출 조건에서 치유성능이 크게 향상되었다.

• Composites Research
• /
• 제30권1호
• /
• pp.7-14
• /
• 2017

In this paper, the inter-lamina shear strength (ILSS) of multi-wall carbon nanotube (MWNT) reinforced carbon fiber reinforced plastics (CFRP) and thin-ply composites were verified under low earth orbit (LEO) space environment. CFRP, MWNT reinforced CFRP, thin-ply CFRP and MWNT reinforced thin-ply CFRP were tested after aging by using accelerated ground simulation equipment. The used ground simulation equipment can simulate high vacuum ($2.5{\times}10^{-6}torr$), atomic oxygen (AO, $9.15{\times}10^{14}atoms/cm^2{\cdot}s$), ultraviolet light (UV, 200 nm wave length) and thermal cycling ($-70{\sim}100^{\circ}C$) simultaneously. The duration of aging experiment was twenty hours, which is an equivalent duration to that of STS-4 space shuttle condition. After the aging experiment, ILSS were measured at room temperature ($27^{\circ}C$), high temperature ($100^{\circ}C$) and low temperature ($-100^{\circ}C$) to verify the effect of operation temperature. The MWNT and thin-ply shows good improvement of ILSS at ground condition especially with the thin-ply. And after LEO exposure large degradation of ILSS was observed at MWNT added composite due to the thermal cycle. And the degradation rate was much higher under the high temperature condition. But, at the low temperature condition, the ILSS was largely recovered due to the matrix toughening effect.

• 대한안전경영과학회지
• /
• 제26권2호
• /
• pp.87-92
• /
• 2024

This study aims to compare six observational methods for assessing arm- and hand-intensive tasks, based on literature review. The comparison was conducted in viewpoints of body regions, force/external load, motion repetition, other factors including static posture, coupling, duration/break, pace, temperature, precision task, and final risk or exposure level. The number of risk factors assessed was more, and assessment procedure was more complex than the observational methods for assessing whole-body postural loads such as Ovako Working Posture Analysis System(OWAS), Rapid Upper Limb Assessment(RULA), and Rapid Entire Body Assessment(REBA). Due to these, the intra- and inter-reliabilities were not high. A past study showed that while Hand Arm Risk Assessment Method(HARM) identified the smallest proportion of the work tasks as high risk, Strain Index(SI) and Quick Exposure Check(QEC) hand/wrist were the most rigorous with classifying most work tasks as high risk. This study showed that depending on the observational technique compared, the evaluation factors, risk or exposure level, and evaluation results were different, making it necessary to select a technique appropriate for the characteristics of the work being assessed.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2002년도 가을 학술발표회 논문집
• /
• pp.307-312
• /
• 2002

This paper deals with structural behavior of reinforced concrete beams under fire and fire damaged condition. The main purpose of this study is to investigate the structural behavior of the beams under high temperature condition and to evaluate the remaining strength of flexural members by exposure time to fire. For this purpose, twelve beam specimens are fabricated and experimented. Ten specimens are exposed to the fire for 1 and 2 hours and to the failure. After being cooled in room temperature, the specimens are loaded to the failure. The research result shows that the main variables of the test, concrete cover and exposure time to fire are much influenced on the structural behavior and the remaining strength.

• Plant Resources
• /
• 제8권3호
• /
• pp.217-224
• /
• 2005

We tested the hypothesis that alpine plants have special physiological and biochemical mechanisms in addition to their structural adaptation in order to survive under extreme conditions. The photosynthetic organs of Pinus pumila were used to examine the seasonal changes in sugar concentration, antioxidative enzyme, and lipid peroxidation. The concentrations of sucrose, glucose, fructose and reducing sugar were the highest in the leaves in April. But sugar contents in buds and inner barks did not respond sensitively on temperature change. Meanwhile superoxide dismutase (SOD) activity responded sensitively on the change of temperature and SOD in all tissues maintained high activity in April. Meanwhile anthocyanin content increased rapidly in June but the increase of anthocyanin content was not enough to prevent their tissues from the damage by the exposure of high temperature or other stress. In conclusion, under low temperature condition, P. pumila increased the concentration of soluble sugars and SOD activity in their tissues in order to overcome extreme environmental condition. But in summer, these stress defense system against high temperature might be disturbed slightly. This results in the increase of malondialdehyde (MDA) contents in three tissues by lipid peroxidation.

• 열처리공학회지
• /
• 제37권3호
• /
• pp.114-120
• /
• 2024

AA 2026, which is used as an aviation material, is an improved version of 2024 and has higher physical properties, and is a material that has the potential to be applied to supersonic aircraft to be developed in the future. However, when an aircraft exceeds supersonic speeds, the surface heats up and the material must be resistant to this. Therefore, this study confirmed the high-temperature properties of AA 2026, an aviation structural material. AA 2026, solution treated at 500℃ for 4hr, was naturally aged at room temperature for more than 168 hr. Changes in microstructure and physical properties were confirmed over several hours of exposure to 100℃, 200℃, and 300℃, respectively. As a result of microstructure analysis, there was no significant change at 100℃, and from 200℃, GPB, a strengthening mechanism, grew and formed an S Phase. It was confirmed that the S Phase grew as the exposure time increased. Through a tensile test, it was confirmed that physical properties deteriorated as the precipitates grew. However, it was confirmed that the properties were stably maintained at 100℃, which is the temperature when the speed of a supersonic aircraft is less than Mach 2.

• Steel and Composite Structures
• /
• 제52권2호
• /
• pp.121-134
• /
• 2024

To investigate the compressive behavior of partially encased recycled aggregate concrete (PERAC) stub columns after exposed to elevated temperatures, 22 specimens were tested. The maximum temperature suffered, the replacement ratio of recycled coarse aggregate (RCA), the endurance time and the spacing between links were considered as the main parameters. It was found that the failure mode of post-heated PERAC columns generally matched that of traditional partially encased composite (PEC) columns, but the flange of specimens appeared premature buckling after undergoing the temperature of 400℃ and above. Additionally, the ultimate strength and ductility of the specimens deteriorated with the elevated temperatures and extended heating time. When 400℃< T ≤ 600℃, the strength reduction range is the largest, about 11% ~ 17%. The higher the replacement ratio of RCA, the lower the ultimate strength of specimens. At the temperature of 600℃, the ultimate strength of specimens with the RCA replacement ratio of 50% and 100% is 0.94 and 0.91 times than that of specimens without RCA, respectively. But the specimen with 50% replacement ratio of RCA showed the best ductility performance. And the bearing capacity and ductility of PERAC stub columns were changed for the better due to the application of links. When the RCA replacement ratio is 100%, the ultimate strength of specimens with the link spacing of 100 mm and 50 mm increased 14% and 25% than that of the specimen without links, respectively. Based on the results above, a formula for calculating the ultimate strength of PERAC stub columns after exposure to high temperatures was proposed.

• 한국신뢰성학회지:신뢰성응용연구
• /
• 제17권1호
• /
• pp.78-82
• /
• 2017

Purpose: The purpose of this study is to evaluate failure characteristic and mechanism of four commercial water-repellent coatings for elevated temperature machinery applications. Method: Thermal degradation was performed for up to 64 thermal cycles. 1 cycle consists of 15 minute holding at 523K under 300rpm revolution and 15 minute-natural cooling. Contact angle was measured and microstructure of the coating layer was observed by using a scanning electron microscope. Results: Four kinds of commercial repellent coating showed hydrophobic or super-hydrophobic property implying that all coatings are suitable for room temperature application. Contact angle of three kinds of commercial coatings decreased rapidly after thermal exposure, while only one specimen having hydrophobic surface showed extremely slow degradation. Conclusion: Observed decrease in contact angle of the coatings were attributed to formation of macro-sized pores and disappearance of micro-protrusion during thermal exposure. Optimum water-repellent coating needs to be selected under the consideration of initial contact angle as sell as service temperature.

• 한국산업보건학회지
• /
• 제28권3호
• /
• pp.241-256
• /
• 2018

Objectives: This study aimed to review the characteristics of three-dimensional printing technology focusing on printing types, materials, and health hazards. We discussed the methodologies for exposure assessment on hazardous substances emitted from 3D printing through article reviews. Methods: Previous researches on 3D printing technology and exposure assessment were collected through a literature review of public reports and research articles reported up to July 2018. We mainly focused on introducing the technologies, printing materials, hazardous emissions during 3D printing, and the methodologies for evaluation. Results: 3D printing technologies can be categorized by laminating type. Fused deposition modeling(FDM) is the most widely used, and most studies have conducted exposure assessment using this type. The printing materials involved were diverse, including plastic polymer, metal, resin, and more. In the FDM types, the most commonly used material was polymers, such as acrylonitrile-butadiene-styrene(ABS) and polylactic acids(PLA). These materials are operated under high-temperature conditions, so high levels of ultrafine particles(mainly nanoparticle size) and chemical compounds such as organic compounds, aldehydes, and toxic gases were identified as being emitted during 3D printing. Conclusions: Personal desktop 3D printers are widely used and expected to be constantly distributed in the future. In particular, hazardous emissions, including nano sized particles and various thermal byproducts, can be released under operation at high temperatures, so it is important to identify the health effects by emissions from 3D printing. Furthermore, appropriate control strategies should be also considered for 3D printing technology.