• 콘크리트학회논문집
• /
• 제15권5호
• /
• pp.739-746
• /
• 2003

Various researches on the application of polymer dispersions to the cement mortar and concrete have been carried out in many countries like America, Japan and Germany and so on due to their high performance and good modification effect. PAE of polymer dispersion widely used in situ was employed that the high flowability may be induced in the cement mortar. In order to investigate the modification of cement mortar with high flowability by PAE and fracture mode of adhesive strength properties in tension of that, experimental parameters were set as PAE solid-cement ratio(P/C) and cement: fine aggregate(C:F) and the experiments such as unit weight, flow, consistency change, crack resistance and segregation that inform on the general properties have been done. Adhesion in tension is measured with a view to comprehending the properties and fracture mode in tensile load. Consistency change of cement mortar modified by PAE did grow better as the ratio of PAE solid-cement increased and was much superior to that of resin based flooring such as polyurethane and epoxy which recorded the loss of consistency in 90 min. after mixing. Adhesive strength in tension increased with continuity during curing period and showed the maximum in case of C:F=1:1 and P/C=20%.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2022년도 가을 학술논문 발표대회
• /
• pp.157-158
• /
• 2022

A problem arose about the lack of strength of dry mortar for flooring. To solve the problem of lack of strength, a high-strength dry mortar was applied. However, problems arose about the increase in the amount of cracks. It is necessary to analyze the causes of the increase in the amount of cracking in high-strength dry mortar and take countermeasures.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2016년도 춘계 학술논문 발표대회
• /
• pp.45-46
• /
• 2016

As the demand for super tall buildings is currently increased in domestic and foreign countries, some kinds of ultra-high strength concretes are being developed actively. Since the cross section of concrete becomes smaller thanks to such kinds of ultra-high strength concretes, the concrete structures can be much bigger, more gigantic and much ultra-high. And as another benefit which is generated thanks to the enhancement of the durability performance, the maintenance expenses are also saved. However, since low W/B ultra-high concrete has a high possibility that many cracks can occur in the initial period due to the self-shrinkage caused by the self-desiccation as one of the blending characteristics, the problem becomes bigger by influencing the safety of a structure. Therefore, in this study, it is intended to analyze the effects of substituting some limestone-based ultra-high strength mortar with electric arc furnace oxidizing slag fine aggregates on the self-shrinkage of mortar.

• 한국농공학회지
• /
• 제40권5호
• /
• pp.52-58
• /
• 1998

The objective of this study was to develop a polymer mortar protection block with high strength and durability using unsaturated polyester resin to complement defects of conventional cement mortar protection block. Physical and mechanical properties of the polymer mortar protection block were also investigated. Low absorptivity, high impact strength, and great bending strength of the polymer mortar protection block was compared with those of the conventional cement protection block. In conclusion, the polymer mortar protection block is excellent and useful as industrial products for erosion control works.

• Computers and Concrete
• /
• 제19권2호
• /
• pp.121-126
• /
• 2017

This paper presents the effect of aggregate type on high temperature resistance of self-compacting mortars (SCM) produced with normal and lightweight aggregates like expanded perlite and pumice. Silica fume (SF) and fly ash (FA) were used as mineral additives. Totally 13 different mixtures were designed according to the aggregate rates. Mini slump flow, mini V-funnel and viscometer tests were carried out on the fresh mortar. On the other hand, bulk density, porosity, water absorption and high temperature tests were made on the hardened SCM. After being heated to temperatures of 300, 600 and $900^{\circ}C$, respectively, the tensile strength in bending and compressive strength of mortars determined. As a result of the experiments, the increase in the use of lightweight aggregate increased total water absorption and porosity of mortars. It is observed that, the increment in the usage of lightweight aggregate decreased tensile strength in bending and compressive strengths of mortar specimens exposed to high temperatures but the usage of up to 10% expanded perlite in mortar increased the compressive strength of specimens exposed to $300^{\circ}C$.

• 한국농공학회지
• /
• 제24권3호
• /
• pp.92-99
• /
• 1982

The objective of this study was to investigate the compressive and bending strength characteristics of epoxy resin mortar, which is still in an early stage of its use and study in Korea. The results obtained are summarized as follows; 1. The compressive strengths of epoxy resin mortar after 1 day, 2 days and 3 days were gained 87%, 91% and 95%, respectively, in view of that of mortar at the age of 7 days. This result showed that the initial compressive strength within 1 day was very high. 2. The highest compressive strength of epoxy resin mortar was 914 kg/cm2 at the point of having the mixing ratio of one to two. It reached up to 3.7 times that of the normal portland cement mortar at the age of 28 days. 3. The bending strengths of epoxy resin mortar after 1 day, 2 days and 3 days came up to 88%, 93% and 97%, respectively, in comparing that of mortar at the age of 7 days. It was expressed to be simielar to the tendency of compressive strength. 4. The highest bending strength of epoxy resin mortar was 384 kg/cm2 at mixing ratio of one to two. It came up to as much as 6.5 times in comparing with that of the normal portland cement mortar at the age of 28 days. Therefore, the epoxy resin mortar would be effective for promoting the bending strength of structural members. 5. The regression equation between compressive and bending strength was obtained as follows; oo~=0.391 oc+27.54 (r=0.99) And the estimated value of bending strength was corresponded to about 44 per cent in comparing with that of the compressive strength.

• 한국건축시공학회지
• /
• 제11권6호
• /
• pp.538-546
• /
• 2011

This paper is to experimentally investigate the strength and autogenous shrinkage of high strength mortar with the 20 % of water?binder ratio(W/B). In this study, the water substituting liquid(WSL) was used including gasoline, light oil, lamp oil, edible oil, HFE, ethanol, methanol and acetone in order to explore changes in strength and autogenous shrinkage depending on WSL type and replacement. For fresh properties, the replacement of WSL did not affect the fluidity of mortar mixtures considerably, except for ethanol and methanol. However, the replacement of WSL resulted in a slight decrease in flexural and compressive strength. For autogenous shrinkage, the replacement of WSL led to reduce autogenous shrinkage, and especially, the replacement of edible oil led to reduce autogenous shrinkage significantly due to saponification between edible oil and cement.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1995년도 봄 학술발표회 논문집
• /
• pp.142-147
• /
• 1995

In this study, styrene-maleic anhydride copolymer (SMA) was synthesized from styrene and maleic anhydride and further reacted with sulfuric acid to obtain water-soluble SMA and the flow and strength tests of cement mortar mixed with copolymers were carried out to evaluate the capability of copolymers as high range water reducer for the concrete. It was found from flow experiment that the fluidity of cement mortar mixed with sulfonated SMA (SSMA) was larger than that miced with aminophenol-substituted SSMA (SmSMA). The decreasing rate of the flow of cement mortar mixed with SSMA and SmSMA was decreasing rate of the flow of cement mortar mixed with SSMA and SmSMA was significantly lower than that mixed with naphthalene condensate (NSC). The compressive strength of the hardened cement mortars containing 0.5% copolymers after 28 days curing was examined. The compressive strength of hardened cement mortar containing SSMA and SmSMA was increased up to 32% and 13%, respectively, when compared to the plain. As the results, the copolymers (SSMA and SmSMA) used in this study are greatly expected as a good high range water reducers for the concrete.

• 한국구조물진단유지관리공학회 논문집
• /
• 제16권4호
• /
• pp.79-88
• /
• 2012

본 연구에서는 고강도 모르타르 충전식 기계적 슬리브 철근이음에 대한 단조가력 하에서의 강성을 보다 적절하게 평가하기 위하여, 슬리브 철근이음의 주요한 구조요소가 미치는 단조가력 하에서의 철근이음 강성에 대한 영향을 검토하였고 AIJ 규준에서 설정한 단조가력 하에서의 슬리브 철근이음에 대한 강성 기준과 비교평가하였다. 이것을 위하여 단조가력을 실시한 국내외 189여개 고강도 모르타르 충전식 기계적 슬리브 철근이음의 실험데이터를 조사하고 그 실험결과를 분석하였다. 그 결과, AIJ 규준에서 규정하는 목표 강성을 확보하는데 필요한 $f_g$(L/d)의 한계값을 철근의 종류와 슬리브의 종류에 따라서 각각 제시하였다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1999년도 학회창립 10주년 기념 1999년도 가을 학술발표회 논문집
• /
• pp.191-194
• /
• 1999

Recently in Korea, may workers have reported the effects of the granulated blast furnace slag[BFS] of high fineness on the strength development of slag cement. We have studied the effect of slag fineness on the strength development of mortar with curing conditions, in order to get the basic data of high strength concrete using BFS. In this paper, we discussed the effects of slag fineness and porosity of mortar and the reaction of slag in hardened slag cement.