• 한국세라믹학회지
• /
• 제27권4호
• /
• pp.495-500
• /
• 1990

Investigation for the preparation of high strength hardened cement paste using ordinary portland cement, hydroxypropyl methyl cellulose (HPMC) with admixtures was carried out. For molding of the specimen, the paste was mixed with 0.1 of water cement ratio by twin roll mill. The maximum flexural strength of dried hardened cement paste was about 600∼700kg/㎠. When the SiC was added to the paste, the dry flexural strength was about 920kg/㎠ and the young's modulus was 5.2×105kg/㎠. When the admixtures were added to the specimens, wet strength of the harened cement paste immersed in water was showed around 50∼100kg/㎠ higher than that of plain specimen. Consequently it is recognized the water stability of hardened cement paste was remarkably improved by adequate admixture.

• 대한환경공학회지
• /
• 제37권7호
• /
• pp.412-417
• /
• 2015

본 연구는 하수처리장에서 발생하는 하수슬러지 소각재와 Geobond를 이용한 응용 블록의 개발을 위하여 수행하였다. 실험은 무소성 공정으로 진행하였으며, Sewage Sludge Ash (SSA)를 Geobond(무기바인더)와 특수시멘트인 초조강 시멘트 마이크로 시멘트, 모래 등의 바인더를 혼합한 각각의 페이스트 시편을 성형 후 건조 및 양생과정을 거친 시편을 단기 압축강도를 측정한 후 28일 장기 양생한 결과 압축 강도가 64.6 MPa로 발현하였다. 이는 KS기준치 22.54 MPa ($229.7kg/cm^2$)을 훨씬 상회하는 고강도의 압축강도를 나타내었다. 하수슬러지 소각재(SSA) 첨가율은 각 바인더 별 약 10~40%까지 혼합 가능한 것으로 나타났다. 따라서 SSA를 무기바인더인 Geobond와 특수시멘트(HESPC, MC)의 대체 물질로의 사용이 가능함을 입증하였다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1997년도 가을 학술발표회 논문집
• /
• pp.408-415
• /
• 1997

Bond strength of reinforcing bar to high-performance concrete using Belite cement is explored using beam end test specimen. The key parameters for the bond test are slump of concrete, top bar effect, and strength of concrete in addition to concrete covers. Specimen failed in the typical brittle bond failure splitting the concrete cover as the wedging action. The test results show that for the group with portland cement I using superplasticizer additional slump does not decrease the bond strength of the top bar is less than bond strength of bottom bar, but the top bar factor satisfy the modification factor for top reinforcement. The result also show that bond strength is function of square root of concrete compressive strength and cover thickness. More detailed evaluation will be conducted from the test specimen with high strength concrete using the belite cement.

• 콘크리트학회논문집
• /
• 제23권6호
• /
• pp.757-763
• /
• 2011

콘크리트의 효율적인 조기강도 확보를 위해 시멘트의 성능 향상에 주안점을 두고 연구를 진행하였다. 이 연구는 선행 연구인 시멘트 생산 공정 중 부수적으로 발생되는 크기가 작은 시멘트(이하 미립자 시멘트, FC라 함)를 이용하는 콘크리트의 조기강도 발현 특성 연구에 대한 후속 연구로서 내구성 검토를 실시하였다. 실험 결과 굳지 않은 콘크리트에서는 각 배합별 목표 범위를 모두 만족하는 것으로 나타났고, 미립자 시멘트를 혼입하였을 때 응결시간은 촉진되었고 압축강도는 증진되었으며 수화열은 유사한 수준인 것으로 평가되었다. 특히, 내구성 측면에서는 미립자 시멘트 혼입 유 에 따라 모든 실험 항목에서 유사한 수준인 것으로 평가되었다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2000년도 봄 학술발표회 논문집
• /
• pp.47-52
• /
• 2000

Recently, it is very necessary the development of the manufacturing techniques for high strength concrete(HSC) for the large-scale size and good quality of civil structure. But, the manufacture and quality control of HSC of which shrinkage, heat of hydration and workability at construction filed are considered, is very difficult due to its low water-cement ratio and high quantity of unit cement content. In the present study, we tried to know and assess the influences of chemical and physical properties of cement on the material properties of HSC. We analyzed basic properties of 4 kinds of cement whose chemical and physical properties are different each other through various tests such as chemical analysis and mortal test. Also, we performed the assessment of the material properties of HSC for each dement by the test for the conditions of same mix design and similar compressive strength. From the results in the study, the assessment of the important quality factors of cement influencing the properties of HSC may be utilized to quality control of applied cement to manufacture the HSC of high quality.

• 콘크리트학회논문집
• /
• 제15권5호
• /
• pp.739-746
• /
• 2003

Various researches on the application of polymer dispersions to the cement mortar and concrete have been carried out in many countries like America, Japan and Germany and so on due to their high performance and good modification effect. PAE of polymer dispersion widely used in situ was employed that the high flowability may be induced in the cement mortar. In order to investigate the modification of cement mortar with high flowability by PAE and fracture mode of adhesive strength properties in tension of that, experimental parameters were set as PAE solid-cement ratio(P/C) and cement: fine aggregate(C:F) and the experiments such as unit weight, flow, consistency change, crack resistance and segregation that inform on the general properties have been done. Adhesion in tension is measured with a view to comprehending the properties and fracture mode in tensile load. Consistency change of cement mortar modified by PAE did grow better as the ratio of PAE solid-cement increased and was much superior to that of resin based flooring such as polyurethane and epoxy which recorded the loss of consistency in 90 min. after mixing. Adhesive strength in tension increased with continuity during curing period and showed the maximum in case of C:F=1:1 and P/C=20%.

• 한국도로학회논문집
• /
• 제17권2호
• /
• pp.63-70
• /
• 2015

PURPOSES: As a part of our research into repair techniques for roads that have collapsed as a result of a natural disaster, this study set out to find the optimum mix proportion for gravels to be used to restore a damaged area. METHODS: This study considered flow and strength-development characteristics. The experimental variables were the W/C ratio, the usage of the admixture, the types of cement, and the quantity of fine aggregate over three different experimental stages. The compressive strength was measured at 12 hours, one day, three days, and seven days. RESULTS : The flow varied with the amount of fine aggregate and the use of a high-range water-reducing (HRWR) admixture. The compressive strength also varied with respect to the type of cement and the W/C ratios. The strength satisfied the expected requirement of 21 MPa after one day, provided the mix proportion was appropriate. CONCLUSIONS: A gravel-filling high-flow cement-based mortar exhibited strength and consistency with a W/C ratio in the range of 0.40 to 0.45, assuming the use of HRWR at 0.5 to 0.7% and a fine aggregate/cement ratio of 1.0 to 1.5.

• Advances in concrete construction
• /
• 제5권1호
• /
• pp.65-74
• /
• 2017

This study was focused on the use of partial replacement of cement with glass powder in high strength concrete and also copper slag as a partial replacement of coarse sand in concrete. The high strength concrete was prepared with different mineral admixtures like silica fume, fly ash and rice ash husk in different proportions. An experimental investigation has been carried to study about the effect of glass powder on high strength copper slag concrete. The range of glass powder was 10%, 15% and 20% as a replacement of cement. The range of copper slag was 0%, 20%, 40% and 60% as a replacement of natural sand. In addition to the different percentage of fly ash, silica fume, and rice husk ash 5% and 10% was also studied in copper slag concrete. Thus, a total of 51 cubes were casted and compressive strength test was performed on them. The result of the study shows that the value of average compressive strength of concrete after addition of 10%, 15% and 20% of glass powder are 70.47, 72.01 and 73.31 respectively. The value of average compressive strength after addition of 20%, 40% and 60% copper slag as a replacement of sand are 72.18, 74.38 and 73.08 respectively. The value of average compressive strength after addition of 5% and 10% fly ash as a replacement of cement are 71.56 and 73.22. The value of average compressive strength after addition of 5% and 10% silica fume as a replacement of cement are 72.33 and 73.53. The value of average compressive strength after addition of 5% and 10% rice husk ash as a replacement of cement are 72.86 and 69.49. At the level of 20% replacement of cement by glass powder meets maximum strength as compared to that of controlled concrete and copper slag high strength concrete.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2007년도 춘계학술논문 발표대회
• /
• pp.51-54
• /
• 2007

This study investigates the properties of paste and mortar from different types and forms of silica fume on cement binder for ultra high strength. Although most Silica Fumes distributed in the market fulfill the KS quality standard, each type showed different levels of loss of ignition. When evaluating cement binder for ultra high strength in a form of paste. Flow, viscosity and moving freely time show great difference depending on the Silica Fume's form and type of primary particle's dispersibility. The evaluation of Silica Fume's dispersibility can be possible with the paste test since there is a high correlation of flow quality between paste and mortar. The compressive strength when using Silica Fume was correlated to the SiO2 content. Synthetically, selecting Silica Fume with the most the ideal primary particle is the key to optimizing the formation for cement binder for ultra high strength.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2014년도 추계 학술논문 발표대회
• /
• pp.113-114
• /
• 2014

Though polymer cement mortar is widely used to repair or reinforce concrete as it has superior adhesion, dense internal structure, chemical resistance, and workability in comparison to those of general cement mortar, studies on its behaviors in high temperature environment such as fire is urgently required. Accordingly, in this experiment, the degrees of reduction in the compressive strength at different temperatures was grasped applying ISO834 Heating Curve, and the effect of polymer content and type on compressive strength could be determined. As a result of this experiment, it is found that polymer type and content have a big effect on reduction of compressive strength in high temperature range, and not only the dynamic characteristics but also the combustion characteristics in high temperature range are required to be studied considering occurrence of a fire in the future.