• 한국초전도학회:학술대회논문집
• /
• v.11
• /
• pp.58-58
• /
• 2001

• Transactions on Electrical and Electronic Materials
• /
• v.5 no.2
• /
• pp.55-60
• /
• 2004

High-temperature Superconductor(HTS) tubes were fabricated in terms of different chemical compositions and various SrSO$_4$additions by centrifugal forming method. For powder melting by induction the optimum range of melting temperatures and preheating temperature were 1050$^{\circ}C$, 1100$^{\circ}C$ and 550$^{\circ}C$ for 30 min, respectively. The mould rotating speed was 1000 rpm. A tube was annealed at 840$^{\circ}C$ for 72 hours in oxygen atmosphere. The plates like grains more than 20 $\mu\textrm{m}$ were well developed along the rotating direction of mould regardless of initial chemical compositions and the amounts of SrSO$_4$in Bi2212. The specimen with Bi2212 composition exhibited T$\_$c/ of 83 K, while the specimens fabricated with other compositions are lower than 60 K. The measured I$\_$c/ and J$\_$c/ at 77 K(B = 0 T) in Bi2212 with 7 % SrSO$_4$ composition were about 680 A and 380 A/$\textrm{cm}^2$.

• Progress in Superconductivity
• /
• v.3 no.2
• /
• pp.198-212
• /
• 2002

The effects of reacted precursors on phase evolution, microstructure, $J_{c}$ and junctional characteristic of the inter-granular contacts were investigated in Ag-sheathed T1-1223 tapes prepared using three kinds of reacted precursors, and compared to those in the tape prepared using an unreacted precursor The precursors were prepared by heat-treating a mixture of Sr-Ba-Ca-Cu-O, $Tl_2$$O_3$, PbO and $Bi_2$$O_3$ powders at $805^{\circ}C$ (precursor I ), $840^{\circ}C$ (precursor II ) and $905^{\circ}C$(precursor III) for 20 min. Tl-1223 phase content, grain size and J\ulcorner in the tapes appeared to increase in an order of precursors I, II and III Compared to tapes prepared using an unreacted precursor, the tapes prewar ed using precursors II and III revealed reduced pore and impurity densities and an enhanced texture. Also characteristic of inter -granular contacts and fraction of strong-links were improved. The improved properties are attributed to enhanced densification resulting from using the reacted precursors.s.

• Progress in Superconductivity
• /
• v.3 no.1
• /
• pp.130-133
• /
• 2001

A multifilamentary Bi-2223 HTS tape for superconducting power applications was studied through the fabrication of 250-meter long tapes by the PIT(powder in tube) process. To fabricate continuous long wire, a drawing machine, a two-drum bull block and a rolled tape winding machine were developed. Especially, 250-meter long tapes were heat treated in the shape of pancake coil to reduce the heat affect zone and to achieve the high critical current. Engineering critical current density was improved through both the enhancements of critical current density by control of thermal process and the increase of filling factor by using thin Ag alloy sheath tubes less than 1.5 mm in thickness. We have made successfully 250-meter long 37 filamentary tapes with high filling factor up to 31 % employing the modified drawing and rolling technique. The critical current of 250-meter long tapes with pancake coil type was measured by transport method at self-field up to 250 gauss of center field. The measured values, based on the transport critical current at self-field, $I_{c}$ -B characteristics and magnetic field analysis, are 34 A of I$_{c}$ and 4.0 $kA/\textrm{cm}^2$ of $J_{e}$ at 250 m, 77 K, and 0 T. We also have achieved the 56 A of I$_{c}$ and 7.0 $0 kA/\textrm{cm}^2$ of$ J_{e}$ in short tapes at 77K, self-field, and 1$mutextrm{V}$/cm.

• Progress in Superconductivity
• /
• v.9 no.1
• /
• pp.62-67
• /
• 2007

The effects of the heat-treatment temperature on the carbon (C) substitution amount, full width at half maximum (FWHM) value, critical temperature ($T_c$), critical current density ($J_c$) have been investigated for 10 wt % malic acid ($C_4H_6O_5$)-doped $MgB_2/Fe$ wires. All the samples were fabricated by the in-situ powder-in-tube (PIT) method and heat-treated within a temperature range of $650^{\circ}C$ to $1000^{\circ}C$. As the heat-treatment temperature increased, it seemed that the lattice distortion was increased by a more active C substitution into the boron sites from the malic acid addition. These increased electron scattering defects seemed to enhance the $J_c-H$ properties in spite of an improvement in the crystallinity, such as a decrease of the FWHM value and an increase of the $T_c$. Compared to the un-doped wire heat-treated at $650^{\circ}C$ for 30 min, the $J_c$ was enhanced by the C doping in a high-field regime. The wire heat-treated at $900^{\circ}C$ resulted in a higher magnetic $J_c$ of approximately $10^4\;A/cm^2$ at 5 K and 8 T.

• 한국초전도학회:학술대회논문집
• /
• v.9
• /
• pp.280-290
• /
• 1999

The microstructures of a Tl$_{0.8}Pb_{0.2}Bi_{0.2}Sr_{1.6}Ca_2Cu_3O_{9+{\delta}}$/Ag tape (tape I ) with J$_c$ of 17,600 A/cm$^2$ at 77 K and 0 T and three Tl$_{0.8}Pb_{0.2}Bi_{0.2}Sr_{1.8}Ba_{0.2}Ca_{2.2}Cu_3O_{9+{\delta}}$/Ag tapes with J$_c$'s of 9,300 (tape II), 16,700 (tape III) and 25,200 A/cm$^2$ (tape IV)prepared using the powder-in-tube method and an in-situ reaction method, were investigated using scanning electron microscopy and high-resolution transmission electron microscopy, and compared each other. ln the tape preparation, an intermediate rolling process was incorporated during final heat-treatment for the last tape, but not for the rest of the tapes. The microstructural analysis revealed clear differences in grain-texturing, crystallographic defects and impurity phases, depending on the chemical composition of the tape. Tendency of directional grain-alignment increased in an order of tapes I, II III and IV. In tape IV, T1-1223 grains are textured, at least in local regions. In crystallographic defects, while stacking faults were prevalent in the former composition, dislocations and voids were frequently observed in the latter. Also impurity phases were appeared to be more abundant in the former than in the latter. The relationship between 1,and the microstructure in the tapes was attempted to explain in a term of grain-linking.

• Progress in Superconductivity
• /
• v.9 no.1
• /
• pp.68-73
• /
• 2007

We fabricated the in-situ $MgB_2$ wires using the powder-in-tube method and investigated the effects of sintering temperature and SiC contents on the microstructure and superconducting properties. Pure $MgB_2$ wires and 5, 10, 20 wt.% SiC doped $MgB_2$ wires were sintered at $600-1000^{\circ}C$ for 30 minutes in Ar atmosphere. We found that $MgB_2$ phase was mostly formed at the sintering temperature of $700^{\circ}C$ and above, and the critical temperature ($T_c$) increased with increasing sintering temperature. For the $MgB_2$ sintered at $850^{\circ}C$, the highest critical current density ($J_c$) was obtained to be $3.7{\times}10^5\;A/cm^2$ at 5 K and 1.6 T by a magnetic properties measurement system (MPMS). The addition of SiC to the $MgB_2$ wires changed microstructure and critical properties. SEM observation showed that the $MgB_2$ core had considerable micro-cracks in undoped wire and the density of micro-cracks decreased with increasing SiC contents. The critical temperature decreased as the SiC contents increased, on the other hand, the critical current density of SiC doped $MgB_2$ wires in high magnetic field was enhanced compared to that of undoped $MgB_2$ wires.