• 소성∙가공
• /
• 제28권3호
• /
• pp.123-129
• /
• 2019

Hypereutectic Al-Si alloys have been widely utilized for wear-resistant components in the automotive industry. In order to expand the application of Hypereutectic Al-Si alloys, the addition of alloying elements forming a stable precipitate at high temperature is required. Thermally stable inter metallic compounds can be formed through the addition of transition elements such as Fe, Ni to Al alloys. However, the amount of transition element to be added to Al alloys is limited due to their low solid solubility. Also, hypereutectic Al-Si-Fe alloys form coarse primary Si phases and needle-shaped intermetallic compounds during solidification in the general casting processes. In this study, the effects of the destruction of Intermetallic compound and Si phase are investigated via hot extrusion. Both the microstructure and mechanical properties are discussed under different extrusion conditions.

• 열처리공학회지
• /
• 제12권3호
• /
• pp.221-230
• /
• 1999

The surface nitrogen permeation of Al alloyed 0.14%C-13%Cr stainless steels was investigated after heat treating at $1050^{\circ}C{\sim}1150^{\circ}C$ in the nitrogen gas atmosphere. The strong affinity between Al and nitrogen permeates the nitrogen through the interior of the steels. Two precipitates of round type and needle type are observed at the surface layer. These precipitates mainly consist of AlN containing plenty of aluminum. The surface layer of 0.53%Al alloyed specimen shows ferrite phase, while the surface layers of 1.65%Al and 2.27%Al alloyed specimens appear ${\gamma}$ plus ${\alpha}$ phases. The depth of nitrogen permeation depends upon the Al content and microstructure of the matrix. The 1.65%Al alloyed specimen representing ${\alpha}+{\gamma}$ matrix phases at the nitrogen permeation temperature shows the maximum case depth in this experiment. Although the surface hardness increases by raising the Al content of the specimen owing to the increase of nitride precipitation density, the nitride precipitation deteriorates the corrosion resistance in the solution of HCl, $H_2SO_4$, and $FeCl_3$.

• 열처리공학회지
• /
• 제19권1호
• /
• pp.10-19
• /
• 2006

Microstructure and morphology of precipitates in $Ni_3Al$- and TiAl-based intermetallics containing carbon have been investigated in terms of transmission electron microscopy(TEM). In an $L1_2$-ordered $Ni_3Al$ alloy with 4 mol.% of chromium and 0.2~3.0 mol.% of carbon, fine octahedral precipitates of $M_{23}C_6$ type carbide were formed in the matrix by aging at temperatures around 973 K after solution annealing at 1423 K. TEM examination revealed that the $M_{23}C_6$ phase and the matrix lattices have a cube-cube orientation relationship and keep partial atomic matching at the {111} interface. After prolonged aging or by aging at higher temperatures, the $M_{23}C_6$ precipitates then adopt a rod-like morphology elongated parallel to the <100> directions. In the $L1_0$-ordered TiAl containing 0.1~2.0 mol.% carbon, TEM observations revealed that needle-like precipitates, which lie only in one direction parallel to the [001] axis of the $L1_0$ matrix, appear in the matrix and preferentially at dislocations. Selected area electron diffraction(SAED) patterns analyses have shown that the needle-shaped precipitate is $Ti_3AlC$ of perovskite type. The orientation relationship between the $Ti_3AlC$ and the $L1_0$ matrix is found to be $(001)_{Ti3AlC}//(001)_{L10\;matrix}$ and $[010]_{Ti3AlC}//[010]_{L10\;matrix}$. By aging at higher temperatures or for longer period at 1073 K, plate-like precipitates of $Ti_2AlC$ with a hexagonal structure are formed on the {111} planes of the $L1_0$ matrix. The orientation relationship between the $Ti_2AlC$ and the $L1_0$ matrix is $(0001)_{Ti2AlC}//(111)_{L10\;matrix}$ and $_{Ti2AlC}//_{L10\;matrix}$.

• 한국식품영양학회지
• /
• 제19권2호
• /
• pp.161-168
• /
• 2006

식물체의 향기성분을 분리하는데 주로 사용되는 headspace(DHS, RPHS)법, SPME법, SDE법, SFE법과 최근에 개발된 PDE법으로 솔잎의 휘발성 성분을 추출하였다. 추출된 성분을 Ge/MS를 이용하여 총 65종의 휘발성 성분을 확인하였다. 확인된 성분은 terpene류 25종, alcoholfb류 16종, carbonyls류 9종, esters류 6종, acids류 7종, esters 화합물이 2종인 것으로 나타났다. Headspace(DHS, RPHS)법과 SPME 법에서는 휘발성이 강한 ethyl acetate, 2-ethyl furan, $\beta$-myrcene 등과 같은 저비점 휘발성 성분들이 많이 추출되었다. 반면에, 고비점 휘발성 성분들인 nerolidol, spathulenol, benzoic acid 등은 휘발 성분 추출시 열이 가해지는 SDE법, SFE법, PDE법 등에서는 확인되었으나 headspace법과 SPME법에서는 확인되지 않았다. 이들 6가지 추출방법에서 저비점 휘발성 성분 분석에는 headspace(DHS)법이 가장 좋은 것으로 나타났으며, 고비점 휘발성 성분 분석에는 SDE법이 가장 적합한 것으로 나타났다. 최근에 개발된 PDE법은 SDE법에 비해 추출효율 변에서 약간 떨어지나 전처리 방법이 간단하므로 짧은 시간에 많은 시료를 분석할 때 가장 적합한 방법인 것으로 판단된다.

• 대한기계학회논문집B
• /
• 제29권11호
• /
• pp.1229-1238
• /
• 2005

The objective of the present study was to investigate the efficacy of physical water treatment (PWT) technologies using different catalytic materials and an electronic anti-fouling device in the mitigation of mineral fouling in a once-through flow system with mini-channel heat exchanger. Effects of flow velocity and water hardness on the effectiveness of PWT technologies were experimentally studied. The artificial water hardness varied from 5.0 to 10 mo1/m$^{3}$ as CaCO$_{3}$. For 10 mo1/m$^{3}$ solution, fouling resistance reduced by 13-40$\%$ depending on flow velocity and types of PWT devices. On the other hand, fouling resistance reduced by 21-29$\%$ depending on the PWT devices for 5 mo11m3 solutions. The PWT device using alloy of Cu and Zn as catalyst (CM2) was slightly more effective than the others. SEM photographs of scale produced from the 10 mol/m$^{3}$ solution at 1.0 m/s indicated that calcium carbonate scales without PWT devices were needle-shaped aragonite, which is sticky, dense and difficult to remove. Scales with the PWT devices showed a cluster of spherical or elliptic shape crystals. Both the heat transfer test results and SEM photographs strongly support the efficacy of PWT technologies using catalytic materials and an electronic anti-fouling device in the mitigation of mineral fouling.

• 한국주조공학회지
• /
• 제22권6호
• /
• pp.281-287
• /
• 2002

In order to investigate the variation of microstructure and property of the Electro-slag Remelted M2 steel, microstructure observation, hardness, and bending test were performed by using optical microscope. SEM/EDS, rockwell hardness tester, charpy impact tester and bending tester, respectively. It was revealed that the number of inclusions and content of gas elements(S, O, N) in M2 steel fabricated by ESR process decreased markedly compared to those of AIM. It seems to be due to refining effect of ESR process. The volume fraction of carbides in quenched and tempered specimens after austenitizing at 1150$^{\circ}C$ and 1240$^{\circ}C$ was measured. The volume fraction of grain boundary carbides were found to be similar for both specimens. However, The volume fraction of carbides in grain decreased with an increase of austenitizing temperature. When specimen was austenitized at 1150$^{\circ}C$, grain boundary carbides showed needle like morphology. But, the carbides were broken with an increase of austenitizing temperature. The specimen austenitized at 1240$^{\circ}C$ showed higher hardness and lower bending strength compared to that of 1150$^{\circ}C$. As expected, toughness increased with sub-zero quenching treatment.

• 한국한의학연구원논문집
• /
• 제16권1호
• /
• pp.43-50
• /
• 2010

Background : The varieties of manifestations referred to headache and vertigo have been long complicated physicians in the efficient diagnosis and treatment of these diseases. Objectives : Establish a distinctive and efficient acupuncture method for the treatment of headache and dizziness based in literature research. Method : We reviewed four Korean medical literature, "治腫指南Guide to Swollen Sore Treatment", "東醫寶鑑Treasured Mirror of Eastern Medicine", "鍼灸經驗方Experiential Prescriptions of Acupuncture and Moxibustion", and "舍岩鍼法Essential Rhymes on Acupuncture and Moxibustion by Master Sa-am", and analyzed the therapeutic characteristics in the treatment of headache and vertigo. Result : 1. "治腫指南Guide to Swollen Sore Treatment" inserted needle in GV20百會 and waited until the skin erupts and heat burns, then applied in those regions affected. 2. "東醫寶鑑Treasured Mirror of Eastern Medicine" mostly applied moxibustion on headache, however, needling acupoints such as GV20百會, GV24神庭, GV23上星, GV22顖會 were also considered important. 3. "鍼灸經驗方Experiential Prescriptions of Acupuncture and Moxibustion" used moxa cones on headache in order to disperse heat and direct Gi downward. 4. "校勘 舍岩道人鍼法Essential Rhymes on Acupuncture and Moxibustion by Master Sa-am" defined the cause of dizziness, wood excavates earth and earth kills water. Conclusions : After previous study on eye, oral, glottal, labial, dental diseases and stroke, we could also find various efficient methods according to headache and vertigo, through literature research of Korean medical classics. This study will concurrently result in establishing distinctive therapeutic method characteristic of Korea.

• 소성∙가공
• /
• 제17권7호
• /
• pp.523-527
• /
• 2008

In this study, mechanical properties of Alloy 718 welded after forgings for jet propulsion component was investigated. Hot-forged and machined work-pieces($230mm\times70mm\times15mm$) which have different grain sizes are welded by electron beam welding technique. After welding, the components were solution heat-treated and aged. Samples were sectioned to analyze the microstructural evolution and formation of micro-crack. It was found that HAZ grain boundary liquation crack generally initiates in the coarse grains rather than the fine grains. Needle-like phases with high Nb contents were found at the outer part near the base metal. Vickers hardness and tensile tests were carried out at room temperature and at $649^{\circ}C$. The tensile properties of electron beam welding specimens exhibited around 100MPa and 10% decrease in strength and elongation, respectively.

• Journal of Acupuncture Research
• /
• 제28권2호
• /
• pp.133-141
• /
• 2011

Objectives : Although the thermo-sensitivity test in Well points in 12 Meridians(井穴知熱感度測定法) has been used for several decades, it is still performed by a manual way, and lack in objectivity consequently. To make it more objective, accurate and convenient test, we have developed a novel system to test thermo-sensitivity in Well points. Methods : To enhance the blindness of the test, we made a shielded system which give heat to some fingers of subjects in random way. To perform the test in quantitative manner, we developed a fully automated, computer-controlled system composed of heating bulbs and response button array. Results : The developed system showed linearity in heating the finger phantom. It also gave acceptable but interesting features in pilot tests with several young adult subjects. Conclusions : By the developed system, we could improve objectivity and convenience of the thermo-sensitivity test in Well points.

• 동력기계공학회지
• /
• 제10권3호
• /
• pp.51-57
• /
• 2006

The effect of grain size on corrosion resistance and high temperature oxidation behavior was studied in 22Cr-15Ni-5W super austenitic stainless steels for desulfurization equipment as a heat power station. In the high temperature oxidation test, oxidation rate was increased as the temperature increased from $600^{\circ}C\;to\;800^{\circ}C$. In vapor, oxidation rate was faster than that in air. Because the vapor was inhibited nucleation of $Cr_2O_3$ film. And the high temperature oxidation resistance at $600^{\circ}C{\sim}800^{\circ}C$ was excellent from all specimens and specimen of the smallest grain size was the most excellent. Because increasing of diffusion course through the grain-boundary was promoted nucleation and growth of $Cr_2O_3$ film. In the test temperature at $600^{\circ}C{\sim}800^{\circ}C$, Cr rich round particle oxide was formed in air, whereas Fe rich needle type oxide was developed in vapor.