Natural graphite is obtained from an abandoned open-cast mine and purified by a simple, eco-friendly and affordable beneficiation process including ball milling and flotation process. Both raw graphite (55 wt %) and its concentrate (85 wt %) were electrochemically tested in order to evaluate these materials as anode materials for Li-ion and Na-ion batteries. It was found that both raw and purified graphites exhibit good electrochemical activities with respect to lithium and sodium ions through completely different reaction mechanisms. The encouraging results demonstrated in this work suggest that both raw and graphite concentrates after flotation could be used respectively for stationary and embedded applications. This strategy would help in developing local electrical storage systems with a significantly low environmental footprint.

• 자원리싸이클링
• /
• 제31권6호
• /
• pp.66-72
• /
• 2022

국내산 인상흑연정광의 리튬이온전지 소재로서 활용을 위해 고강도 혼합기를 이용하여 구형화 실험 후 건식분급을 진행하여 각 산물에 대한 구형화도와 입도를 분석하였다. 3,000 rpm의 로터속도에서는 정광시료와 산물의 입도와 구형화도의 차이가 관찰되지 않았으나, 로터속도를 6,000 rpm, 10,000 rpm 12,000 rpm으로 조절하여 구형화도 실험을 진행한 결과, 로터속도와 구동시간의 증가에 따라 구형화도는 증가하고 입도는 감소하였다. 로터속도 12,000 rpm에서 10분간 구동한 결과, 구형화도는 0.870으로부터 0.936까지 증가하였다. 구형화실험 후 건식분급을 진행하였을 때 조립자의 구형화도는 0.947까지 증가하였고 SEM 결과에서 구형입자가 확인되어 구형화가 성공적으로 이루어졌다고 판단되었다.

• 자원리싸이클링
• /
• 제32권3호
• /
• pp.38-44
• /
• 2023

국내산 흑연정광으로부터 불순물을 제거하기 위해 황산용액 및 수산화나트륨용액을 이용하여 침출실험을 진행하였다. 황산용액과 수산화나트륨용액을 각각 사용하여 침출실험을 진행한 결과, 수산화나트륨과 황산의 농도가 2 mol/L 이상에서 제거효과의 차이가 미미하고, 황산용액침출에서 온도가 증가함에 따라 고정탄소함량이 증가하는 것에 비해 수산화나트륨용액에서는 150℃ 이상에서 큰 차이가 나타나지 않았다. 수산화나트륨용액침출은 2 mol/L NaOH, 200℃, 1시간의 조건으로 선정하고, 황산용액침출은 2 mol/L H₂SO₄, 100℃, 1 시간의 조건으로 선정하여 5회까지 반복하여 침출을 진행하였다. 황산용액침출 후 수산화나트륨용액침출을 5회 반복했을 때 고정탄소는 99.95 %까지 증가하였고, 회분은 0.048 %까지 감소하였다. 수산화나트륨용액침출 후 황산용액침출을 5회 반복한 결과, 고정탄소는 99.98 %, 회분은 0.018까지 감소하여 수산화나트륨용액 침출 후 황산용액침출을 수행한 결과가 다소 높게 나타났다.