• The Korean Journal of Ceramics
• /
• v.6 no.2
• /
• pp.159-163
• /
• 2000

Alumina fibre has been synthesized successfully by sol-gel technique. Boehmite sol was prepared by hydrolyzing aluminium iso-propoxide and peptizing it with nitric acid. The stable sol thus obtained was used for fibre drawing when their viscosity reached the required value as a result of progress of the hydrolyzation and polycondensation reaction. The fibres dried at 11$0^{\circ}C$ for 12 hours were sintered at 1$600^{\circ}C$ for 5 hours. A reasonable sintered density with better microstructure and strength have been attained using 2 wt% of urea, magnesia and silica as sinter additives. Thermal analysis with sintering additives of 2 wt% and phase determination of the heat treated fibres using XRD and FT IR spectra confirms the phase transitions. The observation of surface and cross-section of the fibres were made using SEM. Fibres of uniform circular cross-section is obtained by fixing the shape in a setting solution.

• Journal of the Korean Ceramic Society
• /
• v.32 no.2
• /
• pp.197-208
• /
• 1995

${\gamma}$-LiAlO2 fibers for fiber reinforced molten carbonate fuel cell (MCFC) matrix have been produced from LiAlO2 complex polymeric sols using the sol-gel process. The stable and spinnable LiAlO2 sols could be synthesized by mixing LiNO3 alcohol solutions in aluminum complex polymeric sols prepared through the condensationpolymerization reaction of 1 more of aluminum tri-sec-butoxide with 0.55 mole of mixed chelates (mole ratio of acetylaceton/triethanolamine=0.25/0.3). It was found that the viscosity range for fiber-spinning should be higher than 30 poise. The defect-free flexible ${\gamma}$-LiAlO2 fibers with the average tensile strength of 350 MPa could be obtained when the spinned fibers were heat-treated to 120$0^{\circ}C$ on the specified heating schedule after dried at room temperature.

• International Journal of Industrial Entomology and Biomaterials
• /
• v.27 no.1
• /
• pp.180-184
• /
• 2013

Recently, silk sericin has attracted the attention of researchers owing to its useful properties as a biomaterial including 1) good wound healing and cell activities, 2) fast gelation character, and 3) high water retention property. In the present study, silk sericin was prepared using different extraction times in hot water and the effect of extraction time on the rheological properties of sericin solutions and gels was examined. It was found that the production yield of sericin increased with extraction time. The shear viscosity of sericin solutions and gels decreased with increasing extraction time due to a decrease in sericin molecular weight. When the sericin solution transformed to a gel, the viscosity increased and the shear thinning behavior was more evident. In addition, the shear stress measurements indicated that the slip between the sericin samples and the measuring plate of the rheometer was increased by the gelation of sericin. The compression strength of sericin gel could be increased remarkably (by more than 100 fold) by preparation using the freezing and thawing method.

• Journal of the Korean Ceramic Society
• /
• v.46 no.6
• /
• pp.653-656
• /
• 2009

Alumina bushing used for manufacturing glass fiber was fabricated by gel-casting which can fabricate complex forms. When solid loading is increased, density was increased and shrinkage and absorption were decreased. The sample loading with 57 vol% solid was optimum for alumina suspension, which showed the best physical properties. The cast sample was sintered at $1550{^{\circ}C}$ for two hours with sintering additive, $Y_2O_3$. The result showed that the alumina bushing with $Y_2O_3$ sintering additive has a density of 98%, shrinkage of 11% and bending strength of 196 kg/$cm^2$.

• Electrical & Electronic Materials
• /
• v.10 no.1
• /
• pp.61-67
• /
• 1997

We have studied dielectric properties of sol-gel derived tantalum oxide thin films as the insulators. As the sample is annealed from 300.deg. C to 700.deg. C, it is found amorphous below 600.deg. C and crystalline over it. Dielectric constant is maximum(18.6) when Ta$_{2}$O$_{5}$ film was annealed at 400.deg. C. It is found that dielectric strength in Ta$_{2}$O$_{5}$ film annealed at 400.deg. C (1.5MV/cm) increases and then decreases over annealed at 500.deg. C. This phenomenon was attributed to pinhole effect and crystallization. The de conduction properties can be interpreted by Poole-Frenkel effect.ect.

• Proceedings of the PSK Conference
• /
• 2003.10b
• /
• pp.235.2-235
• /
• 2003

To develop the buccal delivery system of rhEGF for the treatment of buccal mucosal ulcer, polymer films and hydrogels were investigated. Methods: Hydrogels for thermosenstive sol/gel systems were prepared by the cold method (Schmolka, 1972). And mucoadhesive films were prepared by mixing sod. alginate/polycarbophil 974p. To find an optimum buccal mucosal adhesive gel or film, the gel strength of the poloxamer and sod. alginate/polycarbophil 974p hydrogels were determined by the Simple Rheology Method and their mucoadhesiveness were measured by the Instron (M 4400, Instron Co., U.S.A.) method. (omitted)

• Journal of the Korean Ceramic Society
• /
• v.36 no.8
• /
• pp.829-834
• /
• 1999

The silica aerogels opacified via adding oxides were prepared by the sol-gel supercritical drying technique and their characteristics of mechanical strength and thermal conduction were investigated. The compressive strength of SiO2-10 mol% TiO2 and SiO2-10mol% Fe2O3 aerogels were 0.11 and 0.047 MP a respectively much higher than 0.025 MPa of pure silica aerogels. The thermal conductivity of silica aerogels opacified by TiO2 was as low as 0.02505 W/m${\cdot}$K at $400^{\circ}C$ It was found that the TiO2 -opacifier for improving mechanical strength and suppressing high temperature conduction of pure silica aerogels was more effective than the Fe2O3 -opacifier

• Food Science of Animal Resources
• /
• v.35 no.6
• /
• pp.841-846
• /
• 2015

This study was investigated to determine the effect of microbial transglutaminase (MTG) with or without red bean protein isolate (RBPI) on the porcine myofibrillar protein (MP) gel functionality at different pH values (pH 5.75-6.5). Cooking yield (CY, %), gel strength (GS, gf), differential scanning calorimetry (DSC), and scanning electron microscopy (SEM) were determined to measure gel characteristics. Since no differences were observed the interaction between 1% RBPI and pH, data were pooled. CY increased with the addition of 1% RBPI, while it was not affected by pH values. GS increased with increased pH and increased when 1% RBPI was added, regardless of pH. There were distinctive endothermic protein peaks, at 56.55 and 75.02℃ at pH 5.75, and 56.47 and 72.43℃ at pH 6.5 in DSC results, which revealed decreased temperature of the first peak with the addition of 1% RBPI and increased pH. In SEM, a more compact structure with fewer voids was shown with the addition of 1% RBPI and increased pH from 5.75 to 6.5. In addition, the three-dimensional structure was highly dense and hard at pH 6.5 when RBPI was added. These results indicated that the addition of 1% RBPI at pH 6.5 in MTG-mediated MP represent the optimum condition to attain maximum gel-formation and protein gel functionality.

• Applied Chemistry for Engineering
• /
• v.5 no.3
• /
• pp.443-450
• /
• 1994

Polyelectrolytes of various ionization degrees, which are prepared by neutralization of poly(acrylic acid)(PAA), were crosslinked by ethylane glycol diglycidyl ether(EGDE) in aqueous solution. $C_{gel}$, the minimum polymer concentration at which gelation occurs, was higher than expected. $C_{gel}$ was comparable with that of neutral polymer. This is considered to be due to the size contraction of polyelectrolyte, which comes from ionic strength increase as polymer concentration is increased. $C_{gel}$ is low when molecular weight of the sample becomes high. It reveals that polyelectrolyte is crosslinked in coil form not in extended rod form. This behavior is similar to the crosslinking of neutral polymers. Polyelectrolytes of partially ionized sample generally follow the behavior of fully ionized polyelectrolyte. Polyelectrolyte with added salt was also studied. Considering the pH dependence of EDGE reactivity it was difficult to compare the system which differs in pH significantly.

• International Journal of Concrete Structures and Materials
• /
• v.3 no.2
• /
• pp.97-101
• /
• 2009

It has been known that acid-resistant concretes on the liquid glass basis have high porosity (up to 18${\sim}$20%), low strength and insufficient water resistance. Therefore they can not be used as materials for load-bearing structural elements. Significant increasing of silicate matrix strength and density was carried out by incorporation of special liquid organic alkali-soluble silicate additives, which block of superficial pores and reduces concrete shrinkage deformation. It was demonstrated that introduction of tetrafurfuryloxisilane additive sharply increases strength, durability and shock resistance of silicate polymer concrete in aggressive media. This effect is attributable to hardening of contacts between silicate binder gel globes and modification of alkaline component owing to "inoculation" of the furan radical. The optimal concrete composition with the increased strength, chemical resistance in the aggressive environments, density and crack resistance was obtained.