• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2008년도 추계학술대회 논문집
• /
• pp.304-307
• /
• 2008

In order to evaluate the effect of permanent softening behavior on springback prediction, 2D-draw bending simulations were compared with experiments for friction stir welded DP590 steel sheets. To account fur the nonlinear hardening behavior, the combined isotropic-kinematic hardening law was utilized with and without considering the permanent softening behavior during reverse loading. Also, the non-quadratic orthotropic yield function, Yld2000-2d, was used to describe the anisotropic initial-yielding behavior of the base sheet while anisotropic properties of the weld zone were ignored for simplicity.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2005년도 춘계학술발표대회 개요집
• /
• pp.384-386
• /
• 2005

Initial oxide layer on the butt surface fragments during friction stir welding (FSW) and then often remains as a faint zigzag-line pattern on the cross section. When remnant of the oxide layer often adversely affects the mechanical properties in the weld, it is called as 'kissing-bond'. The present study systematically examines effect of oxide array on bend property in the root of friction stir (FS) welded Al alloy 1050 by transmission electron microscopy (TEM), and then clarifies identity of the kissing-bond.

• 대한기계학회논문집A
• /
• 제38권12호
• /
• pp.1317-1323
• /
• 2014

본 연구의 목적은 마찰교반용접된 Al7075-T651의 피로균열전파 거동에 미치는 시험편의 채취방향의 영향을 고찰하기 위한 것이다. 피로균열전파 실험은 마찰교반용접된 공시재로부터 모재와 용접재에 대하여 CT 시험편을 채취하여 일정응력확대계수범위 제어하에서 수행되었다. 균열이 용접선에 수직하여 전파하는 것(TL 시험편으로 명명)과 균열이 용접선과 나란히 전파하는 시험편(LT 시험편으로 명명)에 대하여 3가지 다른 응력확대계수범위에서 실험이 수행되었다. 시험편의 채취 방향에 따라 피로균열전파거동에 주요한 영향을 미침을 알 수 있었다. Paris 법칙에 적합시킨 결과 지수 m값은 WM-LT 시험편이 3.56으로 가장 높게 나타났다.

• 대한기계학회논문집A
• /
• 제37권9호
• /
• pp.1109-1116
• /
• 2013

본 연구의 목적은 마찰교반용접된 7075-T651 알루미늄 합금 용접부에 대한 피로균열전파율의 공간적 불규칙성을 고찰하기 위한 것이다. 본 연구에서는 이전의 피로균열전파 실험 데이터를 활용하였다. 피로균열전파율의 공간적 불규칙성을 명확히 이해하기 위하여, 피로균열전파 실험은 일정 응력확대 계수범위 제어하에서 수행되었다. 재질, 즉 마찰교반용접된 7075-T651 알루미늄 합금 용접부의 용접재와 모재에 대하여 피로균열전파율의 공간적 불규칙성을 조사하기 위하여 실험 데이터가 해석되었다. 결론적으로 용접재의 변동성이 모재의 변동성보다 높게 나타났으며, Weibull 통계 해석에 의하여 변동성을 평가할 수 있음을 알았다.

• Metals and materials international
• /
• 제24권6호
• /
• pp.1232-1240
• /
• 2018

Corrosion properties of dissimilar friction stir welded 6061 aluminum and HT590 steel were investigated to understand effects of galvanic corrosion. As cathode when coupled, HT590 was cathodically protected. However, the passivation of AA6061 made the aluminum alloy cathode temporarily, which leaded to corrosion of HT590. From the EIS analysis showing Warburg diffusion plot in Nyquist plots, it can be inferred that the stable passivation layer was formed on AA6061. However, the weld as well as HT590 did not show Warburg diffusion plot in Nyquist plots, suggesting that there was no barrier for corrosion or even if it exists, the barrier had no function for preventing and/or retarding charge transport through the passivation layer. The open circuit potential measurements showed that the potential of the weld was similar to that of HT590, which lied in the pitting region for AA6061, making the aluminum alloy part of the weld keep corrosion state. That resulted in the cracked oxide film on AA6061 of the weld, which could not play a role of corrosion barrier.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2003년도 추계학술대회
• /
• pp.1747-1751
• /
• 2003

The paper shows properties such as vickers hardness, yielding and ultimate stresses for the weld zone of the butt and the lap jointed specimens, and compare maximum loads, stress-strain curves, deformation appearance after guided bending test and fracture appearance for butt and lap jointed specimens. The research in this experiment also shows the weldability of the butt joint specimen is better than that of the lap joint specimen using FSW with $2mm^{t}$ aluminum alloy sheet in milling machine.

• Journal of Welding and Joining
• /
• 제32권5호
• /
• pp.50-57
• /
• 2014

Friction Stir Welding (FSW) is a complex process with several mutually interdependent parameters. A slight difference from known settings may lead to imperfections in the stirred zone. These inhomogeneities affect on the mechanical properties of the FSWed joints. In order to prevent the failure of the welded joint it is necessary to detect the most critical defects non-destructive. Especially critical defects are wormhole and lack of penetration (LOP), because of the difficulty of detection. Online thermography is used process-accompanying for defect detecting. A thermographic camera with a fixed position relating to the welding tool measures the heating-up and the cool down of the welding process. Lap joints with sound weld seam surfaces are manufactured and monitored. Different methods of evaluation of heat distribution and intensity profiles are introduced. It can be demonstrated, that it is possible to detect wormhole and lack of penetration as well as surface defects by analyzing the welding and the cooling process of friction stir welding by passive online thermography measurement. Effects of these defects on mechanical properties are shown by tensile testing.

• International Journal of Advanced Culture Technology
• /
• 제3권1호
• /
• pp.145-152
• /
• 2015

The article aims to apply a friction stir spot welding for producing the lap joint between AA5052 aluminum alloy and C11000 copper alloy. The dimension of the materials was 100 mm in length, 30 mm in width and 1.0 mm in thickness. The copper plate was set overlap the aluminum plate by 30 mm. The welding parameter was the rotating speed of 2500-4000 rpm, the pin inserting rate of 2-8 mm/min and the holding time of 6 sec. The mechanical properties test and the microstructure investigation were performed to evaluate the lap joint quality. The summarized results are as follows. The friction stir spot welding could produce effectively the lap joint between AA5052 and C11000 copper. Increase of the rotating speed and holding time directly affected to decrease the tensile shear strength of the lap joint. The optimized welding parameters in this study that indicated the tensile shear strength of 864 N was the rotating speed of 3500 rpm, the pin inserting rate of 6 mm/min and the holding time of 4sec. The experimental results also showed that the hardness of the weld metal was lower than that of the base materials.

• 동력기계공학회지
• /
• 제17권4호
• /
• pp.86-93
• /
• 2013

This paper deals with the effects of driving force and material properties on statistical distribution of fatigue crack growth rate (FCGR) for the friction stir welded joints of Al 7075-T651 aluminum plate. In this work, the statistical probability distribution of fatigue crack growth rate was analyzed by using our previous constant stress intensity factor range controlled fatigue crack growth test data. As far as this study are concerned, the statistical probability distribution of fatigue crack growth rate for the friction stir welded (FSWed) joints was found to evaluate the variability of fatigue crack growth rate for base metal (BM), heat affected zone (HAZ) and weld metal (WM) specimens. The probability distribution of fatigue crack growth rate for FSWed joints was found to follow well log-normal distribution. The shape parameter of BM and HAZ was decreased with increasing the driving force, however, the shape parameter of WM was decreased and increased with increasing the driving force. The scale parameter of BM, HAZ and WM was increased with the driving force.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.522-527
• /
• 2002

The microstructure and mechanical properties of friction stir welded OFC plates with 2mm in thickness were examined with the changing welding parameters such as welding speed, rotation speed in this study. The sounding welding conditions was acquired at the optimum welding conditions of the 41mm/min to 61mm/min of welding speed at 1250 rpm of rotation speed. The microstructure of weld zone was divided into four parts such as the base metal region (EM), thermal mechanical affected zone (TMAZ), heat affected zone (HAZ), stir zone (SZ). The grain size in the SZ and the width of weld nugget were increased with increasing welding speed. The hardness profiles of the base metal were distributed about 80HV. The HAZ is a slightly softened region of about 60~75 HV relative to the base metal. The hardness profiles of the SZ were higher than that of base metal. The tensile strength was increased with increasing welding speed. In case increasing rotation speed, tensile strength was decreased. The maximum tensile strength was about 220:MPa which was 110% of joint efficience of that of base metal at 41mm/min of welding speed, 1250rpm of rotation speed.