• KSTLE International Journal
• /
• v.6 no.2
• /
• pp.39-44
• /
• 2005

Friction and wear properties of the Boron carbide ($B_{4}C$) coating 100 nm thickness were studied under various relative humidity (RH). The boron carbide film was deposited on silicon substrate by DC magnetron sputtering method using $B_{4}C$ target with a mixture of Ar and methane ($CH_4$) as precursor gas. Friction tests were performed using a reciprocation type friction tester at ambient environment. Steel balls of 3 mm in diameter were used as counter-specimen. The results indicated that relative humidity strongly affected the tribological properties of boron carbide coating. Friction coefficient decreased from 0.42 to 0.09 as the relative humidity increased from $5\%$ to $85\%$. Confocal microscopy was used to observe worn surfaces of the coating and wear scars on steel balls after the tests. It showed that both the coating surface and the ball were significantly worn-out even though boron carbide is much harder than the steel. Moreover, at low humidity ($5\%$) the boron carbide showed poor wear resistance which resulted in the complete removal of coating layer, whereas at the medium and high humidity conditions, it was not. X-ray photoelectron spectroscopy (XPS) and Auger electron spectroscopy (AES) analyses were performed to characterize the chemical composition of the worn surfaces. We suggest that tribochemical reactions occurred during sliding in moisture air to form boric acid on the worn surface of the coating. The boric acid and the tribochemcal layer that formed on steel ball resulted in low friction and wear of boron carbide coating.

• Journal of Advanced Marine Engineering and Technology
• /
• v.23 no.4
• /
• pp.440-446
• /
• 1999

This study is mainly concerned with the friction and wear properties for the specimens of crank shaft which are made of ductile cast iron. The friction and wear tests were carried out for the nor-malized ductile cast iron specimens and their properties were compared with each other at reheat-ing temperatures(550^{\circC,\; 600^{\circ}C,\; 650^{\circ}$) and in dry condition at different friction velocity(0.94 m/s 1.88m/s 2.83m/s) range. After austenized at $910^{\circ}C$ it is observed that the higher the reheating temperature is the hardness becomes decrease which is supposedly attributed to the fact that the amount of pearlite austenite matrix is rduced by reheating after normalizing and that as the reheating temperature goes up the pearlite generated is less and the interval between the pearlites were widened at last to make pearlite globular. At the low velocity the friction coefficient increase in the beginning and gets stabilized as the sliding distance increases. As the friction velocity grows the friction coefficient decreases suppos-edly since the abrasive wear is heavier at low velocity than at the high velocity as the friction tem-perature at low velocity is lower than at high velocity.

• Journal of the Korean institute of surface engineering
• /
• v.43 no.6
• /
• pp.278-282
• /
• 2010

In this research, the friction and wear characteristic behaviors of coating materials of TiAlN and CrAlN were investigated. The wear test was conducted in air and un-lubricated state using the reciprocating friction wear tester. Temperature were 50 and $120^{\circ}C$, and load were 3, 7, and 11 kgf for tests. By comparing the coefficient of friction and observing the wear microstructure, the friction and wear characteristic behaviors of TiAlN and CrAlN coating layers on SKD61 were investigated. The coefficient of friction of CrAlN coating was lower than that of TiAlN at all conditions. Therefore, CrAlN was suggested to be more advantageous coating than TiAlN for the extrusion mold of aluminum.

• Journal of the Korean Society for Precision Engineering
• /
• v.21 no.12
• /
• pp.167-173
• /
• 2004

Recently, it has been reported that frictional behavior at nanometer scale can be different from that at macro scale. In this article, friction and wear tests were conducted using an AFM to investigate the effect of real contact area on the coefficient of friction and wear property. SiO$_2$, Hica, and SiGe were used in friction test and the AFM tip was Si$_3$N$_4$. The real contact area between an AFM tip and flat surface was calculated by the Johnson-Kendall-Roberts (JKR) theory. Wear specimen was Mica, and the diamond tip was used. We found that the coefficient of friction is constant below a critical area, but it is degraded over the area. Moreover, it is found that wear depth increased rapidly from a certain load and was degraded as a function of the number of the scanning cycles. Also, the range of scanning velocity used in this study had little effect on the wear depth.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.33 no.10
• /
• pp.1125-1131
• /
• 2009

O-rings are commonly used in machines as a seal. Due to prolonged use the surface of an O-ring can degrade which can lead to leakage as well as contamination. Damage of O-rings used in vacuum applications such as sputter is caused by various mechanisms. Particles detached from the O-ring may cause significant problems on the performance of the system in the vacuum chamber. Therefore, understanding the tribological behavior of O-rings is important to tackle the damage caused by repeated contact. In this work, FKM rubber was used for friction and wear tests conducted to investigate the tribological behavior of O-rings. A reciprocating type of a tribo-tester was used for the tests. The friction coefficient between the steel ball and the FKM specimen was quite high. Also, in order to identify the wear behavior, the surface of the FKM specimen was characterized using both optical and scanning electron microscopes. Evidence of wear due to adhesion and extrusion could be found. The results of this work will aid in improving the durability of O-rings.

• Tribology and Lubricants
• /
• v.23 no.1
• /
• pp.14-18
• /
• 2007

SCM415 alloy was implanted with nitrogen ions using plasma source ion implantation (PSII), at a dose range of $1{\times}10^{17}\;to\;6{\times}10^{17}N^{+}cm^{-2}$. Auger electron spectrometry (AES) was used to investigate the depth profile of the implanted layer. Friction and wear tests were carried out on a block-on-ring wear tester. Scanning electron microscopy (SEM) was used to observe the micro-morphology of the worn surface. The results revealed that after being implanted with nitrogen ions, the frictional coefficient of the surface layer decreased, and the wear resistance increased with the nitrogen dose. The tribological mechanism was mainly adhesive, and the adhesive wear tended to become weaker oxidative wear with the increase in the nitrogen dose. The effects were mainly attributed to the formation of a hard nitride precipitate and a supersaturated solid solution of nitrogen in the surface layer.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1997.10a
• /
• pp.183-190
• /
• 1997

The wear behaviors of $Al_2O_3-40%TiO_2$ deposited on casting aluminum alloy(ASTM A356) by plasma spray against SiC ball have been investigated experimentally. Friction and wear tests are carried out at room temperature. The friction coefficient of $Al_2O_3-40%TiO_2$ coating is lower than that of pure $Al_2O_3$ coating(APS). It is found that low friction correspond to low wear and high friction to high wear in the experimental result. The thickness of $Al_2O_3-40%TiO_2$ coatings indicated the existence of the optimal coating thickness. It is found that a voids and porosities of coating surface result in the crack generated. As the tensile stresses in coating increased with the increased friction coefficient. The columnar grain of coating will be fractured to achieve the critical stress. It is found that the cohesive of splats and the porosity of surface play a role in wear characteristics. It is suggested that the mismatch of thermal expansion of substrate and coating play an important role in wear performance. Tensile and compressire under thermo-mechanical stress may be occurred by the mismatch between thermal expansion of substrate and coating. This crack propagation above interface is observed in SEM.

• Journal of the Korean institute of surface engineering
• /
• v.44 no.6
• /
• pp.233-238
• /
• 2011

The friction and wear characteristics of CrN and TiN coatings on SKD61 which is mold material using for extrusion of AZ80 magnesium alloy were investigated. The coatings were deposited by the arc ion-plating method, and the thickness were about $3.59{\mu}m$ and $3.28{\mu}m$, respectively. Reciprocating friction wear tests were conducted by varying pin load and temperature of counter substrate at un-lubricated condition. The pin loads were 11, 15 and 19 kgf, and the substrate temperatures were room temperature and $120^{\circ}C$. CrN coating which has a lower friction coefficient and a smaller adhesive wear with AZ80 magnesium alloy showed better wear resistance than TiN coating.

• Tribology and Lubricants
• /
• v.16 no.3
• /
• pp.173-181
• /
• 2000

Friction, wear and corrosion characteristics of various MoS$_2$ bonded film lubricants were investigated to apply them to automotive wheel joints. MoS$_2$ bonded film lubricants were formulated by combinations of several additives and binders, and they were coated onto the pre-treated surfaces of specimens. Friction and wear characteristics were evaluated with Falex pin & vee-block test and LFW-1 block-on-ring test. For the corrosion resistant characteristics of the films, salt solution spray corrosion tests were performed. Results showed that MoS$_2$ bonded films containing both inorganic and organic corrosion-resistant additives yielded a synergy effect on anti-corrosion resistance. Also, binders having the better water-proof and thermal stability showed the lower friction and higher corrosion resistance.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.10 no.6
• /
• pp.89-94
• /
• 2011

The wear characteristics between nonmetal and metals have been investigated using a disc on disc system. The specimens of nonmetal are made by the nylon and teflon materials. The specimens of the metal are used as eight kinds of along their hardness. The kinds of metals are copper(Hv96), aluminum(Hv186), brass(Hv234), aluminum bronze(Hv294), stainless steel(Hv327), annealing mild steel(Hv345), mild steel(Hv372), Hard steel(Hv434). In this study, a upper and lower specimens have been used the same size and shape. Using experimental data we figured the relationship between friction coefficient of nonmetal and metals. We figured the relationship between friction temperature of nonmetal and metals. The result had been verified a wear characteristics of nonmetal and metals in the wear tests.