• 한국농공학회:학술대회논문집
• /
• 한국농공학회 2002년도 학술발표회 발표논문집
• /
• pp.153-156
• /
• 2002

The purpose of this research was to evaluate on the properties of fresh and hardened high-performance concrete(HPC) incorporating high-reactivity metakaolin(HRM). Setting time, heat of hydration, compressive strength, resistance to chloride-ion penetration, and repeated freezing and thawing test were carried out in order to investigate the properties of fresh and hardened state concrete. The properties of the HRM concrete were also compared with those of the portland cement concrete and silica fume(SF) concrete. The laboratory test results indicate that HRM material can be used as a supplementary cementitious material to produce high-performance concrete.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2003년도 봄 학술발표회 논문집
• /
• pp.775-780
• /
• 2003

The propose of this study is to discover concrete secondary products for proper mixing by lightweight concrete. The standard of water ratio 50% and weight substition 0%, 10%, 20% by Fly-ash. When produce manufactures, there use for maintain its form weight substition and addition among the viscosity agent each Silica-fume and Hydroxy propyl methyl cellulos. Testing method was to operate slump, air content, compressive strength test, rapid freezing and thawing test. The result of this study is appeared when substition Fly-ash generally it had better use Silica-fume.

• 콘크리트학회논문집
• /
• 제19권5호
• /
• pp.639-646
• /
• 2007

본 연구에서는 환경에 유해한 휘발성 유기화합물 (VOC)을 사용하지 않은 나노합성 세라믹 도장재를 도포한 콘크리트의 내구성 증진 효과를 평가하기 위하여 건조상태 부착강도 실험, 습윤상태 부착강도 실험, SEM 촬영, MIP 분석, 탄산화 촉진 실험, 전기적 촉진법에 의한 염소이온 확산실험, 동결융해에 대한 저항성, 내알칼리 실험 및 내염수성 실험을 실시하여 기존의 표면처리제와 비교 평가하였다. 부착강도 측정 결과 나노합성 세라믹 도장재가 건조상태 및 습윤상태에서 가장 이상적인 결과를 나타내었는데 이는 가수분해와 중축합반응을 통하여 무기질계 세라믹 구조를 형성한 나노합성 세라믹이 콘크리트 내의 C-A-S (calcium silicate aluminate)나 C-S-H (calcium silicate hydrate)와 같은 수화물과의 수소결합을 통해 콘크리트 표면과 일체화되어 나타난 결과로 판단된다. 또한 SEM 및 MIP 분석의 결과를 통해 미세한 공극을 가진 표면 조직을 보여주었다. 그리고 탄산화 및 염소이온 확산 실험과 동결융해 저항성에서 기존의 유기도장재를 능가하는 결과를 보였으며 내알칼리성 및 내염수성 실험에서도 좋은 성능을 나타내었다. 이상의 결과를 통해 기존의 휘발성 유기화합물을 사용하는 유기도장재의 대안으로써 해안 구조물, 하수 처리장 등 콘크리트 구조물의 내구성 향상을 위한 나노합성 세라믹 도장재의 사용이 기대된다.

• 헤리티지:역사와 과학
• /
• 제44권3호
• /
• pp.78-91
• /
• 2011

일본 우스키 석불군의 주요 구성암석은 용결응회암으로 암회색을 띠며 렌즈상 피아메가 발달되어 있고 부분적으로 암편을 함유하고 있다. 이 암석은 대체로 장석 및 불투명 광물 등으로 이루어진 기질에 석영과 장석 반정이 관찰되며 강용결에서 약 또는 미 용결까지 다양한 산출상태를 보인다. 또한 지하수에 의한 염류 석출, 동결 파쇄 등 다양한 풍화요인에 의해 강도가 저하된 상태이다. 이 암석의 용결 및 풍화상태에 따라 보존처리제의 표면처리 실험 결과, 흡수율은 발수제가 강화제에 비해 높은 감소를 보이며 강화제 중에서는 OH 100이 높은 감소율을 보인다. 초음파속도는 전체적으로 KSE 300과 OH 100이 비슷한 강도증가를 보이며 에코팁 표면경도는 모든 시료에서 KSE 300이 높은 경도증가를 나타냈다. 색변화는 강화제가 발수제에 비해 적었으며 발수제 SNL은 표면색의 변화가 현저하므로 주의가 요구된다. 동결-융해 실험 결과, 미처리 시료에 비해 KSE 300으로 처리한 시료가 균열 및 깨짐 등에 대한 풍화 저항성이 가장 높은 것으로 나타났다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2006년도 춘계 학술발표회 논문집(II)
• /
• pp.329-332
• /
• 2006

This paper presents the experimental results for durability of an ECC designed with ground granulated blast furnace slag (BFS) through the test method of chloride ion resistance and freezing-thawing resistance. In order to compare with ECC, normal mortar was also tested. Test results showed that BFS ECC exhibited higher durability performance than ordinary mortar. These results suggest that by adding BFS in ECC, its matrix density is increased which results in decreased of deterioration and it also adds to the fiber bridging that contributes in control of cracking.

• 콘크리트학회논문집
• /
• 제20권5호
• /
• pp.653-660
• /
• 2008

본 연구는 펄라이트를 이용한 흡음재료의 흡음성능을 개선시키기 위한 최적배합에 대한 분석을 실시하였다. 결합재로서 폴리머 시멘트 슬러리와 무기질 결합재를 사용하여 흡음재료를 각종 배합조건에 따라 제작하여, 강도, 동결 융해 저항성, 그리고 흡음성능에 대하여 실험을 실시하였다. 실험 결과, 관내법에 의한 흠음재의 흠음계수는 배합에 따라 약간의 차이가 있으나 폴리머 디스퍼션을 결합재로 사용한 경우 흡음재의 감음계수 (NRC)는 $0.48{\sim}0.51$로 시멘트만 결합재로 사용한 경우에 비해 약간 크게 나타났으나, 방음벽의 환경부 고시 기준에서의 흡음재로서 감음계수 0.70에 비하면 낮은 수치이다. 그러나 잔향실법에 의한 흡음용 패널의 저주파수 영역($250\;Hz{\sim}500\;Hz$)에서 흡음계수가 $0.84{\sim}1.00$로 매우 높게 나타났으며, 고주파 영역에서도 $0.57{\sim}0.77$ 정도로 비교적 높은 흡음률을 나타내 감음계수가 0.77로 높게 나타났다. 폴리머 디스퍼션을 결합재로 사용한 흡음재는 압축강도, 휨강도 및 동결융해 저항성 등에서 방음벽 재료로서 적당한 성능을 발휘하였으며, 성능과 가격면에서 밸런스를 확보할 수 있는 배합을 도출할 수 있었다.

• Corrosion Science and Technology
• /
• 제16권3호
• /
• pp.141-150
• /
• 2017

Impregnating with quality silicone water repellent on the concrete surface is an effective method of protecting concrete. Quality silicone water repellent has been widely used in the engineering profession because of its desirable properties such as hydrophobicity, keeping concrete breathable and preserving the original appearance of the concrete. The companies in China that produce silicone water repellent are listed. Test methods in the specifications or standards about silicone water repellent in China are summed. The test methods relative to durability of concrete impregnated with silicone water repellent (such as resistant to chloride ion penetration, resistant to alkali, resistance to freezing and thawing and weatherability etc.) and the constructive quality (such as water absorption rate, impregnating depth and the dry velocity coefficient etc.) are compared and analyzed. The results indicate that there are differences among test methods relative to different specifications with the same index and therefore, confusion has ensued when selecting test methods. All test methods with the exception of the method of water absorption rate by using a Karsten flask are not non-destructive methods or conducted in a laboratory. Finally, further research on silicone water repellent during application is proposed.

• Clinical and Experimental Reproductive Medicine
• /
• 제25권2호
• /
• pp.129-134
• /
• 1998

본 연구는 인간 전핵기 수정란의 동결시 election microscope grid론 사용하는 초급속 동결방법이 유용하는지 여부를 조사하고자 실시하였다. 본 실험에서는 인간 IVF 시술시 생성되는 다-전핵기 (>2PN) 수정란을 정상 2PN 수정란 대신 사용하였으며, 또한 이들은 3PN과 $\geq4PN$ 수정란으로 나누어 전핵의 수에 따른 냉해와 융해 후 체외 배발달율을 조사하였다. 동해제는 30% ethylene glycol, 18% ficoll, 0.5 M sucrose와 10% FBS 등이 D-PBS에 첨가되어 제작된 EFS30을 사용하였다. 본 연구에서 얻어진 결과는 다음과 같다. 초급속동결-융해 후, 인간 다-전핵기 수정란의 생존율은 85.5%였다. 대조군과 동결군의 난할율을 진핵의 수에 따가 니누어 비교하였을 때, 각 군간에는 유의한 차이를 나타내지 않았다 (3PN; 81.3%와 85.4%, $\geq4PN$; 90.0%와 95.7%). 또한, 융해 후 체외발달율을 조사하였던바, $\geq4PN$수정란에서는 동결군 (4.5%)의 체외발달이 대조군 (44.4%)보다 유의하게 낮게 나타났던 반면, 3PN 수정란에서는 동결군 (22.0%)의 결과가 대조군 (38.5%)에 비해 유의한 차이를 나타내지 않았다. (p<0.05). 따라서 인간 다-전핵기 수정란은 EM grid와 EFS30 동결액을 이용한 초급속 동결로 배발달을 유도할 수 있다는 것을 알 수 있었다.

• 대한토목학회논문집
• /
• 제1권1호
• /
• pp.9-19
• /
• 1981

고강도(高强度)콘크리트의 제조방법중(製造方法中) 가장 대표적(代表的)이고 실용적(實用的)인 것으로 고성능감수제(高性能減水劑)와 고온고압양생(高溫高壓養生)에 의(依)한 방법등(方法等)이 있다. 본연구(本硏究)에서는 이와같은 고강도(高强度)콘크리트로 만든 콘크리트 Pile을 원심력성형(遠心力成形)과 손다짐으로 만들어 각각(各各)에 대(對)하여 Autoclave 양생(養生), Steam 양생후(養生後) 수중(水中) 14일(日) 양생(養生) 및 표준수중양생(標準水中養生)하여 동결융해시험(凍結融解試驗)을 하였으며 각종(各種)에 대(對)하여 내구성(耐久性)의 상관적(相關的)인 관계(關係)를 규명하였다. 이들 공시체(供試體)들의 동결융해(凍結融解)에 대(對)한 내구성(耐久性)은 일반적(一般的)으로 적당량(適當量)의 공기량(空氣量)을 함유(含有)하고 있을 때 상기(上記) 여러 가지 양생(養生)에 대(對)하여 비교적(比較的) 충분(充分)한 내구성(耐久性)이 있는 것으로 판명(判明)되었으나 AE제(劑)를 사용(使用)하지 않은 경우에는 Autoclave 양생(養生)한 고강도(高强度)콘크리트는 타양생(他養生)한 고강도(高强度)콘크리트보다 강도면(强度面)에서는 높았으나 동탄성계수(動彈性係數)가 좀 낮았고 시험후(試驗後)의 내구성계수(耐久性係數)도 극(極)히 약(弱)하였다. 그러나 원심력성형(遠心力成形)한 non AE 콘크리트 Pile은 표준양생(標準養生)하였을 때 내구성계수(耐久性係數)가 100 이상(以上)이었으며 중량감소(重量減少)도 없었다는 사실로 미루어 타 공시체보다 내구성(耐久性)이 우수함을 알 수 있었다.

• 한국방재학회 논문집
• /
• 제9권5호
• /
• pp.31-38
• /
• 2009

본 연구의 목적은 콘크리트 포장의 한 종류인 줄눈콘크리트 포장의 열화정도를 평가하는 것이다. 첫째로, 열화종류를 관찰하기 위하여 콘크리트 포장 육안조사를 실시하였다. 육안조사 결과 콘크리트 포장 파손의 형태는 대부분 줄눈 부위에서 조사되었고, 내구성 균열과 줄눈 파손이 주를 이루는 것으로 나타났다. 둘째로, 육안조사 결과에 기초하여 콘크리트 포장을 양호한 단면(4개소)과 불량한 단면(4개소)으로 구분하여 총 8개소에서 콘크리트 코어시편을 채취하였고, 콘크리트 열화 원인을 콘크리트 코어시편의 초음파 강도추정, 쪼갬인장강도 실험 및 화상분석 실험을 이용하여 분석하였다. 화상분석 실험결과, 총 21개의 시험편에서 Kansas DOT 기준(간격계수 $250\;{\mu}m$이하)을 만족하는 시험편은 단지 2개에 불과했고, 나머지 19개의 시험편의 간격계수는 $250\;{\mu}m$ 이상으로 평가되어 내구성 지수가 매우 낮은 것으로 나타났다. 따라서 조사된 콘크리트 포장의 주 열화 원인은 동결융해작용인 것으로 분석되었다.