• Magazine of the Korea Concrete Institute
• /
• v.7 no.4
• /
• pp.149-156
• /
• 1995

The fracture process zone in concrete is a region ahead of a traction-free crack, in which two major mechanisms, microcracking and bridging, play important roles. The toughness due to bridging is dominant compared to toughness induced by microcracking, so that the bridging is dominani: mechanism governing the fracture process of concrete. Fracture mechanics does work for concrete provided that the fracture process zone is being considered, so that the development of model for the fracture process zone is most important to describe fracture phenomena in concrete. In this paper the bridging zone, which is a part of extended rnacrocrack with stresses transmitted by aggregates in concrete, is modelled by a Dugdale-Barenblatt type model with linear tension-softening curve. Two finite element techniques are shown for the analysis of progressive cracking in concrete based on the discrete crack approach: one with crack element, the other without crack element. The advantage of the technique with crack element is that it dees not need to update the mesh topology to follow the progressive cracking. Numerical results by the techniques are demonstrated.

• Magazine of the Korea Concrete Institute
• /
• v.6 no.3
• /
• pp.201-214
• /
• 1994

The fracture process zone in concrete is a region ahead of a traction-free crack, in which two major mechanisms, microcracking and bridging, play important roles. The toughness due to bridging is dominant compared to toughness induced by microcracking, so that the bridging is dominani: mechanism governing the fracture process of concrete. Fracture mechanics does work for concrete provided that the fracture process zone is being considered, so that the development of model for the fracture process zone is most important to describe fracture phenomena in concrete. In this paper the bridging zone, which is a part of extended rnacrocrack with stresses transmitted by aggregates in concrete, is modelled by a Dugdale-Barenblatt type model with linear tension-softening curve. Two finite element techniques are shown for the analysis of progressive cracking in concrete based on the discrete crack approach: one with crack element, the other without crack element. The advantage of the technique with crack element is that it dees not need to update the mesh topology to follow the progressive cracking. Numerical results by the techniques are demonstrated.

• Journal of Welding and Joining
• /
• v.7 no.2
• /
• pp.35-48
• /
• 1989

This study is concerned with a correlation of microstructure and local brittle zone (LBZ) in offshore structural steel welds. The influence of the LBZ on fracture toughness was investigated by means of simulated heat-affected zone (HAZ) tests as well as welded joint tests. Micromechanical processes involved in void and cleavage microcrack formation were also identified using notched round tensile tests and subsequent SEM observations. The LBZ in the HAZ of a multiphase welded joint is the interstitially reheated coarse grained HAZ, which is influenced by metallurgical factors such as effective grain size, the major matrix structure and the amount of high-carbon martensite-austenite (M-A) constituents. The experimental results indicate that Chirpy energy was found to scale monotonically with the amount of M-A constituents, confirming that the M-A constituent is the major microstructural factor controlling the HAZ toughness. In addition, voids and microcracks are observed to initiate at M-A constituents by the shear cracking process. Thus, the M-A constituent played an important role in initiating the voids and microcracks, and consequently caused brittle fracture.

• Journal of Welding and Joining
• /
• v.3 no.2
• /
• pp.42-51
• /
• 1985

The dynamic fracture toughness, fracture characteristics, impact tension and tensile properties of Al-Mg-Si T5 alloy and Al-Zn-Mg T6 alloy respectively welded with filler metal of Alcan 4043 were investigated. The dynamic fracture toughness values were obtained rapidly and simply for the specimen of small size by using instrumented Chirpy impact testing machine. the testing temperatures of the specimen were a range of room temperature and-196.deg. C. The results obtained in this experiment are summarized as follows. With decreasing the testing temperatures, dynamic tensile stress and fracture load were increased, on the other hand the deflection and impact value showed decreasing tendency in order of base metal>HAZ>weld. Changes of total absorbed energy were more influenced by the crack propagation energy than the crack initiation energy. At the low temperatures, the unstable rapid fracture representing the crack propagation appeared for the specimens of Charpy press side notched in Al-Zn-Mg alloy, but it was difficult to obtain the unstable rapid fracture in Al-Mg-Si alloy. Because of the development of plastic zone at the notch root, it was difficult to obtain thevalid $K_{1d}$ value in Al-Mg-Si alloy. Therefore the fatigue cracked specimens were effective in both Al-Mg-Si and Al-Zn-Mg alloys. With decreasing the impact testing temperatures, specimens underwent a transition from dimple-type transgranular fracture to lamella surface-type intergranular fracture because of the precipitate at the grain boundaries, impurities and crystal structure of the precipitates.s.

• Journal of Welding and Joining
• /
• v.31 no.6
• /
• pp.96-106
• /
• 2013

In this study, the effect of laser source($CO_2$ and Nd:YAG) on the microstructure and tensile properties of laser welded Al-Si coated boron steel(1.2mmt) was investigated with before and after hot-stamping. In case of as welds condition, fracture occurred in base metal unrelated to the laser source. It could be explained that tensile strength of fusion zone composed of martensite and bainite is higher than that of base metal that contains a lot of ferrite despite dilution of Al and Si from coating layer to fusion zone. In case of hot-stamping condition, the fracture occurred in fusion zone irrelevant to laser source and the tensile strength was lower than hot stamped base metal. In the $CO_2$ laser welds, $Fe_3$(Al,Si) formed near the bond line was transformed into ferrite during hot-stamping. Therefore tensile strength of bond line is lower than that of base metal and center of fusion zone and the fracture occurred in the bond line. On the other hand, in the Nd:YAG laser welds, the higher concentration of Al formed the ferrite in the fusion zone during hot-stamping treatment. Also, the thickness of centerline was thinner than that of base metal. Therefore, it is considered that fracture occurred in centerline of fusion zone due to effect of concentration stress, and it leaded to a lower tensile strength and elongation.

• Journal of the Korean Society for Precision Engineering
• /
• v.33 no.10
• /
• pp.865-873
• /
• 2016

The aim of this study was to examine the validity of fracture criterion for PMMA plates that have a V-notch with an end hole. The predicted stress intensity factors and crack initiation angles by the fracture criterion based on the maximum circumferential stress and the novozhilov's criteria were compared with the experimental results. By increasing the radius of end hole, the differences of predicted stress intensity factors and experimental results increased, possibly due to the plastic zone size. The results indicated that when the radius of end hole is < 1 mm, the fracture criterion would be useful.

• Smart Structures and Systems
• /
• v.23 no.2
• /
• pp.173-184
• /
• 2019

The main objective of this study is to evaluate the true fracture energy and monitor the damage progression in steel fibre reinforced concrete (SFRC) specimens using acoustic emission (AE) features. Four point bending test is carried out using pre-notched plain and fibre reinforced (0.5% and 1% volume fraction) - concrete under monotonic loading. AE sensors are affixed at different locations of the specimens and AE parameters such as rise time, AE energy, hits, counts, amplitude and duration etc. are obtained. Using the captured and processed AE event data, fracture process zone is identified and the true fracture energy is evaluated. The AE data is also employed for tracing the damage progression in plain and fibre reinforced concrete, using both parametric- and signal- based techniques. Hilbert - Huang transform (HHT) is used in signal based processing for evaluating instantaneous frequency of the acoustic events. It is found that the appropriately processed and carefully analyzed acoustic data is capable of providing vital information on progression of damage on different types of concrete.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.22 no.3
• /
• pp.261-275
• /
• 2020

When excavating a small cross-section tunnel in a fault fracture zone using the shield TBM method, there is a high possibility of excessive convergence and collapse. Appropriate ground reinforcement is required to minimize construction cost loss and trouble due to a fault fracture zone. In this study, the optimal reinforcement area was suggested and the surrounding ground behavior was investigated through numerical analysis using MIDAS GTS NX (Ver. 280). For the parameters, the width of the fault fracture zone, the existence of fault gouge, and the groundwater level and depth of cover were applied. As a result, when there is not fault gouge, the convergence and ground settlement are satisfied the standard when applying ground reinforcement by up to 0.5D. And, due to the high permeability coefficient, it is judged that it is necessary to apply 0.5D reinforcement. There is a fault gouge, it was possible to secure stability when applying ground reinforcement between the entire fault fracture zone from the top of the tunnel to 0.5D. And, because the groundwater discharge occurred within the standard value due to the fault gouge, reinforcement was unnecessary.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 1998.03a
• /
• pp.287-292
• /
• 1998

In this study behavior of fatigue crack and fatigue fracture is observed under rotary bending fatigue testing in friction welded dissimilar materials. Fatigue fracture most occurred in SM15C heat affected zone around Interface. In case of fatigue test, stress is reduced the position of fracture gradually moves to the welded Interface. Micro crack of heat affected zone surface on SM15C is observed at any different stress.

• Journal of the Korea Concrete Institute
• /
• v.11 no.3
• /
• pp.181-192
• /
• 1999

The progressive failure following strain localization in concrete can be analyzed effectively using finite element modeling of fracture process zone of concrete with a finite element embedded discontinuity. In this study, a finite element with embedded discontinuous line is utilized for the analysis of progressive failure in concrete. The finite element with embedded discontinuity is a kind of discrete crack element, but the difficulties in discrete crack approach such as remeshing or adding new nodes along with crack growth can be avoided. Using a discontinuous shape function for this element, the displacement discontinuity is embedded within an element and its constitutive equation is modeled from the modeling of fracture process zone. The element stiffness matrix is derived and its dual mapping technique for numerical integration is employed. Then, a finite element analysis program with employed algorithms is developed and failure analysis results using developed finite element program are verified through the comparison with experimental data and other analysis results.