• Restorative Dentistry and Endodontics
• /
• 제12권2호
• /
• pp.33-44
• /
• 1987

The use of composite resin for the posterior teeth gives rise to clinical problem due to the lack of mechanical properties. The purpose of this study was to observe the fractured surfaces of light posterior composite resins which are P-10, Clearfil posterior, Adaptic anterior & posterior, P-30, Lite-fil posterior, Estilux posterior, Helio-molar, and Ful-fil com pules (Table 1). The failure of composite resin specimens of I, T and Y-Type (Fig. 1,2) occured under compression. Fractographical observations by SEM (JSM-T20, JEOL) were carried out in order to examine the fracture behaviour of eight composite resins in different types of specimens. The results obtained from this study were as follows: 1. Similar features were found in fractured surfaces of eight composite resins. 2. The crack growth was initiated at the regions of porosities. 3. The crack propagated on the filler-matrix interface. 4. As the crack increased in size, it accelerated to form secondary crack. 5. The fracture behaviour was dependent on the content, size, shape, and distribution of fillers.

• 대한기계학회논문집
• /
• 제10권2호
• /
• pp.198-207
• /
• 1986

본 연구에서는 Fig.1과 같이 시편 부위에 균일응력분포가 작용하도록 M.Arcan 등에 의해 제시된 비대칭형상의 시편고정물에 층간균열을 가진 시편을 부착한 다음 하중각도를 바꾸어가며 모우드 II뿐 아니라 혼합모우드 및 모우드 I까지도 실험 할 수 있는 실험장치를 사용하여 균열면에서의 섬유방향이 〔0/0〕이고 초기균열길이비가 0.4, 0.5, 0.6인 시편의 모우드I, 혼합모우드 및 모우드II 층간파괴인 성치들을 실험 적으로 구해 혼합모우드 파괴결정조건식들에 적용시켜 보았다. 또한 균열면에서의 섬유방향이 〔0/0〕, 〔0/30〕, 〔0/45〕및 〔0/60〕인 경우의 층간파괴인성치와 이때 의 파괴현상에 대해 관찰하였다.

• 대한기계학회논문집
• /
• 제17권12호
• /
• pp.3083-3093
• /
• 1993

Friction and wear at ceramic coated surfaces of aluminum alloy were experimentally studied using a Ring-on-Block wear test machine. Ceramic materials coated on aluminum alloy surfaces were WC, CrC, $Al_{2}O_{3}$ by a plasma spray; and $Al_{2}O_{3}$,$Al_{2}SiO_{5}$, $Na_{2}B_{4}O_{7}$,$Na_{4}P_{2}O_{7}$, and $Al_{2}O_{3}-ZrO_{2}$ composite coating by an Anodic Spark Depositon. They were tested under the sliding wet contact and compared with aluminum alloys and steels. Test results showed that ceramic coated surfaces, in general, have better anti-wear property than those of aluminum alloys due to increase in the surface hardness ; however, they also showed higher coefficients of friction and changes in wear mechanisms, resulting in brittle fractures.

• 마이크로전자및패키징학회지
• /
• 제7권2호
• /
• pp.7-12
• /
• 2000

Copper-based leadframe sheets were oxidized in a black-oxide forming solution, and molded with epoxy molding compound (EMC) to form sandwiched double-cantilever beam (SDCB) specimens. The adhesion strength of leadframe/EMC interface was measured in terms of fracture toughness by using SDCB specimens and the fracture surfaces were analyzed by various equipments such as glancing-angle XRD, AFM, and SEM. Results showed that three types of failure paths, which were closely related to the surface condition of leadframes before molding.

• Computers and Concrete
• /
• 제2권3호
• /
• pp.239-248
• /
• 2005

The article presents the results of examination of the fractal dimension D of concrete specimen fracture surfaces obtained in fracture toughness tests. The concretes were made from three different types of coarse aggregate: gravel, dolomite and basalt aggregate. Ordinary concretes (C40) and high-performance concretes (HPC) were subjected to testing after 7, 14, 28 and 90 days of curing, respectively. In fracture toughness and compressive tests, different behaviours of concretes were found, depending on the type of aggregate and class of concrete (C40, HPC). A significant increase in the strength parameters tested occurred also after a period of 28 days (up to the $90^{th}$ day of curing) and was particularly large for concretes C40. Fractal examinations performed on fracture replicas showed that the fractal dimension D was diverse, depending on the coarse aggregate type and concrete class being, however, statistically constant after 7 and 14 days for respective concretes during curing. The fractal dimension D was the greater, the worse strength properties were possessed by the concrete. A cross-grain crack propagation occurred in that case, due to weak cohesion forces at the coarse aggregate/mortar interface. A similar effect was observed for C40 and HPC made from the same aggregate. A greater dimension D was exhibited by concretes C40, in which case the fracture was easier to form compared with high-performance concretes, where, as a result of high aggregate/mortar cohesion forces, the crack propagation was of inter-granular type, and the resulted fracture was flatter.

• 한국해양공학회지
• /
• 제10권4호
• /
• pp.75-83
• /
• 1996

Polymeric composites can be subjected to a wide variety of environmemtal conditions in practical use. One of most important conditions to be considered in the stuctural design using such materials is the miisture envirnment. Thus the moisture effect on interlaminar fracture toughness $G_IC$ and $G_IIC$ of CFRP(carbon fiber reinforced plastic) composed of carbon fibers and epoxy resin is studied in this paper. Specimens were first processed in 25, 50, $80^{\circ}C$ flesh water and $25^{\circ}C$ sea water for various periods of time. After that, the water absorption and fracture toughness tests were performed under laboratory atmosphere. As result, the specimen processed in $80^{\circ}C$ flesh water indicates the highest misture absorbing capability, the second in $50^{\circ}C$ flesh water, the third in $25^{\circ}C$ sea water, and the specimen in $25^{\circ}C$ flesh water does the lowest. The interlaminar fracture toughness $G_IC$ increases, approaches to the maximum, and decreases as the immersion time increases. In case of interlaminar $G_IIC$, the value of the specimen processed in $80^{\circ}C$ flesh water turns out to be higher than others. In addition, the scanning electron micrographs(SEM) of fracture surfaces were also examined in order to explain the mechanism of fracture.

• Restorative Dentistry and Endodontics
• /
• 제12권1호
• /
• pp.95-105
• /
• 1986

For the purpose of obtaining a basic data in selecting a suitable material with clinical care, this study was designed to measure the shear stress and to examine the fracture pattern of various dentin bonding restorative materials using 43 extracted bicuspids. The following results were obtained. 1. In dentin, Silux/Scotchbond group showed the highest value ($34.5{\pm}14.7kg/cm^2$) and Fuji Ionomer Type II group and Heliosit/Dentin-Adhesit group showed almost same bond strength in the next place. Durafill/Dentin-Adhesive group showed an infinitesimal value. ($3.1{\pm}1.4kg/cm^2$) 2. Every group showed no difference in bond strength between upper and lower teeth. Between buccal and lingual surfaces. Fuji Ionomer Type II and Durafill/Dentin-Adhesive groups showed too. But, in Silux/Scotchbond and Heliosit/Dentin-Adhesit groups, it was shown that the bond strength in lingual was stronger than in buccal. 3. There was resin fracture with cohesive fracture of bonding agent in Enamel group. In dentin, adhesive-cohesive fracture and adhesive fracture were shown. 4. The stronger bond strength was, the more frequently cohesive fracture occurred. Dentin-Adhesit group showed specific shining appearance as if varnish became hard.

• 대한금속재료학회지
• /
• 제49권9호
• /
• pp.726-731
• /
• 2011

The present work shows how the flexural displacement-induced fracture strength of silicon devices, whose back surfaces have wafer grinding-induced scratch marks, depends on the crystallographic orientation. Experimental results indicate that silicon devices with scratch marks parallel to their lateral direction (i.e. reference axis in this work) are very susceptible to flexural fracture, as compared to devices with marks which deviated from the direction. The 3-point bending test shows that the fracture strength of silicon devices having marks which are oriented away from the reference axis is 2.6 times higher than that of devices with marks parallel to the axis. It was particularly interesting to see that silicon devices with identical preferred marks even reveal different fracture strengths, depending on whether the marks are involved in specific crystal planes such as {111} or {011}, called cleavage planes. This work demonstrates that silicon devices with the reference axis-aligned scratch marks not existing on such cleavage planes can have higher fracture strength approximately 20% higher than those existing on the planes.

• 한국가구학회지
• /
• 제10권1호
• /
• pp.23-32
• /
• 1999

The ultrastructural characteristics of shear fracture surfaces of laminated wood prepared from major four Korea wood specimens were examined. Commercial urea and urethan resin were used as adhesives for laminated woods of both homospecies and heterospecies. The morphology of fracture surface was observed using an optical microscopy and scanning electron microscopy. Three anatomical failure types were recognized : intercell failure, intrawall failure and transwall failure. In dry specimen, failure occurred mainly in woods. Laminated woods of softwoods showed mostly intrawall failure and transwall failure of tracheids, and them of hardwoods indicated mainly intrawall failure and interwall failure. Laminated woods prepared with urethan resin showed coarse fracture surface, on the other hand, those prepared with an urea formaldehyde resin had clean surface. In wet specimen, failure occurred dominantly in glue line. Intrawall failure and flags were characterized in laminated wood prepared with urethan resin. In heterospecies laminated woods, failure was occurred mainly in softwood. Consequently, fracture morphology of laminated wood may be influenced by adhesives, moisture content, species and anatomical characteristics.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2005년도 추계학술발표대회 논문집
• /
• pp.256-259
• /
• 2005

Mixed-mode interlaminar fracture toughness of carbon fabric/epoxy composites, which are applicable to tilting train carbody, was evaluated through the MMB (Mixed-mode bending) test. Specimens were made of CF3327 plain woven fabric with epoxy and a starter delamination at one end was made by inserting Teflon film with the thickness of 12.5 μ m. Mixed-mode interlaminar fracture test was conducted for 6 types of specimens with the mode II ratio of 20 ,35, 50, 65, 80, 90%. Also crack propagating behaviors and fractured surfaces were examined through an optical travelling scope and a scanning electron microscope, respectively.