• 한국분말재료학회지
• /
• 제1권2호
• /
• pp.198-207
• /
• 1994

In order to find an optimal friction-welding condition for Ni-base ODS alloy (MA 754) produced by mechanical alloying, joint experiments were performed with various conditions of friction pressures (50~500 MPa), friction times (1~5 sec) and upset pressures (50~600 MPa). The optimal friction pressure and upset pressure must be above 400 MPa and 500 MPa, respectively, which are determined by tensile strengths and fracture features of as-welded joints. A maximum stress설h of 975 MPa could be obtained under these pressure conditions at friction time of 2 sec. Microstructural features of bonded interface by optical microscope and SEM revealed that the interface regions of all specimens are consisted with three distinct regions and defects such as voids, cracks and wavy interfaces exist in the joints produced under not-optimized conditions. EDS results showed that these defects include oxides composed with elements of Al, Y and Ti. The hardness on the bonded interface was higher than in the base metal region. Specimens fractured in bonded interface region had lower strength values compared to those fractured in base metal region. Surfaces of the former showed a typical intergranular fracture.

• 대한치과기공학회지
• /
• 제33권1호
• /
• pp.1-6
• /
• 2011

Purpose: To examine the shear bond strengths of zirconia and veneering ceramic according to their surface processing. Methods: The test samples were divided into three groups: one without zirconia surface processing, one sandblasted, and one sandblasted then 3% etched. Then veneering ceramic was fired on all test samples, and their shear bond strengths were measured. Results: The test samples of the control group (Z1) showed the lowest shear bond strengths of $21.82{\pm}1.02$ MPa. The shear bond strengths of Z2 and Z3 ($28.25{\pm}0.72$ and $26.23{\pm}0.82$ MPa, respectively) were relatively higher than those of the control group. The fracture surface of the control group showed adhesive fractures while the test groups had relatively large numbers of cohesive fractures. Conclusion: The shear bond strength was high in the test groups with surface processing while the fracture surfaces showed compound fractures of adhesive and cohesive fractures.

• 한국군사과학기술학회지
• /
• 제18권4호
• /
• pp.343-349
• /
• 2015

This is a study for the improvement of the fractured lug structure that connects the landing gear to the fuselage of the aircraft using the composite leaf spring landing gear. The lug surface was analyzed to find out the cause of fracture. The lug was destroyed by the crack initiation and propagation under the repeated stresses. The frictional wears of the lug structure were proceeded and that affected adversely to the crack. Also, the square protrusion of the lug has a weak shape to bring about stress concentration. The design changes were conducted and the test was performed to verify changed design results.

• 한국재료학회지
• /
• 제15권1호
• /
• pp.1-5
• /
• 2005

Copper-based leadframe sheets were immersed in two kinds of hot alkaline solutions to form brown-oxide or black-oxide layer on the surface. The oxide-coated leadframe sheets were molded with epoxy molding compound (EMC). After post mold curing, the oxide-coated EMC-leadframe joints were machined to form sandwiched double-cantilever beam (SDCB) specimens. The SDCB specimens were used to measure the fracture toughness of the EMC/leadframe interfaces under quasi-Mode I loading conditions. Fracture surfaces were analyzed by various equipment to investigate failure path. The present paper deals with the failure path, and the cause of the failure path formation with an adhesion model will be treated in the succeeding paper.

• 대한금속재료학회지
• /
• 제49권10호
• /
• pp.760-765
• /
• 2011

This paper presents a study of the tensile behavior of carbon and glass fiber reinforced epoxy hybrid laminates manufactured by vacuum assisted resin transfer molding (VARTM). The objective of this study was to develop and characterize carbon fiber reinforced plastic hybrid composite material that is low cost and light-weight and that possesses adequate strength and stiffness. The effect of position and content of the glass fabric layer on the tensile properties of the hybrid laminates was examined. The strength and stiffness of the hybrid laminates showed a steady decrease with an increase of the glass fabric content this decrease was almost linear. Fracture strain of these laminates showed a slight increasing trend when glass fabric content was increased up to 3 layers, but at a glass fabric content > 3 layers the strain was almost constant. When glass fabric layers were at both outer surfaces, the hybrid laminate exhibited a slightly higher tensile strength and elastic modulus due to the small amount of glass yarn pull-out.

• 한국전산구조공학회논문집
• /
• 제24권6호
• /
• pp.637-643
• /
• 2011

본 논문에서는 결합 기반 페리다이나믹스 해석법을 사용하여 동적취성 파괴시뮬레이션을 수행하였다. 페리다이나믹스 모델은 분기 균열, 균열 불안정성, 균열 경로의 비대칭성, 연쇄 분기 균열, 2차 균열 전파 등 다양한 동적취성 파괴현상을 잘 해석해 낼 수 있다. 본 논문에서는 분기 균열의 분기 각도와 균열 전파속도에 대한 응력파의 영향에 대해 연구하였다. 극한 시점에 도달한 균열은 둘 이상으로 분기되어 전파되고 그 전파속도는 기존 균열의 전파속도와 크게 달라지지 않는다는 사실이 여러 실험을 통해서 입증이 되었다. 페리다이나믹스로 해석된 분기 균열은 실험을 통해 제안된 균열 전파현상들과 잘 부합되는 것을 확인할 수 있었다.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2001년도 춘계학술발표대회 논문집
• /
• pp.89-92
• /
• 2001

Drop weight impact tests were performed to investigate the impact behavior of carbon fiber/epoxy composite laminates reinforced by short fibers and other interleaving materials. Characterization techniques, such as cross-sectional fractography and scanning acoustic microscopy, were employed quantitatively to assess the internal damage of some composite laminates. Scanning electron microscopy was used to observe impact damage and fracture modes on specimen fracture surfaces. The results show that composite laminates experience various types of fracture; delamination, intra-ply cracking, matrix cracking and fiber breakage depending on the interlayer materials. Among the composite laminates tested in this study, the composites reinforced by Zylon fibers showed very good impact damage resistance with medium level of damage, while the composites interleaved by poly(ethylene-co-acrylic acid) (PEEA) film is expected to deteriorate the bulk strength due to the reduction of fiber volume fraction, even though the damaged area is significantly reduced.

• 동력기계공학회지
• /
• 제10권3호
• /
• pp.45-50
• /
• 2006

In this paper, creep tests of Mg-Zn-Mn and Mg-Zn-Mn-Ca alloy casted by mold under the temperature range of 473.00-573.00K, and the stress range of 23.42-87.00Mpa were done with the equipment of automatic controlled temperature and computer for data acquisition. The activation energies were obtained by relationship between creep rate and temperature, and the stress exponents were obtained by relationship between creep rate and stress. From the experiment results, the activation energies of Mg-Zn-Mn and Mg-Zn-Mn-Ca alloy were 149.87kJ/mol, 147.97kJ/mol, respectively, and the stress exponents of those alloy were 5.13, 5.59, respectively, under the temperature of 473.00-493.00K and the stress range of 62.43-78.00Mpa. And the activation energies of those alloy were 134.41kJ/mol, 129.22kJ/mol, respectively, and the stress exponent of those alloy were 3.48, 3.77, respectively, under the temperature of 553-573Mpa and the stress range of 23.42-39.00Mpa. Also the lifes of Mg-Zn-Mn-Ca alloy were higher than those of Mg-Zn-Mn alloy, and the results of SEM showed fracture surfaces under low temperature had smaller dimples than those under high temperature.

• Journal of the Korean Wood Science and Technology
• /
• 제39권2호
• /
• pp.179-186
• /
• 2011

In an effort to understand the hydrolytic degradation process of cured urea-formaldehyde (UF) resins responsible for the formaldehyde emission of wood-based composite panels, this study analyzed the influence of acid hydrolysis on the morphology of cured UF resins with different formaldehyde/urea (F/U) mole ratios such as 1.6, 1.4, 1.2 and 1.0. Field emission-scanning electron microscopy (FE-SEM) was employed to observe both exterior and fracture surfaces on thin films of cured UF resins before and after the etching with hydrochloric acid as a simulation of the hydrolytic degradation process. FE-SEM images showed that the exterior surface of cured UF resin with the F/U mole ratio of 1.0 had spherical structures after the acid hydrolysis while the other cured UF resins were not the case. However, the fracture surface observation showed that all the samples possessed spherical structures in the cured state of UF resins although their occurrence and size decreased as the F/U mole ratio increased. For the first time, we found the spherical structures in cured UF resins of higher F/U mole ratio of 1.4. After the acid hydrolysis, the spherical structures became a much predominant at the fracture surface. These results indicated that the spherical structures in cured UF resinswere much more resistant to the hydrolytic degradation by the acid than amorphous region.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2003년도 춘계학술대회
• /
• pp.101-106
• /
• 2003

In order to investigate the mechanical behavior of newly developed materials, the evaluation of mechanical properties using small-size specimen is essential. For those purposes, an instrumented impact testing apparatus, which provides the load-displacement curve under impact loading without oscillations, was devised. To develop the test procedure with the setup, the impact behaviors of various kinds of structural materials such as S45C, SCM4, Ti alloys (Ti-6V-4Al) and Zr-based bulk amorphous metal, were investigated through the instrumented Charpy V-notch impact tests. The calibrations of the dynamic load and displacement that was calculated based on the Newton' second law were carried out through the quasi-static load test and the comparison of a directly measured value using a laser displacement meter. Satisfactory results could be obtained. The crack initiation and propagation processes during impact fracture could be well divided on the curve, depending on the intrinsic characteristic of specimen tested; ductile or brittle. The absorbed impact energy in Zr-basd BAM was largely used for crack initiation not for crack propagation process. The fracture surfaces under impact loading showed different feature when compared with the static cases.