• Journal of Korea Foundry Society
• /
• v.34 no.5
• /
• pp.170-178
• /
• 2014

Using the Gleeble test, the effects of [Mn/S] ratios and the presence of sulfides on the high-temperature fracture morphology of heavy-section steel castings were analysed via the observations of the microstructures. The specimens for which the [Mn/S] ratio was in the range of 60~80 showed a ductile fracture morphology with an area reduction of more than 60%, while some specimens with similar [Mn/S] ratios showed a brittle fracture morphology with an area reduction of 0.0% due to the liquidation of sulfides at the grain boundary. The fracture morphology was classified into three types in the Gleeble high-temperature tensile test specimens. The first type showed dimple formation at the grain boundary, the formation of globular MnS sulfides, and plastic deformation of sulfides at an elevated temperature, indicating a needle-point type of ductile fracture with area reductions of 96.0~97.8%. The second type was a knife-edge type brittle fracture with an area reduction of 0.0% due to the film-type liquidation of sulfides at the grain boundary, band-type liquidation, and the liquidation of a terraced nipple pattern. The third type was the typical ductile fracture with an area reduction of 31.3~81.0%, in accordance with the mixture of dimples with in the grains and terraced nipple pattern at the grain boundary.

• Journal of Korea Foundry Society
• /
• v.14 no.1
• /
• pp.52-61
• /
• 1994

The effect of Ni addition, on the mechanical properties and fracture characteristics of Mo-Cu and Mo-Ni-Cu alloyed ductile iron austenitized at $900^{\circ}C$ and austempering temperatures of $250^{\circ}C$, $300^{\circ}C$ and $350^{\circ}C$. The tensile strength, yield strength and hardness are decreased and elongation and impact value are increased in both Mo-Cu and Mo-Ni-Cu alloyed austempered ductile iron, with increased austempering temperature. According to the austempering temperature are increased, the amount of retained austenite are increased. Maximum value of fracture toughness is obtained at $350^{\circ}C$ austempering temperature at this condition, the amount of retained austenite came to 40% in Mo-Ni-Cu alloyed ADI and 34% in Mo-Cu alloyed ADI. The fracture surface of ADI which had represented high toughness are showed a quasi-cleavage pattern and a dimple pattern with micro void. Comparing the fracture characteristics of Mo-Cu alloyed ADI with that of Mo-Ni-Cu alloyed ADI, the latter was superior to the former.

• Proceedings of the Korean Society of Soil and Groundwater Environment Conference
• /
• 2000.11a
• /
• pp.69-73
• /
• 2000

We systematically analyze the influence of fracture junction, solute transfer characteristics on transport patterns in discrete, two-dimensional fracture network models. Regular lattices and random fracture networks with power-law length distributions are considered in conjunction with particle tracking methods. Solute transfer probabilities at fracture junctions are determined from analytical considerations and from simple complete mixing and streamline routing models. For regular fracture networks, mixing conditions at fracture junctions are always dominated by either complete mixing or streamline routing end member cases. Moreover bulk transport properties such as the spreading and the dilution of solute are highly sensitive to the mixing rule. However in power-law length networks there is no significant difference in bulk transport properties, as calculated by assuming either of the two extreme mixing rules. This apparent discrepancy between the effects of mixing properties at fracture junctions in regular and random fracture networks is explained by the statistics of the coordination number and of the flow conditions at fracture intersections. We suggest that the influence of mixing rules on bulk solute transport could be important in systematic orthogonal fracture networks but insignificant in random networks.

• Journal of Korean Neurosurgical Society
• /
• v.46 no.6
• /
• pp.528-531
• /
• 2009

Objective : Although gadolinium enhancement of compression fractures is well known, the enhancement pattern of the acute stage of a fracture is not completely understood. Here, we investigated the enhancement pattern of acute vertebral compression fractures (VCFs). Methods : We conducted a retrospective study of patients with acute osteoporotic VCFs admitted to hospital between January 2004 and December 2005. The demographic details, stage of the fracture, management data, and results were analyzed. There were nine men and 22 women, and the mean age was 71 years (range, 53-92 years). According to the onset of pain, patients were divided into the following four groups : Group I (less than 3 days), Group II (4-7 days), Group III (8-14 days), and Group IV (14-30 days). Results : All patients had central low-signal intensity of the nonenhancing part of vertebral bodies on T1 images. Enhancing box sign (EBS) was seen 7 days of VCF development. After 7 days of onset (Groups III and IV), patch or Kummell's enhancements occurred. EBS has been statistically correlated with stage of compression fracture (Pearson's correlation = -0.774). However, EBS had no statistically significant correlation with prognosis in our study (Pearson's correlation = 0.059). Conclusion : EBS represents a characteristic sign 7 days of VCF development.

• Journal of Welding and Joining
• /
• v.5 no.2
• /
• pp.53-59
• /
• 1987

The effect of applied stress, current density and heat-treatment after welding on the time to fracture, fracture behavior was investigated by the method of constant load tensile testing under catholic charging with hydrogen in E.B. welded 250,300 Grade 18% Ni Maraging steel sheet. The main results obtained are as follows: 1. All specimen showed the characteristic delayed failure and the time to fracture showed decreasing tendency with the increase in current density and applied stress. 2. Hydrogen embitterment susceptibility of notched specimen after solution-treatment and aging after welding was more increased than that of aged smooth specimen and as welded specimen. 3. Fracture surface showed a typical intergranular fracture on the border, a dimple pattern in the center of specimen and some quasi-cleavage fracture between the intergranular and the dimple.

• Restorative Dentistry and Endodontics
• /
• v.19 no.1
• /
• pp.64-72
• /
• 1994

Zinc Phosphate Cement hand been used for about more than 100 years in luting of cast gold inlay. But many scientists had been trying to develop the new form of luting agent because the ZPC hand shown the lack of adhesiveness on the tooth structure and the toxicity to the pulp tissue. Recently many researches about the surface treatment of the cast body are being done to increase the adhesion of cement to it. The conventional Class I gold inlays were fabricated in the 20 permanent molars. After the internal surface of the cast body was sandblasted with $Al_2O_3$ particles and was tin-plated, the inlays were cemented with adhesive cement [G I cement and resin cement(Super-Bond & $Panavia_{EX}$)] and the evaluation on the adhesion pattern, adhesive strength and the fracture pattern of the adhesive cast gold inlay was compared to that of the cast gold inlay cemented conventionally with ZPC. The results were as follows : 1. The surface roughness of the cast body was increased significantly after sandblasting with the $Al_2O_3$ particles and the tin oxide layer, which was consisted of round particles, came into being. 2. The bond strength was in the order of Super-Bond, ZPC, Fuji I, $Panavia_{EX}$ group. The group cemented with Super-Bond showed statistically greater strength than the other groups(p<0.05). 3. The group cemented with ZPC was fallen apart by principal adhesion failure and that with Fuji I was by complete adhesion failure. But the group with Super-Bond showed pricncipal cohesive failure pattern and in the group with $Panavia_{EX}$, complete cohesive fracture pattern was shown and small protion of tooth structure was fractured out with cast body and the fractured surface showed the figure just as the enamel prism. 4. Various gaps were shown at the pulpal side regardless of little gap at the side walls of the cavity in all groups. Only the Super-Bond was attached to the tooth structure and the other cements were detached from both the tooth and the cast body.

• Journal of Korea Foundry Society
• /
• v.11 no.3
• /
• pp.228-235
• /
• 1991

The Effects of the matrix structures and the amount of the retained austenite in austempered ductile iron(ADI) which contains Ni, Cu and Mo on fracture characteristics were inverstigated. The structures were changed from lower bainite to mixture of Lower and upper bainite, and then to upper bainite as austempering temperature increased. A higher austempering temperature yielded lower tensile strength and hardness, but higher impact valve and $K_{IC}$. In addition, the amount of the retained austenite increased with the austempering temperatures. Fracture surface showed a fibrous pattern and a dimple pattern with increasing the retained austenite amount.

• Journal of the Korean Ceramic Society
• /
• v.35 no.12
• /
• pp.1257-1265
• /
• 1998

Hertzian contact tests were used to investigate the evolution of fracturedamage in the coating layer as functions of contact load and coating thickness by studying crack patterns in porcelain on glass-infiltrated alumina bilayer system conceived to simulate the crown structure of a tooth. Cone cracks initiated at the coating top surface without delamination at interface and crack propagation to substrate. Preferentially the cracks made multi-cracks at the coating top surface rather than proceeding to interface. The cracks were highly stabilized with wide ranges between the loads to initiate first cracking and to cause final failure im-plying damage-tolerant capability. Finite element modelling was used to evaluate the stress distribution. Maximum tensile stress were responsible for the cracking at the coating layer and had a profound influence on the crack pattern and fracture damage in the layered structure materials.

• Journal of Veterinary Clinics
• /
• v.38 no.5
• /
• pp.240-243
• /
• 2021

Complications of pelvic fractures and sacroiliac joint luxation include hemoabdomen, pulmonary trauma, and soft tissue injury. Among them, rectal perforation accounts for 1% of pelvic fracture complications. Delayed diagnosis is commonly associated with a poor prognosis. A mixed-breed dog was presented to Jeonbuk Animal Medical Center (JAMC) after a traffic accident with no signs of rectal perforation. After fracture surgery, rectal perforation was seen as a perianal fistula. This report describes a case of a perianal fistula progressed from rectal perforation after a traffic accident that was curatively treated with lateral caudal axial pattern flap surgery to the perianal skin.

• Computers and Concrete
• /
• v.18 no.6
• /
• pp.1135-1151
• /
• 2016

For investigating the effect of the pre-existing joints on the initiation pattern of hydraulic fractures, the numerical simulation of circular holes under internal hydraulic pressure with a different pattern of the joint distributions are conducted by using a finite element code, FRANC2D. The pattern of hydraulic fracturing initiation are scrutinized with changing the values of the joint length, joint offset angle. The hydraulic pressures with 70% of the peak value of borehole wall breakout pressure are applied at the similar models. The simulation results suggest that the opening-mode fracture initiated from the joint tip and propagated toward the borehole for critical values of ligament angle and joint offset angle. At these critical values, the crack grow length is influenced by joint ligament length. When the ligament length is less than 3 times the borehole diameter the crack growth length increases monotonically with increasing joint length. The opening-mode fracture disappears at the joint tip as the ligament length increases.