• Journal of Magnetics
• /
• v.16 no.2
• /
• pp.186-191
• /
• 2011

[ $YBa_2C_3O_{7-x}$ ]films were fabricated on a $SrTiO_3$ (100) substrate using a trimethylaceate propionic acid (TMAP)-based MOD process by controlling the precursor solution viscosity, firing temperature, and by using various coatings. The viscosity of the precursor solution was controlled by the addition of Xylenes. The films were heat treated with different temperatures from 750 to $800^{\circ}C$. c-axis oriented films were obtained. After adding 9 ml of Xylene into the precursor solution, the $T_c$ of the YBCO film, which was coated 2 times and heat treated at $800^{\circ}C$, was 86 K and the measured $J_c$ was above 2.5 MA/$cm^2$ at 77 K in a zero-field.

• Progress in Superconductivity and Cryogenics
• /
• v.8 no.1
• /
• pp.15-18
• /
• 2006

A new precursor solution wilt low fluorine content was synthesized for MOD processing of coated conductors. In this study, the precursor solution for MOD processing was synthesized using F-free yttrium and copper precursor. It was shown that crack-free and uniform precursor films were formed after calcination in humidified oxygen atmosphere. Less than 2 hours were required to finish the calcination process. The relatively gradual weight loss during the calcination process is attributed to the feasibility of fast calcination profile. The calcined precursor film was converted to a YBCO film without any secondary phases after annealing in wet $Ar/O_2$ atmosphere. Fully converted film shows uniform microstructure and high critical current density. $(Jc=2.7MA/cm^2) $.

• Progress in Superconductivity and Cryogenics
• /
• v.9 no.1
• /
• pp.1-4
• /
• 2007

The total Fluorine content in the precursor solution for MOD processing of YBCO coated conductors can be significantly reduced by synthesizing precursor solution with F-free Y & Cu precursor and Barium trifluoroacetate(TFA). It was shown that crack-free and uniform precursor films were formed after calcinations in humidified oxygen atmosphere. Less than 2 hours are required to finish the calcinations process and XRD measurement shows that $BaF_2,\;CuO,\;Y_2O_3$ are major constituent of calcined precursor films. Film thickness after calcinations was improved to be 2.8um by applying slot-die coating method. In particular, addition of Samarium shows critical current of $I_c=273A/cm-w(J_c=3.8MA/cm^2)$. It is shown that uniform and fast processing route to YBCO coated conductor with high Ic can be provided by employing F-free Y & Cu precursor solution in MOD process.

• Resources Recycling
• /
• v.27 no.5
• /
• pp.49-53
• /
• 2018

In developing an optimum steelmaking process, the purity of the product, environmental impact, capability and cost of the process should be considered. Desulfurization of molten iron is conducted during preliminary treatment stage before converter operation. Although fluorite is added as a desulfurizing agent in CaO and $CaCO_3$ based agents, the concentration of fluorine in slag is strictly regulated. In order to develop desulfurizing agent without fluorine, CaO was mixed with Al dross and ladle slag containing alumina. The characteristics and desulfurizing capacity of the CaO based desulfurizing agent thus prepared were tested by varying temperature of Kanvara Reactor. Our results showed that the desulfurizing capacity of the samples prepared in this work was found to be similar to that of the traditional desulfurizing agents with fluorine.

• Progress in Superconductivity
• /
• v.8 no.1
• /
• pp.22-26
• /
• 2006

Total Fluorine content in the precursor solution for MOD processing of YBCO coated conductors can be significantly reduced by synthesizing precursor solution with F-free Y & Cu precursor and Barium trifluoroacetate(TFA). It was shown that crack-free and uniform precursor films were formed after calcinations in humidified oxygen atmosphere. Less than 2 hours are required to finish the calcination process, and XRD measurement shows that $BaF_2,\;CuO,\;and\;Y_2O_3$ are major constituent of calcined precursor films. Film thickness after calcination was measured to be ${\sim}2.8$ um by applying slot-die coating method. In particular, addition of Samarium shows critical current of Ic=226 A/cm-w($Jc=3.4\;MA/cm^2$). Also discussed are recent developments in the reel-to-reel processing using F-free Y & Cu precursor solutions. It is shown that uniform and fast processing route to YBCO coated conductor with high Ic can be provided by employing F-free Y & Cu precursor solutions in MOD process.

• Progress in Superconductivity and Cryogenics
• /
• v.8 no.1
• /
• pp.5-8
• /
• 2006

The growth properties of MOD-YBCO films were investigated. To enhance the growth rate of YBCO layer and inhibit the build-up of HF gas during the annealing process in TFA-MOD for YBCO coated conductors the method of low pressure annealing was employed. Total pressure was changed from 700Torr to 1Torr and its effect on growth of YBCO films was compared with atmospheric one. The lower Pressure was effective to control of the pore size in MOD method . Surface morphology of YBCO films processed at low total pres sure was rough and composed of random YBCO (103) grains. But large pores, usually observed at atmospheric process in MOD disappeared and also the number of pores was reduced at low pressure annealing. Also discussed ate the effects of Fluorine-free Y and Cu precursor solution on the development of microstructure. Dense surface me phology and with less and small pores can be provided through controlling Fluorine content.

• Progress in Superconductivity and Cryogenics
• /
• v.10 no.1
• /
• pp.6-9
• /
• 2008

We have investigated the MOD process successfully for the fabrication of the YBCO thick film on the $LaAlO_3$(001) single crystalline substrate. The cracking problem in YBCO thick film, a serious problem in the conventional TFA-MOD method, could be overcome with a careful control of precursor materials. Thus coating solution was prepared for the YBCO thick film by using fluorine-free precursor material. The precursor solutions were coated on the LAO(001) single crystalline substrate using the dip coating method, calcined at the temperature up to $500^{\circ}C$, and fired at various high temperatures for 2 h in a reduced oxygen atmosphere. Optimally processed YBCO thick film exhibited high critical current($I_c$) over 200 A/cm-width at 77K in self-field.

• Progress in Superconductivity and Cryogenics
• /
• v.8 no.4
• /
• pp.12-14
• /
• 2006

YBCO coated conductors have been fabricated by the reel-to-reel processing using TFA-MOD method. In this work, the fluorine-free Y & Cu precursor solution was synthesized to shorten the calcining time by reducing the evolution of HF gas, thus the meter-long YBCO precursor films can be made within few hours by the continuous slot-die coating & calcination step using the F-free Y & Cu precursor solution. The annealing step was followed to make the YBCO films by the reel-to-reel method with the vertical gas flow system onto the moving tape. To increase the growth rate of the YBCO films by enhancing the removal of HF gas, the low total pressure was adopted in the annealing processing. And the water partial pressure and the oxygen partial pressure were varied to optimize the growth conditions of the MOD-YBCO films on the buffered metal tape. FE-SEM and XRD were used to investigate the surface morphologies and the texture of the meter-long YBCO films. The end-to-end critical current $(I_c)$ of 63A/cm-width and the critical current density $(J_c)$of $0.9MA/cm^2$ with the thickness of $0.7{\mu}m$ were obtained in the 0.42m long coated conductor.

• Progress in Superconductivity and Cryogenics
• /
• v.11 no.4
• /
• pp.20-24
• /
• 2009

YBCO coated conductors (CC) on the $CeO_2$-buffered IBAD-MgO template were fabricated by metal-organic deposition (MOD) Process with Ba-trifluoroacetate and fluorine-free Y and Cu precursor materials. The precursor solution was coated on $CeO_2$-buffered IBAD MgO templates using the multiple dip-coating method, decomposed into inorganic precursors by pyrolysis up to $400^{\circ}C$ within 3 h, and finally fired at $740{\sim}800^{\circ}C$ in a reduced oxygen atmosphere. Microstructure, texture, and superconducting properties of YBCO films were found highly sensitive to both the firing temperature and time. The high critical current density ($J_C$) of $1.15\;MA/cm^2$ at 77.3K in the self-field could be obtained from $1\;{\mu}m$ thick YBCO CC, fired at $740^{\circ}C$ for 3.5 h, implying that high performance YBCO CC is producible on IBAD MgO template. Further enhancement of $J_C$ values is expected by improving the in-plane texture of $CeO_2$-buffer layer and avoiding the metal substrate contamination.

• Journal of Powder Materials
• /
• v.25 no.3
• /
• pp.226-231
• /
• 2018

F-containing $TiO_2$ nanopowders are synthesized using simple wet processes (precipitation-based and hydrothermal) from ammonium hexafluorotitanate (AHFT, $(NH_4)_2TiF_6$) as a precursor to apply as a photocatalyst for the degradation of rhodamine B (RhB). The surface properties of the prepared samples are evaluated using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), field-emission scanning electron microscopy (FESEM), and transmission electron microscopy (TEM). The results confirm that the synthesized anatase $TiO_2$ has sphere-like shapes, with numerous small nanoparticles containing fluorine on the surface. The photocatalytic activity of F-containing $TiO_2$ compared with F-free $TiO_2$ is characterized by measuring the degradation of RhB using a xenon lamp. The photocatalytic degradation of F-containing $TiO_2$ exhibits improved photocatalytic activity, based on the positive effects of adsorbed F ions on the surface.