• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05b
• /
• pp.301-304
• /
• 2006

The purpose of this study is to evaluate bonding properties of PMMA mortars using EPS with silane coupling agent. PMMA mortars are prepared with various silane coupling agent, and tested for flexural strength test, adhesion test in flexure and tensile strength in underwater and air. It is estimated that the application of silane coupling agent to PMMA mortar is more effective in underwater than air.

• Elastomers and Composites
• /
• v.46 no.3
• /
• pp.218-222
• /
• 2011

The effect of cycled temperature change on the mechanical properties of wood flour(50 wt.% and 70 wt.%) polypropylene WPC(Wood Plastic Composites) was investigated in this study. Flexural modulus and flexural strength of the WPC showed a decrease due to the degradation of interfacial adhesion between polymer matrix and wood flour by the freeze-thaw test regardless of the cycled number. At the higher loading level of wood flour, the reduction of the flexural modulus was remarkable. After the cycled heat-freeze test, it was found that the flexural modulus and flexural strength of the WPC were lower at the high temperature ($60^{\circ}C$) and higher at the low temperature ($-20^{\circ}C$). At the low temperature ($-20^{\circ}C$) which is below glass transition temperature of polypropylene ($-10^{\circ}C$), WPC is in a glassy state which brings about the high stiffness and strength. At the high temperature ($60^{\circ}C$), the flexural modulus and flexural strength of the WPC with 50 wt.% wood flour were lower because of the increase of polymer ductility.

• Journal of Adhesion and Interface
• /
• v.2 no.2
• /
• pp.1-10
• /
• 2001

Silica for Epoxy Molding Compound (EMC) was coated via plasma-polymerization with RF plasma (13.56 MHz) as a function of treatment time, power and pressure. 1,3-diaminopropane, allylamine, pyrrole, 1,2-epoxy-5-hexene, allylmercaptan or allylalcohol were utilized for plasma polymerization coating and adhesion of coated silica was evaluated by measuring flexural strength. CTE and water absorption of EMC were also measured, and fracture surface of flexural specimen was analyzed by SEM in order to elucidate the failure mode. The plasma polymer coated silica was analyzed by FT-IR and reactivity of plasma polymer coating with epoxy resin was evaluated with DSC in order to investigate the adhesion mechanism. The EMC prepared from the silica coated with 1,3-diaminopropane or allylamine exhibited high flexural strength, low CTE, and low water absorption compared with the control sample, and also exhibited 100% cohesive failure mode. These results can be attributed to the chemical reaction between the functional groups in the plasma polymer coating and epoxy resin, and also consistent with the results from FT-IR and DSC analysis.

• Magazine of the Korean Society of Agricultural Engineers
• /
• v.41 no.1
• /
• pp.97-105
• /
• 1999

Recently , polymer concrete has been widely used in the construction industry because of its quick setting, high strength, excellect adhesion, watertightness and chemical resistance compared to ordinary cement concrete. Its application is also increased. In this paper, lightweight polymer mortars using unsaturated polyester resin and lightweight aggregate are prepared with various mix proportations, and tested for slump working life, apparent specific gravity , flexural and compressive strengths. As a result, the slump and working life can be controlled and thier flexural and compressive strengths are 9.7 to 22.0 MPa , and 23.0 to 100.8 MPa respectively at apparent specific gravities of 0.86 to 1.73.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2005.11a
• /
• pp.79-82
• /
• 2005

In this study, mechanical properties of carbon fabrics composite under the thermal shock cycling were evaluated. Due to the interactions between fiber and polymer matrix, it is reasonable to conclude that both thermal cycles of thermal shock result in improvement of interlaminar shear strength(ILSS) for the longer conditioning time duration. The rise in ILSS may be attributed to the improved adhesion by cryogenic compressive stress and also by the post-curing strengthening effect. However, the flexural and tensile strength were decreased with increasing conditioning time of thermal cycle.

• Journal of the Korean Society of Industry Convergence
• /
• v.27 no.2_2
• /
• pp.371-375
• /
• 2024

Epoxy resins are widely used in various fields due to their high adhesion, mechanical strength, and solvent resistance. However, as the volume decreases during the hardening process and the cooling process after hardening, stress is generated and when an external force is applied, the brittle material exhibits destruction behavior. To complement this, research has been conducted using inorganic nanofillers such as halloysite nanotube(HNT). HNT has a nanotube structure with the chemical formula of Al₂Si₂O₅(OH)₄·nH₂O and is a natural sediment of aluminosilicate. It has been used as additive to improve the mechanical properties of epoxy composites with exchange of amine group as a terminal functional group. In order to simplify complicated procedures of common wet method, a dry coating machine was designed and used for amine group exchange in previous research. In this study, they were applied as filler in epoxy composites, and mechanical properties such as tensile strength and flexural strength of composites were examined.

• Journal of the Korean Ceramic Society
• /
• v.41 no.6
• /
• pp.430-434
• /
• 2004

The values of fracture energy and mechanical flexural strength of Fiber Reinforced Cement (FRC) with polypropylene (PP) fiber modified by Ion Assisted Reaction (JAR), by which functional groups were grafted on the surface of PP fiber, was improved about 2 times as those of fracture energy and flexural strength of cement reinforced by untreated PP fiber. PP fiber was irradiated in O$_2$ environment by Ar$\^$+/ ion. The contact angle of PP treated by IAR decreased largely when compared with untreated PP. From this result, we expected that surface energy and interfacial adhesion force of treated PP fiber increased. The strain hardening occurred in the strain-stress curve of FRC including PP treated by IAR when compared with that of FRC with untreated PP. These enhanced mechanical properties might be due to strong interaction between hydrophilic group on modified PP fiber and hydroxyl group in cement matrix. This hydrophilic group on surface modified PP fiber was confirmed by XPS analysis. We clearly observed hydration products that were fixed at modified PP fiber due to the strong adhesion force of interface in cement reinforced modified PP by SEM (Scanning Electron Microscopy) study.

• Journal of Adhesion and Interface
• /
• v.17 no.3
• /
• pp.96-103
• /
• 2016

In this work, pellets consisting of cellulose-based natural fiber bamboo and poly(lactic acid) (PLA) was prepared by extrusion process and then bamboo fiber/PLA biocomposites with various fiber contents were produced by injection molding process. The water treatment effect of bamboo fibers on the flexural, tensile, and impact properties and heat deflection temperature of the biocomposites were investigated. The thermal stability of bamboo and the flexural properties, tensile modulus, and impact strength depended on the presence and absence of water treatment as well as on the fiber content, whereas the heat deflection temperature are influenced mainly by water treatment. The increase of the mechanical and impact properties of biocomposites is ascribed to the improvement of the interfacial adhesion between the bamboo fibers and the PLA matrix by the water treatment. The result suggests that the pre-treatment of natural fibers by using water, which is environment-friendly and labor-friendly, may contribute to enhancing the performance of biocomposites.

• The Journal of Advanced Prosthodontics
• /
• v.10 no.1
• /
• pp.43-49
• /
• 2018

PURPOSE. The purpose of this in vitro study is to examine the effects of a nano-structured alumina coating on the adhesion between resin cements and zirconia ceramics using a four-point bending test. MATERIALS AND METHODS. 100 pairs of zirconium bar specimens were prepared with dimensions of $25mm{\times}2mm{\times}5mm$ and cementation surfaces of $5mm{\times}2mm$. The samples were divided into 5 groups of 20 pairs each. The groups are as follows: Group I (C) - Control with no surface modification, Group II (APA) - airborne-particle-abrasion with $110{\mu}m$ high-purity aluminum oxide ($Al_2O_3$) particles, Group III (ROC) - airborne-particle-abrasion with $110{\mu}m$ silica modified aluminum oxide ($Al_2O_3+SiO_2$) particles, Group IV (TCS) - tribochemical silica coated with $Al_2O_3$ particles, and Group V (AlC) - nano alumina coating. The surface modifications were assessed on two samples selected from each group by atomic force microscopy and scanning electron microscopy. The samples were cemented with two different self-adhesive resin cements. The bending bond strength was evaluated by mechanical testing. RESULTS. According to the ANOVA results, surface treatments, different cement types, and their interactions were statistically significant (P<.05). The highest flexural bond strengths were obtained in nano-structured alumina coated zirconia surfaces (50.4 MPa) and the lowest values were obtained in the control group (12.00 MPa), both of which were cemented using a self-adhesive resin cement. CONCLUSION. The surface modifications tested in the current study affected the surface roughness and flexural bond strength of zirconia. The nano alumina coating method significantly increased the flexural bond strength of zirconia ceramics.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.10 no.6
• /
• pp.1298-1303
• /
• 2009

The effect of blending weight and fiber length on the tensile and flexural strength for Basalt fiber reinforce cement composites is discussed. The increase of physical properties is mainly affected by blending quantity of fibers instead of the fiber length. Also it is believed that the interfacial adhesion between Basalt fiber and cement matrix gives positive influence to the physical strength. Basalt fiber in saturated $Ca(OH)_2$ solution, which is similar to the alkaline hydration environment of cement, shows very low weight loss even after 3 weeks of immersion.