• Journal of the Korean Wood Science and Technology
• /
• 제40권5호
• /
• pp.335-342
• /
• 2012

To prepare the eco-friendly fire retardant wood, Japanese red pine (Pinus densiflora), Hemlock (Tsuga heterophylla), and Radiata pine (Pinus radiata) were treated with inorganic chemicals, such as sodium silicate, boric acid, ammonium phosphate, and ammonium borate. Different combination and concentration of those chemicals were impregnated by vacuum/pressure treatment methods. The electron-beam treatment was used to increase the chemical penetration into the wood. The fire performance of the fire retardant treated wood was investigated. The penetration of chemicals into the wood was enhanced after electron beam treatment. Ignition time of the treated wood was the most effectively retarded by sodium silicate, ammonium phosphate, and ammonium borate. The most effective chemical combination was found at 50% sodium silicate and 3% ammonium borate, which satisfied flammability criteria for a fire retardant material in the KS F ISO 5660-1 standards.

• 한국가구학회지
• /
• 제19권6호
• /
• pp.475-486
• /
• 2008

In this study, fire-retardant chemicals were melt with mixed composition ratios of dibasic ammonium phosphate and each half of boric acid and borax in hot water, in which hammer-milled chips were immersed to increase swelling of waste particleboards. Also, fire-retardant treated particles from sawn lumber chip and recycled particleboard chip were composed in ratio of 70:30 in core layer to improve boards' properties. Retention ratio of fire-retardant chemicals for the particles for face layer was high due to high specific surface area, and that of sawn lumber chips was somewhat higher than that of recycled particleboard chips. The mixture of particles from sawn lumber chips and recycled PB of 70:30 in weight ratio exceeded bending strength of 100 $kgf/cm^2$. It seemed that the relatively greater portions of dibasic ammonium phosphate affected adversely to dimensional stability, however fire-retardants treatment resulted in distinct effect lowering formaldehyde emission such as $E_0$ type(0.5mg/$\ell$ or less) in KS F 3104. In fire-retardancy, the recycled boards with a mixed ratio of dibasic ammonium phosphate to boric acid borax(50:50 mixture) of 70% to 30% in weight satisfied fire-retardancy 3rd grade in KS F 2271, and also this composition from cone calorimeter test met same standard grade figuring total heat release of 4.6MJ/$m^2$.

• 한국화재소방학회논문지
• /
• 제25권6호
• /
• pp.146-155
• /
• 2011

본 연구에서는 현장방염처리(방염후처리)가 적용되고 있는 MDF 목재에 국내에서 유통되는 5개사 제품을 MDF 목재에 부착한 방염필름과 MDF 목재(무처리, 비방염필름)에 수성 유성 방염도료로 도포된 시편을 대상으로 현재 시중에서 사용되고 있는 방염처리 방법에 따라 방염성능을 비교하는 실험을 실시하였다. MDF 목재에 5개사의 방염필름을 부착하여 연소 시험한 결과 2개사 제품은 4가지 기준 내에 적합한 값을 나타냈으나 나머지 3개사 제품은 10~40 %의 불합격률을 나타냈다. 방염도료의 특성별로는 유성방염도료가 수성방염도료보다 방염성능 기준 내에서는 더 우수한 것으로 나타났지만 유성방염도료를 도포한 MDF 목재에서 수성방염도료를 도포한 MDF 목재에서 보다 독성지수의 위험등급은 상대적으로 더 높은 위험도를 나타내었다.

• Journal of the Korean Wood Science and Technology
• /
• 제13권4호
• /
• pp.3-57
• /
• 1985

본(本) 시험(試驗)에 있어서 파아티클보오드와 콤플라이보오드용(用)의 칩은 공(共)히 메란티 수종(樹種)(Shorea spp.)을 팔만칩퍼로 제조(製造)하였으며 콤플라이보오드의 표층단판(表層單板)의 수종(樹種)은 아피통(Dipterocarpus spp.)을 사용(使用)하였다. 칩의 크기는 6메쉬를 통과(通過)하고 25 메쉬위에 남는 것을 이용(利用)하였으며 콤플라이보오드의 단판(單板)두께는 0.9mm, 1.6mm 및 2.3mm의 것을 사용(使用)하였고 접착제(接着劑)로는 요소수지(尿素樹脂)를 파아티클의 전건조량(全乾燥量)에 대(對)해 10%첨가(添加)한 후 성형(成型)하여 파아티클보오드를 만들었고 표층용단판(表層用單板)의 접착(接着)에는 36g/(30.48cm)$^2$을 도포(塗布)하였다. 내화약제(耐火藥劑)로는 제2인산(第二燐酸)암모늄, 황산(黃酸)암모늄, 제1인산(第一燐酸)암모늄, 파이래소트, 미나리스의 5종(種)에 대(對)해 단판(單板)에는 20% 농도(濃度)로 파아티클에는 5, 10, 15, 20%의 농도(濃度)로 침지법(浸漬法)을 적용(適用)하여 처리(處理)하였다. 이런 조건(條件)으로 만든 내화(耐火)파아티클보오드와 콤플라이보오드의 물성(物性) 기계적(機械的) 성질(性質) 및 내화도(耐火度)를 조사(調査)하여 내화처리(耐火處理)파아티클 및 콤플라이보오드 제조가능성(製造可能性)을 구명(究明)하고져 하였다. 본(本) 연구(硏究)에서 얻은 결론(結論)을 요약(要約)하면 다음과 같다. 1. 파아티클보오드와 콤플라이보오드의 5종(種)의 약제보유량중(藥劑保有量中) 5% 황산(黃酸)암모늄처리(處理)가 1.34kg/(30.48cm)$^3$로 가장 적었으나 모두가 최저보유량(最低保有量) 1,125kg/(30.48cm)$^3$ 보다도 높은 것을 나타내었다. 2. 파아티클보오드와 콤플라이보오드의 파괴계수(破壞係數), 탄성계수(彈性係數), 박리강도(剝離强度) 및 나사못 유지력(維持力)은 제2인산(第二燐酸)암모늄처리(處理)가 다른 약제처리(藥劑處理)보다 우수(優秀)하였다. 3. 내화처리(耐火處理)콤플라이보오드의 파괴계수(破壞係數) 및 탄성계수(彈性係數)는 내화처리(耐火處理)파아티클보오드보다 더 양호(良好)한 결과(結果)를 나타내었다. 4. 내화처리(耐火處理)콤플라이보오드의 두께 팽창율(膨脹率)은 내화처리(耐火處理)파아티클보오드의 것보다 훨씬 적었다. 5. 파이레소트와 미나리스처리(處理)는 파아티클보오드와 콤플라이보오드의 함수율(含水率)을 증가(增加)시켰으나 제1인산(第一燐酸)암모늄처리(處理)는 오히려 함수율(含水率)을 감소(減少)시켰다. 6. 내화처리(耐火處理)콤플라이보오드는 착화(着火)가 되지 않았고 내화처리(耐火處理)콤플라이보오드는 착화(着火)는 되었지만 대조구(對照區)에 비(比)해 착화시간(着火時間)이 훨씬 지연(遲延)되었다. 또한 단판(單板)만 내화처리(耐火處理)한 콤플라이보오드는 착화(着火)되어 잔염(殘炎)은 있으나 대조구(對照區)에 비(比)해 그 잔염시간(殘炎時間)이 훨씬 짧았다. 단판(單板)과 중층(中層)파아티클보오드에 처리(處理)한 콤플라이보오드는 착화(着火)는 되었으나 잔염(殘炎)은 없었다. 7. 불꽃의 길이, 탄화면적(炭化面積) 및 중량감소율(重量減少率)은 대조구(對照區)에 비(比)해서 훨씬 적었으나 약제간(藥劑間)에 차이(差異)는 없었다. 8. 시험(試驗)한 5종(種)의 약제(藥劑)에서 내화처리(耐火處理)파아티클보오드의 이면온도(裏面溫度)는 처리농도(處理濃度)가 증가(增加)함에 따라서 감소(減少)하는 경향(傾向)을 나타내고 있다. 9. 내화처리(耐火處理)파아티클보오드의 이면온도(裏面溫度)가 가장 높은 약제(藥劑)는 파이레소트처리(處理)이고 가장 낮은 약제(藥劑)는 미나리스처리(處理)였다. 10. 내화처리(耐火處理)콤플라이보오드의 이면온도(裏面溫度)는 대조구(對照區)에 비(比)해서 현저히 낮았다.

• Journal of the Korean Wood Science and Technology
• /
• 제12권2호
• /
• pp.10-19
• /
• 1984

The $3{\times}3{\times}30$ ($cm^3$) sized lumbers of Populus alba-grandulosa L. were treated with four fire-retardant solutions of ammonium sulfate, monoammonium phosphate, diammonium phosphate and aluminium chloride for 1, 15, 30, and 60 minutes and 1, 3, and 7 days. Thereafter they were air-dried and burned at high temperature about $1,800^{\circ}C$ and for short time of five minutes. This study estimated the relationship between absorbed chemical amounts and rate of weight loss or residual bending strength of these burned lumbers. The results were as follows: 1) In absorption amount of fire-retardant chemicals, diammonium phosphate showed the largest, aluminium chloride the smallest, but monoammonium phosphate and ammonium sulfate showed similar level. 2) The absorption amount of chemicals was decreased with the increase of specific gravity in the same species except aluminium chloride. 3) The rate of weight loss was decreased as the absorption amount of chemicals increased, especially monoammonium phosphate was most effective. 4) The MOR value of the residual bending strength was increased as the absorption amount of chemicals increased and especially monoammonium phosphate showed the most efficient effect. 5) Aluminium chloride showed more striking increase of MOR value of residual bending strength with the increase of absorption amount than any other chemical, therefore its MOR value was similar to the maximum MOR value of the most effective monoammonium phosphate. 6) The correlation between weight loss and MOR value of the residual bending strength was negative and aluminium chloride showed the most striking negative relation, but the others showed similar trends. 7) The correlation between work to proportional limit and absorption amount of chemicals was positive and the degree of increase in work to proportional limit was most in aluminium chloride, and the next, in monoammonium phosphate and diammonium phosphate in turn. 8) The correlation between work to maximum load and absorption amount of chemicals showed positive and diammonium phosphate revealed the best result and aluminium chloride showed better results than other two chemicals.

• 한국화재소방학회:학술대회논문집
• /
• 한국화재소방학회 2007년도 춘계학술논문발표회 논문집
• /
• pp.223-229
• /
• 2007

• 한국산림과학회지
• /
• 제78권4호
• /
• pp.419-424
• /
• 1989

내화제간(耐火劑間)의 상대적(相對的)인 내화효과(耐火效果)를 비교(比較), 검토(檢討)하여 보기 위하여 메란티(meranti) 합판(合板)에 5종(種)의 내화제(耐火劑)와 수처리(水處理)를 하고 열판건조(熱板乾燥)시킨 다음, ASTM D 2863-77의 산소지수법(酸素指數法)에 의거하여 Up and Down법(法)을 통하여 각각의 산소지수(酸素指數)를 구하였다. 시험결과(試驗結果)에 의하면 황산(黃酸)암모늄이 28.4, 제(第)1인산(燐酸)암모늄이 26.7, 제(第)2인산(燐酸)암모늄이 43.4, 붕사(硼砂)-붕산(硼酸)이 30.1, 미날리스가 32.4, 그리고 수처리(水處理)가 25.5의 산소지수(酸素指數)를 나타냈는데, 연소성(燃燒性)이 큰 물질(物質)일수록 낮은 산소지수(散素指數)를 지닌다는 사실(事實)로 미루어 볼 때 내화제간(耐火劑間)의 내화효과(耐火效果)는 제(第)2인산(燐酸)암모늄, 미날리스, 붕사(硼砂)-붕산(硼酸), 황산(黃酸)암모늄, 제(第)1인산(燐酸)암모늄의 순(順)으로 크다는 것을 구명할 수 있었다.

• Journal of the Korean Wood Science and Technology
• /
• 제30권2호
• /
• pp.172-179
• /
• 2002

본 연구에서는 MDF와 잣나무 판재에 대한 난연처리 및 난연도장 처리 시험편에 대한 난연 효과에 대해 고찰하였다. 무처리 MDF와 잣나무판재에 대한 td𝜃은 각각 279.5, 182.5로 나타났으나 난연침지 처리된 무늬단판을 오버레이한 MDF를 난연도장 처리 한 경우 높은 난연성능을 나타냈다. 난연처리한 잣나무판재에 난연도장 처리를 할 경우 th𝜃가 90으로 나타났고, 난연침지 처리 된 무늬단판이 오버레이 된 MDF에 난연도장처리한 경우에는 th𝜃가 0으로 나타난 가장 뛰어난 난연성능을 나타냈다. 전체적으로 난연처리 및 난연도장처리를 한 경우 th𝜃가 감소하는 것으로 나타나 난연성능이 개선되는 것으로 나타났다. 또한 연소도 시험결과 시험편의 중량감소율은 난연처리와 난연도장처리에 의해 감소함으로써 난연성능이 개선되는 것으로 나타났다. 또한 착화시간과 잔염시간의 측정결과도 유사하게 나타났으며 난연침지 처리 된 무늬단판이 오버레이 된 MDF 및 난연처리된 잣나무판재에 난연도장 처리한 경우 무처리된 경우에 비해 착화시간은 증가되고, 잔염시간은 감소하는 것으로 나타났다.

• Journal of the Korean Wood Science and Technology
• /
• 제32권6호
• /
• pp.7-13
• /
• 2004

In this study, the Korean pine wood (Pinus densiflora Sieb. et Zucc) and Italian poplar wood (Populus euramericana Guinier) was treated with a mixture of monoammonium phosphate (MAP) and boric acid. Their usability as fire retardant and as decay-resistant construction and interior materials were evaluated by testing of chemicals, corrosion rate and absorption rate, weight loss and chemical contents. An experiment was performed to compare treated pine wood and Italian poplar wood. According to the results, Italian poplar wood had higher specific gravity and retention of chemicals than pine wood, and treated wood showed higher decay-resistance than untreated one. Weight loss was less in treated wood than untreated one because the degree of decay was lower in the former than the latter. Corrosion rate and absorption rate met the KS standard for wood preservative performance. The chemical contents analysis was carried out to determine the degree of decay and it was found that the preservative effect of chemical treatment was lower in Italian poplar wood than in pine wood.

• Journal of the Korean Wood Science and Technology
• /
• 제40권5호
• /
• pp.311-318
• /
• 2012

This study investigated the flame retardant performance of developed four types of flame retardant chemicals (FRC), FRC-A, B, C and D. Four kinds of soft wood species, Sugi (Cryptomeria), Spruce (Picea abies), Hinoki (Chamaecyparis obtusa) and Korean pine (Pinus koraiensis), were used. The wood specimens were treated by spreading the FRC on the surface with different quantities, 30, 50, 70, 90, 110 g/$m^2$, respectively. The charred area, charred length, after flame time and after glow time were tested. And their suitabilities as incombustible materials were evaluated. The specimen treated by FRC-D showed better incombustible properties than others, even though with lower quantity. Therefore it is supposed that the FRC-D could be able to be applied on the cultural heritage, such as Korean wooden house for preventing fire.