• 한국재료학회지
• /
• 제20권3호
• /
• pp.142-147
• /
• 2010

Nano-sized $BaNd_2Ti_5O_{14}$ powders were prepared by the spray pyrolysis process. Sucrose used as the organic additive enabled the formation of nano-sized $BaNd_2Ti_5O_{14}$ powders. The powders prepared from the spray solution without sucrose had a spherical shape, dense structure and micron size before and after calcination. However, the precursor powders prepared from the spray solution with sucrose had a large size, and hollow and porous morphology. The precursor powders had an amorphous crystal structure because of the short residence time of the powders inside the hot wall reactor. The complete decomposition of sucrose did not occur inside the hot wall reactor. Therefore, the precursor powders obtained from the spray solution with sucrose of 0.5M had a carbon content of 39.2wt.%. The powders obtained from the spray solution with sucrose of 0.5M had a slightly aggregated structure of nano-sized primary powders of $BaNd_2Ti_5O_{14}$ crystalline phase after calcination at $1000^{\circ}C$. The calcined powders turned into nano-sized $BaNd_2Ti_5O_{14}$ powders after milling. The mean size of the $BaNd_2Ti_5O_{14}$ powders was 125 nm.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1996년도 봄 학술발표회 논문집
• /
• pp.172-179
• /
• 1996

Recently, the broken concrete lumps resulting from the demolition of concrete structures are creshed for reuse as aggregates(i.e. recycled fine and gravel). And also, in the processing of crusing, the recycled powder of an equivalent of between 20% to 30% by wt.% of the broken concrete lumps is generated. The extensive research of recycled concrete aggregates has been carried out in various parts of the world. But less reseatch on the reuse of recycled concrete powder has been carried out. It is the purpose of this report that the study on the quality evaluation of recycled aggregates for recycled concrete. In specially, this report deals with the properties such as flow, compressive strength, bending strength, drying shrinkage and wight loss rate of mortars replaced standard fine aggregate with recycled powders at the rate of 3, 7, 15, 20 and 30 wt.%. Since the characteristics of recycled mortars with the recycled powders were comparable to those of the normal mortar without the recycled powders as described above, its concretes could be found extensive application in such field as concrete products.

• 한국분말재료학회지
• /
• 제12권3호
• /
• pp.179-185
• /
• 2005

As the electrodes of secondary battery are made with sulfur compounds, excellent electrode system of environmental non-toxicity, high specific energy density and low material cost can be obtained. In this study, the $FeS_2$ fine compound powders for active material in the battery were synthesized by mechanical alloying. Fine Fe-53.5 wt.%S powders of 450 nm of mean size were fabricated by mechanical alloying for 60 hours at the horizontal attritor. As the mechanical alloying time increases, particle size of Fe-53.5 wt.%S was decreased and steady state of Fe-53.5 wt.%S compound powders was obtained at 30 hours. Fe-53.5 wt.%S cathode shows the excellent discharge capacity (1011 mAh/g).

• 한국분말재료학회지
• /
• 제24권2호
• /
• pp.108-114
• /
• 2017

We fabricate fine (<$20{\mu}m$) powders of $Bi_{0.5}Sb_{1.5}Te_3$ alloys using a large-scale production method and subsequently consolidate them at temperatures of 573, 623, and 673 K using a spark plasma sintering process. The microstructure, mechanical properties, and thermoelectric properties are investigated for each sintering temperature. The microstructural features of both the powders and bulks are characterized by scanning electron microscopy, and the crystal structures are analyzed by X-ray diffraction analysis. The grain size increases with increasing sintering temperature from 573 to 673 K. In addition, the mechanical properties increase significantly with decreasing sintering temperature owing to an increase in grain boundaries. The results indicate that the electrical conductivity and Seebeck coefficient ($217{\mu}V/K$) of the sample sintered at 673 K increase simultaneously owing to decreased carrier concentration and increased mobility. As a result, a high ZT value of 0.92 at 300 K is achieved. According to the results, a sintering temperature of 673 K is preferable for consolidation of fine (<$20{\mu}m$) powders.

• 한국분말재료학회지
• /
• 제18권4호
• /
• pp.340-346
• /
• 2011

In order to improve the weak mechanical properties of cast Mg alloys, Mg-$Zn_1Y_2$ (at%) alloy powders were synthesized using gas atomization, a typical rapid solidification process. The powders consist of fine dendrite structures less than 3 ${\mu}m$ in arm spacing. In order to fabricate a bulk form, the Mg powders were compacted using magnetic pulse compaction (MPC) under various processing parameters of pressure and temperature. The effects of the processing parameters on the microstructure and mechanical properties were systematically investigated.

• 한국결정성장학회지
• /
• 제2권1호
• /
• pp.60-69
• /
• 1992

$TiCl_4$와(NH_4)_2SO_4$를 액상 반응시켜 암모늄 티타늄 설페이트를 형성시킨 뒤 하소하여 미립의 $TiO_2$분말을 만들었다. Anatase 분말로 Verneuil장치에서 Rutile단결정을 성장시킨 뒤 물성을 조사하였다. 최적의 성장조건은 $H_2:O_2=3:1$ 성장온도는 $1900^{\circ}C$ 분말공급속도는 10g/hr였다.

• 한국분말재료학회지
• /
• 제13권6호
• /
• pp.427-431
• /
• 2006

Mg-4.3Zn-0.7Y (at%) alloy powders were prepared using an industrial scale gas atomizer, followed by warm extrusion. The powders were almost spherical in shape. The microstructure of atomized powders and those extruded bars was examined using Scanning Electron Microscopy (SEM), Energy Dispersive X-ray Spectroscope (EDS) and X-ray Diffractometer (XRD). The grain size of the powders was coarsen as the initial powder size increased. After the extrusion, the grain size became fine due to the severe plastic deformation during the extrusion with the ratio of 10:1. Both the ultimate strength and elongation were enhanced with the decrease of initial particle size.

• 한국세라믹학회지
• /
• 제31권3호
• /
• pp.337-345
• /
• 1994

The reaction-sintered alumina and zirconia-alumina ceramics having low firing shrinkage were prepared from the Al/Al2O3 or Al/ZrO2(Ca-PSZ) powder mixtures via the attrition milling. And in this milling process the effect of the characteristics of used powders was investigated. Attrition milling was much more effective in reducing the particle size of ceramic/metal mixed powders than ball milling. Powder mixtures of flake-type Al with coarse alumina was much more effectively comminuted by the attrition milling than the mixtures of globular-type Al with coarse alumina powders. And coarse alumina than fine alumina was much more beneficial in cutting and reducing the ductile Al particles. In the contrary to Al/Al2O3 powder mixtures, Al/ZrO2 powder mixtures was not effectively comminutd. But whether using the alumina ball media or attrition milled with Al2O3 powder rather than Al, the milling efficiency was much more increased.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.759-760
• /
• 2006

Ti-6Al-4V has low specific gravity, high corrosion resistance and superior mechanical properties but it is very difficult to control oxygen content in MIM process. It is necessary to use powders with coarse particle size to decrease oxygen content of powders, so feedstocks with poor fluidity and sintered bodies with lower density are obtained in such cases. Fine titanium hydride-dehydride powders were blended with atomized powders to accomplish higher fluidity and sintered density. Sintered bodies had higher sintered density and mechanical properties equivalent to those of wrought materials by controlling oxygen content less than 0.35mass%.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1264-1265
• /
• 2006

Study about the feasibility and effect of high-energy ball milling on a specific Mg alloy under protection medium of alcohol was presented via comparing with conventional vacuum milling. More fine particles with wider powder size distribution but more irregular shape were shown of the powder milled under alcohol. No obvious oxide was revealed from the two kinds of Mg alloy powders with limited milling time. And since slip induced in a preferential direction, the (002) texture was formed in the Mg alloy powders at the initial stage of alcohol milling. More O and Fe contaminants were introduced into the powders milled under alcohol according to the EDS analysis.