• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2000년도 추계학술대회 논문집
• /
• pp.473-476
• /
• 2000

Recently, many studies focus on mixed-mode fatigue-fracture characteristics of characteristics of materials. In order to reveal crack initiation and propagation mechanisms in combined -mode fatigue. This paper investigates the initiation and propagation behavior of the fatigue crack of the STS304 specimens under mixed mode loading conditions. moreover crack arrest and branch phenomena were analyzed with respect to the change do the angle of inclined loading. The relationship between the angle of inclined loading and the angle of branched crack was studied. A greate number of cycles are necessary to initiate a new crack from the initial crack. The direction of the new crack propagation is determined by MTS theory.

• International Journal of Ocean Engineering and Technology Speciallssue:Selected Papers
• /
• 제4권1호
• /
• pp.44-50
• /
• 2001

Existing surface defects in structural members often act as sites of fatigue crack initiation, and if undetected, these cracks may grow through the thickness of the member, leading to catastrophic failure of the structure. Thus, in-service monitoring of fatigue cracks through reliable and effective nondestructive techniques is an important ingredient in the leak-before-break (LBB) design and safe operation of defects critical structures. An advanced, waveform-based, acoustic emission (AE) technique has been used in this paper to study the characteristics of the signals emanating from the initiation, growth and through-the -thickness penetration of surface fatigue crack in a 6061 aluminum plate. The goal of this experimental study is to determine whether the evolution of the fatigue crocks could be identified from the properties of the waveforms produced during the tests. The AE waveform signals detected at different stages of crack growth was found to have different temporal and spectral characteristics. The data analysis technique presented here can be applied to real-time monitoring of the initiation and propagation of fatigue cracks in structural components.

• Tribology and Lubricants
• /
• 제20권5호
• /
• pp.252-258
• /
• 2004

In this study, using high cycle fatigue (HCF) criteria, the simulation of rolling contact fatigue is conducted under elliptical contact. The HCF criteria fall into three categories: the critical plane approach, the stress invariant approach and the approach based on the mesoscopic scale. The accurate calculation of contact stresses and subsurface stresses is essential to the prediction of crack initiation life. Contact stresses are obtained by contact analysis of a semi-infinite solid based on the use of influence functions and the subsurface stress field is obtained using rectangular patch solutions. The simulation results show that the critical load is decreasing rapidly and the site of crack initiation also moves rapidly to the surface from the subsurface when the friction coefficient exceeds a specific value for all of three fatigue criteria.

• Journal of Advanced Marine Engineering and Technology
• /
• 제10권1호
• /
• pp.65-73
• /
• 1986

Surface fatigue crack propagation tests by plane bending fatigue were conducted on the welding specimens of an aluminium alloy, A5083-0, having an edge through thickness notch to study the fatigue crack growth characteristics. Moreover, the experiments were performed in order to clarify the fatigue crack initiation and growth. The properties of fatigue crack growth were quantitatively inspected in welded metal, heat-affected zone and base metal of the welding specimens. The main results obtained are summarized as follows: 1. It is found that the hardness distributions of A5083-0 aluminium alloy weldments are quite different with those of steel material weldments, so that the hardness distribution becomes lower in the following order: base metal, heat-affected zone and weld metal. 2. It is observed that the grain size of this specimen weldment appears to be almost equal to the base metal, when TIC welding method is adopted. 3. In a surface fatigue crack initiation and growth, the fatigue crack does not begin by opening-closing mechanism until hardening is saturated at the crack tip. 4. The fatigue crack growth characteristics of A5083-0 alluminium alloy weldments can be concluded.$${\frac{da}{dn}}=C({\Delta}K)^n=3.8{\times}10^{-9}{({\frac}{1}{2}{\Delta}S_t{\sqrt{{\pi}a}})}^{2.4}$$

• 대한기계학회논문집A
• /
• 제34권1호
• /
• pp.103-110
• /
• 2010

본 연구에서는 프랑스의 RCC-MR A16 절차에 기초하여 Mod.9Cr-1Mo 강(ASME Grade 91) 구조의 크리프-피로 균열 개시 및 성장 평가법을 확장 개발하였다. 현재의 A16 지침은 오스테나이트 스테인리스강에 대해서만 크리프-피로 균열 개시 및 성장 평가법을 제시하고 있지만, 현재 초초임계(USC) 화력발전소는 물론 미래형 원자로 시스템의 구조재료로서 폭넓게 채택되고 있는 Mod.9Cr-1Mo 강에 대한 지침은 제시하지 않고 있다. 본 연구에서는 FMS(페리틱-마르텐사이트강)에 대한 크리프-피로 균열 개시 및 성장 평가법을 제시하고 있고, 구조물에 대한 크리프-피로 균열 거동 평가를 수행하였다. 평가결과는 구조시험을 수행한 결과 얻은 관찰 이미지와 비교하였다.

• 대한기계학회논문집A
• /
• 제24권6호
• /
• pp.1584-1592
• /
• 2000

Reversed plane bending fatigue tests were conducted on SiC whisker reinforced aluminum composite which were consolidated by squeeze casting process. Initiation and growth of small surface fatigue c racks were investigated by means of a plastic replica technique. The fatigue crack initiated in the vicinity of SiC whisker/matrix interface. It was found that a fatigue crack deflected along SiC whisker and grew in a zig-zag manner microscopically, although the crack propagated along the direction normal to the loading axis macroscopically. The coalescence of micro-cracks was observed in the tests conducted at high stress levels, but were not evident in tests in which lower levels of stress were applied. Due to the coalescence, a higher crack growth rate of small cracks rather than those of long cracks was recognized in da/dn -ΔK realtionship.

• 한국정밀공학회지
• /
• 제18권11호
• /
• pp.174-178
• /
• 2001

Chrome-molybden steel or chrome steel for machine structures has been shown to excellent hardenability adding boron of a small amount at low carbon steel. These days, boron steel has been used high strength bolt and wear resistant components of construction equipment. SEM results showed classical fatigue fractures, consist with surface crack initiation. The specimens were tested repeatedly(9 times) under controlled load rotary bending fatigue tests. In the study, the fatigue crack initiation as well as fatigue crack growth behavior and the fracture mechanism were investigated through observations of fracture of boron steel surface(AISI 51B20).

• 대한기계학회논문집A
• /
• 제31권3호
• /
• pp.344-354
• /
• 2007

The objective of this study is to investigate the effect of arbitrarily located defect around the circular hole in the aircraft structural material such as Al/GFRP laminates and monolithic Al alloy sheet under cyclic bending moment. The fatigue behavior of these materials may be different due to the defect location. Material flaws in the from of pre-existing defects can severely affect the fatigue crack initiation and propagation behavior. The aim of this study is to evaluate effects of relative location of defects around the circular hole in monolithic Al alloy and Al/GFRP laminates under cyclic bending moment. The fatigue behavior i.e., the stress concentration factor($K_t$), the crack initiation life($N_i$), the relationship between crack length(a) and cycles(N), the relationship between crack growth rate(da/dN) and stress intensity factor range(${\Dalta}K$) near a circular hole are considered. Especially, the defects location at ${\theta}_1=0^{\circ}\;and\;{\theta}_2=30^{\circ}$ was strongly effective in stress concentration factor($K_t$) and crack initiation life($N_i$). The test results indicated the features of different fatigue crack propagation behavior and the different growing delamination shape according to each location of defect around the circular hole in Al/GFRP laminates.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2003년도 춘계학술대회
• /
• pp.381-388
• /
• 2003

The material deficiencies in the form of pre-existing defects can initiated cracks and fractures. The stress distribution and fatigue crack initiation life of engineering materials may be associated with the size, the shape and the relative location of defects contained in the component. The objective of this study is to investigate the effect of arbitrarily located hole defect around the rivet hole of a wing section in monolithic aluminum and Al/GFRP laminates under cyclic bending moment during a service load. The stress distribution and the fatigue crack initiation behavior near a rivet hole of on the relationships between stress concentration factor ($K_t$) and relative position of defects were considered. The test results indicated the features of different stress field. Therefore, the stress concentration factor ($K_t$) and the fatigue crack initiation behavior was illustrated different behavior according to each position of hole defect around the rivet hole in monolithic aluminum and Al/GFRP laminates.

• 한국생산제조학회지
• /
• 제7권5호
• /
• pp.66-71
• /
• 1998

It is required the superior materials for the parts of machines or structures, which could be endurable in severe load and environment. According to advancement of casting technology, nodular graphite cast iron is used as suitable for such condition. But nodular graphite cast iron is scattering of fatigue strength and low reliability. Therefore in this study, the effect of matrix structure and number of nodular graphite on the initiation of fatigue crack and fatigue strength. It was found that the material which has relatively high ferrite volume fraction was more easily cracked than other materials and fatigue limit was low. The material which has not found pinhole on the surface, the crack was initiated in graphite went through ferrite and propagated into through graphite, but separated graphite and ferrite grain boundary and combined with other cracks to fro large one.