• 한국안전학회지
• /
• 제14권2호
• /
• pp.3-10
• /
• 1999

Fatigue crack growth rates in commercial plate of high strength Al 7075-T651 were investigated for the T-L direction in air, water and sea water. In this paper the effect of cyclic load wave-form(trapezoid and triangle) on fatigue crack growth rates in air, water and sea water environments were investigated using standard LEFM testing procedures. It was founded that the fatigue crack growth behaviors were not affected by cyclic load wave-forms. In region II (stable crack growth region), the fatigue crack growth behaviors were insensitive to cyclic load wave-forms and were sensitive to environment i.e. fatigue crack growth behaviors were higher in sea water than in air for all cyclic load wave-form. The result of fractographical morphology in air, water and sea water by SEM showed obvious dimple rupture and typical striation in air, but transgranular fracture surface in water and sea water. The values m are not affected by corrosion environments but C are different values.

• 한국안전학회지
• /
• 제8권2호
• /
• pp.64-71
• /
• 1993

In this study, the purpose is to investigate the influence of initial residual stresses on the fatigue crack growth behaviors after the distribution of initial residual stresses Is measured when the crack is growing from the compressive residual stresses field to the tensile residual stress field. Also, the Influence of the variation of residual stress distribution on the fatigue crack growth behaviors at the crack tip is studied when the initial crack li applied on base metal, weld metal and HAZ respectively.

• 한국해양공학회지
• /
• 제9권2호
• /
• pp.112-122
• /
• 1995

In this work, prediction of fatigue life and fatigue crack growth are studied. 4th order polynominal function is presented to describe the crack growth behaviors from artifical pit of SM45C steel. Crack growth curves obtained from 4th order polyminal growth equations are in good agreement with experimental data The crack growth behaviors at arbitrary stress levels and investigated by the concept of elastic-plastic fracture mechanics using ${\Delta}J$. Fatigue life prediction are carried out by numerical integral method. Prediction lives obtained by proposed method in this study, is in good agreement with the experimental ones. Life prediction results calculated by using of ${\Delta}J$ better than those of ${\Delta}K$.

• 한국기계가공학회지
• /
• 제11권4호
• /
• pp.82-89
• /
• 2012

In order to clarify the effect of overload on crack growth behaviors, fatigue tests for overload were carried out for round plain specimens of SM45C steel. In the experiment, typical semi-elliptical crack shape was found and further crack growth behaviors were tested. Using three types of single overload fatigue tests, Crack growth retardation phenomenon were examined. The growth rate of surface crack(da/dN) during retardation period was analyzed in terms of ${\Delta}K$ and ${\Delta}K_{eff}$. On the growth rate of surface crack analyzed by ${\Delta}K$, the dependence of overload stress levels appears. However, on the growth rate by ${\Delta}K_{eff}$ obtained by Willenborg analysis, there is a liner relationship between da/dN and ${\Delta}K_{eff}$ with narrow scatter band.

• 한국해양공학회지
• /
• 제12권1호
• /
• pp.39-49
• /
• 1998

In this work, fatigue tests by axial loading were carried out to investigate the effect of stress ratio on the growth behaviors of surface fatigue crack for SM45C steel and Al 2024-T4 alloy. The growth behaviors of surface crack have been monitored during fatigue process by measuring system attached CCTV and monitor. When the growth rates of surface crack were investigate by the concept of LEFM based on Newman-Raju's .DELTA.K, the dependence of stress ratio appears both SM45C steel and Al 2024-T4 alloy. Therefore, modified stress intensity factor range, .DELTA.K' [=(1+R)/sup n/.DELTA.K] are intorduced to eliminate the dependence of stress ratio. Using .DELTA.K', it is found that the dependence of stress ratio disappears both SM45C steel and Al 2024-T4 alloy.

• 한국기계가공학회지
• /
• 제11권5호
• /
• pp.13-20
• /
• 2012

In order to clarify the effect of overload on crack growth behaviors, fatigue tests for overload were carried out for round plain specimens of SM45C steel. In the experiment, typical semi-elliptical crack shape was found and further crack growth behaviors were tested. Using three types of single overload fatigue tests, Crack growth retardation phenomenon were examined. The growth rate of surface crack(da/dN) during retardation period was analyzed in terms of ${\Delta}K$ and ${\Delta}K_{eff}$. On the growth rate of surface crack analyzed by ${\Delta}K$, the dependence of overload stress levels appears. However, on the growth rate by ${\Delta}K_{eff}$ obtained by Willenborg analysis, there is a non-liner relationship between da/dN and ${\Delta}K_{eff}$ with narrow scatter band.

• 한국생산제조학회지
• /
• 제5권3호
• /
• pp.31-39
• /
• 1996

The objective of this study is to investigate the influence of welding residual stresses on the fatigue crack growth behavior of cracks located transverse to the weld bead. For this purpose, G. T. A (Gas Tungsten Arc) welding was performed on hte Al alloy 1100-O plate and the same initial crack is made on HAZ(Heat Affected Zone), weld metal and base meta respectively. Specimens were used CT(Compact Tension) specimens. Initial welding residual stresses were measured by using strai gage sectioning method. All specimens were tested under constant amplitude load with stress ratio R=0.1, It is possible to predict fatigue crack growth behaviors and the fatigue life, using numerical analysis together with distribution of initial residual stress and the values of C and m obtained from $da/dN-{\Delta}K$

• 한국안전학회지
• /
• 제16권3호
• /
• pp.1-6
• /
• 2001

The study is to investigate the influence on the fatigue crack growth behaviors for the welded configuration in pressure vessel stiffener. In order to perform this goal, the automatic welded specimens were prepared. The material is ASTM A516 grade 60 steel used in pressure vessel mainly. In skip welding of pad-on-plate, continuous fillet welding and PWHT specimen, fatigue crack is generally initiated at the starting and end old toe zone, and ruptured at the starting old toe zone. The fatigue life of pad-on-plate of the continuous fillet welding specimen is larger than that of pad-on-plate skip fillet welding specimen about 85% under low load, about 20% under high load and less than that of two-pad continuous fillet welding specimen about 85%. In da/dN-$\Delta$K curve under low load, skip fillet welding specimen of pad-on-plate showed retardation on the initial crack, and the fatigue crack growth rate at the low region of $\Delta$K greater specimen E($3.8 {\times} 10^{-6}mm/cycle$). And the fatigue life of welding specimen was smaller than that of PWHT specimen.

• 대한기계학회논문집
• /
• 제13권3호
• /
• pp.461-471
• /
• 1989

본 연구에서는 혼합 모우드 균열문제의 연구를 위하여 .KAPPA.$_{II}$ /.KAPPA.S1I\ulcorner조절이 간편하고, 균열진전경로가 하중방향에 따른 균일전면의 자유표면의 영향을 균일하게 한 시험편(이하 RCM 또는 round compact mixed-mode 시험편이라 한다)을 고안하여 균열길이 및 하중작용 방향에 따른 .KAPPA.$_{I}$ 및 .KAPPA.S1II를 수치해석한 다음 일반화 하였다. 또 고강도와 용접성이 요구되는 항공기부품, 압력용기, 지상운송차량 등에 사용되고 있는 5083-H115 알루미늄 합금에 대해 혼합 모우드 균열진전 방향 및 피로균열 진전특성을 분석하고자 한다.다.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2004년도 춘계학술발표대회 논문집
• /
• pp.219-222
• /
• 2004

The effects of short fiber and particle hybrid reinforcement on fatigue crack propagation behaviors in aluminum matrix composites have been investigated. Single and hybrid reinforced 6061 aluminum containing same 20 $Al_2O_3\;volume\%$ with four different constituent ratios of short fibers and particles were prepared by squeeze casting method and tested to check the near-threshold and stable crack growth behavior. The fatigue threshold of the composites increased with portion of particle contents and showed the improved crack resistance especially in low stress intensity range. Addition of particle instead of short fiber also increased fracture toughness due to increase of inter-reinforcement distance. These increase in both fatigue threshold and fracture toughness eventually affected the fatigue crack growth behavior such that the crack growth curve shift low to high stress intensity factor value. Overall experimental results were shown that particle reinforcement was enhanced the fatigue crack resistance over the whole stress intensity factor range.