• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2009년도 춘계학술대회 논문집
• /
• pp.302-305
• /
• 2009

This paper examines the effect of nitride formation on formability for Cu bearing high strength extra low carbon (ELC) steel sheets. For this purpose, we have investigated the effect of addition of aluminium (Al) and boron (B) on texture and precipitation behavior of the ELC steel during continuous annealing. Mechanical properties and microstructures of the ELC steel sheets were analyzed as well using uni-axial tensile test, electron back-scattered diffraction (EBSD) technique and transmission electron microscopy (TEM) following pilot rolling and continuous annealing. It has been found that the addition of Al and B increases the precipitation of AlN and BN. What is more, the scavange of solute nitrogen is effective in increasing the formability of the ELC steels. In addition, the Al and B addition improves the aging property of the ELC steel.

• 한국재료학회지
• /
• 제14권12호
• /
• pp.863-869
• /
• 2004

The purpose of this research is to investigate the mechanical property and ductile-brittle transition temperature of Ti-Nb-P added extra low carbon interstitial free steel having a tensile strength of 440 MPa. The mechanical property and transition temperature of hot rolled steel sheets were more influenced by the coiling temperature rather than by the small amount of alloying element. Further, at the same composition, the property of the specimen coiled at low temperature was superior to that obtained at higher coiling temperature. The fracture surface of 0.005C-0.2Si-1.43Mn steel coiled at $630^{\circ}C$ showed a ductile fracture mode at $-100^{\circ}C$, but coiling at $670^{\circ}C$ showed a transgranular brittle fracture mode at $-90^{\circ}C$. The galvannealed 0.006C-0.07Si-1.33Mn steel sheet annealed at $810^{\circ}C$ has tensile strength and elongation of 442.8 MPa and $36.6\%$, respectively. The transition temperature of galvannealed 0.006C-0.07Si-1.33Mn steel sheet was increased with a drawing ratio, and the transition temperature of the galvannealed 0.006C-0.07Si-1.33Mn steel was $-60^{\circ}C$ at a drawing ratio of 1.8

• 한국재료학회지
• /
• 제3권2호
• /
• pp.131-139
• /
• 1993

극저탄소 알루미늄 킬드강내에 합금원소로 첨가된 Al, Ti, Nb, B등은 열처리 공정중 질화물이나 탄화물로 석출되어 강의 재결정집합조직을 변화시킴으로써 강판재의 디입드로잉 특성에 결정적인 영향을 미친다. 본 연구에서는 Ti및 Nb를 단독으로 또는 동시에 첨가한 데 이어, B, P, Si 및 Mn등을 추가로 첨가한 극저탄소 고강도 강판의 집삽조직에 미치는 질화물, 탄화물과 같은 미세 석출물의 영향을 TEM, SEM, 광학현미경분석에 의하여 조사하였다. Nb 및 Ti를 동시에 첨가한 강에서는 미세한 N$b_2$C 및 T$i_2$AIN가 주로 석출되는 반면, Nb를 단독으로 첨가한 강에서는 미세한 AIN 및 조대한 BN이 석출되고,Ti를 단독으로 첨가한 강에서는 비교적 조대한 T${i_4}{N_3}$및 조대한 ${N_10}{N_22}$/T$i_68$이 석출되는 것으로 관찰되었다. 또한 이러한 탄질화물들의 석출에 의하여 세 강이 서로 다른 결정입도를 나타내는데, 결정입도는 Nb 및 Ti동시첨가강과 Nb단독첨가강이 서로 비슷하고, Ti단독첨가강이 가장 큰 것으로 나타났다.

• 한국재료학회지
• /
• 제3권1호
• /
• pp.43-49
• /
• 1993

AI킬드한 극저탄소강에 Ti, Nb등의탄화물 또는 질화물 형성원소를 첨가하면 우수한 디프드로잉특성과 내시효성을 나타내는 강판을 얻을 수 있다고 알려져 있으므로 본 연구에서는 Ti및 Nb를 단독 또는 동시에 첨가하거나 B를 추가로 첨가한 고강도 극저탄소 강판을 제조하여 각각의재결정 집합조직과 기계적 성질을 측정비교하여 보았다. 역극점도에 나타난 집합조직강도의 변화를 조사한 결과 어닐링처리에 의하여 (100)면 강도와 (111)면 강도의 변화가 가장 많이 나타난 것은 Nb첨가강이며, Nb와 Ti를 단독으로 첨가한 강과 Ti를 단독으로 첨가한 강은 변화정도가 비슷하였다.극점도를 비교하면,Nb와 Ti를 동시에 첨가한강, Nb를 단독으로 첨가한 강 그리고 Ti를 단독으로 첨가한강 모두 냉간 압연한 상태에서는{112}<110>집합조직이 발달하였으며 어닐링처리한 후에는 {111}<112>집합조직이 잘 발달하였다. 그러나 세 종류의 강간에 집합조직의 차이는 별로 없었다. 결정립도와 관계가 깊은 경도에서는 결정립도가 가장 작은 Nb 및 Ti동시첨가강에서 경도가 가장 높고, Nb단독첨가강, Ti단독첨가강의 순서로 감소하는 경향을 보였다.

• 열처리공학회지
• /
• 제19권4호
• /
• pp.208-218
• /
• 2006

The effects of the grain size on the magnetic properties in extra-low carbon steel after strain annealing were investigated. Two kinds of sample were prepared. One is the annealed sheet, which was annealed at $670^{\circ}C$ and $850^{\circ}C$ for various time periods after cold rolling. The other is the strain annealed sheet, which was temper rolled by 0.4% and subsequently strain annealed at the temperature ranging between $670^{\circ}C$ and $850^{\circ}C$ for various time periods. The grains after strain annealing became more coarse than those after primary annealing. The grains were coarsened due to the strain induced grain boundary migration (SIGM). It was found that the permeability tended to be increased and coercivity tended to be decreased with the increase of grain size. The optimum magnetic properties was achieved after strain annealing at $850^{\circ}C$ for 30 minites. Under this condition, the coercivity was measured to be 0.6 and the permeability was measured up to be 13000.

• 한국표면공학회지
• /
• 제31권5호
• /
• pp.286-296
• /
• 1998

Galvannealing is becomming the main stream of the coating technology applied to automobile outer and inner panels due to its low cost and easy application applied to automobile outer and inner panels due to its low cost and easy application in thick Zn coating, compared to electro galvanizing. Despite of filed up data with an experience in this field, galvannealing in thick Zn coating is getting more difficult because of the absence of Fe deposition in Zn coating. As a result, it exhibits, with different steel sheet and grain size there is a proper temperature range which is good for the tarket coating thickness of galvannealing. In case of 1,200mm wide and 0.77 mm thick extra low carbon steel with 20$mu extrm{m}$ grain size, its proper temperature range for galvannealing of one side 60g/$\textrm{m}^2$ is 470-$480^{\circ}C$.

• 대한금속재료학회지
• /
• 제48권3호
• /
• pp.187-193
• /
• 2010

The solute carbon content in ferrite is one of the important factors to obtain good formability in low carbon steels. Although most of the carbons are consumed by the formation of grain boundary cementite during coiling after hot-rolling, the carbon content after coiling is normally observed much more than that of equilibrium. In this study, a classical nucleation and growth model is used to simulate the precipitation kinetics of the grain boundary cementite from coiling temperature (CT) to room temperature (RT). The predicted precipitation behaviors depending on the initial carbon content and the cooling rate are compared with the reported. As a result, the lateral growth of thickening of cementite is a major factor for the sluggish reaction of grain boundary cementite. The reduction of solute carbon content after coiling is divided into three regions: a) increase due to no cementite precipitation, b) decrease due to the fast length-wise growth of cementite, c) increase due to the slow thickness-wise growth of cementite.

• 대한금속재료학회지
• /
• 제46권10호
• /
• pp.609-616
• /
• 2008

Conventional bake-hardenable(BH) steels should be annealed at higher temperatures because of the addition of Ti or/and Nb which forms carbides and raises recrystallization start temperature. In this study, the development of new BH steels without Ti or Nb addition has been reviewed. The new BH steels have nearly same mechanical properties as the conventional BH steels even though it is annealed at lower temperature. The steels also show smaller deviation of the mechanical properties than that of the conventional BH steels because of the conarol of solute carbon content during steel making processes. The deviation of mechanical properties in conventional BH steels is directly dependent on the deviation of solute carbon which is greatly influenced by the amount of the carbide formers in conventional BH steels. Less alloy addition in the newly developed BH steels gives economical benefits. By taking the advantage of sulfur and/or nitrogen which scarenge in Interstitial-Free or conventional BH steels, fine manganese sulfides or nano size copper sulfides were designed to precipitate, and result in refined ferrite grains. Aluminum nitrides used as a precipitation hardening element in the developed steels were also and resull in fine and well dispersed. As a result, the developed steels with less production cost and reduced deviation of mechanical properties are under commercial production. Note that the developed BH steels are registered as a brand name of MAFE(R) and/or MAF-E(R).

• 한국재료학회지
• /
• 제4권1호
• /
• pp.44-54
• /
• 1994

Ti, Nb B를 합금원소로 첨가한 알루미늄 킬드 극저탄소 고강도 강판의 재결정 집합조직에 미치는 코일링처리시의 냉각속도, 냉간가공도, 연속어닐링처리등의 효과를 조사하였다. 집합조직계수비 TC(222)/TC(200)는 코일링시의 냉각속도 감소와 냉간압연시의 입하율 증가에 따라 증가하는 경향을 나타내었다. 그러나 압하율이 80%에서 90%로 증가됨에 따라 집합조직계수비가 오히려 감소하는 경향을 나타내는데, 이것은 주집합조직이 {554}<225>로부터 {111}<112>로부터 {111}<112>로 바뀌기 때문인것으로 보여진다. 집합조직계수비를 최대로 만들기위한 최적의 강판제조 공정 조건을 제시하면, 코일링처리시 노냉하고, 냉간압연시의 압하율은 80%로 하며, 연속열처리시 $800^{\circ}C$에서 1분간 유지한다음 $20^{\circ}C$로 수냉하고 다시 $450^{\circ}C$에 5분간 과시효처리하는 것이다.

• 소성∙가공
• /
• 제11권1호
• /
• pp.24-35
• /
• 2002

Recent trend and future prospect of flat rolling of steel has been summarized based on the earlier reports. Key technology in the plate rolling is to have ultra fine microstructure having high resistance against crack propagation during application. Heavy accelerated cooling facility and high power rolling mill will be helpful to develope the high toughness steel. Precise modeling of properly prediction based on deformation and transformation imposed on microstructure of steel during processing is highly anticipated. For the hot strip rolling process, new trend is lies on the production of ultra-thin gauged hot strip to substitute cold rolled strip. For the substitution of cold rolled strip into hot rolled strip widely, high formable property of hot strip is highly required. For the formabilit, the ferritic rolling of extra low carbon steel under high lubricated condition is essential. Recently introduced semi-continuous thin slab and rolling mill line is very plausible to develope those kinds of products easily In the view groin facility combination. New idea to modify the existing continuous hot strip mill line to produce the ultra thin-gauged hot strip in an economic way is suggested in this report.