• Journal of the Korean Applied Science and Technology
• /
• v.32 no.3
• /
• pp.512-521
• /
• 2015

In this research, environmental friendly organic acid containing microetching system to improve adhesion strength between photoresist resin and Copper Clad Laminate(CCL) was developed without using strong oxidant $H_2O_2$. Etching rate and surface contamination on CCL were examined with various etching conditions with different etchants, organic acids and additives. to develope an optimum microetching condition. Etching solution with 0.04 M acetic acid showed the highest etching rate $0.4{\mu}m/min$. Etching solution with the higher concentration of APS showed the higher etching rate but surface contamination on CCL is very serious. In addition, stabilizer solution also played an important role to control the surface contamination. As a result of research, the etching solution containing 0.04 M of acetic acid, 0.1 M of APS with 4 g/L of stabilizer solution(ST-1) was best to improve adhesion between CCL and photoresist resin as well as showed the most clean and rough surface with the etching rate of $0.37{\mu}m/min$.

• Journal of the Korean institute of surface engineering
• /
• v.26 no.5
• /
• pp.271-279
• /
• 1993

Experiments on electorchemical etching of aluminum foils with high cubic textures were carried out in this study. Etching behaviours and pit shapes with respect to various conditions of eletrochemical etching were in-vestigated. When HCl and NaCl solutions were used as electrolytes, the highest capacitanes were observed in solutions of 1MHCl and 5M NaCl. It was foundd that capacitance was improved by addition of H2SO4 to HCl so-lution which is considered to be due to the suppression of oxide film formation on the aluminum surface. The homogeneous distribution of each pits obtained in the HCl solution, while the degree of weight loss was lowest in the Nacl solution. The best etching properties in 1M HCl solution were obtained at the etching condi-tions of 0.15 A/$\textrm{cm}^2$, 150sec and$ 90^{\circ}C$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.70-71
• /
• 2007

Multicrystalline silicon(mc-Si) solar cells are steadily increasing their share of the PV market due to the lower material costs. However, commercial mc-Si solar cells have lower efficiency than singlecrystalline silicon solar cells. To improve efficiency of mc-Si solar cells, it is important to reduce optical losses from front surface reflection. Isotropic etching with acid solution based on hydrofluoric acid(HF) and nitric acid$(HNO_3)$ is one of the promising methods that can reduce surface reflectance for mc-Si solar cells. Anisotropic etching is not suitable for mc-Si because of its various grain orientations. In this paper, we isotropically etched mc-Si using acid solution. After that, etched surface was observed by Scanning Electron Microscope(SEM) and surface reflectance was measured. We obtained 29.29% surface reflectance by isotropic etching with acid solution in wavelength from 400nm to 1000nm for fabrication of mc-Si solar cells.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2004.05a
• /
• pp.245-249
• /
• 2004

Transparent materials such as fused silica are important materials in optical and optoelectronics field because of its outstanding properties, such as transparency in a wide wavelength range, strong damage resistance for laser irradiation, and high thermal and chemical stability. However, these properties make it difficult to micromachine silica in micro-sized quantities. In this study, we fabricated a micro patterns on the surface of fused silica plate using laser induced wet etching. KrF excimer laser was used as a light source. There were no burrs and micro cracks on the etched surface of fused silica and the flatness of the etched surface was fairly good. We investigated the influence of etchant upon the etch rate and quality in laser induced wet etching. Pyrene-acetone, toluene, and pyrene-toluene solution were used as etchant. In the side of etch rate, toluene and pyrene-toluene solution were better than pyrene-acetone solution.

• Applied Chemistry for Engineering
• /
• v.20 no.5
• /
• pp.557-560
• /
• 2009

In this study, a new wet etching method and the solution for thinning the glass with the thickness below $100{\mu}m$ were investigated. For the preparation of etching solution with low hydrofluoric acid, it was effective to use $NH_4F$ or $NH_4HF_2$ as a main ingredient with the addition of sulfuric acid or nitric acid. Influence of the composition of mixed acid solution and the temperature on the etching rate was investigated. The addition of anionic surfactant provides the function to prevent the adhesion of sludge generated by the etching reaction. A new wet etching pilot device equipped with streaming generation parts was used to test etching of commercial non-alkali glass and soda lime glass. The non-alkali glass with the thickness of 640 ${\mu}m$ and soda lime glass with the thickness of $500{\mu}m$ were etched to $45{\mu}m$ and $100{\mu}m$, respectively, by using the pilot device. After the etching by pilot device, the roughness degree of the glass surface was maintained at $0.01{\sim}0.02{\mu}m$.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.1
• /
• pp.60-72
• /
• 1996

A photoetching process is widely used for small and high precision parts in machinery, electronic and semi-conductor industries. One of the high precision parts, grid is very important part of digitron which use electron display, and it is fabricated by only photoetching process because of high precision. In this study, to develop high precision digitron grid, characteristics of etching solution were investigated with electrochemical test, that was potentiodynamic test and immersion test in the ferric chloride solution and added some additives. Based on the electrochemical etching test, grid was fabricated by continuous photoetching process at various etching condition. From the result of measured line width and etching depth under-cut and etching factor were calculated. For the fabrication of 25$\mu\textrm{m}$ line width, optimal etching condition was etching temperature 40~$45^{\circ}C$, spray pressure 1.5kg/$\textrm{cm}^2$ and etching time 3~4min.

• Journal of the Korean institute of surface engineering
• /
• v.27 no.3
• /
• pp.158-165
• /
• 1994

Cu-Cr alloy thin film requires good quality of etching be used for TAB technology. The etched cross sec-tion was clean enough when the etching was performed in 0.1M $FeCl_3$ solution at $50^{\circ}C$. The etching rate was increased with the amount of $KMnO_4$. For enhanced profile of cross section and rate, the spray etchning was found to be superior compared to the immersion etching. A series of experiments were performed to improve the uniformity of the current distribution in electrodeposition onto the substrate with lithographic patterns. Copper was electrodeposited from quiescent-solution, paddle-agitated-solution, and air-bubbled-solution to in-vestigate the effect of the fluid flow. The thickness profile of the specimen measured by profilmetry has the non uniformity at feature scale in quiescent-solution, because of the longitudinal vortex roll caused by the natural convection. However, uniform thickness profile was achieved in paddle-agitated or air bubbled solu-tion.

• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.1344-1348
• /
• 2003

It is generally known to be difficult to etch a surface of a transparent material such as fused silica by conventional laser ablation in which the surface is simply irradiated with a laser beam. A lot of studies have been done to provide a method capable of efficiently etching transparent materials without defects such as cracks. One of the promising methods or the micro-machining of optically transparent materials is laser induced etching. In this study, micro-drilling of fused silica by laser induced wet etching was conducted. KrF excimer and YAG laser were used as light sources. Acetone solution pyrene and ethanol solution of rhodamine were used as etchant.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1997.11a
• /
• pp.397-400
• /
• 1997

This paper presentes the characteristics of Si anisotropic etching and electrochemical etch-stop in aqueous TMAH/IPA/pyrazine solution. (100) Si etching rate of 0.747 $\mu\textrm{m}$/min which faster 86% than TMAH 25 wt.%/IPA 17 vol.% solution was obtained using best etching condition at TMAH 25 wt.%/IPA 17 vol.%/pyrazine 0.1 g and the etching rate of (100) Si was decreased with more additive quantity of pyrazine. I-V curve of p-type Si in TMAH/IPA/pyrazine was obtained. OCP(Open Circuit Potential) and PP(Passivation Potential) were -2 V and -0.9 V, respectively. Si diaphragms were obtained by electrochemical etch-stop in aqueous TMAH/IPA/pyrazine solution.

• Journal of the Semiconductor & Display Technology
• /
• v.2 no.4
• /
• pp.19-22
• /
• 2003

In this paper, Si anisotropic etching characteristics of tetramethylammonium hydroxide (TMAH)/ammonium persulfate (AP) solutions were investigated to realize the optimum structure of a diaphragm for the piezoresistive pressure sensor application. Due to its low toxicity and its high compatibility with the CMOS processing, TMAH was used as Si anisotropic etchants. The variations of Si etch rate on the etching temperature, TMAH concentration, and etching time were obtained. With increasing the etching temperature and decreasing TMAH concentrations, the Si etch rate is increased while a significant non-uniformity exists on the etched surface because of formation of hillocks on the <100> surface. With the addition of AP to TMAH solution, the Si etch rate is increased and an improvement in flatness on the etching front is observed. The Si etch rate is also maximized with increasing the number of addition of AP to TMAH solution per one hour. The Si square diaphragms of 20$\mu\textrm{m}$ thickness and 100-400 $\mu\textrm{m}$ one-side length were fabricated successfully by adding AP of (5/6)g to 800 ml TMAH solution every 10 minutes.