• Proceedings of the KIEE Conference
• /
• 2001.07c
• /
• pp.1890-1892
• /
• 2001

This paper described on the fabrication of microstructures by DRIE(Deep Reactive Ion Etching). SOI(Si-on-insulator) electric devices with buried cavities are fabricated by SDB technology and electrochemical etch-stop. The cavity was fabricated the upper handling wafer by Si anisotropic etch technique. SDB process was performed to seal the fabricated cavity under vacuum condition at -750 mm Hg. In the SDB process, captured air and moisture inside of the cavities were removed by making channels towards outside. After annealing(1000$^{\circ}C$, 60 min.), the SDB SOI structure was thinned by electrochemical etch-stop. Finally, it was fabricated microstructures by DRIE as well as a accurate thickness control and a good flatness.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.8
• /
• pp.711-714
• /
• 2008

Metal-oxide-semiconductor (MOS) capacitors were fabricated to investigate the plasma damage caused by reactive ion etching (RIE) on (100) oriented silicon-on-insulator (SOI) substrates. The thickness of the top-gate oxide, SOI, and buried oxide layers were 10 nm, 50 nm, and 100 nm, respectively. The MOS/SOI capacitors with an etch-damaged SOI layer were characterized by capacitance-voltage (C-V) measurements and compared to the sacrificial oxidation treated samples and the reference samples without etching. The measured C-V curves were compared to the numerical results from corresponding 2-dimensional (2-D) structures by using a Silvaco Atlas simulator.

• Journal of the Korean Institute of Telematics and Electronics D
• /
• v.34D no.9
• /
• pp.64-71
• /
• 1997

A new etching technique of meltback was investigated for GaAs lensed optical devices with selective windows opending in the LPE (liquid phase epitaxy) system. In the meltback process, the etch depth and the etch shape were controlled by the degree of under-saturation, etch time and other parameters. A GaAs/AlGaAs DH layer was grown on the selectively etched hemispherical well for optical device application such as lensed surface emitting LED. The regrowth process were related with the coolin grate and the well to well spacing. A novel surface emitting LED with hemispherical AlGaAs lens was fabricated using the meltbakc and regrowth as the key process for AlaAs lens array. The light emitting efficiency of the LED was upto three times higher than the similar structure LED without lens. The meltback and regrowth technique was applicable to manufacture the optical device in LPE.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2000.04a
• /
• pp.97-102
• /
• 2000

We have studied etching characteristic of Ta film using Electron Cyclotron Resonance (ECR) etcher system. Microwave source power. RF bias power. and working pressure were varied to investigate the etch Profile. And we have used two step etching method to acquire the goWe have studied etching characteristic of Ta film using Electron Cyclotron Resonance (ECR) etcher system. Microwave source power. RF bias power. and working pressure were varied to investigate the etch Profile. And we have used two step etching method to acquire the good etch profile preventing the microloading effect.od etch profile preventing the microloading effect.

• Journal of the Korean Ceramic Society
• /
• v.31 no.5
• /
• pp.485-490
• /
• 1994

The reactive ion etching characteristics of aluminum oxide films, prepared by PECVD, were investigated in the CCl4 plasma. The atomic chlorine concentration and the DC self bias were determined at various etching conditions, and their effects on the etch rate of aluminum oxide film were studied. The bombarding energy of incident particles was found to play the more important role in determining the etch rate of aluminum oxide rather than the atomic chlorine concentration. It is considered to be because the bombardment of ions or neutral atoms breaks the strong Al-O bonds of aluminum oxide to help activate the formation reaction of AlCl3 which is the volatile etch product.

• Journal of the Korean institute of surface engineering
• /
• v.30 no.1
• /
• pp.44-56
• /
• 1997

Influence of electrochemical etching conditions on capacitance gain of aluminium electrolytic on capacitor foil has been investigated by etching cubic textured high purity aluminum foil in dilute hydrochloric acid. Uniformly distributed etch pit tunnels on aluminum surface have been obtained by pretreatment aluminium foil in 10% NaOH solution for 5 minutes followed by electrochemical etching. Electrostatic capacitance of etched aluminium foil anodized to high voltage increased with the increase of current density, total charge, temperature and concentration of electrolyte up to maximum CV-value and then deceased. Election optical observation of the etched foil revealed that the density of etch of etch pits increased with the increase of current density and concentration of electrolyte. this increase of etch pit density enlarged of the increase of capacitance. However, abnormal high current density and high electrolyte concentration induced the local dissolution of the foil surface which resulted the decrease of foil capacitance.

• Applied Science and Convergence Technology
• /
• v.23 no.4
• /
• pp.169-178
• /
• 2014

Fluid model based numerical analysis is done to simulate a low damage etch back system for 20 nm scale semiconductor fabrication. Etch back should be done conformally with very high material selectivity. One possible mechanism is three steps: reactive radical generation, adsorption and thermal desorption. In this study, plasma generation and transport steps are analyzed by a commercial plasma modeling software package, CFD-ACE+. Ar + $CF_4$ ICP was used as a model and the effect of reactive gas inlet position was investigated in 2D and 3D. At 200~300 mTorr of gas pressure, separated gas inlet scheme is analyzed to work well and generated higher density of F and $F_2$ radicals in the lower chamber region while suppressing ions reach to the wafer by a double layer conducting barrier.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.11a
• /
• pp.244-245
• /
• 2015

PEALD TiN 금속 전극을 갖는 MOS device에서 SC1 ($NH_4/H_2O_2/H_2O=1:2:5$), SPM ($H_2SO_4/H_2O_2=10:1$), $H_2O_2$ etch chemical을 이용해 TiN 식각 후 oxide 표면 잔류 Ti에 의한 전기적 특성 분석을 진행 하였다. Etch chemical 중 SPM을 이용한 소자의 전기적 특성이 우수하였는데, 이는 잔류Ti atom의 양이 다른 etch chemical을 사용한 것 대비 낮았기 때문이다. 이로 인하여 낮은 leakage current, less frequency dependence의 특성이 관찰되었다. 또한, 후속 열처리를 통해 더욱 우수한 특성이 관찰 되었다. 이러한 공정기술은 single 전극을 갖는 CMOS 형성 시 사용 될 수 있을 것으로 기대된다.

• Journal of Integrative Natural Science
• /
• v.2 no.3
• /
• pp.207-210
• /
• 2009

Multiple rugate structures can be etched on a silicon wafer and placed in the same physical location, showing that many sharp spectral lines can be obtained in the optical reflectivity spectrum. Porous silicon samples were prepared by electrochemical etch of heavily doped p-type silicon wafers. The etching solution consisted of a 3:1 volume mixture of aqueous 48% hydrofluoric acid and absolute ethanol. Galvanostatic etch was carried out in a Teflon cell by using a two-electrode configuration with a Pt mesh counterelectrode. A sinusoidal current density waveform varying between 51.5 and $74.6mA/cm^2$ is applied. The anodization current was supplied by a Keithley 2420 high-precision constant current source which is controlled by a computer to allow the formation of PSi multilayer.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.06a
• /
• pp.423-426
• /
• 1998

Piezoresistive pressure sensors have fabricated using electrochemical etch-stop technique. Si diaphragm having thickness of n-epi. layer was fabricated and used to detect pressure range from 0 to 1 kg/$\textrm{cm}^2$. Piezoresistors were diffused 3${\times}$10$\^$18/ cm$\^$-3/ and placed at diaphragm edge for maximum pressure detection. The characteristics of electrochemical etch-stop in TMAH/lPA/pyrazine solution were also discussed. I-V curves of n and p-type Si in TMAH/lPA/pyrazine solution were obtained. Etching rate is highest at optimum etching condition, TMAH 25wt.%/IPA 17vo1.%/pyrazine 0.1/100m1, thus the elapsed time of etch-stop was reduced.