• Corrosion Science and Technology
• /
• v.7 no.6
• /
• pp.370-374
• /
• 2008

In this study, we evaluated anti-corrosion properties of both commercial unleaded and lead epoxy primer for automotive substrate before applying to actual painting lines by salt spray test, and cyclic corrosion test, potentiodynamic test and electrochemical impedance spectroscopy. The difference in the corrosion resistance between automotive epoxy primers contained $Bi(OH)_{3}$ and leaded one was investigated. And it was also discussed the effect of zinc phosphate pretreatment to the epoxy primers. The specimen coated epoxy primer contained $Bi(OH)_{3}$ showed 0.5 V higher corrosion potential than that of bare steel. The result of salt spray test did not indicate remarkable difference of corrosion resistance in all specimens above $10{\mu}m$ thickness up to 1200 hours. In the cyclic corrosion test, epoxy primers contained $Bi(OH)_{3}$ on phosphated substrate performed good corrosion properties until 800 hours. The epoxy primer contained $Bi(OH)_{3}$ performed the equivalent corrosion resistance as leaded coating on phosphated steel, but slightly inferior to that of leaded on bare steel. These results show that the pre-treatment of zinc phosphate is effective as well as pigment changing in performing anti-corrosion properties in automotive bodies.

• Corrosion Science and Technology
• /
• v.14 no.2
• /
• pp.59-63
• /
• 2015

Airless spray which is widely used for painting to ship blocks and hull sides is the coating method for attaching atomized paint material to the substrate using spray tip nozzle with compressed air. When the paint material which has high solid contents such as epoxy primer paint is atomized by passing through spray tip nozzle with high pressure, the nozzle composed of tungsten carbide(WC) undergoes the erosive wear, leading to widening of nozzle hole. The deformation of nozzle hole induces improper spray pattern and coating failures such as finger pattern and sagging because the conditions of spray pump pressure and paint flow rate for developing full spray pattern are changed. In this study, an appropriate replacement cycle of spray tip was predicted by measuring the erosive wear tendency as increasing the spraying time of epoxy primer paint.

• Journal of the Korean Applied Science and Technology
• /
• v.24 no.4
• /
• pp.399-409
• /
• 2007

Characteristics of polyaniline anti-corrosive coatings with various primer coating resins(epoxy resin, urethane resin, and others) and top coating resins(epoxy and acrylic urethane resins) were investigated through adhesion, acid resistance, alkaline resistance, water resistance, and anti-corrosion tests. As a result, the anti-corrosive properties of the prepared coatings using polyaniline varied with the types of primer and top coating resins. In this condition, the properties of adhesion, chemical resistance, and water resistance were found to be very satisfactory when using emeraldine base (EB) of polyaniline blended with single-packaged urethane and acrylic urethane resins as the primer coatings, and using acrylic urethane resin as the top coatings. Also, the anti-corrosive function of these anti-corrosive coatings was well preserved for 1000 hr in the salt spray experiment.

• Korean Journal of Materials Research
• /
• v.9 no.12
• /
• pp.1160-1169
• /
• 1999

In this study, the silane primers were introduced to improve the interface adhesion between copper and epoxy. Especially, the polymer types obtained by solution and emulsifier-free emulsion polymerization of vinyltriethoxysilane and the low molecular weight types of 3-aminopropyltriethoxysilane(3-APTES) and 3-glycidoxypropyltrimethoxysilane(3-GPTMS) were used to improve the adhesion strength between epoxy and copper. Also, the surface of copper was treated by 1,1,1-trichloroethane. According to the results, the interfacial adhesion strength of copper-epoxy increased about 2~5 times with the introduction of silane primer. Also, the optimum treatment time of copper surface was about 10 minutes. Additionally, the adhesion strength as a function of concentration of low molecular weight silane was maximum at about 0.5 vol.% for 3-APTES and about 0.2 vol% for 3-GPTMS.

• Journal of Electrical Engineering and Technology
• /
• v.8 no.3
• /
• pp.603-609
• /
• 2013

In this paper, we describe the analysis of inkjet-printed silver (Ag) patterns on epoxy-coated substrates according to several reliability evaluation test method guidelines for conventional printed circuit boards (PCB). To prepare patterns for the reliability analysis, various regular test patterns were created by Ag inkjet printing on flame retardant 4 (FR4) and polyimide (PI) substrates coated with epoxy for each test method. We coated the substrates with an epoxy primer layer to control the surface energy during printing of the patterns. The contact angle of the ink to the coated epoxy primer was $69^{\circ}$, and its surface energy was 18.6 $mJ/m^2$. Also, the substrate temperature was set at $70^{\circ}C$. We were able to obtain continuous line patterns by inkjet printing with a droplet spacing of $60{\mu}m$. The reliability evaluation tests included the dielectric withstanding voltage, adhesive strength, thermal shock, pressure cooker, bending, uniformity of line-width and spacing, and high-frequency transmission loss tests.

• Corrosion Science and Technology
• /
• v.6 no.5
• /
• pp.219-226
• /
• 2007

Pre-construction primer (PCP), or shopprimer, have been applied to steel plates to control temporary corrosion during ship fabrication. For surface preparation at ship block stage, in common shipyard practices, welding beads, burnt and rusted areas shall be blasted or power tool cleaned and the contamination such as zinc salt shall be removed with blasting or power tool. Whereas, the sound film of PCP needs not to be removed or roughened as the paint having good compatibility with PCP is used for the first coat. In many cases, however, full blasting or sweep blasting on the sound PCP treated block assemblies was requested. There still has been argument about the legitimacy of this practice, thus, it is critical to evaluate the quality of the coating system applied on the sound PCP retained condition, comparing with the one applied on the full blasted or sweep blasted condition. In this study, two different epoxy systems for water ballast tank were applied on the surfaces with sound PCP condition, full blasted condition, and sweep blasted condition. Coating performances such as durability, anti-corrosion, cathodic disbondment resistance were evaluated. The test results clearly indicated that the sound film of PCP needed not to be removed or roughened as the paint having good compatibility with PCP based on inorganic zinc silicate.

• Elastomers and Composites
• /
• v.35 no.2
• /
• pp.89-97
• /
• 2000

Waterborne epoxy resins have been developed in order to meet environmental regulations for reduction of the emission of organic solvents from coating industry As each generation has filled a performance gap in the previous technology, new waterborne epoxy resin has developed. Initially, waterborne epoxy resins were used primarily on masonry, but the subsequent generations have found utility for the protection of metallic substrates as well. Indeed, the third generation systems have been formulated to produce the high performance industrial maintenance primers which possess the desirable combination of good corrosion resistance and low volatile organic compound levels. This paper outlines the important guidelines for formulating waterborne epoxy primers from waterborne epoxy resin that has recently developed in our company. The importance of using the appropriate resin-curing agent system at the optimized epoxy to amine ratio is stressed.

• Corrosion Science and Technology
• /
• v.10 no.3
• /
• pp.80-86
• /
• 2011

Welding was widely used in shipbuilding industries as a joining method. In present study, the effects of welding fume contaminated on steel surface on corrosion protection were examined by water ballast simulation test and condensation chamber test. Pull-off adhesion test, blistering test and cathodic disbondment test were carried out to evaluate the effects of residual welding fume. Consequently, it was clearly indicated that the residual welding fume didn't affect the corrosion protection of epoxy coated on steel when surface was treated by light sweep blasting to heavy sweep blasting which was applied in this study.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.11a
• /
• pp.997-1002
• /
• 2001

Tensile strength of CFRP (Carbon Fiber Reinforced Polymer) is approximately 10 times higher than that steel reinforcement, but the design strength of CFRP is normally reduced by the bond failure between RC and CFRP. Many researches have been carried out, concerned with bond behavior between RC and CFRP to prevent the unpredicted bond failure of RC beam strengthened by CFRP, but the national design code for design bond strength of CFRP hasn't been constructed. In this study, 3 beams specimen strengthened by CFRP under the variable of bonded length were tested to derive the design bond strength of CFRP to the RC flexural members. Also 2 beams specimen strengthened by CFRP were tested to inspect the construction environment effects such as mixing error of epoxy resin and the amount of primer epoxy resin. From the test results, It is concluded that the maximum design bond strength of CFRP to RC flexural member is considered to be $\tau_{a}$=8kgf/$cm^{2}$.

• Corrosion Science and Technology
• /
• v.6 no.2
• /
• pp.62-67
• /
• 2007

Several heavy duty coatings at an every kind industry facilities to various systems currently have been applied review to the many industry fields. Corrosion-protective characteristics in the case of novolac epoxy among them and unsaturated polyester have been applied most widely. epoxy and flake heavy duty coatings are applied for such reason in an every kind facilities(stack, FGD, cooler, chemical tank etc) of a fossil-fuel power plants Cases of the fossil-fuel power plants are exposed to more severe corrosion environment compared with other facilities and It is difficult to display the performance of long-term method at apply to be the partial. Our study shows fluoro-polymer composite coating method to overcome of the limit. The comparison did previous method and heavy duty coating about FGD plants most at a corrosion environment among fossil-fuel power plants. Additionally, other facilities examined different heavy duty method. The design mode of fluoro-polymer composite coating according to an every kind facilities show extensive methods that are characteristic revelation of film(top, middle and primer layer) composition of the paint, film thickness in accordance with a facilities corrosion and the corrosion protective effectiveness to come into being use fluoro-polymer composite with heavy duty paint(epoxy).