• 한국재료학회:학술대회논문집
• /
• 한국재료학회 1999년도 춘계학술발표강연 및 눈문개요집
• /
• pp.127-127
• /
• 1999

• 한국표면공학회지
• /
• 제31권6호
• /
• pp.393-399
• /
• 1998

The composition and the properred orientation of Co-Fe-Cr alloy electrodeposits were invesigated according to the electrolysis conditions using sulface bath. The current efficiency and the cathode overpotential decrased noticeably with the increase of Cr content in the bath. As the D.C. current density increased increased, the Cr content in the alloy increasd, while Co content decreased and Fe content remained constant, In the pulse current electrolysis, the Cr content of the alloy increased with the mean current density and off-time and then its content increased mord more noticeably with the peak current density than that of D.C. electrolysis. The preferred orientation of the alloy changed from (220)+(111) to (220) with decreasing cathode overpotential.

• 한국표면공학회지
• /
• 제30권3호
• /
• pp.202-212
• /
• 1997

The composition and the microstructure of the Sn-Ni alloy electrodeposited in pyrophosphate bath were investigated according to the electrolysis conditions. The cathode current efficiency increased with the addition of $NH_4CI$ and glycine, while it decreased with the increase of current density. The Sn content of the alloy deposits increased with the increase of $NH_4CI$ in the bath. The alloys with 51~71wt.% Sn had the NiSn single phase structure. The preferred orientation of the single phase alloys changed from (110) to (110)+(101) with the increase of current density and cathode overpotential. The single phase alloys with 50~60wt.%Sn had the smooth surface structure with fine crystallite, while the multiphase alloys showed the surface structure with crystal size and cracks at high curret density.

• 한국표면공학회지
• /
• 제28권6호
• /
• pp.352-360
• /
• 1995

The effect of electrolysis conditions on the composition, the magnetic properties and the preferred orientation of Ni-Fe-Co alloy deposits was investigated using the sulfate-chloride bath paddle agitated. Cathode current efficiency increases with the current density, showing the different tendency of the variation from that of the Ni-Fe electrodeposits. The Co content of the deposits decreases with increasing current density, while the content of Ni and Fe is shown to be minimum or maximum at 3A/$dm^2$ respectively. The Ni/Fe ratio of the alloy deposits is lower than that of Ni-Fe deposits. The coercive force($H_c$) of the deposits increases with the Co content in deposit, showing the relatively low value in the range of 1.8~5.0Wt.% Co. The anisotropy field ($H_k$) of the deposits is higher than that of Ni-Fe alloy deposits, The preferred orientation of the deposits is generally (200), but the orientation factor(R) changes with both the increase of current density and the magnetic field applied during deposition.

• 한국표면공학회지
• /
• 제21권4호
• /
• pp.149-159
• /
• 1988

Electrodeposition of chromium from low concentration chromjum (III) sulfate complexess in aqueous using sodium formate-glycine mixtures as a complexing agent was studied. In the bath formation, it is found that the optimum again temperature and time for equilibration of the electrolytes are nrcessary for 24 hrs at 45$^{\circ}C$and the optimum elecrical charge for low current electrolysis which might be produced Cr(II) ions in the electrolytes is necessary for minum 2Ah/$\ell$. The optmun concentration off standard electrolyte for main composition is 0.05M chromium(III) sulfate, 0.2M sodium formate-0.2M glycine, and I mMNaSCN as a catalysea, respectivwly. The standard electrolyte is shows good covering, good throwing power, and 6% of current efficiency (Cr(III)basis). The oppearance of electrodeposits shows att active bright chromium. The SEM morphology of the chromjum coating is observed as smooth surfaces and dispersed micro prcro pores. X-ray diffraction analysis shows a bcc structure which the perferred orintation of the chromium electrodeposits is strongin(200)plane.

• 한국표면공학회지
• /
• 제47권3호
• /
• pp.116-120
• /
• 2014

The addition of cyclo propane carbonyl (cpc) to chromium electroplating bath resulted in a chromium deposit which had greatly improved mechanical properties compared to conventional chromium deposits in condition of heat treatment at high temperature. The as-deposited layers had a Vicker's hardness of about 1170, which is comparable to that of conventional chromium plating deposits. With annealing, the hardness goes through a maximum of 1650 at $600^{\circ}C$. Generally speaking, the hardness of conventional plating decreases monotonically with heat treatment. X-ray diffraction show that annealing up to above $400^{\circ}C$ causes formation and growth of chromium crystallites and that chromium carbides form at above $500^{\circ}C$ temperature.

• 한국표면공학회지
• /
• 제17권3호
• /
• pp.73-77
• /
• 1984

The surface residual stresses in 1mm thick nickel electrodeposits obtained from four types of nickel sulphamate baths at 40 to 60$^{\circ}C$ and 5 to 25 amps./$dm^2$ were measured by a X-ray method. An increase in nickel chloride concentration in the bath tends to increase tensile residual stresses in the deposits. Addition of no chloride or little chloride in the baths gave rise to little residual stresses or even compressive stresses in the deposits. The residual stresses in most specimens did not exceed 80 MPa and showed minimum in the specimens obtained at 50$^{\circ}C$.

• 한국표면공학회지
• /
• 제37권1호
• /
• pp.13-21
• /
• 2004

The deposition rate, the current efficiency and surface morphology of trivalent Cr deposits were investigated according to additives in sulfate bath and current density. The deposition rate of the Cr deposits plated from the formic acid complexed bath was noticeably higher than that of the glycine complexed bath. The current efficiency of the deposition from formic acid bath was higher than that of the glycine bath and increased with current density in the range of 20-50 A/d$\m^2$. The current efficiency of the deposition from the formic acid bath with boric acid buffer was higher than that of the bath with aluminum sulfate or boric acid-aluminum sulfate buffers. The nodular crystallite size of the Cr deposits increased with current density and the uniform and crack-free growth of the deposits for the aluminum sulfate was observed compared to the other buffers.

• 한국표면공학회지
• /
• 제37권1호
• /
• pp.28-39
• /
• 2004

The effect of trace metallic additives on microstructure, surface appearance and hardness of zinc electrodeposits was investigated by using sulfate bath and flow cell system. The preferred orientation of Zn deposit with Fe additive was (103)(104)+(002) mixed texture and that of Zn deposits with both Fe-Ni and Fe-Co additives was (10 1), while Zn deposits with Fe-Cr additives had (002) preferred orientation. The surface morphology of the zinc deposits was closely related to the preferred orientation of the deposits. The glossiness of Zn deposit with Fe-Ni additives was higher than that of pure Zn deposit, while the glossiness of Zn deposits with both Fe-Co and Fe-Cr additives was lower than that of pure Zn deposit. The hardness of Zn deposits with both Fe-Ni and Fe-Co additives was noticeably higher than that of Zn-Fe deposit, while that of Zn deposit with Fe-Cr additives was similar to that of Zn-Fe deposit.

• 한국표면공학회지
• /
• 제22권4호
• /
• pp.207-214
• /
• 1989

The surface morphology and the proferred orientation of the Pb-Sn alloy electrodeposite were investated by the change of electrolysis conditions in pulse current electroplating. The preferred orientation of Pb-phase in alloy deposits was changed in the sequence of (110)longrightarrow(100)or(100)+(111)longrightarrow(111) with increasing peak current density, while that of $\beta$-Sn phase changed from (321)+(301)to(301)+(111) mixed orientation. The surface morphology was closely related to the preferred orientation of alloy electrodeposits. The alloy deposits, which had (100)or(111) for pb-phase and (321)or(100)(301)for $\beta$-Sn sespectively, showed the surface structure of granular crystallites. The alloy deposits whih mixed orientations for both phases had microstructure of closely the closely stacked crysrallites, which was inclined to the surface.