• Corrosion Science and Technology
• /
• v.7 no.1
• /
• pp.35-39
• /
• 2008

We have been studying application of electrochemical noise (Fluctuation) analysis for localized corrosion. Foils of Zinc, Aluminum and Magnesium were used as specimens for electrochemical cell simulating localized corrosion. These specimens were dipped in sodium chloride solutions adjusted to each exponent of Hydrogen ion concentration (pH) condition of 5.5, 10, 12 respectively. Time variations of potential and current were measured in those solutions, and simultaneously the surfaces of specimens were observed using microscope with television monitor. Two types of electrochemical cells were arranged for experiments simulated localized corrosion. The fluctuations on trendy component of short-circuited potential and short-circuited current were appeared in synchronization. It was seemed that these fluctuations result from hydrogen evolution on the aluminum active site in the crevice from the microscopic observation. In the case of zinc and magnesium, fluctuations appeared on the trendy component of the corrosion potential. Two types fluctuation were detected. First one is the fluctuation varied periodically. The second one is the random fluctuation. It was seemed that these fluctuations result from generation of corrosion products and hydrogen evolution on the active site in the crevice of zinc and magnesium from the microscopic observation.

• Corrosion Science and Technology
• /
• v.3 no.3
• /
• pp.102-106
• /
• 2004

Al foil used was 99.9 and 99.99 %. Test solution used was NaCl solution. The noise was determined using controlled potential electrolysis at -200 and -700 mV vs. NHE. The current fluctuation was caused by breakdown and repaired process of aluminum oxide film. The current fluctuation value of noise was proportion to degree of growth. The number of noise was proportion to the number of pit. The examining of current flutulation value and number of noise could be evaluated corrosion. A 99.99 % Al foil was the mostly crystal of {100} plane, and showed three-dimensional, as azimuth pit with along the direction of this place piled up. A 99.9 % Al foil was polycrystal, and in order of (311) >(222) >(200) >(111) plane. The azimuth pit did not occurred as the dissolution was occurred from each plane.