• 한국염색가공학회지
• /
• 제10권4호
• /
• pp.1-6
• /
• 1998

It is important in the durable water and oil repellent finishing for wool fabric what kinds of water-repellent agents will be used. Water repellent agents and its concentration were aleady chosen in the previous paper, one of the crosslinking agents which has less damages(harsh handle or yellowing) to the treated fabrics was a low molecular weight urethane-based resins(eg. Elastron BN-11). In repellent finishing, fabrics were padded in a bath which contained aqueous solution of water-repellent agents, and crosslinking agents, and wetting agents, followed by drying and curing. The most suitable treating condition for excellent repellency and durability to dry-cleaning was as follows ： Fabrics are padded at liquor pick-up ratio of 50%, with aqueous solution which contained $30g/\ell$ of water-repellent agents, and $1g/\ell$ of crosslinking agents, and 40g/s of wetting agents. And the padded fabrics were dried at $110^\circ{C}$ for 1 minute, and cured at $160^\circ{C}$ for 1 minute. For the fabrics, water and oil repellencies and durability to repeated dry-cleanings were observed. For enhancing the durability to dry-cleaning, the role of crosslinking agents was important for they bonds water-repellent agents and fibers to 3-dimensional net structure. Therefore, the most suitable drying and curing conditions should be selected according to the kinds of crosslinking agents.

• 한국염색가공학회지
• /
• 제10권1호
• /
• pp.33-37
• /
• 1998

It is rather important in the water and oil repellent finishing for wool fabric what kind of water-repellent agents will be used. In many cases, Fluorocarbon-based water-repellent agents(eg.Oleophobol-S), the surface tensions of which very low, were recom-mended on account of good water and oil repellencies. In repellent finishing, fabrics were padded in a bath which contained aqueous solution of water-repellent agents, and wetting agents, followed by drying and curing. The most suitable treating condition for excellent repellency was as follows Fabrics were padded at liquor pick-up ratio of 50%, with aqueous solution which contained $30g/\ell$ of water-repellent agents, and $40g/\ell$ of wetting agents. And the padded fabrics were dried at $110^\circ{C}$ for 1 minute, and cured at $160^\circ{C}$ for 2 minutes. For the fabrics, water and oil repellencies and durability to repeated dry-cleanings are observed.

• 폴리머
• /
• 제29권5호
• /
• pp.433-439
• /
• 2005

내구발수성 고분자를 얻기 위해 불소화 알킬아크릴레이트-스테아릴아크릴레이트-m-이소프로페닐-$\alpha,\;alpha$-디메틸벤질 이소시아네이트(TMI)를 유화중합시켜 불소화 알킬기와 이소시아네이트기를 가지는 공중합체를 제조하였다. 3 단량체의 공중합속도는 비이온 유화제 및 비이온-양이온 혼합 유화제의 사용에 따라 상당히 의존하였고 그 최적조건을 얻었다. 공중합체의 입자크기는 105에서 222nm의 범위에 있었고 비이온-양이온의 혼합 유화제에 의해 만들어진 공중합체가 비이온 유화제로 만들어진 공중합체보다 입자가 작았다. 나일론과 면의 모델 화합물로 N-메틸아세트아미드와 셀로비오스 각각과 TMI는 반응하지 않았다. 반면에 TMI와 부틸아민은 실온에서 반응하였다. 혼합 유화제에 의해 제조된 공중합체를 코팅한 나일론과 PET 천에 대한 세탁 전후의 물의 접촉각은 $139^{\circ}$와 $133^{\circ}$ 정도였다. 따라서 공중합체의 내구발수성은 우수하였다

• 한국응용과학기술학회지
• /
• 제5권1호
• /
• pp.63-70
• /
• 1988

The quaternized compound of the copolymer between 2-diethylaminoethyl methacrylate and stearyl methacrylate (DSACC) was chosen as the mother resin for the water repellent of acrylics. The quaternized compound of 1-lauroyl dis (amino ethyl)-2-dodecyl imidazoline (LDDIC) was used to promote softening effect and hydrostatic pressure for the water repellent. The water repellent (EDUWC) obtained from the DSACC and LDDIC blended with waxes and emulsifiers improved the properties such as the water repellency, washable, tear strength and crease recovery when it was treated on the nylon fabrics with and without the resin. The reaction mechanism between the Nylon fiber and EDLWC was examined, and EDLWC was confirmed as the durable water repellent.

• 공업화학
• /
• 제5권2호
• /
• pp.345-356
• /
• 1994

내구유연발수제를 제조할 목적으로 전보에서 합성한 poly(OMA-co-DAMA)[PODC], poly(DMA-co-DAMA)[PDDC], poly(EMA-co-DAMA)[PEDC] 각각의 양이온화물, 본 실험에서 합성한 지방산 카르바미드의 양이온화물(ODTCC), 왁스류 및 유화제들을 블렌드시켜 발수제 PODCW, PDDCW, PEDCW를 각각 제조하였다. 발수제 PODCW, PDDCW, PEDCW 각각을 면직물에 단독 및 수지병용으로 처리하여 내세탁성, 인열강도, 방추도 및 접촉각 등을 측정해 본 결과, 물성의 향상을 가져왔다. 그러나 발수도는 PODCW의 경우 80 정도로 사용 가능하였으나, PDDCW와 PEDCW의 발수도는 현저히 저하되었다. 제조된 발수제의 적정 열경화온도는 $140^{\circ}C$, 적정 사용농도는 3wt%이었고, 사용된 발수제용 촉매 중 아세트산나트륨이 가장 좋았으며, 촉매의 사용농도는 0.6wt%가 적당하였다. 또한 발수제와 셀룰로오스 섬유화의 반응메카니즘을 규명하고 내세탁성 결과치를 검토한 결과, 제조된 발수제가 내구성 발수제임을 입증하였으며, SEM으로 발수처리된 면직물의 표면구조를 관찰하였다.

• 한국응용과학기술학회지
• /
• 제36권2호
• /
• pp.531-540
• /
• 2019

친수성 및 소수성 나노실리카를 tetraethyl orthosilicate(TEOS)를 커플링제로 사용하여 유리 표면에 거친 스파이크 구조 형성과 반응성 hydroxyl기를 동시에 도입한 후 불소를 함유한 실란으로 2차 코팅처리하여 궁극적으로 발수성 유리 표면 형성의 최적 조건을 확립하는 연구를 수행하였다. 소수성 나노실리카인 실리카 에어로졸을 이용한 초소수 도막의 형성은 나노실리카 표면에 반응성인 -OH기가 존재하지 않아 내구성이 있는 소수성 도막을 형성할 수 없었다. 이에 반하여 친수성기를 가진 나노실리카와 가수분해된 TEOS를 포함하는 코팅액 이용하여 유리 표면을 1차 코팅한 후 2차로 trichloro-(1H,1H,2H,2H)perfluorooctylsilane(TPFOS) 용액으로 코팅하여 $150^{\circ}$ 이상의 수접촉각을 가지는 초소수 표면을 제조하였으며, $1^{\circ}$ 이하의 물 슬라이딩각을 보여 초발수성도 동시에 가지고 있었다. 이에 덧붙여 친수성 나노실리카의 함량이 증가할수록 광투과도가 감소하였으며, TPFOS 용액에 의해서도 광투과도가 감소하였다. 코팅된 유리시편의 내구성 50회 문지름까지는 초소수성을 유지하였으나, 200회 문지름에서는 단지 소수성만을 유지하였다. 결론적으로 최적의 코팅액의 조건은 친수성 나노실리카의 함량이 0.3 g인 HP3 코팅액을 2회 코팅한 후 2차로 TPFOS 용액으로 코팅하는 것이었다. 이렇게 제조된 코팅액은 광투과도가 중요한 솔라셀의 표면 처리제로 사용이 가능할 것으로 판단된다.