• 한국재료학회지
• /
• 제24권1호
• /
• pp.13-18
• /
• 2014

In order to clarify the effect of Nb addition on the ductile-brittle transition property of sintered TiC, TiC-10 mol% Nb composites were researched using a three-point bending test at temperatures from room temperature to 2020 K, and the fracture surface was observed by scanning electron microscopy. It was found that the Nb addition decreases the ductile-brittle transition temperature of sintered TiC by 300 K and increases the ductility. The room temperature bending strength was maintained at up to 1800 K, but drastically dropped at higher temperatures in pure TiC. The strength increased moderately to a value of 320MPa at 1600 K in TiC-10 mol% Nb composites, which is 40% of the room temperature strength. Pores were observed in both the grains and the grain boundaries. It can be seen that, as Nb was added, the size of the grain decreased. The ductile-brittle transition temperature in TiC-10 mol% Nb composites was determined to be 1550 K. Above 1970 K, yieldpoint behavior was observed. When the grain boundary and cleavage strengths exceed the yield strength, plastic deformation is observed at about the same stress level in bending as in compression. The effect of Nb addition is discussed from the viewpoint of ability for plastic deformation.

• 한국공작기계학회:학술대회논문집
• /
• 한국공작기계학회 1999년도 춘계학술대회 논문집
• /
• pp.51-55
• /
• 1999

Recently, manufacturing work has been transformed to advanced technology intensive form from mass production with a little items required in the past. It was demanded that superior workpiece surface integrity. However, the study of ductile mode machining was proceeded actively.In this paper, it is developed Ultra-Micro Indentation Device using the PZT actuator. Experimentally, by using theUltra-Micro Indentation device, the micro fracture behavior of the silicon wafer was invesgated. It was possible that ductile-brittle transition point in ultimate surface of brittle material can be detected by adding an acoustic emission sensor system to the Ultra-Micro Indentation apparatus.

• 한국기계가공학회지
• /
• 제19권11호
• /
• pp.23-28
• /
• 2020

In general, lithography techniques are applied when machining single-crystal silicon in nanoscale applications; however, these techniques involve low degrees of freedom for the vertical shapes. By applying mechanical techniques to machine silicon, nanopatterns having various types of vertical shapes can be manufactured. In this study, we determined the ductile-brittle machining transition point and analyzed the- variation of the specific cutting resistance within the ductile machining region in nanoscale applications. When brittle fracture occurred during the nanoscale cutting, the depth of cut and cutting force increased and decreased rapidly, respectively. The first point of rapid increase in the depth of cut was defined as the ductile-brittle machining point. Subsequently, the shape of the machining tool was observed using a scanning electron microscope to calibrate the machining area, considering the tip blunting. The specific cutting resistance decreased continuously and converged to a certain value during the nanoscale cutting. The decrease and convergence in the value can be attributed to the decrease in the ratio of the arc length to the area of the machining tool and silicon.

• 한국생산제조학회지
• /
• 제9권1호
• /
• pp.38-44
• /
• 2000

The background of this study lies in he investigation of the formation mechanism of ductile mode(nkanometer-size) chips of brittle materials such as fine ceramics glass and silicon. As the first step to achieve this purpose this paper intends to observe the micro-deformation behavior of these materials in sub${\mu}{\textrm}{m}$ depth indentation tests using a diamond indentor. In this study it was developed Ultra-Micro Indentation. Device using the PZT actuator. Experimentally by using the Ultra-Micro Indentation device the micro fracture behavior of the silicon wafer was investigated. It was possible that ductile-brittle transition point in ultimate surface of brittle material can be detected by adding an acoustic emission sensor system to the Ultra-Micro Indentation appartus.

• 한국재료학회지
• /
• 제4권5호
• /
• pp.590-599
• /
• 1994

취성재료의 균열첨단에서 전위의 이동에 대한 거동을 이해하기 위하여 단결정의 알루미나에 대한 취성-연성 전이(BDT)에 대한 한 연구가 진행되었다. 여러 온도에서, 예비균열된 시편으로 4점 굽힘시험을 이용하여 임계응력확대계수와 항복강도가 측정되었다. 그 결과로, BDT온도는 변형속도와 시편 방향에 따라 달랐다.:(1120)파단면에 대하여 $4.2 \times 10^{-6}$와 $4.2 \times 10^{-7}s^{-1}$에서 BDT온도는 각각$1034^{\circ}C$, $1150^{\circ}C$이었다. 또한 4점굽힘 시험을 이용하여 연성영역에서 균열첨단으로 부터 방출된 전위의 이동거리과 방향은 에칭 피트법에 의해서 측정되었다. 이중 에칭법을 이용하여 즉정된 사파이어에서 전위의 이동속도는 모델링 연구에 응용되었다.

• Journal of Welding and Joining
• /
• 제22권6호
• /
• pp.57-63
• /
• 2004

Fracture toughness is an important parameter in designing offshore structures to ensure resistance to fracture at various temperatures. In this study, a series of experiments is carried out to obtain fracture toughness values (CTOD) of API 2W Gr.50B, welded using FCAW(Flux Cored Arc Weld). In particular, a comparison of absorbed impact energy and CTOD values are made with respect to two different welding groove shapes; double-V-groove and double-bevel-groove. Charpy impact tests are performed for specimens sampled near the root gap, and CTOD tests are carried out for three point bending specimens having the notch at weld zone. While Charpy impact test result is determined to be a good qualitative measure of fracture toughness, no quantitative correspondence between impact absorbed energy and CTOD values was found. Based on the experiment, it is observed that double-V-groove welds give lower transition temperature than those of double-bevel-groove.

• 대한기계학회논문집A
• /
• 제25권7호
• /
• pp.1064-1072
• /
• 2001

It is very important to evaluate material degradation like temper and carbide embrittlements to secure the reliable and efficient operational conditions and to prevent brittle failure in service. The extent of material deterioration can be accurately evaluated by mechanical test such as impact test or creep test. But it is almost impossible to sample a large specimen from in-service plants. Thus, the material degradation evaluation by a non-destructive method is earnestly required. Recently the non-destructive test technique which uses the grain boundary etching characteristics owing to the variation of material structures has been proposed. However the program for material degradation evaluation using the grain boundary etching method(GEM) in Windows 98 domain doesnt be developed now. The aims of this paper are to develop the program and to complete the new master curve equations for the evaluation of material degradation on in-serviced high temperature components.

• Korea-Australia Rheology Journal
• /
• 제15권1호
• /
• pp.9-17
• /
• 2003

The rheological behaviour of anatase $TiO_2$ with organic coating has been investigated extensively in this study. The yield stress was measured over a wide range of solids concentration and pH using stress-controlled and speed-controlled rheometers. The organic treatment leads to a shift of the isoelectric point (IEP) from around pH 5.5 to pH 2.4. A maximum yield stress occurs in the vicinity of the isoelectric point determined by electrokinetic measurements. The transition of rheological behaviour between elastic solid and viscous liquid is represented by a stress plateau in a plot of stress against strain. It is hypothesised that the slope of the stress plateau reflects the uniformity of the structure, and hence the distribution of bond strength. Altering the concentration and the surface chemistry can vary the bond strength and its distribution. therefore, resulting in different type of failure: "ductile-type" or "brittle-type". pH and volume fraction dependence of yield stress could be described quantitatively using existing models with reasonable agreement.easonable agreement.

• Journal of Advanced Marine Engineering and Technology
• /
• 제12권3호
• /
• pp.57-67
• /
• 1988

Although handicapped by the inability to bridge the size gap between small laboratory sample and large engineering component, the V charpy test sample method does possess certain advantages, such as each of preparation, simplicity of test method, speed, low cost in test machinery, and low cost per test. On the other hand, the COD test method does posses advantages, which reduce the size gap between the laboratory sample and actual engineering component. Consequently, the correlation between V charpy absorbed energy and the critical COD value is required for estimating critical COD value from the simple V charpy test results. In this paper, the high tensile strength steel AH36 plate specimens having a single edge cracked notch were investigated to find out the correlation between V charpy absorbed energy and critical COD value in the welded parts under such various welding methods as shielded metal arc welding, the submerged arc welding and the electro gas welding by means of V charpy impact test and static 3-point bending test. Main results obtained are as follow ; 1. The relationships between V charpy absorbed energy Wc' and critical COD value ($\delta_c$)show; $\delta_c$=0.0065 Wc'+0.1906. 2. Ductile- brittle transition behaviours can be estimated by means of fracture appearance and general yielding behaviours. 3. The V charpy absorbed energy of SMAW is higher than that of SAW, EGW and similar relationships are obtained in the COD tests.

• 폴리머
• /
• 제33권5호
• /
• pp.446-451
• /
• 2009

신뢰성 평가 시험법인 RS M 0042에 따라, 열화시간 경과에 따른 선형저밀도 폴리에틸렌 파이프의 신뢰성 평가를 수행하였다. 열화시간이 증가함에 따라, 인장강도는 250일 열화시점까지 비례적으로 증가하였고, 경도는 비교적 미소한 증가를 보였으며, 연신율은 점진적으로 감소하는 경향을 보였다. 이러한 결과는 열화시간이 증가함에 따른, 결정화도의 증가와 열산화에 의한 가교밀도의 증가, 사슬 전단 및 사슬 운동성의 감소 등에 기인한 것으로 판단된다. 장기정수압시험 결과는 초기의 연성파괴에서 차후 취성파괴로 전환되는 시점이 존재함을 확인하였다. 산화유도시간 측정은 선형저밀도폴리에틸렌 파이프의 열산화 정도를 관찰하기 위해 도입되었다. 측정 결과는 250일 이후 선형저밀도폴리에틸렌 파이프에 첨가된 산화방지제가 거의 고갈되었음을 보여준다. $100^{\circ}C$ 열화 조건에서 산화방지제의 잔존량을 계산할 수 있는 실험식을 열화시간의 함수로 표현하여 제안하였다. 적외선분광분석 결과는 열화된 선형저밀도폴리에틸렌 파이프 표면상에 카르보닐 및 하드록실 관능기가 증가하였음을 보여준다. 이는 선형저밀도폴리에틸렌 표면의 탄화수소 그룹의 산화가 국부적으로 발생하였음을 나타낸다.