• Journal of the Korean Society for Nondestructive Testing
• /
• v.16 no.1
• /
• pp.10-18
• /
• 1996

This study verified the relationship between fracture mechanics parameters and X-ray parameters for normalized SS41 steel with homogeneous crystal structure and M.E.F. dual phase steel(martensite encapsulated islands of ferrite). The fatigue crack propagation test were carried out and X-ray diffraction technique was applied to fatigue fractured surface. The change in X-ray parameters(residual stress, half-value breadth) according to the depth of fatigue fractured surface were investigated. The depth of maximum plastic zone, $w_y$, were determined on the basis of the distribution of the half-value breadth for normalized SS41 steel and that of the residual stress for M.E.F. dual phase steel. $K_{max}$ could be estimated by the measurement of $w_y$.

• Transactions of Materials Processing
• /
• v.29 no.1
• /
• pp.11-19
• /
• 2020

For microstructural analysis of a friction stir welded (FSWed) joint of advanced high-strength steels, dual phase (DP) and complex phase (CP) steels, are studied. FSWed joints are successfully fabricated in the following four cases: (i) DP/DP; (ii) CP/CP; (iii) DP/CP, where the advancing side is DP and the retreating side is CP; (iv) CP/DP, where the advancing side is CP and the retreating side is DP. The stir zone (SZ) of (i) the DP/DP joint mainly consists of lath martensite, while the stir zone of (ii) the CP/CP joint consists not only of lath martensite but also of bainite. In the case of (iii) DP/CP and (iv) CP/DP, they exhibit a similar microstructure including acicular-shaped phases in the joints; however, cross-sections of the joints show differences in material mixing in each case. In (iv) the CP/DP joint, temperature towards the CP steel is sufficient to cause softening, thus leading to better mixing than that in (iii) DP/CP. The phases of the SZ in each of the four cases are formed by phase transformation during the FSWed process; however, the transformed phase volume fraction of CP steel is lower than that of DP steel, indicating that dynamic recrystallization occurs mainly in CP steel. The hardness values of the SZ are significantly higher than those of the base materials, especially, the SZ of (iii) the DP/CP joint has the highest value due to highest fraction of lath martensite.

• Journal of Ocean Engineering and Technology
• /
• v.5 no.2
• /
• pp.198-198
• /
• 1991

Not only difference of fatigue crack growth and propagation behavior resulted from the grain size, the hardness ratio and volume fraction in M.E.F. dual phase steel composed of martensite in hard phase and ferrite in soft phase, but also the effects of the plastic constraint were investigated by fracture mechanics and microstructural method. The main results obtained are as follows: 1) The fatigue endurance of M.E.F. steel increases with decreasing the grain size, increasing the ratio of hardness and volume fraction. 2) The initiation of slip and crack occures faster as the stress level goes higher. These phenomena result from the plastic constraint effect of the second phase. 3) The crack propagation rate in the constant stress level is faster as the grain size gets larger, the ratio of hardness lower and volume fraction smaller.

• Corrosion Science and Technology
• /
• v.5 no.1
• /
• pp.23-26
• /
• 2006

Recent development of ultrafine grained (UFG) low carbon steels by using equal channel angular pressing (ECAP) and their room temperature tensile properties are reviewed, focusing on the strategies overcoming their inherent mechanical drawbacks. In addition to ferrite grain refinement, when proper post heat treatments are imposed, carbon atom dissolution from pearlitic cementite during ECAP can be utilized for microstructural modification such as uniform distribution of nano-sized cementite particles or microalloying element carbides inside UFG ferrite grains and fabrication of UFG ferrite/martensite dual phase steel. The utilization of nano-sized particles is effective on improving thermal stability of UFG low carbon ferrite/pearlite steel but less effective on improving its tensile properties. By contrast, UFG ferrite/martensite dual phase steel exhibits an excellent combination of ultrahigh strength, large uniform elongation and extensive strain hardenability.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.169-170
• /
• 2006

Advanced melting technology is now being employed in the manufacture of stainless steel powders. The new process currently includes electric arc furnace (EAF) technology in concert with Argon Oxygen Decarburization (AOD), High Performance Atomizing (HPA) and hydrogen annealing. The new high performance-processing route has allowed the more consistent production of existing products, and has allowed enhanced properties, such as improved green strength and green density. This paper will review these processing changes along with the potential new products that are being developed utilizing this technology. These include high strength stainless steels such as duplex and dual phase as well as stainless steel powders used in high temperature applications such as diesel filters and fuel cells.

• Journal of the Korean Society for Heat Treatment
• /
• v.10 no.2
• /
• pp.128-137
• /
• 1997

The formation processes of the retained austenite(${\gamma}_R$) in SHCP100 steel sheets were investigated in order to improve the transformation induced plasticity(TRIP) effect of ${\gamma}_R$. An excellent combination of elongation about 23% and high strength over 830 MPa was achieved by processing of intercritical annealing and isothermal holding. The mechanical properties of TRIP-aided dual phase steel was found to depend on the volume ratio of each phase and the volume fraction of ${\gamma}_R$. It was also noted that the proper mechanical stability of ${\gamma}_R$ improved the mechanical properties. In this work, the best balance of strength-ductility was obtained by holding the steel at $420^{\circ}C$ for 500sec. after annealing at $730^{\circ}C$ for 300 sec.

• Journal of Welding and Joining
• /
• v.29 no.5
• /
• pp.99-105
• /
• 2011

In this study, effect of Si content on nugget diameter in electric resistance spot welded dual-phase(DP) steel was investigated. The cold rolled DP steels with different Si content (0.5, 1.0, 1.5, 2.0 wt.%) were used and thickness of those sheet was 1.2mm. With increasing Si content, nugget diameter was increased at the same welding current. This is attributed to increase of heat input result from high resistivity. Also, nugget diameter was increased with an increase in Si content for the same heat input. For this reason, the melting point of DP steel is lowered with an increase in the Si content. And solid DP steel can easily be transformed to a liquid phase because the low melting point. Finally, a prediction formula for the nugget diameter(N.D.) could be obtained in terms of heat input(Q) and melting point(M.P) as follows: N.D.(mm) = 0.11Q(J) - 0.0031 M.P.($^{\circ}C$) + 0.32.

• Journal of the Korean Society for Heat Treatment
• /
• v.30 no.3
• /
• pp.106-112
• /
• 2017

In this study dual-phase steels with different ferrite grain size and martensite fraction were fabricated by varying micro-alloying elements and intercritical anneling temperatures, and then the tensile properties were investigated in terms of yield and tensile strengths, elongation, and yield ratio. The addition of micro-alloying elements reduced ferrite grain size, and the increased intercritial transformation tempeature increased the martensite fracton. The tensile test results showed that yield and tensile strengths of all the steel specimens increased with increasing the martensite fraction. However, the elongation and yield ratio were differently changed according to variations in the morphology and carbon content of martensite, ferrite grain size, and precipitates resulting from the addition of micro-alloying elements and intercritical annealing.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2003.10a
• /
• pp.269-273
• /
• 2003

There is a growing interest to replace the commercial steels with non-heat treated steels, which does not involve the spheroidization and quenching-tempering treatment. However, Non-heat treated steels should satisfy high strength and good formability without performing heat treatment. Therefore, it is important to investigate optimum materials showing a good combination of strength and formability after the drawing process. In this study, Dual-Phase Steels were studied as candidate materials for non-heat treated steels, which have different martensite morphologies and volume fractions obtained through heat-treatment of intercritical quenching (IcQ), intermediate quenching (ImQ) and step quenching (SQ). The mechanical properties of DP steels were measured by tension and compression tests. Also, the cold formability of three DP steels which have similar tensile strength value was investigated by estimating the deformation resistance and the forming limit. The deformation resistance which is important factor in determining die life was estimated by calculating the deformation energy. And the forming limit was estimated by measuring the critical strain revealing crack initiation at the notch tip of the specimens.

• Transactions of Materials Processing
• /
• v.13 no.1
• /
• pp.84-89
• /
• 2004

There is a growing interest to replace the commercial steels with non-heat treated steels, which does not involve the spheroidization and quenching-tempering treatment. However, Non-heat treated steels should satisfy high strength and good formability without performing heat treatment. Therefore, it is important to investigate optimum materials showing a good combination of strength and formability after the drawing process. In this study, Dual-Phase Steels were studied as candidate materials for non-heat treated steels, which have different martensite morphologies and volume fractions obtained through heat-treatment of intercritical quenching (IcQ), intermediate quenching (ImQ) and step quenching (SQ). The mechanical properties of DP steels were measured by tension and compression tests. Also, the cold formability of three DP steels which have similar tensile strength value was investigated by estimating the deformation resistance and the forming limit. The deformation resistance which is important factor in determining die life was estimated by calculating the deformation energy. And the forming limit was estimated by measuring the critical strain revealing crack initiation at the notch tip of the specimens.