We have demonstrated that simple brush-painted Ti-doped $In_2O_3$(TIO) films can be used as a cost effective transparent anodes for organic solar cells (OSCs). We examined the RTA effects on the electrical, optical, and structural properties of the brush painted TIO electrodes. By the direct brushing of TIO nanoparticle ink and rapid thermal annealing (RTA), we can simply obtain TIO electrodes with a low sheet resistance of 28.25 Ohm/square and a high optical transmittance of 85.48% under atmospheric ambient conditions. Furthermore, improvements in the connectivity of the TIO nano-particles in the top region during the RTA process play an important role in reducing the resistivity of the brush-painted TIO anode. In particular, the brush painted TIO films showed a much higher mobility ($33.4cm^2/V-s$) than that of previously reported solution-process transparent oxide films ($1{\sim}5cm^2/V-s$) due to the effects of the Ti dopant with higher Lewis acid strength (3.06) and the reduced contact resistance of TIO nanoparticles. The OSCs fabricated on the brush-painted TIO films exhibited cell-performance with an open circuit voltage (Voc) of 0.61 V, shot circuit current (Jsc) of $7.90mA/cm^2$, fill factor (FF) of 61%, and power conversion efficiency (PCE) of 2.94%. This indicates that brush-painted TIO film is a promising cost-effective transparent electrode for printing-based OSCs with its simple process and high performance.

• Korean Journal of Materials Research
• /
• v.23 no.5
• /
• pp.255-259
• /
• 2013

An effect of thermal annealing on activating phosphorus (P) atoms in ZnO nanorods (NR) grown using a hydrothermal process was investigated. $NH_4H_2PO_4$ used as a dopant source reacted with $Zn^{2+}$ ions and $Zn_3(PO_4)_2$ sediment was produced in the solution. The fact that most of the input P elements are concentrated in the $Zn_3(PO_4)_2$ sediment was confirmed using an energy dispersive spectrometer (EDS). After the hydrothermal process, ZnO NRs were synthesized and their PL peaks were exhibited at 405 and 500 nm because P atoms diffused to the ZnO crystal from the $Zn_3(PO_4)_2$ particles. The solubility of the $Zn_3(PO_4)_2$ initially formed sediment varied with the concentration of $NH_4OH$. Before annealing, both the structural and the optical properties of the P-doped ZnO NR were changed by the variation of P doping concentration, which affected the ZnO lattice parameters. At low doping concentration of phosphorus in ZnO crystal, it was determined that a phosphorus atom substituted for a Zn site and interacted with two $V_{Zn}$, resulting in a $P_{Zn}-2V_{Zn}$ complex, which is responsible for p-type conduction. After annealing, a shift of the PL peak was found to have occurred due to the unstable P doping state at high concentration of P, whereas at low concentration there was little shift of PL peak due to the stable P doping state.

• Journal of the Korean Magnetics Society
• /
• v.5 no.4
• /
• pp.275-280
• /
• 1995

The sites for $Fe^{+3}$ are partly substituted by $Co^{+2}$ and $Ti^{+4}$ cations to control coercivity of Ba-ferrite particles for use in high density magnetic recording. The substituted $Co^{+2}$ cation has very much different effects on magnetic properties and particle characteristics from that $Ti^{+4}$ cation has. The decrease in the coercivity with the $Co^{+2}$ substitution is attributed to the formation of excessive spinel-block(S-block) in pure Ba-ferrite crystal, while saturation magnetization is increased and the distributions of coercivity and particle size become broad. The substitution with the $Ti^{+4}$ decreases the sauration magnetization, but has less effect on a change in coercivity than the $Co^{+2}$. The $Ti^{+4}$ acts as a nucleation agent in amorphous phase of formulated compound, and consequently particle size and aspect ratio are decreased. Furthermore, the enhancement of substitution of the $Co^{+2}$ for the $Fe^{+3}$ sites in rhombohedral-block(R-block) by the $Ti^{+4}$ retards the nucleation of spinel phase of Ba-ferrite, which results in uniform magnetic properties of Ba-ferrite particles. It is suggested that the contents of the cations to be substituted for the $Fe^{+3}$ sites are optimized on the bases of magnetic properties and particle characteristics rather than on the base of electrical charge balance.

• Korean Journal of Materials Research
• /
• v.11 no.3
• /
• pp.227-235
• /
• 2001

In this work, Zn$_2$SiO$_4$:Mn phosphors were prepared by solid state reaction. The effect of sintering/reduction temperature, flow rate of H$_2$-5%/$N_2$-95% mix gas, and ball milling conditions have been investigated on the sake of PDP(Plasma Display Panel) application. The characteristics such as particle morphology and photoluminescence of prepared phosphors were compared to those of commercial Zn$_2$SiO$_4$:Mn Phosphors. It was found that the Phosphor synthesized at 130$0^{\circ}C$ with 0.08 Mn concentration had a maximum brightness, This brightness was increased more 20% by reduction treatment under 100me/min flow rate of 5%H$_2$-95%$N_2$ mixed gas. The size of particles decreased under 3$\mu\textrm{m}$ after ball milling. Especially, higher luminescence was obtained in our Zn$_2$SiO$_4$:Mn phosphors than commercial Zn$_2$SiO$_4$:Mn phosphors, so that they are able to be applied for PDP.