• Nuclear Engineering and Technology
• /
• 제46권5호
• /
• pp.681-688
• /
• 2014

Hydride reorientation behaviors of PWR cladding tubes under typical interim dry storage conditions were investigated with the use of as-received 250 and 485ppm hydrogen-charged Zr-Nb alloy cladding tubes. In order to evaluate the effect of typical cool-down processes on the radial hydride precipitation, two terminal heat-up temperatures of 300 and $400^{\circ}C$, as well as two terminal cool-down temperatures of 200 and $300^{\circ}C$, were considered. In addition, two cooling rates of 2.5 and $8.0^{\circ}C/min$ during the cool-down processes were taken into account along with zero stress or a tensile hoop stress of 150MPa. It was found that the 250ppm hydrogen-charged specimen experiencing the higher terminal heat-up temperature and the lower terminal cool-down temperature generated the highest number of radial hydrides during the cool-down process under 150MPa hoop tensile stress, which may be explained by terminal solid hydrogen solubilities for precipitation, and dissolution and remaining circumferential hydrides at the terminal heat-up temperatures. In addition, the slower cool-down rate generates the larger number of radial hydrides due to a cooling rate-dependent, longer residence time at a relatively high temperature that can accelerate the radial hydride nucleation and growth.

• 세라미스트
• /
• 제23권2호
• /
• pp.114-131
• /
• 2020

Fracture in the titanium carbonitride-metal composites occurs by crack propagation through the carbonitride grains or in the interfaces. Thus, intrinsic properties of the carbonitride need to be enhanced and the interfaces should be also modified to coherent structure to strengthen the composites. Especially, interfacial structure can be the main factor to determine the mechanical properties of titanium carbonitride-metal composites because the interfaces between carbonitride grains and metallic phase are weak parts due to heterogeneous nature of carbonitride and metallic phase. In this paper, methodologies for improving the interfacial structure of titanium carbonitride-metal composites are suggested. Total area of the interfaces can be reduced using solid solution type carbonitrides as raw materials instead of a mixture of various carbonitrides in the composites. Also, synthesis of titanium carbonitride-metal composite powders and the low-temperature sintering of the composite powders for short time can be the way for formation of coherent interfaces. The sintering of the composite powders for short time at low temperature can reduce the potential of formation of interfaces by dissolution and precipitation of carbonitride in the liquid metal. As a result of formation of coherent boundaries due to low-temperature and short-time sintering, interfaces between titanium carbonitride grains and metallic phase have the favorable structure for the enhanced fracture toughness. It is believed that the low-temperature sintering of solid solution type composite powders for short time can be the way to improve the low toughness of the titanium carbonitride-metal composites.

• 한국표면공학회지
• /
• 제54권5호
• /
• pp.285-293
• /
• 2021

High-entropy TiAlCrSiN nano-composite coating was designed to improve mold life for high temperature liquid molding. Alloy design, powder fabrication and single alloying target fabrication for the high-entropy nano-composite coating were carried out. Using the single alloying target, an arc ion plating method was applied to prepare a TiAlCrSiN nano-composite coating had a 30 nm TiAlCrSiN layers are deposited layer by layer, and form about 4 ㎛-thickness of multi-layered coating. TiAlCrSiN nano-composite coating had a high hardness of about 39.9 GPa and a low coefficient of friction of less than about 0.47 in a dry environment. In addition, there was no change in the structure of the coating after the dissolution loss test in the molten metal at a temperature of about 1100 degrees.

• Corrosion Science and Technology
• /
• 제2권5호
• /
• pp.233-237
• /
• 2003

Pickling inhibitors can be used to form an adsorbed layer on the metal surface to hinder the discharge of H^+$ and dissolution of metal ions. Nitrogen-containing inhibitors were selected as corrosion inhibitors for mild steel (MS) in pickling acid process. In this study, the addition of inhibitor, the pickling temperatures and the pickling times were the parameters to investigate the effects on the inhibition efficiency (IE) for MS by using weight loss measurement. Preliminary results show that the IE increased with the increase in pickling time from 10 minutes to 60 minutes, and the IE also increased with the increase in temperature at room temperature and $40^{\circ}C$. At the higher temperature. the IE values are higher and almost independent with the pickling time. Furthermore, the potentiodynamic polarization, open circuit corrosion potential-time and corrosion current-time studies show that nitorgen-containing inhibitor behaves predominantly as cathodic polarization. The roughness test and SEM investigation are also studied in this paper.

• Journal of Welding and Joining
• /
• 제13권1호
• /
• pp.89-102
• /
• 1995

The evaluation of reheat cracking susceptibility in CrMoV turbine rotor steel was performed using thermally simulated heat affected zones. The examinations were carried out in terms of microstructural characterization, microhardness measurement and a Charpy type notch opening three point bend test. It was found that reheat cracking susceptibility increased as the peak temperature increased. This effect was due to the combined effects of the carbide dissolution and unrestricted grain growth at 1350.deg. C peak temperature. Reheat cracking susceptibility was estimated based on microhardness measurement and prior austenite grain size. It was established that for this particular material, reheat cracking in coarse grained heat affected zone can be eliminated if the microhardness is below about 360DPH and the grain size is below about 30.mu.m. It is evident that reheat cracking susceptibility can be eliminated or reduced by carefully controlling the welding parameters such that a refined structure is produced in the coarse grained heat affected zone.

• The Plant Pathology Journal
• /
• 제32권6호
• /
• pp.563-569
• /
• 2016

The spatial patterns for temperature distribution on crape myrtle leaves infested with sooty mold were investigated using a digital infrared thermal imaging camera. The mean temperatures of the control and sooty regions were $26.98^{\circ}C$ and $28.44^{\circ}C$, respectively. In the thermal images, the sooty regions appeared as distinct spots, indicating that the temperatures in these areas were higher than those in the control regions on the same leaves. This suggests that the sooty regions became warmer than their control regions on the adaxial leaf surface. Neither epidermal penetration nor cell wall dissolution by the fungus was observed on the adaxial leaf surface. It is likely that the high temperature of black leaves have an increased cooling load. To our knowledge, this is the first report on elevated temperatures in sooty regions, and the results show spatial heterogeneity in temperature distribution across the leaf surface.

• Restorative Dentistry and Endodontics
• /
• 제8권1호
• /
• pp.115-121
• /
• 1982

Sodium hypochlorite solution has been widely used as endodontic irrigant due to its ability to dissolve pulp tissue debris and its antimicrobial action. This in vitro study was conducted to evaluate the solvent action of sodium hypochlorite solution on vital pulp tissue under various conditions include concentration, exposure time, and temperature. The percentage of weight loss due to pulp tissue dissolution was calculated with weight difference of lyophilized specimens before and after the exposure to test solutions. The results were as follows; Statistical analysis indicated that the ability of both 5.0% and 2.5% sodium hypochlorite solutions to dissolve pulp tissue was significantly greater than that of distilled water, but no significant difference was found between 5.0% and 2.5% sodium hypochlorite solutions. There was no significant increase in the pulp tissue dissolving ability of sodium hypochlorite solutions; as exposure time increased 2 minutes, 5 minutes, and 10 minutes. Of the given temperatures, no significant difference was found in the solvent aciton of sodium hypochlorite solution on pulp tissue between $20^{\circ}C$ (room temperature) and $37^{\circ}C$(body temperature).

• 대한금속재료학회지
• /
• 제48권6호
• /
• pp.543-550
• /
• 2010

This paper investigated the synthesis conditions of nano-sized $TiO_2$ powder in a hydrothermal process at a temperature range of $100{\sim}180^{\circ}C$ considering the precipitation agent, precipitation pH, reaction temperature and time. Titanium hydroxide formed by $NH_4OH$ exhibited a lower crystallization temperature than that by NaOH and formed less aggregated $TiO_2$ particles. As the precipitation pH increased above 8, the shape of the particles changed from spherical to needle form, which appeared to be caused by dissolution and re-precipitation of the titanium hydroxide in an alkali environment.

• KEPCO Journal on Electric Power and Energy
• /
• 제7권1호
• /
• pp.153-159
• /
• 2021

A two-step process for increasing the leaching efficiency of yttrium and neodymium from coal fly ash were investigated at solid loadings of 5.0 g ash ~1,000 g ash/l of 1.0 N~10.0 N H₂SO₄, temperature ranging from 30℃ to 90℃, ultrasonic leaching time of 1~10 hours, and ultrasonic power of 25~200 W. The yttrium and neodymium from coal fly ash were effectively leached into ion phases by step change of the first conventional dissolution at room temperature and then the second heating process with the aid of ultrasonic wave, and maximum leaching efficiency of yttrium and neodymium obtained were 66 % and 63 %, respectively. The activation energies for the leaching reaction of yttrium and neodymium at second heating process dependent on leaching time and temperature were derived to be 41.540 kJmol^-1 and 507.92 kJmol^-1, respectively. The optimum conditions for the maximum leaching of yttrium and neodymium were found to be the solid loading of 250 g ash/l of H₂SO₄, solvent concentration of 2.0 N H₂SO₄, and second step process of temperatures of 30℃ for 3 hours and then 90℃ for 4 hours with ultrasonic intensity of 100 W.

• 열처리공학회지
• /
• 제7권1호
• /
• pp.25-34
• /
• 1994

To investigate the effect of austenitizing tempratures on the mechanical properties and corrosion resistance of 0.19%C-13.6%Cr martensitic stainless steel, the changes in martensitic trasformation temperatures, mechanical properties and anodic polarization curve were examined after changing the austenitizing temperatures and tempering temperatures. On increasing heating rate at the same austenitizing temperatures, $A_s$, $A_r$ and $M_s$ increased. And the $M_s$ temperature showed to be decreased with increasing austenitizing temperature. With increasing tempering temperature up to $500^{\circ}C$, strength, hardness and impact value were not changed remarkably, on the other hand the tensile strength and hardness decreased and impact value increased after tempering above $550^{\circ}C$ owing to the $M_{23}C_6$ carbide precipitation. The abrupt decrease in elongation at the tempering temperture of $500^{\circ}C$ proved to the precipitation of $M_7C_3$ carbide. The effect of austenitizing temperature on the mechanical properties of the tempered specimen showed to be decreased in impact value and elongation at the austenitizing temperature of $1150^{\circ}C$. At low tempering temperatures the corrosion resistance of the tempered specimen was not changed obviously with increasing tempering temperature. On the other hand, the resistance decreased above the tempering temperature of $600^{\circ}C$ due to the precipitation of $M_{23}C_6$ carbides. The corrosion resistance showed to be improved with increasing the austenitizing temperature owing to the dissolution of carbides.