• Proceedings of the Materials Research Society of Korea Conference
• /
• 1999.11a
• /
• pp.97-97
• /
• 1999

• Journal of information and communication convergence engineering
• /
• v.1 no.2
• /
• pp.67-69
• /
• 2003

The experimental studies for the etch properties of the oxide grown on silicon substrate, which is in diluted hydrogen fluoride (HF) solution, are presented. Using different ion implantation dosages, dopants and energies, silicon substrate was implanted. The wet etching in diluted HF solution is used as a mean of wafer cleaning at various steps of VLSI processing. It is shown that the wet etch rate of oxide grown on various implanted silicon substrates is a strong function of ion implantation dopants, dosages and energies. This phenomenon has never been reported before. This paper shows that the difference of wet etch rate of oxide by ion implantation conditions is attributed to the kinds and volumes of dopants which was diffused out into $SiO_2$ from implanted silicon during thermal oxidation.

• Journal of the Korean institute of surface engineering
• /
• v.28 no.3
• /
• pp.182-191
• /
• 1995

A highly porous silicon layer was fabricated by anodizing single crystalline silicon in a dilute solution of hydrofluoric acid. The color of the porous silicon changed from red and blue to yellow gold during the anodizing process. The current-voltage (I-V) curve of the anodizing process showed a typical Schottky diode rectification form. The cell voltage decreased with the increase of HF concentration in the solution at high current range. However, the voltage was independent on HF concentration in the solution at low current range. The pore size was dependant on anodizing condition (HF concentration, current and anodizing time). The pore size and wall width of porous silicon layer were 4~6 and 1~3 nm, respectively. Surface of the porous silicon was covered with silicon compound ($SiH_x$etc.) according to IR spectrum analysis. The peak wavelength and width of photoluminescence (PL) spectrum of porous silicon were 650~850 nm (1.5~1.9 eV) and 250 nm, respectively. The photoluminescence intensity and peak wavelength, and porosity of porous silicon increased with increasing anodizing current and decreased with increasing HF concentration in the anodizing solution.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.2
• /
• pp.117-122
• /
• 2001

In this paper, we report on photoelectrochemical etching process of 6H-SiC semiconductor wafer. The etching was performed in two-step process; anodization of SiC surface to form a deep porous layer and thermal oxidation followed by an HF dip. Etch rate of about 615${\AA}$/min was obtained during the anodization using a dilute HF(1.4wt% in H$_2$O) electrolyte with the etching potential of 3.0V. The etching rate was increased with the bias voltage. It was also found out that the adition of appropriate portion of H$_2$O$_2$ into the HF solution improves the etching rate. The etching process resulted in a higherly anisotropic etching characteristics and showed to have a potential for the fabrication of SiC devices with a novel design.

• Journal of the Korean Ceramic Society
• /
• v.39 no.3
• /
• pp.315-320
• /
• 2002

Treatment effects of dilute hydrofluoric acid (6 wt% HF) on the surface properties of $Al(OH)_3$ were investigated at the molar ratio of F/Al(fluoride/aluminum)=0.15. Temperature and pH variations in the reaction system were recorded to analyze reaction mechanism between $Al(OH)_3$ and aqueous Hf. The reaction of HF to the surface of $Al(OH)_3$ accompanied with a quantity of heat evolution, resulting in increasing temperature of a reactionsystem. And also the reaction was proceeded as transitional state which metastable ${\alpha}-form\;AlF_3{\cdot}3H_2O$ was transferred to insoluble ${\beta}$-form. The resulting ${\beta}-form\;AlF_3{\cdot}3H_2O$ formed by a surface treatment was identified by FT-IR and X-ray diffractormetry. The formation of ${\beta}$-form aluminum fluoride hydrates with diameter less than $1{\mu}m$ on the surface of $Al(OH)_3$ could be visulaized by SEM imgae, making up a coating layer as precipitate-like. The surface whiteness of $Al(OH)_3$ treated with aqueous HF was furthermore increased approximately 6.6% due to the formation of surface hydrates.

• The Korean Journal of Ceramics
• /
• v.4 no.1
• /
• pp.28-32
• /
• 1998

This paper reports on photoluminescence (PL), luminescence decay curves, and compositional analysis of porous silicon(PS) which is aged under air ambient by Fourier transform infrared vibrational spectroscopy (FTIR) and by Auger electron spectroscopy (AES). Porous silicos which has been aged under air ambient yields two PL band structures, i.e. blue/violet PL and red PL. The evolution of a blue/violet band is pronounced, especially for thin PS film which is prepared in dilute HF solution. The blue/violet PL band has been observed initially to increrase rapidly with aging, then saturated with further atmospheric aging. The ambient air aged PS exhibits a fast decay time of sub-nanosecond at room temperature and shows appreciably faster decay time than that at 20K. Atmospheric aging of this thin blue/violet luminescing PS yield non-stoichiometric oxide judging from the vibrational spectra of Si-O and AES analysis.