• Journal of the Korean Vacuum Society
• /
• v.6 no.S1
• /
• pp.122-126
• /
• 1997

the Cu/polyimide system is known to be the best candidate for a multilevel interconnection system due to the low resistance of Cu and to the low dielectric constant of polyimide respectively. Ion beam mixing of Cu(40nm)/polyimide was carried out at room temperature with 80 keV Ar+ and N2+ form $1.5\times$1015 to 15$\times$1015 ions/cm2. The quantitative adhesion strength was measured by a standard scratch test. X-ray photoelectron spectroscopy and x-ray emission spectrocopy are employed to investigate the chemical bonds and the interlayer compound formation of the films Cu/Al/polyimide showed more adhesion strength than Cu/polyimide after ion beam mixing and N2+ ions are more effective in the adhesion enhancement than Ar+ with the same sample geometry. The XES results shows the formation of interlayer compound of CuAl2O4 which can reflect more adhesive Cu/Al/polyimide which has not been reported previously. The latter results is understood by the fact that N2+ ions produce more pyridinelike moiety, amide group and tertiary amine moiety whcih are known as adhesion promotors.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.362-362
• /
• 2014

Atomic layer deposition (ALD) can be regarded as a special variation of the chemical vapor deposition method for reducing film thickness. ALD is based on sequential self-limiting reactions from the gas phase to produce thin films and over-layers in the nanometer scale with perfect conformality and process controllability. These characteristics make ALD an important film deposition technique for nanoelectronics. Tantalum pentoxide ($Ta_2O_5$) has a number of applications in optics and electronics due to its superior properties, such as thermal and chemical stability, high refractive index (>2.0), low absorption in near-UV to IR regions, and high-k. In particular, the dielectric constant of amorphous $Ta_2O_5$ is typically close to 25. Accordingly, $Ta_2O_5$ has been extensively studied in various electronics such as metal oxide semiconductor field-effect transistors (FET), organic FET, dynamic random access memories (RAM), resistance RAM, etc. In this experiment, the variations of chemical and interfacial state during the growth of $Ta_2O_5$ films on the Si substrate by ALD was investigated using in-situ synchrotron radiation photoemission spectroscopy. A newly synthesized liquid precursor $Ta(N^tBu)(dmamp)_2$ Me was used as the metal precursor, with Ar as a purging gas and $H_2O$ as the oxidant source. The core-level spectra of Si 2p, Ta 4f, and O 1s revealed that Ta suboxide and Si dioxide were formed at the initial stages of $Ta_2O_5$ growth. However, the Ta suboxide states almost disappeared as the ALD cycles progressed. Consequently, the $Ta^{5+}$ state, which corresponds with the stoichiometric $Ta_2O_5$, only appeared after 4.0 cycles. Additionally, tantalum silicide was not detected at the interfacial states between $Ta_2O_5$ and Si. The measured valence band offset value between $Ta_2O_5$ and the Si substrate was 3.08 eV after 2.5 cycles.

• Journal of the Korean Ceramic Society
• /
• v.39 no.9
• /
• pp.863-870
• /
• 2002

The Single phase $Pb(Fe_{1/2}Ta_{1/2})O_3$ (x=0.0∼1.0) solid solutions were successfully synthesized and their ordering structures as well as dielectric properties were investigated ${{r(Nb^{5+})=r(Ta^{5+})=0.78 {\AA},\;AW(Nb^{5+})=92.91,\;AW(Ta^{5+})=180.95}}$. While $Pb(Fe_{1/2}Ta_{1/2})O_3$ showed typical relaxor ferroelectric characteristics such as dielectric relaxation and diffuse phase transition, the sharpeness of the phase transition increased as $Ta^{5+}$ was replaced by $Nb^{5+}$ and finally $Pb(Fe_{1/2}Nb_{1/2})O_3$ showed normal ferroelectric characteristics with no dielectric relaxation. By using Raman spectroscopy, it was revealed that the $Fe^{3+}\;and\;Ta^{5+}\;of\;Pb(Fe_{1/2}Ta_{1/2})O_3$ were stoichiometrically 1:1 ordered within the short range which can be hardly probed even by TEM. Also, The degree of ordering in $Pb(Fe_{1/2}Ta_{1/2})O_3$ decreased as $Ta^{5+}$ was replaced by $Nb^{5+}$ and finally $Fe^{3+}\;and\;Nb^{5+}\;of\;Pb(Fe_{1/2}Nb_{1/2})O_3$ were completely disordered. The relaxor ferroelectric characteristics of $Pb(Fe_{1/2}Ta_{1/2})O_3$ could be correlated with the stoichiometric 1:1 ordering of B-site cations within the short range which can be hardly probed even by TEM. Also, the decrease of the relaxor ferroelectric characteristics with the replacement of $Ta^{5+}\;by\;Nb^{5+}$ could be correlated with the weakening of the ordering and the normal ferroelectric characteristics of $Pb(Fe_{1/2}Nb_{1/2})O_3$ could be correlated with the complete disordering of B-site cations.

• Journal of the Korean Vacuum Society
• /
• v.15 no.1
• /
• pp.89-96
• /
• 2006

Recent ULSI and multilevel structure trends in microelectronic devices minimize the line width down to less than $0.25{\mu}m$, which results in high current densities in thin film interconnections. Under high current densities, an EM(electromigration) induced failure becomes one of the critical problems in a microelectronic device. This study is to improve thin film interconnection materials by investigating the EM characteristics in Ag, Cu, Au, and Al thin films, etc. EM resistance characteristics of Ag, Cu, Au, and Al thin films with high electrical conductivities were investigated by measuring the activation energies from the TTF (Time-to-Failure) analysis. Optical microscope and XPS (X-ray photoelectron spectroscopy) analysis were used for the failure analysis in thin films. Cu thin films showed relatively high activation energy for the electromigration. Thus Cu thin films may be potentially good candidate for the next choice of advanced thin film interconnection materials where high current density and good EM resitance are required. Passivated Al thin films showed the increased MTF(Mean-time-to-Failure) values, that is, the increased EM resistance characteristics due to the dielectric passivation effects at the interface between the dielectric overlayer and the thin film interconnection materials.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.145-145
• /
• 2008

High-k materials have been paid much more attention for their characteristics with high permittivity to reduce the leakage current through the scaled gate oxide. Among the high-k materials, $ZrO_2$ is one of the most attractive ones combing such favorable properties as a high dielectric constant (k= 20 ~ 25), wide band gap (5 ~ 7 eV) as well as a close thermal expansion coefficient with Si that results in good thermal stability of the $ZrO_2$/Si structure. During the etching process, plasma etching has been widely used to define fine-line patterns, selectively remove materials over topography, planarize surfaces, and trip photoresist. About the high-k materials etching, the relation between the etch characteristics of high-k dielectric materials and plasma properties is required to be studied more to match standard processing procedure with low damaged removal process. Among several etching techniques, we chose the inductively coupled plasma (ICP) for high-density plasma, easy control of ion energy and flux, low ownership and simple structure. And the $BCl_3$ was included in the gas due to the effective extraction of oxygen in the form of $BCl_xO_y$ compounds. During the etching process, the wafer surface temperature is an important parameter, until now, there is less study on temperature parameter. In this study, the etch mechanism of $ZrO_2$ thin film was investigated in function of $Cl_2$ addition to $BCl_3$/Ar gas mixture ratio, RF power and DC-bias power based on substrate temperature increased from $10^{\circ}C$ to $80^{\circ}C$. The variations of relative volume densities for the particles were measured with optical emission spectroscopy (OES). The surface imagination was measured by scanning emission spectroscope (SEM). The chemical state of film was investigated using energy dispersive X-ray (EDX).

• Journal of the Korean Vacuum Society
• /
• v.19 no.1
• /
• pp.22-27
• /
• 2010

To improve surface wettability, each sample was treated by atmospheric pressure plasma (APP) using dielectric barrier discharge (DBD) system. Argon and oxygen gases were used for treatment gas to modify the $TiO_2$ surface by APP with RF power range from 50 to 200 W. Water contact angle was decreased from $20^{\circ}$ to $10^{\circ}$ with argon only. However, water contact angle was decreased from $20^{\circ}$ to < $1^{\circ}$ with mixture of argon and oxygen. Water contact angle with $O_2$ plasma was lower than water contact angle with Ar plasma at the same RF power. It seems to be increasing the polar force of $TiO_2$ surface. Also, analysis result of X-ray photoelectron spectra (XPS) shows the increase of intensity of O1s shoulder peak, resulting in increasing of surface wettability by APP. Moreover, each water contact angle increased according to increase past time. However, contact angle increase with plasma treatment was lower than without plasma treatment. Additionally, the efficiency of $TiO_2$ photocatalyst was improved by plasma surface-treatment through the degradation experiment of phenol.

• Journal of the Korean Vacuum Society
• /
• v.2 no.2
• /
• pp.188-198
• /
• 1993

We have developed a technique for growing thin oxides (6~10 nm) by the Last step TCA method. N-channel metal-oxide-semiconductor (n-MOS) capacitor and n-channel metal-oxide-semiconductor field-effect transistor's (MOSFET's) having a gate oxide with chlorine incorporated $SiO_2/Si$ interface have been analyzed by electrical measurements and physical methods, such as secondary ion mass spectrometry (SIMS) and electron spectroscopy for chemical analysis (ESCA). The gate oxide grown with the Last strp TCA method has good characteristics as follows: the electron mobility of the MOSFET's with the Last step TCA method was increased by about 7% and the defect density at the $SiO_2/Si$ interface decreases slightly compared with that with No TCA method. In reliability estimation, the breakdown field was 18 MV/cm, 0.6 MV/cm higher than that of the gate oxide with No TCA method, and the lifetime estimated by TDDB measurement was longer than 20 years. The device lifetime estimated from hot-carrier reliability was proven to be enhanced. As the results, the gate oxide having a $SiO_2/Si$ interface incorporated with chlorine has good characteristics. Our new technique of Last step TCA method may be used to improve the endurance and retention of MOSFET's and to alleviate the degradation of thin oxides in short-channel MOS devices.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2002.11a
• /
• pp.477-480
• /
• 2002

Si-O-C(-H) thin film with a tow dielectric constant were deposited on a P-type Si(100) substrate by an inductively coupled plasma chemical vapor deposition (ICPCVD). Bis-trimethylsilymethane (BTMSM, H$_{9}$C$_3$-Si-CH$_2$-Si-C$_3$H$_{9}$) and oxygen gas were used as Precursor. Hybrid type Si-O-C(-H) thin films with organic material have been generated many voids after annealing. Consequently, the Si-O-C(-H) films can be made a low dielectric material by the effect of void. The surface characterization of Si-O-C(-H) thin films were performed by SEM(scanning electron microscope). The characteristic analysis of Si-O-C(-H) thin films were performed by X-ray photoelectron spectroscopy (XPS).

• Journal of the Korean Ceramic Society
• /
• v.49 no.5
• /
• pp.475-483
• /
• 2012

High capacitance X5R MLCCs based on $BaTiO_3$ ceramic dielectric layers exhibit a single broad, asymmetric arc shape impedance and modulus response over the wide frequency range between 1 MHz to 0.01 Hz. Analysis according to the conventional brick-layer model for polycrystalline conductors employing a series connection of multiple RC parallel circuits leads to parameters associated with large errors and of little physical significance. A new parametric impedance model is shown to satisfactorily describe the experimental spectra, which is a parallel network of one resistor R representing the DC conductivity thermally activated by 1.32 eV, one ideal capacitor C exactly representing bulk capacitance, and a constant phase element (CPE) Q with complex capacitance $A(i{\omega})^{{\alpha}-1}$ with ${\alpha}$ close to 2/3 and A thermally activated by 0.45 eV or ca. 1/3 of activation energy of DC conductivity. The feature strongly indicate the CK1 model by J. R. Macdonald, where the CPE with 2/3 power-law exponent represents the polarization effects originating from mobile charge carriers. The CPE term is suggested to be directly related to the trapping of the electronic charge carriers and indirectly related to the ionic defects responsible for the insulation resistance degradation.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.129-129
• /
• 2016

Graphene, as a single layer of $sp^2$-bonded carbon atoms packed into a 2D honeycomb crystal lattice, has attracted much attention due to its outstanding properties. In order to synthesize high quality graphene, transition metals, such as nickel and copper, have been widely employed as catalysts, which needs transfer to desired substrates for various applications. However, the transfer steps are not only complicated but also inevitably induce defects, impurities, wrinkles, and cracks of graphene. Furthermore, the direct synthesis of graphene on dielectric surfaces has still been a premature field for practical applications. Therefore, cost effective and concise methods for transfer-free graphene are essentially required for commercialization. Here, we report a facile transfer-free graphene synthesis method through nickel and carbon co-deposited layer. In order to fabricate 100 nm thick NiC layer on the top of $SiO_2/Si$ substrates, DC reactive magnetron sputtering was performed at a gas pressure of 2 mTorr with various Ar : $CH_4$ gas flow ratio and the 200 W DC input power was applied to a Ni target at room temperature. Then, the sample was annealed under 200 sccm Ar flow and pressure of 1 Torr at $1000^{\circ}C$ for 4 min employing a rapid thermal annealing (RTA) equipment. During the RTA process, the carbon atoms diffused through the NiC layer and deposited on both sides of the NiC layer to form graphene upon cooling. The remained NiC layer was removed by using a 0.5 M $FeCl_3$ aqueous solution, and graphene was then directly obtained on $SiO_2/Si$ without any transfer process. In order to confirm the quality of resulted graphene layer, Raman spectroscopy was implemented. Raman mapping revealed that the resulted graphene was at high quality with low degree of $sp^3$-type structural defects. Additionally, sheet resistance and transmittance of the produced graphene were analyzed by a four-point probe method and UV-vis spectroscopy, respectively. This facile non-transfer process would consequently facilitate the future graphene research and industrial applications.