• Restorative Dentistry and Endodontics
• /
• v.28 no.6
• /
• pp.491-497
• /
• 2003

The purpose of this study was to evaluate the correlation between hybrid layer thickness and bond strength using confocal laser scanning microscope and microtensile bond strength test of two adhesive systems. The dentin surface of human molars. sectioned to remove the enamel from the occlusal surface. Either Scotchbond Multi-Purpose(3M Dental Product, St. Paul, MN, U.S.A) or Clearfil SE Bond (Kuraray, Osaka, Japan) was bonded to the surface. and covered with resin-composite. The resin-bonded teeth were serially sliced perpendicular to the adhesive interface to measure the hybrid layer thickness by confocal laser scanning microscope. The specimen were trimmed to give a bonded cross-sectional surface area of $1\textrm{mm}^2$, then the micro-tensile bone test was performed at a cross head speed of 1.0 mm/min. All fractured surfaces were also observed by stereomicroscope. There was no significant differences in bond strengths the materials(p>0.05). However. the hybrid layers of three-step dentin adhesive system, SM, had significantly thicker than self-etching adhesive system. CS(p<0.05). Pearson's correlation coefficient showed no correlation between hybrid layer thickness and bond strengths(p>0.05). Bond strengths of dentin adhesive systems were not dependent on the thickness of hybrid layer.

• Restorative Dentistry and Endodontics
• /
• v.47 no.4
• /
• pp.36.1-36.17
• /
• 2022

Objectives: This study aimed to evaluate the effect of aging on the marginal quality of glass hybrid (GH) material used to elevate dentin gingival margins, and to analyze the consistency of the results obtained by 3 in vitro methods. Materials and Methods: Ten teeth received compound class II cavities with subgingival margins. The dentin gingival margins were elevated with GH, followed by resin composite. The GH/gingival dentin interfaces were examined through digital microscopy, scanning electron microscopy (SEM) using resin replicas, and according to the World Dental Federation (FDI) criteria. After initial evaluations, all teeth were subjected to 10,000 thermal cycles, followed by repeating the same marginal evaluations and energy dispersive spectroscopy (EDS) analysis for the interfacial zone of 2 specimens. Marginal quality was expressed as the percentage of continuous margin at ×200 for microscopic techniques and as the frequency of each score for FDI ranking. Data were analyzed using the paired sample t-test, Wilcoxon signed-rank test, and Pearson and Spearmen correlation coefficients. Results: None of the testing techniques proved the significance of the aging factor. Moderate and strong significant correlations were found between the testing techniques. The EDS results suggested the presence of an ion-exchange layer along the GH/gingival dentin interface of aged specimens. Conclusions: The marginal quality of the GH/dentin gingival interface defied aging by thermocycling. The replica SEM and FDI ranking results had stronger correlations with each other than either showed with the digital microscopy results.

• Restorative Dentistry and Endodontics
• /
• v.47 no.4
• /
• pp.43.1-43.13
• /
• 2022

Objectives: This study compared the surface gloss (SG), gloss retention (GR), and color stability (CS) of 2 universal resin composites after chemical (CA) and mechanical (MA) aging. Materials and Methods: Twenty disc-shaped samples of G-ænial A'Chord (GC-Europe) and Filtek Universal (3M-ESPE) were polished with sequential abrasive papers. For CA, specimens were stored in 1 mL of 75% ethanol for 15 days at 37℃, and readings (SG, GR, and CS) were obtained at baseline and 5, 10, and 15 days. For MA, specimens were subjected to 10,750 simulated brushing cycles. SG and CS were evaluated after every 3,583 cycles. SG was measured with a glossmeter (geometrical configuration: 60°), and values were expressed in gloss units. Color was measured with a spectrophotometer using the CIE-L^*a^*b^* color system. The Student's t-test, 1-way analysis of variance, and Scheffé test were used for statistical analysis (α = 0.05). Results: G-ænial presented significantly higher SG values than Filtek (p = 0.02), with GR reductions of 5.2% (CA) and 5.3% (MA) for G-ænial and 7.6% (CA) and 7.2% (MA) for Filtek. The aging protocol had no statistically significant effect on SG or GR (p = 0.25) from baseline to the final readings. G-ænial-MA presented the lowest color difference (ΔE = 1.8), and G-ænial-CA and Filtek-CA had the largest changes (ΔE = 8.6 and ΔE = 11.8, respectively). Conclusion: G-ænial presented higher SG values and better CS. Both restorative materials demonstrated acceptable GR and CS. Aging protocols impacted these properties negatively.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.51 no.2
• /
• pp.132-139
• /
• 2024

This study aimed to compare the fluoride-releasing ability and degree of microbial attachment of a newly developed glass-hybrid restorative material (GH) with those of a high-viscosity glass ionomer (HvGIC), resin-modified glass ionomer (RMGI), and composite resin (CR). In addition, the correlation between fluoride-releasing ability and microbial attachment between materials was evaluated. Specimens were prepared in a disc shape and divided into 4 groups according to the materials (GH, HvGIC, RMGI, and CR). The fluoride release experiments were performed in each group (n = 15). The amount of fluoride released was measured on days 1, 3, 7, 14, 28, and 42 after storage. For the microbial attachment experiment, 12 specimens were produced per group using Mutans Streptococci (S.mutans ), a cariogenic microorganism. S. mutans was cultured on the specimens for 24 hours, and the number of bacteria was measured. GH had the highest cumulative fluoride release and showed a significant difference when compared with RMGI (p = 0.001) and CR (p < 0.0001). Microbial attachment was the lowest in GH; however, no significant difference was observed between the materials (p = 0.169). There was no significant correlation between fluoride release from materials and microbial attachment (p > 0.05). From this perspective, remineralization of low-mineralized areas could be expected due to the high fluoride release of GH, and the effect of delaying the progression of dental caries could be predicted from the low cariogenic microbial attachment. Therefore, GH might be a useful restorative material for treating immature permanent teeth with hypomineralized enamel. However, further studies are needed about the degree of remineralization of hypomineralized areas after restoration and the capacity to recharge fluoride.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.39 no.4
• /
• pp.187-194
• /
• 2023

Purpose: A mismatched size in the post and post space is a common problem during post-fixation. Since this discordance affects the bonding strength of the fiber-reinforced composite resin post (FRC Post), a corresponding luting agent is required. The aim of this study was to evaluate the bonding strength of the FRC post according to the fitness of the fiber post and the type of luting agent. Materials and Methods: Thirty mandibular premolar were endodontic-treated and assigned to two groups according to their prepared post space: Fitting (F) and Mismatching (M). These groups were further classified into three subgroups according to their luting agent: RelyX Unicem (ReX), Luxacore dual (Lux), and Duolink (Duo). A push-out test was performed to measure the push-out bond strengths. The fractured surfaces of each cross-section were then examined, and the fracture modes were classified. Results: In the ReX and Duo subgroups, the F group had a higher mean bond strength; however, the Lux subgroup had no significant difference between the F and M groups. In the analysis of the failure modes, the ReX subgroup had only adhesive failures between the cement and dentin. Conclusion: The result of this study showed that the bond strength of an FRC post was influenced by the type of luting agent and the mismatch between the diameter of the prepared post space and that of the post.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.28 no.3
• /
• pp.403-411
• /
• 2001

The aim of this study was to evaluate the resistance to degradation of four commercial composite resins in an alkaline solution. The brands studied were Unifil(GC, Japan), Palfique(Tokuyama Japan). Definite$Degussa-H\ddot{u}ls$ AG, Germany). Revolution(Kerr, U.S.A.). Preweighed discs of each brand were exposed 0.1N NaOH solution at $60^{\circ}C$. After 14 days they were removed, neutralized with HCl, washed with water and dried. Resistance to degradation was evaluated on the basis of following parameters: (a) mass loss(%) - determined from pre-and post-exposed specimen weights; (b) Si loss(ppm) - obtained from ICP-AE analysis of solution exposed to specimens; and (c) degradation depth$({\mu}m)$ - measured microscopically (SEM) from polished circular sections of exposed specimens. The results were follows: 1. The mass loss of Unifil was 3.21%, it was the highest of materials. But, there was no significant difference among the materials. 2. The degree of degradation layer depth was $107.69\sim47.40{\mu}m$, the sequence of the degree pf degradation layer depth was in descending order by Unifil, Palfique, Revolution, Definite. There was significant difference among the materials except Palfique and Definite. 3. The Si loss of Paltique was 8940.0ppm, it was the highest. There was significant difference among the materials, except Revolution and Definite(p<0.05). 4. The correlation coefficient between mass loss and degradation depth was relatively high(r = 0.06, p<0.05). 5. There was no significant coefficient correlation between Si loss and mass loss, and/or the degree of degradation layer depth and Si loss. 6. When observed with SEM, destruction of bonding is observed between resin matrix and filler. Above results suggested that the hydrolytic degradation is considered as evaluation factor of composite resins.

• The Journal of the Korea Contents Association
• /
• v.12 no.5
• /
• pp.311-322
• /
• 2012

Restoration materials used to investigate effects of fluorine such as enamel strengthening and anti-caries effects in several types of dental restoration materials were five kinds including Ionoseal(VOCO GmbH, Cuxhaven, Germany), Fuji Filling LC(GC Co. Tokyo, Japan), Quadrant Universal LC(CAVEX Holland BV, Netherlands), PermaCem$^{(R)}$(DMG, Hamburg, Germany) and Dyract$^{(R)}$ AP(Dentsply GmbH, Germany), and the amount of fluorine-releasing was measured with ICS-5000 Reagent-FreeTM Ion Chromatography(RFICTM, Dionex, U.S.A.). The results of this study are as follows. 1. In all types of restoration materials, the amount of fluoride-releasing was reduced with time passage and it was declined sharply to show significance in four weeks. Fuji Filling LC(12.445PPM) or resin-reinforced glass ionomer and PermaCem$^{(R)}$(16.121PPM) or compomer were found to release fluorine for a long term(P<.001). 2. Ionoseal(0.887PPM) or glass ionomer and Quadrant Universal LC(0.957PPM) or composite resin released a few fluorine of 1PPM or less than 1PPM after one week, and Dyract$^{(R)}$ AP or compomer released fluorine of 8.631PPM in one week and its amount of releasing decreased dramatically in two and four week by recording 0.175PPM and 0.116PPM, respectively. Therefore, the effect of releasing fluorine in four weeks was observed to be poor (P<.001). 3. Fuji Filling LC or resin-reinforced glass ionomer and PermaCem$^{(R)}$ or compomer released fluorine of 33.372 and 1.902PPM, respectively in one week and their amount of releasing increased to be 36.371 and 18.223PPM, respectively in two weeks. So, their amount of fluorine-releasing recorded the highest levels in two weeks(P<.001).

• Restorative Dentistry and Endodontics
• /
• v.34 no.6
• /
• pp.467-476
• /
• 2009

The aim of this study was to measure the dentinal tubular fluid flow (DFF) during and after amalgam and composite restorations. A newly designed fluid flow measurement instrument was made. A third molar cut at 3 mm apical from the CEJ was connected to the flow measuring device under a hydrostatic pressure of 15 $cmH_2O$. Class I cavity was prepared and restored with either amalgam (Copalite varnish and Bestaloy) or composite (Z-250 with ScotchBond MultiPurpose: MP, Single Bond 2: SB, Clearfil SE Bond: CE and Easy Bond: EB as bonding systems). The DFF was measured from the intact tooth state through restoration procedures to 30 minutes after restoration, and re-measured at 3 and 7days after restoration. Inward fluid flow (IF) during cavity preparation was followed by outward flow (OF) after preparation, In amalgam restoration, the OF changed to IF during amalgam filling and slight OF followed after finishing. In composite restoration, application CE and EB showed a continuous OF and air-dry increased rapidly the OF until light-curing, whereas in MP and SB, rinse and dry caused IF and OF, respectively. Application of hydrophobic bonding resin in MP and CE caused a decrease in flow rate or even slight IF. Light-curing of adhesive and composite showed an abrupt IF. There was no statistically significant difference in the reduction of DFF among the materials at 30 min. 3 and 7 days after restoration (p > 0.05).

• Journal of Dental Rehabilitation and Applied Science
• /
• v.18 no.4
• /
• pp.289-299
• /
• 2002

The bond strength is one of the most important factor in establishing long-term success of esthetic restorative dentistry. So, various restorative materials have been introduced to improve the esthetic and physical properties. Ormocer (organically modified ceramic) was developed as a result of such efforts. This study was performed to compare the shear bond strength of ormocer based adhesive with that of existing dentin adhesive. In this study $Admira^{(R)}$ and $Admira^{(R)}$ bond of the ormocer system are grouped together for ADM, Single $Bond^{(R)}$ which is an one-bottle adhesive and Z-250TM which is hybrid composite resin of BIS-GMA system for SIN, and $Definite^{(R)}$ of ormocer and Etch & $Prime^{(R)}$ 3.0 which is a self etching priming/ bonding agent for ETC. The results of this study were as follows. : (1) In the comparison of shear bond strength according to different adhesive system, shear bond strength was increased in the order of ETC group, SIN group, ADM group. There was no significant difference between ADM group and SIN group. However, there was a significant level of difference between ADM and ETC groups as well as SIN and ETC groups( p<0.05). (2) Examination by a scanning electron microscope showed a well established hybrid layer and resin tag in both ADM group and SIN group, while ETC group showed a minimal formation of the hybrid layer when compared with ADM and SIN groups. From the above results, it may be reasonable to start the clinical application of ormocer system, and it is recommended that ormocer system should be used along with an ormocer based adhesive because ormocer system showed the lower shear bond strength when it used with other existing self etching priming/bonding agent. The self etching priming/bonding agent showed relatively low shear bond strength, and it is considered that the further study should be needed.

• Restorative Dentistry and Endodontics
• /
• v.13 no.1
• /
• pp.185-190
• /
• 1988

The study was designed to establish quantitative method for assessing the marginal leakage of dental restorations. 18 Class V cavities with $45^{\circ}$ bevel joint were prepared and replicas of these teeth were made with polyethylene wax. and classified with three groups. First group was filled with Scotch bond and silux. Second group was filled with glass ionomer cement:scotchbond/silux. Third group was filled with Dentin-Adhesit/Heliosit. After finishing, all specimens were subjected manually to 100 thermal cycles at $0^{\circ}C$ and $100^{\circ}C$ Samarium nitrate solution, irradiated with flux of $6{\times}12^{12}$ neutrons/$cm^2$/sec for 11 hours, woled for 200 hours, counted with the HpGe detector and the tracer uptake was determined by comparison with a standard of samarium ($10{\mu}g$). The following results were obtained. 1) The group filled with glass ionomer cement base showed least marginal leakage. 2) The group filled with Dentin-Adhesit/Heliosit showed less marginal leakage than the group filled with scotchbond/silux.