• Restorative Dentistry and Endodontics
• /
• v.37 no.2
• /
• pp.84-89
• /
• 2012

Objectives: This study analyzed the difference in color caused by different thickness in enamel layer of composite resins when applied with single and layering placement technique, and evaluated if the results agreed with the shade guide from the manufacturers to verify reliability of the color matching process of the manufacturers. Materials and Methods: For single composite resin samples, 6 mm diameter and 4 mm thickness cylindrical samples were fabricated using Ceram-X mono (DENTSPLY DeTrey) and CIE $L^*a^*b^*$ values were measured with spectrophotometer. Same process was done for layering composite resin samples, making 3 dentinal shade samples, 4 mm thickness, for each shade using Ceram-X duo (DENTSPLY DeTrey) and enamel shade resins were layered in 2 mm thickness and CIE $L^*a^*b^*$ values were measured. These samples were ground to 0.2 mm thickness each time, and CIE $L^*a^*b^*$ values were measured to 1 mm thickness of enamel shade resin. Results: Color difference (${\Delta}E^*$) between single and layering composite resin was 1.37 minimum and 10.53 maximum when layering thicknesses were between 1 mm and 2 mm and 6 out of 10 same shade groups suggested by manufacturer showed remarkable color difference at any thickness (${\Delta}E^*$ > 3.3). Conclusion: When using Ceram-X mono and duo for composite resin restoration, following the manufacturer's instructions for choosing the shade is not appropriate, and more accurate information for Ceram-X duo is needed on the variation and expression of the shades depending on the thickness of the enamel.

• Restorative Dentistry and Endodontics
• /
• v.39 no.4
• /
• pp.296-302
• /
• 2014

Objectives: It is difficult to achieve adhesion between resin cement and zirconia ceramics using routine surface preparation methods. The aim of this study was to evaluate the effects of $CO_2$ and Er:YAG laser treatment on the bond strength of resin cement to zirconia ceramics. Materials and Methods: In this in-vitro study 45 zirconia disks (6 mm in diameter and 2 mm in thickness) were assigned to 3 groups (n = 15). In control group (CNT) no laser treatment was used. In groups COL and EYL, $CO_2$ and Er:YAG lasers were used for pretreatment of zirconia surface, respectively. Composite resin disks were cemented on zirconia disk using dual-curing resin cement. Shear bond strength tests were performed at a crosshead speed of 0.5 mm/min after 24 hr distilled water storage. Data were analyzed by one-way ANOVA and post hoc Tukey's HSD tests. Results: The means and standard deviations of shear bond strength values in the EYL, COL and CNT groups were $8.65{\pm}1.75$, $12.12{\pm}3.02$, and $5.97{\pm}1.14MPa$, respectively. Data showed that application of $CO_2$ and Er:YAG lasers resulted in a significant higher shear bond strength of resin cement to zirconia ceramics (p < 0.0001). The highest bond strength was recorded in the COL group (p < 0.0001). In the CNT group all the failures were adhesive. However, in the laser groups, 80% of the failures were of the adhesive type. Conclusions: Pretreatment of zirconia ceramic via $CO_2$ and Er:YAG laser improves the bond strength of resin cement to zirconia ceramic, with higher bond strength values in the $CO_2$ laser treated samples.

• Bulletin of the Korean Chemical Society
• /
• v.19 no.2
• /
• pp.152-154
• /
• 1998

• Imaging Science in Dentistry
• /
• v.48 no.2
• /
• pp.87-96
• /
• 2018

Purpose: The present study aimed to evaluate which of the following imaging methods best assessed misfit at the tooth-restoration interface: (1) bitewing radiographs, both conventional and digital, performed using a photostimulable phosphor plate (PSP) and a charge-coupled device (CCD) system; (2) panoramic radiographs, both conventional and digital; and (3) cone-beam computed tomography (CBCT). Materials and Methods: Forty healthy human molars with class I cavities were selected and divided into 4 groups according to the restoration that was applied: composite resin, composite resin with liner material to simulate misfit, dental amalgam, and dental amalgam with liner material to simulate misfit. Radiography and tomography were performed using the various imaging methods, and the resulting images were analyzed by 2 calibrated radiologists. The true presence or absence of misfit corresponding to an area of radiolucency in regions subjacent to the esthetic and metal restorations was validated with microscopy. The data were analyzed using a receiver operating characteristic (ROC) curve, and the scores were compared using the Cohen kappa coefficient. Results: For bitewing images, the digital systems (CCD and PSP) showed a higher area under the ROC curve (AUROC) for the evaluation of resin restorations, while the conventional images exhibited a larger AUROC for the evaluation of amalgam restorations. Conventional and digital panoramic radiographs did not yield good results for the evaluation of resin and amalgam restorations (P<.05). CBCT images exhibited good results for resin restorations(P>.05), but showed no discriminatory ability for amalgam restorations(P<.05). Conclusion: Bitewing radiographs (conventional or digital) should be the method of choice when assessing dental restoration misfit.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.26 no.3
• /
• pp.339-347
• /
• 2010

Enhancement of bond strength between new and old composite usually requires increasing the surface roughness to promote mechanical interlocking. This study evaluated the effect of different surface treatments on repair bond strength of resin composite after aging condition. Air abrasion with Al2O3, chairside silicacoating, and silanization provided higher resin-resin bond strength values compared to control group and HF group. Air abrasion is necessary to repair a resin restoration and additional application of silane seems to have good effects on bond strength.

• The Journal of Korean Academy of Prosthodontics
• /
• v.51 no.1
• /
• pp.27-32
• /
• 2013

Purpose: The aims of this study were to evaluate the effect of a resin coating on the shear bond strength of indirect composite restoration bonded to dentin with a self adhesive resin cement and to compare the shear bond strength with that of a conventional resin cement. Materials and methods: The occlusal enamels of thirty six extracted noncarious human molars were removed until the dentin flat surfaces of the teeth were exposed. Then, they were divided into 3 groups. The dentin surfaces of group 1 and 3 were left without any conditioning, while the dentin surfaces of group 2 were resin-coated with Clearfil SE bond and a flowable resin composite, Metafil Flo. After all specimens were temporized for 24 hours, indirect composite resin blocks fabricated by Tescera were bonded to dentins by Unicem for group 1 and 2, and by Panavia F for group 3. After 48 hours of water storage, shear bond strengths were measured. The data was analyzed with one-way analysis of variance and multiple comparison test (Tukey method). Results: The shear bond strengths of Unicem applied to resin coated dentin surfaces were significantly higher than those of Unicem and Panavia F used to uncoated dentin surfaces (P<.0001). Conclusion: Application of a resin coating to the dentin surface significantly improved the shear bonding strength of a self adhesive resin cement in indirect restoration.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.2 s.173
• /
• pp.464-471
• /
• 2000

The fracture and wear behavior of dental composite resins containing prepolymerized particle fillers were investigated. Composite resins such as Metafil, Silux Plus, Heliomolar and Palfique Estelite were selected as specimens and contents of filler in specimens in order to evaluate the effect of prepolymerized particle fillers in fracture and wear characteristics. Ball on flat wear tester was used for the wear test at room temperature. The friction coefficient of Metafil was quite high relatively, and the wear resistances of Silux Plus and Palfique Estelite were better than those of Metafil and Heliomolar at the same experimental condition. It was found that the main wear mechanism was abrasive wear containing of plastic deformation of dental material.

• Restorative Dentistry and Endodontics
• /
• v.23 no.1
• /
• pp.413-423
• /
• 1998

Dental ceramics exhibit excellent esthetic property, compressive strength, chemical durability, biocompatibility and translucency. This study evaluated the shear bond strength of composite resin to the new heat-pressed ceramic material (IPS-Empress System) depending on the surface treatments and bonding agents. The surface treatments were etching with 4.0% hydrofluoric acid, application of silane, and the combination of the two methods. Composite resin was bonded to ceramic with four kinds of dentin bonding agents(All-Bond 2, Heliobond, Scotch bond Multi-purpose and Tenure bonding agents). The ceramic specimen bonded with composite resin was mounted in the testing jig, and the universal testing machine(Zwick 020, Germany) was used to measure the shear bond strength with the cross head speed of 0.5 mm/min. The results obtained were as follows 1. The mean shear bond strength of the specimens of which the ceramic surface was treated with the combination of hydrofluoric acid and silane before bonding composite resin was significantly higher than those of the other surface treatment groups(p<0.05). 2. In the case of All-Bond 2 and Scotchbond Multi-purpose bonding agent group, the surface treatment methods did not influenced significantly on the shear bond(p>0.05). 3. Of the four bonding agents tested, the shear bond strength of Heliobond was significantly lower than those of other bonding agents regardless of the surface treatment methods(p<0.05). 4. The highest shear bond strength($12.55{\pm}1.92$ MPa) was obtained with Scotchbond Multipurpose preceded by the ceramic surface treatment with the combination of 4% hydrofluoric acid and silane.

• Restorative Dentistry and Endodontics
• /
• v.46 no.2
• /
• pp.23.1-23.11
• /
• 2021

Objectives: This study assessed the reliability of digital color measurements using images of resin composite specimens captured with a cellphone. Materials and Methods: The reference color of cylindrical specimens built-up with the use of resin composite (shades A1, A2, A3, and A4) was measured with a portable spectrophotometer (CIELab). Images of the specimens were obtained individually or pairwise (compared shades in the same photograph) under standardized parameters. The color of the specimens was measured in the images using RGB system and converted to CIELab system using image processing software. Whiteness index (WI_D) and color differences (ΔE₀₀) were calculated for each color measurement method. For the cellphone, the ΔE₀₀ was calculated between the pairs of shades in separate images and in the same image. Data were analyzed using 2-way repeated-measures analysis of variance (α = 0.05). Linear regression models were used to predict the reference ΔE₀₀ values of those calculated using color measured in the images. Results: Images captured with the cellphone resulted in different WI_D values from the spectrophotometer only for shades A3 and A4. No difference to the reference ΔE₀₀ was observed when individual images were used. In general, a similar ranking of ΔE₀₀ among resin composite shades was observed for all methods. Stronger correlation coefficients with the reference ΔE₀₀ were observed using individual than pairwise images. Conclusions: This study showed that the use of cellphone images to measure the color difference seems to be a feasible alternative providing outcomes similar to those obtained with the spectrophotometer.

• Journal of dental hygiene science
• /
• v.12 no.5
• /
• pp.477-485
• /
• 2012

This study evaluate the influence of food staining food and bleaching on the color (CIELAB) and reflectivity of two-way (anterior & posterior) composite resin and flowable composite resin. There were 6 immersion media: kimchi, red pepper paste, blueberry, tea, curry and distilled water. A total of 36 specimens ($11{\times}11{\times}2$ mm) were prepared and immersed in each immersion media for 8 days at $37^{\circ}C$. Their color and reflectivity measured with the spectrophotometer at baseline and every 24 hours. Data from the color change and reflectivity were collected and subjected to statistical analysis by ANOVA, ANCOVA and RM-ANOVA. Curry showed the highest influence on color change and blueberry on brightness (p<0.001) on both resins. Bleaching after polishing made color change more than polishing or bleaching independently on two-way (anterior & posterior) composite resin, but not on flowable composite resin. It was suggested cleaning the mouth after taking curry and blueberry be needed to maintain the original color of composite resin.