• Journal of Technologic Dentistry
• /
• v.21 no.1
• /
• pp.77-85
• /
• 1999

When producing partial denture using a Chrome-cobalt alloy being used universally, 45 pattern of them to compare casting characters according to 5 burying methods(special ring method, plastic ring method, general metal ring method) and 5 casting directions(straight, upper, lower, left and right directions) were compared and evaluated. The results were as follows : 1. The comparison of casting characters in accordance with burying type shows that the special ring method to install blind air vent using utility wax was the highest rate of 76.9%, followed by 69.1% of the plastic ring to cast without ring and 61.1% of the metal ring method being used universally respectively. Namely the special ring method was best. The significant level was P<0.05 statistically. 2. The comparison of casting character in accordance with casting directions shows that the straight casting was the highest of 77.9%, and followed by right casting of 74.2%, left casting of 66.7%, upper casting of 63.5%, and lower casting of 62.9% respectively, Namely the straight casting was best.

• Korean Journal of Dental Materials
• /
• v.42 no.2
• /
• pp.95-106
• /
• 2015

Hardening mechanism associated with post-firing heat treatment of softening heat treated and then firing simulated Pd-Ag-Au alloy for bonding porcelain was examined by observing the change in hardness, crystal structure and microstructure. By post-firing heat treatment of as-cast, solution treated and pre-firing heat treated specimens at $650^{\circ}C$ after casting, the hardness value increased within 10 minutes. Then, hardness consistently increased until 30 minutes, and gap of hardness value among the specimens was reduced. The increase in hardness after post-firing heat treatment was caused by grain interior precipitation in the matrix. The softening heat treatment did not affect the increase in hardness by post-firing heat treatment. The precipitated phase from the parent Pd-Ag-Au-rich ${\alpha}$ phase with face-centered cubic structure by post-firing heat treatment was $Pd_3$(Sn, In) phase with face-centered tetragonal structure, which has lattice parameters of $a_{200}=4.0907{\AA}$, $c_{002}=3.745{\AA}$. From above results, appropriate post-firing heat treatment in order to support the hardness of Pd-Ag-Au metal substructure was expected to bring positive effects to durability of the prosthesis.

• Journal of Technologic Dentistry
• /
• v.14 no.1
• /
• pp.55-65
• /
• 1992

The purpose of this study was to investigate the comparison of physical properties of nonprecious metal alloys colored goldish yellow. The experimental groups were copper based dental alloy and control group was Ni-Cr based dental alloy used crown and bridges frameworks. Hardness was tested by vickers hardness tester, tensile strength was tested by universal tension tester. After testing the tensile strength of castings, the microstrucure and the pattern of fracture were investigated by scanning electron microscope and metallurgical microscope. The results were as follows : Hardness of Ni based alloy was higher than Cu based alloys. Hardness number of A group was 200.41$\pm$16.10 Hv, B group was 194.33$\pm$1.69 Hv, C group was 139.29$\pm$2.19 Hv and D group was 293.81$\pm$27.17 Hv, respectively. Tensile strength of D group was 56.42$\pm$6.17 $kg/m^2$, A group was 50.39$\pm$5.68 $kg/m^2$, C group was 45.13$\pm$4.53 $kg/m^2$, B group was 45.25$\pm$9.25 $kg/m^2$, in order, and D group was maximum tensile strength. The fractured surfaces of tensile specimens in the all groups showed the tendency to form large voids in the center of specimens. Thus the ductile fracture was changed into the brittle fracture with the fine grain size.

• Journal of Technologic Dentistry
• /
• v.38 no.3
• /
• pp.175-183
• /
• 2016

Purpose: Observation of Oxide Film Formation and Bonding Strength according to surface treatment of Co-Cr Alloy for porcelain fused to Metal. Methods: metal specimens $0.5mm{\times}25mm{\times}4mm$ in size were made using Co-Cr alloys for porcelain fused to metal crown (Heraenium P, Tae jung Medis). Dental porcelain $0.5mm{\times}25mm{\times}4mm$ in size was sintered on the metal specimens after changing the etching time, sandblasting condition, and heat treatment temperature. Subsequently, the bonding strength was compared by the three-point flexural strength test using a universal testing machine (UTM) to observe the fracture surface and oxidized layers. Results: With regard to the experimental group treated with acid-etching, Specimen 1 treated for 25 minutes (B-3) showed the highest bonding strength, and Specimen 2 treated only with sandblasting showed the most excellent bonding force at 3.5 bar (C-3). With regard to the experimental group treated with sandblasting at 3.5 bar after acid-etching for 25 minutes, Specimen 3 with heat treatment at $980^{\circ}C$ (D-3) showed the highest bonding strength. Conclusion: The specimen which went through both sandblasting and etching, showed an excellent ceramicmetal bond strength.

• Journal of Technologic Dentistry
• /
• v.34 no.3
• /
• pp.237-245
• /
• 2012

Purpose: This study was conducted to evaluate the corrosion resistance of metal ions of alloys and use the results as the dental health data. These were performed by examining the corrosion levels of Co-Cr alloys for the full and removable partial denture metal frameworks and porcelain-fused-to-metal crown, among the dental casting nonprecious alloys. Methods: The alloy specimens (N = 10) were manufactured in $15mm{\times}10mm{\times}1.2mm$ and stored in two types of corrosive solutions at $37^{\circ}C$ for seven days. The metal ions were quantitatively analyzed using the Inductively Coupled Plasma-Atomic Emission Spectrometer. Results: Of the three Co-Cr alloys, the Co ion concentration of the porcelain-fused-to-metal alloy was 1.512 ${\mu}g/cm^2$, which indicated the highest metal ion dissolution. The metal corrosion was higher in the more acidic pH 2.2 solution compared with the pH 4.4 solution. In all three Co-Cr alloys, Co ion dissolution was predominant in the two corrosive solutions. Conclusion: The corrosion resistance of the three Co-Cr alloys was high, indicating a good biocompatibility.

• Journal of the Korean institute of surface engineering
• /
• v.42 no.4
• /
• pp.161-168
• /
• 2009

Effects of TiN/Ti multilayer coating on the Ti-30Ta-xZr alloy surface were studied by using various experiments. The Ti-30Ta containing Zr (5, 10 and 15 wt%) were melted 10 times to improve chemical homogeneity by using a vacuum furnace. And then samples were homogenized for 24 hrs at $1000^{\circ}C$. The specimens were prepared for TiN/Ti coating by cutting and polishing. The prepared specimens were coated with TiN/Ti multilayers by using DC magnetron sputtering method. The analyses of coated surface and coated layer were carried out by field emission scanning electron microscope(FE-SEM), EDX, and X-ray diffractometer(XRD). From the microstructure and XRD analysis of Ti-30Ta-xZr alloys, The equiaxed structure was changed to needle-like structure with increasing Zr content. And $\alpha$-peak and elastic modulus increased as Zr content increased. The $\alpha$ and $\beta$ phase predominantly were found in the specimen containing high Zr content. According to the analysis of TiN/Ti coating layer, the surface defects and structures of Ti-30Ta-xZr were covered with TiN/Ti coating layer and surface roughness decreased.

• The Journal of Advanced Prosthodontics
• /
• v.9 no.2
• /
• pp.138-142
• /
• 2017

In restorative treatment using fixed dental prostheses, dentists should select appropriate restoration material among various types of dental materials. The strength, marginal fit, esthetics, wear resistance, biocompatibility, and cost are important factors in the choice of restoration materials. The present case showed a surface stain on a monolithic zirconia restoration that was due to wear between the monolithic zirconia restoration and the base metal alloy restoration. This phenomenon was confirmed by surface roughness measurement and electron probe micro-analysis.

• The Journal of Korean Academy of Prosthodontics
• /
• v.14 no.1
• /
• pp.31-34
• /
• 1976

The author studied the effects of some dental gold alloys and dental nonprecious metals on muscle. The metal specimens were cast in the size of $1.0mm.{\times}5.0mm.{\times}3.0mm.$ and implanted in the gluteus maximus musculus of the two dogs. The subjects were sacrificed at 3 weeks and 5 weeks respectively after implantation. The tissue was examined his to-pathologically. The findings were as follows. 1. The more the alloy contains gold, the less the tissue response to the alloy and the less the connective tissue layer around the specimens. 2. The recovery of connective tissue layer in gold specimens was markedly observed. 3. There were very thick connective layers around nonprecious specimens.

• Journal of Technologic Dentistry
• /
• v.17 no.1
• /
• pp.5-9
• /
• 1995

This study was carried out by obsorving to the conditions of an oxide on the surface of alloy according to the conditions of its heat treatment and analysing the change in composition on its surface. The result of this study is summarized as fellows. 1. It was shown that the higher the more the generated metal oxide while the higher the temperature of heat treatment. 2. The metal oxide was manily composed of Ni and Cr oxides. 3. The Ni composition indicated reduction while the higher the heat treatment in vaccum condition. 4. The Cr composition indicated increase while the higher the heat treatment in vaccum condition.

• Corrosion Science and Technology
• /
• v.8 no.4
• /
• pp.139-142
• /
• 2009

Recently, quaternary titanium alloys of the system Ti-Nb-Ta-Zr received considerable research interest as potential implant materials because of their excellent mechanical properties and biocompatibility. However, only few reported works were available on the corrosion behavior of such alloys. Hence, in the present work, electrochemical corrosion of Ti-35Nb-5Ta-7Zr alloy, which has been fabricated by arc melting and heat treatment, was studied in 0.9 wt% NaCl at $37\pm1^{\circ}C$, along with biomedical grade Ti-6Al-4V and CP-Ti. The phase and microstructure of the alloys were investigated employing XRD and SEM. The results of electrochemical studies indicated that the corrosion resistance of the quaternary alloy was inferior to that of Ti-6Al-4V and CP Ti.