• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.20 no.8
• /
• pp.1546-1552
• /
• 2016

In addition, because it uses preheating to dissolve an alloy in general, it is hard to regulate the appropriate melting temperature of the alloy and brewing time and shows the defect of the supplementation thing due to the super-heating. Once the alloy is molten and then most of the casting by attaching a sight glass or non-contact temperature sensor is suitable casting temperature the operator pressing a button to generate a centrifugal force to inject the molten alloy into a crucible in the casting ring. These results, and most of the cast temperature is too high or too low to generate a lot of casting defects do not get into a uniform cast body. In this paper, we developed a dental casting machine for high frequency using a single temperature sensor which can measure the actual temperature of the alloy than the temperature of the external non-contact measurement using a temperature sensor.

• Journal of Technologic Dentistry
• /
• v.23 no.1
• /
• pp.9-19
• /
• 2001

Microstructure and phase transformation of Ti-Ni-Cu alloy powders produced by using attrition milling method were studied. Mixed powders of Ti-(50-X)Ni-XCu ($X=0{\sim}20$ at%) in composition range were mechanically alloyed for maximum 20 hours by using SUS 1/4" ball in argon atmosphere. Ball to powder ratio was 50: 1 and impeller speed was 350rpm. Mechanically alloyed with attrition millimg method. powder was heat treated at the temperature up to $850^{\circ}C$ for 1 hour in the $10^{-6}$ torr vacuum. Ti-Ni-Cu alloy powders have been fabricated by attrition milling method. and then phase transformation behaviours and microstructual properties of the alloy powders were investigated to assist in improving the the high damping capacity of Ti-Ni-Cu shape memory alloy powders. The results obtained are as follows: 1. After heat treating of fully mechanically alloyed powder at $850^{\circ}C$ for 1hour. most of the B2 and B 19' phases was formed and $TiNi_3$ were coexisted. 2. The B 19' martensite were formed in Ti-Ni-Cu alloy powders whose Cu-content is less than 5a/o. where as the B19 martensite in those whose Cu-content is more than 10at%. 3. The powders of as-milled Ti-Ni-Cu alloys whose Cu-contents is less than 5at% are amorphous. whereas those of as-milled Ti-Ni-Cu alloys whose Cu-content is more than 10at% are crystalline. This means that Cu addition tends to suppress amorphization of Ti-Ni alloy powders.

• Journal of Technologic Dentistry
• /
• v.35 no.2
• /
• pp.105-112
• /
• 2013

Purpose: This study was to analyze the castability, surface oxide characteristic of Co-Cr alloy for porcelain fused to metal crown and the bonding strength of porcelain fused to metal crown. Co-Cr and Ni-Cr alloy for porcelain fused to metal crown was used for tests of the castability and surface oxide state and shear bonding strength by various porcelain. The aim of this study was to suggest the differences of result according to Co-Cr and Ni-Cr alloy. Methods: The kinds of alloy as test specimen was Co-Cr and Ni-Cr alloy. The castability index on the alloy specimens. The surfaces of two alloys were analyzed by SEM and EDX in order to observe oxide characteristic. And the shear test was performed by MTS. Results: The castability index of Co-Cr alloy was 96.8% and Ni-Cr alloy was 94.4%. The strongest bonding strength of Co-Cr alloy was shown 67.37 MPa. Conclusion: The shear bonding strength between Co-Cr alloy and EX3 porcelain was the strongest comparing with others. And all of each alloy was indicated as same level about the castability.

• The Journal of the Korean dental association
• /
• v.12 no.9
• /
• pp.667-677
• /
• 1974

A testing machine was devised and constructed for the purpose of measuring the retentive forces of maxillary complete denture bases in subjects. Forth complete denture bases were made for ten subjects with three different denture base materials, following the usual denture construction technique. Retentive forces of the forty dentures were determined at seven locations. The tests on each base were repeated three times at intervals of 5 minutes. Differences in retention values were evaluated statistically. 1) Differences in retention values were found by the differences of the denture base materials, but acrylic resin was similar to chromium cobalt alloy. 2) The chromium cobalt alloy and acrylic resin bases from master models revealed the best retention values, the gold alloy base from master model was the poor second and the acrylic resin base from snap model was the third. 3) The retention values for hook-1 revealed higher than that for hook-2 and the retention values for hook-3 revealed the lowest value.

• Journal of Technologic Dentistry
• /
• v.24 no.1
• /
• pp.95-104
• /
• 2002

For biomedical applications, Ti-X%Zr-Y%Nb-0.2%Pd(X:10$\sim$20, Y:2$\sim$8) alloys not containing harmful Al and V were newly designed, and the effect of alloy composition and heat treatment on the microstructure and mechanical properties was investigated. From the results, it was shown that the mechanical properties were enhanced with the addition of Zr or Nb. The effect of heat treating on room temperature strength was investigated by aging treatment after solution treatment. The mechanical properties of Ti-20%Zr-4%Nb-0.2%Pd alloy aged at 400$^{\circ}C$ for 10hrs was found to be superior to those of the pure Ti and Ti-6%Al-4%V ELI alloy.

• Journal of Technologic Dentistry
• /
• v.23 no.1
• /
• pp.21-30
• /
• 2001

For biomedical applications. Ti-X%Zr-Y%Pd(X: $10{\sim}20$, Y:0.2 or 0.4) based alloys not containing harmful Al and V were newly designed, and polarization curves for their alloys were measured at $37^{\circ}C$ in 5% HCl solution in order to understand effects of Zr on the corrosion. From the results of anodic polarization behavior, it was found that the corrosion resistance increased with increasing Zr content. The results show their potential to develope Ti-based alloys for biomedical materials. The Ti-20%Zr-0.2%Pd alloy shows excellent corrosion resistance and was superior to those of the Ti. Ti-6%Al-4%V ELI alloy, Co-30%Cr-6%Mo alloy and STS 316L stainless steel.

• Journal of Technologic Dentistry
• /
• v.19 no.1
• /
• pp.21-35
• /
• 1997

The Ag-Pd-Cu alloys containing a small amount of Au is commonly used for dental purposes, because this alloy is cheaper than Au-base alloys for clinical use. However, the most important characteristic of this alloy is age-hardenability, which is not exhibited by other Ag-base dental alloys. The specimens used were Ag-20Pd-20Cu ternary alloy and Au addition alloy. These alloys were melted and casted by induction electic furace and centrifugal casting machine in Ar atmoshpere. These specimens were solution treated for 2hr at $800^{\circ}C$ and were then quenched into iced water, and aged at $350{\sim}550^{\circ}C$ Age-hardening characteristics of the small Au-containing Ag-pPd-Cu dental alloys were investigated by means of hardness testing, X-ray diffraction and electron microscope observations, electrical resistance, differential scanning calorimetric, emergy dispersed spectra and electron probe microanalysis. Principal results are as follows : Hardening occured in two stages, I. e., stage I in low temperature and stage II in high temperature regions, during continuous aging. The case of hardening in stage I was due to the formation of the Llo type face centered tetragonal PdCu-ordered phase in the grain interior and hardening in stage I was affedted by the Cu concentration. In stage II, decomposition of the $\alpha$ solid solution to a PdCu ordered phase(L1o type) and an Agrich ${\alpha}2$ phase occurred and a discontiunous precipitation occurred at the grain boundary. Form the electron microscope study, it was concluded that the cause of age-hardening in this alloy is the precipitation of the PdCu ordered phase, which has AuCu I type face-centered tetragonal structure. Precipitation procedure was ${\alpha}\to{\alpha}+{\alpha}2+PdCu\to{\alpha}1+{\alpha}2+PdCu$ at Pd/Cu = 1 Ag-Pd-Cu alloy is more effective dental alloy as ageing treatment and is suitable to isothermal ageing at $450^{\circ}C$.

• Journal of Technologic Dentistry
• /
• v.28 no.1
• /
• pp.61-66
• /
• 2006

Titanium alloys have been used for dental materials due to it's very good biocompatibility. Ti-6Al-4V alloy instead of pure titanium is being widely used as biomaterials has some characteristics such as high fatigue strength, tensile strength and corrosion resistance. But it has been reported recently that the vanadium element expresses cytotoxicity and carcinogenicity and the aluminium element is related with dementia of Alzheimer type and neurotoxicity. The Ti-Nb alloys has designed and examined corrosion resistance. Ti-3wt.%Nb($\alpha$type), Ti-20wt.%Nb(${\alpha}+{\beta}$type) and Ti-40wt.%Nb($\beta$type) alloys were melted by vacuum arc furnace. The corrosion resistance of Ti alloys was evaluated by potentiodynamic polarization test in the solution of 0.9% NaCl and 5% HCl. The results can be summarized as follows: 1) For the corrosion test in the solution of 0.9% NaCl and 5% HCl, the corrosion behaviour of Ti-Nb alloys was similar to ASTM grade 2 CP Ti. 2) The corrosion resistance of Ti-20Nb alloy was better than that of CP-Ti, Ti-3Nb, Ti-40Nb alloy in 0.9% NaCl and 5% HCl, solutions.

• Journal of Technologic Dentistry
• /
• v.14 no.1
• /
• pp.119-132
• /
• 1992

This paper aims to investigate the effect of B and Si upon the mechanical properties, microstructure and corrosion resistance of Co-Cr base alloy. Ten groups of alloy ingot ingot with various contents of B and Si were remelted by high frequency electrical induction furnace and cast into tensile specimen of ADA Specification No. 14 Tensile and hardness test were carried out by Amsler and Rockwell hardness tester(R-30N), respectively. The microstructures of specimen were observed by SEM. The results obtained are summarized as follows : 1. As B content is increased, tensile strength, yield strength and Rockwell hardness number(R-30N) are also increased significantly, while the elongation is decreased significantly. 2. As Si contect os increased, no significant chang in tensile strength is noticed, yield strength is slightly decreased, but Rockwell hardness number(R-30N) is moderately in creased, Elongation marks maxium value with 1% Si content while with more than 1% Si it is decreased. 3. As B content is increased corrosion resistance is decreased and is at best with 1.5% B content. Corrosion resistance is increased with the increase of Si content and the alloys with Si over 3.0% showed corrosion resistance. 4. As B content increased, precipitates are increased in number at grain boundaries. The grain size tends to become coarse with the increase of Si content. 5. Co rich-Cr alloy is present through matrix whereas at the grain boundaries Cr base precipitates are primarily formed.

• Corrosion Science and Technology
• /
• v.4 no.1
• /
• pp.19-22
• /
• 2005

Two Au-Ag-Cu-Pd dental casting alloys (Au:12% and 20%) used. The test solutions used 0.9 % NaCl solution (isotonic sodium chloride solution), 0.9 % NaCl solution containing 1 % lactic acid, and 0.9 % NaCl solution containing 1 % lactic acid and 0.1 mol $dm^{-3}$ $Na_2S$. The surface of two samples in three sample solutions was not natural discoloration during one year. The alloy containing 12 % gold was easily alloyed and the composition was uniform comparing with the alloy containing 20 % gold. The rest potentials have not a little effect after three months. The kinds of metals could not definitely from the oxidation and reduction waves of metal on the cyclic voltammograms. The dissolutions of gold and palladium were 12 % Au sample in the 0.9 % NaCl solution containing 1 % lactic acid and 0.1 mol $dm^{-3}$ $Na_{2}S$. The pH of solution had an affect on dissolution of copper, and sulfur ion had an affect on dissolution of silver. The copper dissolved amount from 20 % gold sample was about 26 times comparing with that of 12 % gold sample in the 0.9 % solution containing 1 % lactic acid. Corrosion products were silver chloride and copper chloride in NaCl solution, and silver sulfide and copper sulfide in NaCl solution containing $Na_{2}S$.