• Structural Engineering and Mechanics
• /
• v.67 no.5
• /
• pp.545-553
• /
• 2018

Mode II delamination propagation is an important damage mode in laminated composites and this paper aims to investigate the behavior of this damage in laminated composite materials using acoustic emission (AE) technique. Three different lay-ups of glass/epoxy composites were subjected to mode II delamination propagation and generated AE signals were recorded. In order to investigate the propagation of delamination behavior of these specimens, AE signals were analyzed using Wavelet Packet Transforms (WPT) and Fast Fourier Transform (FFT). In addition, conventional AE analyses were used to enhance understanding of the propagation of delamination damage. The results indicate that different fracture mechanisms were the main cause of the AE signals. The dominant mechanisms in all the specimens were matrix cracking, fiber/matrix debonding and fiber breakage, with varying percentage of the damage mechanisms for each lay-up. Scanning Electron Microscopy (SEM) observations were in accordance to the AE results.

• Journal of the Korean Society for Precision Engineering
• /
• v.14 no.7
• /
• pp.116-125
• /
• 1997

An investigation was performed to study the impact damage in CFRP laminated composites subjected to impact loading. A finite element model has been developed for predicting the impact damage in laminated composite plates resulting from the ballistic impact. The finite element model was based on the higher-order shear deformation theory and was used to predict the initial intraply matrix cracking and the shape and size of interface delamination in laminated composites. Numerical simulation was performed and then the initiation of the matrix cracking and the shape and size of impacted induced delamination were predicted, and te results were compared with those of impact experiments with the same dimension and stacking sequences. A linear relationship holds between impact velocity and length and width of delamination. As impact velocity is increased, the increase of delamination length is highger than the increase of delamination width.

• Structural Engineering and Mechanics
• /
• v.30 no.6
• /
• pp.699-712
• /
• 2008

The effectiveness of wavelet transform in detecting delamination damages in multilayered composite beams and plates is studied here. The damaged composite beams and plates are modeled in finite element software ABAQUS and the first few mode shapes are obtained. The mode shapes of the damaged structures are then wavelet transformed. It is observed that the distribution of wavelet coefficients can identify the damage location of beams and plates by showing higher values of wavelet coefficients at the position of damage. The effectiveness of the method is studied for different boundary conditions, damage location and size for single as well as multiple delaminations in composite beams and plates. It is observed that both discrete wavelet transform (DWT) and continuous wavelet transform (CWT) can detect the presence and location of the damaged region from the mode shapes of the structures. DWT may be used to approximately evaluate the size of the delamination area, whereas, CWT is efficient to detect smaller delamination areas in composites.

• Smart Structures and Systems
• /
• v.23 no.2
• /
• pp.195-205
• /
• 2019

An accurate non-model-based method for delamination identification of laminated composite plates is proposed in this work. A weighted mode shape damage index is formulated using squared weighted difference between a measured mode shape of a composite plate with delamination and one from a polynomial that fits the measured mode shape of the composite plate with a proper order. Weighted mode shape damage indices associated with at least two measured mode shapes of the same mode are synthesized to formulate a synthetic mode shape damage index to exclude some false positive identification results due to measurement noise and error. An auxiliary mode shape damage index is proposed to further assist delamination identification, by which some false negative identification results can be excluded and edges of a delamination area can be accurately and completely identified. Both numerical and experimental examples are presented to investigate effectiveness of the proposed method, and it is shown that edges of a delamination area in composite plates can be accurately and completely identified when measured mode shapes are contaminated by measurement noise and error. In the experimental example, identification results of a composite plate with delamination from the proposed method are validated by its C-scan image.

• Advanced Composite Materials
• /
• v.16 no.3
• /
• pp.223-244
• /
• 2007

This study experimentally and numerically investigated the tensile damage progress in stitched laminates. In particular, it focused on the effects of stitching on the damage progress. First, we experimentally confirmed that ply cracks and delamination appeared under load regardless of stitching. We then performed damage-extension simulation for stitched laminates using a layer-wise finite element model with stitch threads as beam elements, in which the damage (ply cracks and delamination) was represented by cohesive elements. A detailed comparison between observation and the simulated results confirmed that stitching had little effect on the onset and accumulation of ply cracks. Furthermore, we demonstrated that the stitch threads significantly suppressed the extension of the delamination.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2001.05a
• /
• pp.69-73
• /
• 2001

Damage induced by low-velocity impact on the curved composite laminates was experimentally evaluated for CFRP cylindrical shells with the radius of curvatures of 50, 150, 300, and 500 mm. The result was then compared with that of flat laminates. The radius of curvatures and the effective shell stiffness appeared to considerably affect the dynamic impact response of curved shells. Under the same impact energy level, the maximum contact force increased with the decreasing radius of curvatures, with reaching 1.5 times that for plates at the radius of curvature of 50 mm. Since the maximum contact force is directly related to the impact damage, curved laminates can be more susceptible to delamination and less resistant to the low-velocity impact damage. The distribution of delamination along the thickness direction of curved laminates are also different from that of flat plates. Delamination was distributed rather even]y at each interface along the thickness direction of curved laminates. This implies that the effect of curvatures has to be considered for the design of a curved composite laminate.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.18 no.5
• /
• pp.1144-1149
• /
• 1994

Damage caused in CFRP laminates by low energy impact of steel ball are investigated ultrasonically. Two types of laminated specimens having different stacking sequence are used as a target material. The effects of pre-bending on the behaviors of impact damage are specifically discussed. The initiation and progagation behaviors of delamination were largely dependent upon the bending rigidity of each specimen. Specimen C having higher bending rigidity produced larger delamination damage than the Specimen D having relatively low bending rigidity, however it was little for the Specimen C. Application of pre-bending increased the apparent bending rigidity of target during impacting, it produced delamination at lower impact energy level compared to the case of no preload.

• Journal of the Korean Society of Safety
• /
• v.28 no.5
• /
• pp.21-26
• /
• 2013

Delamination of cover concrete due to re-bar corrosion is a critical damage reducing structural safety of reinforced concrete structures. Therefore, it should be detected and evaluated to provide appropriate maintenance to recover structural integrity. Impact-echo method, which utilizes thickness vibration characteristics of delaminated concrete section, is effective for detection and evaluation of small areal size delamination. However, it may not be applicable for large areal size delamination in which flexural vibration modes are dominated. In this study, applicability of vibration mode shapes of delaminated concrete section is investigated for visualization of delamination region in concrete structures. Numerical and experimental modal tests are performed to estimate mode shapes of delaminated concrete section and linear absolute summation technique is proposed for effective visualization of delamination region based on estimated mode shapes.

• Journal of the Korean Society of Safety
• /
• v.17 no.1
• /
• pp.1-5
• /
• 2002

An approach for the damage of delamination which is the major concern during mechanical working for composite laminate material is proposed based on linear elastic fracture mechanics. This paper presents method evaluating of damage crack length using by average thrust force with AE characteristics. Also, the relations of AE characteristics are obtained from delamination damages. We found the onset ply of the delamination and a critical energy release rate and expressed a stress intensity factor by AEcount equation.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.17 no.11
• /
• pp.2752-2761
• /
• 1993

The purpose of this study is to confirm the decreasing problems of residual bending strength, and the fracture machanism experimentally when CFRP composite laminates are subjected to Foreign Object Damage. Composite laminates used for this experiment are CFRP orthotropy laminated plates, which have two-interfaces [O/sub 6//sup o//90/sub 6//sup o/]sub sym/ and four-interfaces [O/sub 3//sup o//90/sub 6//sup o//O/sub 3//sup o]/sub sym/. When the specimen is subjected to transverse impact by a steel ball, the delamination area generated by impact damage is observed by using SAM(Scanning Acoustic Microscope). also, Thefracture surfaces obtained by three-point bending test were observed by using SEM (Scanning Electron Microscope). Then, fracture mechanism was investigated based on the observed delamination area and fracture surface. The results were summarized as follows; (1) It is found that for the specimen with more interface, the critical delamination energy is increased while delamination-development energy is decreased. (2) Residual bending strength of specimen A is greater than that of Specimen B within the impact range of impact energy 1. 65J (impacted-side compression) and 1. 45J (impacted-side tension). On the other hand, when the impact energy is beyond the above ranges, residual bending strength of specimen A is smaller than that of specimen B. (3) In specimen A and B, residual strength of CFRP plates subjected to impact damage is lower in the impacted-side compression than in the impacted-side tension. (4) In the case of impacted-side compression, fracture is propagated from the transverse crack generat-ed near impact point. On the other hand, fracture is developed toward the impact point from the edge of interface-B delamination in the case of impacted-side tension.