• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2001년도 추계학술대회 논문집
• /
• pp.247-252
• /
• 2001

Recently the steel parts used at automobiles are required to be used under high stress more than ever before in need of the weight down. To achieve this requirement of a high strength steel, it must be necessary to decrease inclusion content and surface defect as like decarburization, surface roughness etc.. In this study, the surface conditions are measured to know the influence on fatigue properties by two cases of shot peening of two-stage shot peening and single-stage shot peening. And for this study, two kinds of spring steel (SUP7, 50CrV4) are used. This study shows the outstanding improvement of fatigue properties at the case of two-stage shot peening in the rotary bending fatigue test and this is assumed to be from on low stress condition, the 1st stage shot peening is not affected by nonmetallic inclusion under metal. it is possible that the 2nd stage shot peening increases the fatigue life and the high stress but that is affected by nonmetallic inclusion under metal. so far beeasily 50CrV4 have made high stress. But, results also show fatigue failures originated at inclusion near surface, and this inclusion type is turned out to be a alumina of high hardness.

• 한국해양공학회지
• /
• 제15권3호
• /
• pp.93-99
• /
• 2001

Recently the steel parts used at automobils are required to be used under high stress more than ever before in need of the weight down. To achieve this requirement of a high strength steel, it must be necessary to decrease inclusion content and surface defect as like decarburization, surface roughness etc.. In this study, the surface conditions are measured to know the influence on fatigue properties by two cases of shot peening of two-stage shot peening and single-stage shot peening. And for this study, two kinds of spring steel (SAE 9254, DIN50CrV4) are used. This study shows the outstanding improvement of fatigue properties at the case of two-stage shot peening in the rotary bending fatigue test and this is assumed to be from (1) on low stress condition, th 1st stage shot peening is not affected by nonmetallic inclusion under metal.(2) it is possible that the 2nd stage shot peening increases the fatigue life and the high stress but that is affected by nonmetallic inclusion under metal. (3) so far beeasily DIN50CrV4 have made high stress. But, results also show fatigue failures originated at inclusion near surface, and this inclusion type is turned out to be a alumina of high hardness.

• 한국해양공학회지
• /
• 제15권4호
• /
• pp.66-72
• /
• 2001

Recently the steel parts used at automobiles are required to be used under high stress more than ever before in need of the weight down. To achieve this requirement of a high strength steel, it must be necessary to decrease inclusion content and surface defect as like decarburization, surface roughness etc.. In this study, the surface conditions are measured to know the influence on fatigue properties by two cases of shot peening of two-stage shot peening and single-stage shot peening. And for this study, two kinds of spring steel (JISG4081SUP7, DIN 50CrV4) are used. This study shows the outstanding improvement of fatigue properties at the case of two-stage shot peening in the rotary bending fatigue test and this is assumed to be from on low stress condition, the 1st stage shot peening is not affected by nonmetallic inclusion under metal. it is possible that the 2nd stage shot peening increases the fatigue life and the high stress but that is affected by nonmetallic inclusion under metal. so far beeasily DIN50CrV4 have made high stress. But, results also show fatigue failures originated at inclusion near surface, and this inclusion type is turned out to be a alumina of high hardness.

• International Journal of Safety
• /
• 제1권1호
• /
• pp.24-27
• /
• 2002

Recently the steel parts used in automobiles are required to be used under high stress more than ever before due to the need of keeping the weight down. To achieve this requirement of the high strength steel, it must be necessary to decrease inclusion contents and surface defects as like decarburization, surface roughness etc. In this study, the surface conditions are measured to know the influence on fatigue properties by two cases of two-stage shot peening and single-stage shot peening. And for this study, three kinds of spring steel (JISG408l-SUP7, SAE 9254 and DIN 50CrV4) are shaped. This study shows the outstanding improvement of fatigue properties at the case of two-stage shot peening in the rotating bending fatigue test and it results from (1) decreasing the surface roughness (2) unchanging the surface hardness (3) increasing the compressive residual stress. Moreover, results also show fatigue failures originated at the inclusion near the surface, and this inclusion type is turned out to be an alumina of high hardness.

• 한국정밀공학회지
• /
• 제29권4호
• /
• pp.395-408
• /
• 2012

An experimental investigation with 2.8kW Nd:YAG laser system was carried out to study the effects of different laser process parameters on the microstructure and hardness of STD11. The optical lens with the elliptical profile are designed to obtain a wide surface hardening area with uniform hardness. The Laser beam is allowed to scan on the surface of the work piece varying the power (1600, 1800 and 1900kW) and traverse speed (200, 400, 600, 800 and 1000mm/min) at three different F-numbers of lens. After laser surface treatment three zones, In the microstructure have been observed : melted zone(decarburization), heat affected zone(martensite), and the substrate.

• 동력기계공학회지
• /
• 제5권4호
• /
• pp.67-73
• /
• 2001

Recently the steel parts used at automobiles are required to be used under high stress more than ever before in need of the weight down. To achieve this requirement of a high strength steel, it must be necessary to decrease inclusion content and surface defect as like decarburization, surface roughness etc.. In this study, the surface conditions are measured to know the influence on fatigue properties by two cases of two-stage shot peening iud single-stage shot peening for two kinds of spring steel(SUP7, SAE9254). This study shows the outstanding improvement of fatigue properties at the case of two-stage shot peening in the rotary bending fatigue test and this is assumed to be from decreasing the surface roughness unchanging the surface hardness increasing the compressive residual stress. Results also show fatigue failures originated at inclusion near surface, and this inclusion type is turned out to be a alumina of high hardness.

• 한국마린엔지니어링학회:학술대회논문집
• /
• 한국마린엔지니어링학회 2001년도 추계학술대회 논문집(Proceeding of the KOSME 2001 Autumn Annual Meeting)
• /
• pp.71-79
• /
• 2001

Recently the steel parts used at automobiles are required to be used under high stress more than ever before in need of the weight down. To achieve this requirement of a high strength steel, it must be necessary to decrease inclusion content and surface defect as like decarburization, surface roughness etc.. In this study, the surface conditions are measured to know the influence on fatigue properties by two cases of shot peening of two-stage shot peening and single-stage shot peening. And for this study, three kinds of spring steel(JISG4081-SUP ,SAE 9254, DIN 50CrV4, ) are made. This study shows the outstanding improvement of fatigue properties at the case of two-stage shot peening in the rotary bending fatigue test and this is assumed to be from (1) Decreasing the surface roughness (2) Unchanging the surface hardness (3) Increasing the compressive residual stress But, results also show fatigue failures originated at inclusion near surface, and this inclusion type is turned out to be a alumina of high hardness.

• 열처리공학회지
• /
• 제19권3호
• /
• pp.149-155
• /
• 2006

The effects of eight types of spheroidizing annealing conditions including annealing temperature, annealing time, cooling rate, and gas atmosphere in the annealing furnace on the microstructure were determined in SM45C steel which has been widely used for automotive parts. The well-developed spheroidized structure and minimum hardness were obtained when the steel was heat-treated 6 hours at $740^{\circ}C$, cooled to $710^{\circ}C$ at a cooling rate of $24^{\circ}C/h$, and then kept for 7 hours at the $710^{\circ}C$ followed by air cooling. In order to increase the productivity and to save the manufacturing cost, it is desirable to apply a faster cooling rate in the spheroidizing annealing. It was found that air cooling was the fastest cooling rate applicable to the SM45C steel. The steel heat treated in air showed the decarburized layer of about $110{\mu}m$ in thickness at the surface of the specimen, resulting in serious problems in the quality of the quenched product.

• Applied Microscopy
• /
• 제7권1호
• /
• pp.45-49
• /
• 1977

용탕의 온도는 탄소의 비율을 높이기 위하여 $1500^{\circ}C$ 이하로 해야 하며, 주입온도는 $1460^{\circ}C$ 내외가 적당하다. 주조상태에서 소지의 침상석출물은 orthorhombic $(Fe,\;Mn)_3C$로 판명되었다. 냉간압연비는 클수록 결정이 미세화되고 또한 경도도 증가하였다. 표면탈탄이 얼어 나면 표면층에 martensite가 형성되어 성형하기가 어려우므로 argon 분위기를 쓰는 것이 좋았다. 두께 1 mm 판재의 경우 수인처리 온도가 $950^{\circ}C$ 이하일 때 탄화물 stringer 가 나타났고, $1020^{\circ}C$ 에서 30 분간 가열했을 때 탄화물이 의 소지에 고용되었다. C 함량이 클수록 인장강도와 연신률이 증가하였다. Ni, Cr 및 V 을 미량 첨가했을 때 인장강도 및 연신률이 커졌으며 또한 굽힘성도 좋았다.

• 열처리공학회지
• /
• 제19권5호
• /
• pp.270-279
• /
• 2006

The effects of eight types of spheroidizing annealing conditions including annealing temperature, annealing time, cooling rate, and furnace atmosphere on the microstructure and hardeness were determined in SCM440 steel which has been widely used for automotive parts. The well-spheroidized structure and minimum hardness were obtained when the steel was heat-treated at $770^{\circ}C$ for 6 hours, cooled to $720^{\circ}C$ at a cooling rate of $24^{\circ}C/h$, and then kept for 7 hours at the $720^{\circ}C$ followed by air cooling. In order to increase the productivity and to save the manufacturing cost, it is desirable to apply a faster cooling rate to the spheroidizing annealing. It was found that a cooling rate of $100^{\circ}C/hr$ was the fastest cooling rate applicable to the SCM440 steel among the four cooling rates used in this study. The microstructure consisted of ferrite and very fine spheroidized cementite when the steel was annealed for 13 hours at $720^{\circ}C$ below $A_{C1}$ temperature. This was caused by the short annealing time and the retarding effect of Cr and Mo on both the dissolution of pearlite to cementite and coarsening of spheroidized cementite. The steel heat treated in air showed the decarburized layer of about $125{\mu}m$ in thickness at the surface.