• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2001.11a
• /
• pp.80-87
• /
• 2001

The fatigue crack growth behavior of the SA516/60 steel which is used for pressure vessels was examined experimentally at room temperature $25^{\circ}C, -30^{\circ}C, -60^{\circ}C, -80^{\circ}C, -100^{\circ}C$ and -l2$0^{\circ}C$ with stress ratio of R=0.05, 0.1 and 0.3. Fatigue crack propagation rate da/dN related with stress intensity factor range ΔK was influenced by stress ratio in stable of fatigue crack growth (Region II) with an increase in ΔK. The resistance of fatigue crack growth at low temperature is higher compared with that at room temperature, which is attributed to the extent of plasticity-induced by compressive residual stress according to the cyclic loads. Fractographic examinations reveal that the differences of the fatigue crack growth characteristics between room and low temperatures are mainly explained by the crack closure and the strengthening due to the plasticity induced and roughness induced.

• Journal of Industrial Technology
• /
• v.21 no.B
• /
• pp.341-348
• /
• 2001

The effect of initial ${\alpha}^{\prime}$ in STS 304 Stainless Steel on fatigue resistance, and fatigue crack propagation behavior was studied with using C-T specimens. Higher ${\Delta}K_{th}$ was observed in the specimens with the content of 0% initial ${\alpha}^{\prime}$ than in the contents of 2% and 33% initial ${\alpha}^{\prime}$. The difference of da/dN at the same level of ${\Delta}K$ was distinctive in low and intermediate level of ${\Delta}K$ however became less different as the level of ${\Delta}K$ increased. It is because the formation of strain induced martensite occurred readily in lower ${\alpha}^{\prime}$ at the vicinity of the fatigue crack tip, which causes compressive residual stresses resulting in the enhancement of crack closure. In general fatigue cracks propagated transgranular mode and many segments of ridges were observed on the fracture surfaces. At the higher contents of initial ${\alpha}^{\prime}$ appeared the smaller size of ridge segments. Slips in austenite were blocked more frequently by the martensite colonies formed in austenite.

• Journal of the Korean Society for Precision Engineering
• /
• v.7 no.4
• /
• pp.55-64
• /
• 1990

The fatigue crack growth behavior of physically-short cracks(0.2${\Delta}K$ with $da/dN<1{\times}10^{-7}m/cycle$. The transition crack lengths where similtude with ${\Delta}K$ existed was between 1 and 2mm. The effective stress intensity factor range based on COD measurements gave better correlation between the physically-short and long cracks. Thus it can be considered that the crack closure effect is one of the main factors which causes the differences between these two cracks.

• Journal of the Korean Society of Safety
• /
• v.11 no.4
• /
• pp.10-15
• /
• 1996

In studying the fatigue strength of fillet welded the section of pressure vessel pad, this study was to evaluate the effect of weld toe notch and to compare the results of numerical analysis with the results of fatigue experiments of fillet welded A5l6 grade 60 steel specimens. The fatigue life for the Bead welded specimen was about 1.4 times as much it as the 1Pad welded specimen. Also, The fatigue life for the 2Pad welded specimen was about 1.5 times as much it as the 1Pad welded specimen. In $da/dN-{\Delta}K$ curve, the fatigue crack growth rate for the 1Pad welded specimen appeared higher than that of the 2Pad welded specimen in the same initial region of ${\Delta}K$, had a similar Inclination In the stabled region.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.18 no.9
• /
• pp.2374-2385
• /
• 1994

SiCw/Al composite material is especially attractive because of their superior specific strength, specific stiffness, corrosion fatigue resistance, creep resistance, and wear resistance compared with the corresponding wrought Al alloy. In this study, Fatigue crack growth behavior and fatigue crack path morphology(FCPM) of SiC whisker reinforced Al 6061 alloy with 25% SiC volume fraction and Al 6061 allay were performed. Result of the fatigue crack growth test sgiwed that fatigue crack growth rate of SiCw/Al 6061 composite was slower than that of Al 6061 matrix therefore it was confirmed that Sic whisker have a excellent fatigue resistance. And Al 6061 matrix had only FCPM perpendicular to loading direction. On the other hand SiCw/Al 6061 composite had three types in fatigue crack path morphology. First type is that both sides FCPM of artificial notch are perpendicular to loading direction. Second type is that a FCPM in artifical notch has slant angle to loading direction and the other side FCPM is perpendicular to loading direction. Third type is that both sides FCPM of notch have slant angle to loading direction. It was considered that this kinds of phenomena were due to non-uniform distribution of SiC whisker and confirmed by SEM observation for fracture mechanism study.

• Journal of Welding and Joining
• /
• v.3 no.2
• /
• pp.16-26
• /
• 1985

Post weld heat treatment(PWHT), at more than 600.deg. C, is essential to remove residual stress and hydrogen in weld HAZ and improve fatigue characteristics. However, residual stress during PWHT is responsible for PWHT embitterment and it promotes precipitation of impurities to grain boundary. In this paper, the effect of stress simulated residual stress on fatigue failure was evaluated by fatigue test, microhardness test and fractograph. The obtained results are summarized as follows; (1) The fatigue crack growth rate(da/dN) of parent and heat treated parent was affected by microstructure due to heat treatment and it depended on stress intensity factor (.DELTA.k). (2) The fatigue strength of weld HAZ was dependent on applied stress during PWHT and da/dN after PWHT was slower than as-weld. (3) Softening amount of weld HAZ was bigger than any other due to PWHT. Hardness value of weld HAZ was affected by heat treatment under the applied stress of 10 $kgf/mm^2$, but beyond 20 $kgf/mm^2$ it was increased by the applied stress rather than heat treatment. (4) Beyond the applied stress of 20 $kgf/mm^2$ during PWHT, intergranular fracture surface was observed and its amount was increased with applied stress during PWHT. (5) Effect of applied stress during PWHT on aspect of fracture surface was larger rather than that on fatigue crack growth behavior.

• Journal of Welding and Joining
• /
• v.7 no.1
• /
• pp.51-58
• /
• 1989

The purpose of this study is to investigate the corrosion fatigue crack growth of PWTHT specimens(SS41, SM53B) which are the compact tension ones extracted from the muti-passed weldment and weld block. The corrosion fatigue test was done at the cyclic stress frequency of 3Hz in 3.5% NaCl solution. The results are as follows. 1. Corrosion fatigue crack growth of as-weld was slower than that of base metal. 2. In the low .DELTA.K region, the effect of corrosion environment on crack growth was obvious. However, the corrosion effect decreased with the .DELTA.K slowly. 3. The behaviour of fatigue and corrosion fatigue crack growth depended on the material, heat treatment as well as experimental conditions. 4. Corrosion fatigue crack growth of PWHT specimens(SS41, SM53B) subjected to 1/4hr, was increased compared with that of as-weld. 5. There was a tendency that the exponent value(m) obtained in 3.5% NaCl solution was decreased in comparison with that in air, and the material constant(C)was increased for Paris equation, da/dN=C((.DELTA.K))$^{m}$ , compared with that in air considerably.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.21 no.10
• /
• pp.1674-1682
• /
• 1997

Fatigue tests were performed to investigate the effect of ceramic coatings as in TiN and TiCN on fatigue crack growth properties of ceramic coated 1Cr-1Mo-0.25V steel with different coating thickness in laboratory air conditions. The experimental results are described with respect to a Paris equation, da/dN=C(.DELTA.K)$^{m}$ , where the crack growth rate of coated specimens provided as similar growth rate as that of the uncoated specimen regardless of coating thickness. Furthermore, it was observed that the type of coating layer had virtually no effect on crack growth rate in the full region of stress intensity factor range. And it was also appeared that the final crack length of TiCN coated specimens was short compared to that of TiN coated, and the substrate specimens, in which it was inferred due to lowering the toughness of coated material from high hardness of TiCN coating layer itself.

• International Journal of Automotive Technology
• /
• v.8 no.5
• /
• pp.623-628
• /
• 2007

Reliability analysis based on fracture mechanics requires knowledge of the on statistical parameters m and C in the fatigue crack growth law $da/dN=C({\Delta}K)^m$. The purpose of the present study is to investigate if it is possible to explain the change of parameter m by the fluctuation of C only. In this study, we apply the Paris-Erdogan law treating the parameter C as random and the parameter m as constant. Fluctuations in crack growth rate are assumed to be dependent only on C. The material resistance to fatigue crack growth(Z=1/C) is treated as a spatially random process, that varies along the crack path. The theoretical crack growth rates at various stress intensity factors are discussed. Additionally, the results of constant ${\Delta}K$ fatigue crack growth tests are reported for the structural steel, SM45C. The experimental data have been analyzed to determine the probability distribution of fatigue crack growth resistanc.

• Journal of Fisheries and Marine Sciences Education
• /
• v.9 no.2
• /
• pp.198-208
• /
• 1997

Recently, with rapid increase of gas demand, there occurs much interest their security of safety in the gas storage tanks and pressure vessels etc. In order to solve the problems, the occurrence of corrosion fatigue crack and the propagation behavior must be investigated. Especially the occurrence of corrosion fatigue crack and the propagation behavior in the part which has concentrated stress or defects, must be studied more carefully. In this paper, the high-tensile steel of SPV 50 which is much used for building the LPG storage tanks was tested by the use of a plane bending corrosion fatigue tester under the various marine environment and in the air. These experiments were carried out to investigate the surface crack propagation behavior, the value of experimental constant for Paris' rule(da/dN=$C(K)^m$), the crack depth propagation rate and the accelerative factor of the surface crack propagation rate. The main results obtained are as follows ; 1) As the specific resistances of marine environment decreases, the exponential value of slope m of Paris' rule(da/dN=$C(K)^m$) decreases and the value of intercept C increases. 2) The surface crack propagation rate and the crack depth propagation rate are delayed, as the specific resistances of marine environment is increased. 3) The accelerative factor of the surface crack propagation rate by corrosion fatigue is higher, according as the stress intensity factor range ${\Delta}K_A$ is small.