• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.2
• /
• pp.99-107
• /
• 2014

In this study, the effects of curing procedures on the mechanical properties of recycled aggregate concrete (RAC) were investigated. The replacement ratios by recycled coarse aggregate were 0, 25, 50, 75 and 100% by mass of natural coarse aggregate. Steam curing was adopted to all recycled aggregate concrete mixtures. Compressive and split tensile strength, water porosity, chloride ions penetration resistance and drying shrinkage measurements were carried out to determine performance of the RACs. From the test results, it was found that the mechanical performance of RAC decreased as the recycled aggregate contents increased. Furthermore, steam curing reduced the compressive and split tensile strength, water porosity and total charge of RAC, especially at the early ages. However, at the later ages, the beneficial effect of steam curing was less prominent. This study clearly showed that initial steam curing could be one of practical methods to improve performance of RAC with higher replacement ratio of recycled aggregate.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.10a
• /
• pp.143-146
• /
• 1999

This study is intended to investigate the properties of expansion of concrete under various curing environment with expansive additives. In construction field, expansive additives, which are anaiable to prevent from the diverse cracks caused by drying shrinkage are not expected to accomplish the expantion we expected because of both the absence of the know ledge change, loss of weight and dynamic of elasticty under various unit contents of expansive additives and curing condtion.

• Proceedings of the KACD Conference
• /
• 2001.11a
• /
• pp.578.1-578
• /
• 2001

The aim of this study was to evaluate the efficiency of the recently introduced light curing units to polymerize a light curing resin composite. Four light curing units XL 3000, Optilux 500 for halogen light source, Apollo 95E for plasma arc and Easy cure for LED (blue-light Emitting Diode) were evaluated. Radiometer was used for measure the light intensity.(omitted)

• Journal of the Korea Institute of Building Construction
• /
• v.18 no.6
• /
• pp.517-525
• /
• 2018

The construction of super tall building which structure is RC and must be certainly considered on column shortening estimation and construction reflected concrete creep has been increased. Regarding the Fck 60~80MPa grade high strength concrete applied in the domestic super tall building project, the mechanical properties and creep deflection according to curing conditions(Drying creep/Basic creep) were reviewed in this research. Results of compressive strength and elastic modulus under sealed curing condition were 5% higher than unsealed condition and difference of results according to the curing condition was increased over time. Autogenous and drying shrinkage tendency showed adversely in the case of high strength concrete. Additionally, creep modulus under unseal curing condition was evaluated 2~3 times higher than sealed condition. Modified model of ACI-209 based on test result was applied to estimate long period shortening of vertical members(such as Core Wall/Mega Column) exactly, it is designed to modify and suggest the optimal creep model based on various data accumulated during construction, in the future.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.05a
• /
• pp.151-156
• /
• 2002

Drying shrinkage cracking which may be caused by the relatively large specific surface is a matter of grave concern for latex modified concrete(LMC) overlay and rapid-setting cement latex modified concrete(RSLMC) overlay. LMC and RSLMC were studied for field applications very actively in terms of strength and durability in Korea. However, there were no considerations in drying shrinkage. Therefore, the purpose of this study was to investigate the drying shrinkage properties of LMC and RSLMC with the main experimental variables such as cement types(ordinary portland cement, rapid setting cement), latex contents(0, 5, 10, 15, 20%), W-C ratios, and curing days at a controlled environment of 60% of relative humidity and 2$0^{\circ}C$ of temperature. The drying shrinkage for specimens was measured with a digital dial gauge of Demec. The test results showed that the drying shrinkage of LMC and RSLMC were considerably lower than that of OPC and RSC, respectively. This might be attributed to the interlocking of hydrated cement and aggregates by a film of latex particles, water retention due to hydrophobic, and colloidal properties of the latexes resulting in reduced water evaporation.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.35 no.1
• /
• pp.18-29
• /
• 2008

The purpose of this study was to compare the polymerization shrinkage of several filling methods using strain gauges. In this study, a light-emitting diode(LED) curing unit(Elipar Freeligh2, 3M EPSE, USA) and plasma arc lamp(PAL) curing unit(Flipo, LOKKI, France) were used for curing, Filtek $Z350^{TM}$(3M EPSE, USA) composite resin was used for the cavity filling. Sixty permanent bicuspid teeth, that were extracted for orthodontic treatment, were studied. The cavities were prepared on the occlusal surface and were filled using the following methods : 1) bulk filling, 2) parallel filling, 3) oblique filling The strain was recorded on the buccal, lingual, mesial and distal surfaces and the strain values were computed into stress values. The shear bond strength of each filling method was tested using a Micro Universal Testing machine. The results can be summarized as follows: 1. In the strain changes, all LED and PAL curing groups showed an increase on the buccal surface and a slow decrease as time elapsed. 2. In the strain changes of the mesial and distal surfaces, the decreases and increases were shown repeatedly and reduced as time elapsed. 3. There were no significant statistical strain changes among filling methods in the LED or PAL curing groups. 4. There were significant statistical strain changes between the LED and PAL curing groups on the buccal surface(p<0.05). 5. From the shear bond strength results, in the LED curing group, filling method 3 showed lower surface stress than filling method 1 and 2(p<0.05). In the PAL curing group, there were no significant statistical strain changes between each filling method. 6. The surface stress of each group was lower than the shear bond strength.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.26 no.2
• /
• pp.76-83
• /
• 2022

Since the 3D printing mortar is exposed to the atmosphere immediately after printing, moisture is largely evaporated from the surface of the layer. The evaporation of moisture on the surface of the layer greatly causes drying shrinkage and increases the risk of cracking and damage to the structure due to drying shrinkage. This study experimentally evaluated the shrinkage behavior of the initial age using the mortar used for 3D printing. The change in shrinkage was evaluated by comparing the shrinkage of the specimen cured by the sealing method and the atmospheric exposure method. In addition, compared with the case where type 1 cement was used 100%, the shrinkage amount was evaluated when 20% of fly ash was replaced and 10% of silica fume was used. In particular, the effect of three chemical admixtures applied using 3D printing on shrinkage was evaluated experimentally. When fly ash and silica fume were used, the shrinkage amount increased by 60 - 110% compared to the case when type 1 cement was used. The application of viscosity modifiers and shrinkage reducers reduced the shrinkage by at least 18% and at most 70% depending on the curing conditions. The temperature of the specimen temporarily decreased to 15 ℃ at the beginning of curing, and the correlation between the internal temperature of the specimen and the shrinkage behavior was observed.

• International Journal of Highway Engineering
• /
• v.10 no.1
• /
• pp.117-122
• /
• 2008

Quality control of the concrete pavement in the early stage of curing is very important because it has a conclusive effect on its life span. Therefore, examining and analyzing the initial behavior of concrete pavement must precede an alternative to control its initial behavior. There are largely two influential factors for the initial behavior of concrete pavement. One is the drying shrinkage, and the other is the heat generated by hydration and thermal change inside the pavement depending on the change in the atmospheric temperature. Thus, the coefficient of thermal expansion and drying shrinkage can be regarded as very important influential factors for the initial behavior of the concrete. It has been a general practice up until now to measure the coefficient of thermal expansion from completely cured concrete. This practice has an inherent limitation in that it does not give us the coefficient of thermal expansion at the initial stage of curing. Additionally, it has been difficult to obtain the measurement of drying shrinkage due to the time constraint. This research examined and analyzed the early drying shrinkage of the concrete and measurements of the thermal expansion coefficients to formulate a plan to control its initial behavior. Additionally, data values for the variables of influence were collected to develop a prediction model for the initial behavior of the concrete pavement and the verification of the proposed model. In this research, thermal expansion coefficients of the concrete in the initial stage of curing ranged between $8.9{\sim}10.8{\times}10^{-6}/^{\circ}C$ Furthermore, the effects of the size and depth of the concrete on the drying shrinkage were analyzed and confirmed.

• Journal of Adhesion and Interface
• /
• v.11 no.2
• /
• pp.57-62
• /
• 2010

Photo-curable material can be crosslinked among molecules by light source such as UV and visible light materials. Material properties are controlled by crosslink reaction. Shrinkage is occured during the curing reaction of material structure. Phenomenon of shrinkage stress occurs inside the product and reduce the stability of the product causes problems. Heat shrink the evaluation of the phenomenon has been formalized. But the evaluation of photo shrink is not enough. In this experiment, real-time contract with shrinkage tester phenomena and analysis degree of shrinkage of the material differences. According to the research, experimental results and theoretical analysis of the results were big differences. Shrinkage, especially for a number of different functional groups that were very different theory. These differences are occurred by the molecular structure different and not enough reaction.

• Journal of the Korea Concrete Institute
• /
• v.28 no.3
• /
• pp.317-328
• /
• 2016

This research intends to understand the impact of super-absorbent polymer (SAP) as an internal curing agent in Ultra-High Performance Concrete (UHPC). Two different types of SAPs of acrylic acid (SAP_AA) and acrylic acid-co-acrylamide (SAP_AM) were examined with UHPC formulation. Isothermal calorimetry and x-ray diffraction experiments revealed the impact of polymers with the different chemical bonds on cement hydration. To test its feasibility as a shrinkage reducing admixture for UHPC, a series of experiments including flowability, compressive strength, rapid chloride permeability and autogenous shrinkage profile was performed. While both SAPs showed a reduction in autogenous shrinkage, it has been concluded that the SAP size and chemical form significantly affect the performance as an internal curing agent in UHPC by controlling cement hydration and porosity modification. Between the tested SAPs, SAP_AM which absorbs more water in UHPC than SAP_AA, shows better mechanical and durability performance.