• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.19 no.5
• /
• pp.242-245
• /
• 2009

AlN crystals were grown by a sublimation process without seed crystals and the growth morphology of them was characterized. The grown AlN crystals were a polycrystalline phase, which had a diameter of $60\sim200\;{\mu}m$ and were grown with a growth rate of $0.2\sim0.5\;{\mu}n/hr$. It was observed that the as-grown crystals had a hexagonal crystal structure and revealed that these crystals were grown with a morphology of columnar morphology in the initial stage of the growth before they were enlarged in a way of a lateral growth behavior in the final stage. On the surface, a lot of pinholes were observed on the surface of crystals grown. The evolution of a growth morphology was characterized by optical and scanning electron microscopic observation.

• Journal of Advanced Marine Engineering and Technology
• /
• v.18 no.2
• /
• pp.54-63
• /
• 1994

Mg thin films were prepared on SPCC(cold-rolled steel) substrates by vasuum evapoaration and ion-plating. The influence of argon gas pressure and substrates bias voltage on the crystal orientation and morphology of the film was determined by using X-ray diffraction and scanning electron micrography (SEM), respectively. And the effect of crystal orientation and morphology of the Mg thin films on corrosion behavior was estimated by measuring the anodic polarization curves in deaerated 3% NaCl solution. The crystal orientation of the Mg films deposited at high argon gas pressure exhibited a (002) preferred orientation, regardless of the substrate bias voltage. Film morphology changed from a columnar to a granular structure with the increase of argon gas pressure. The morphology of the films depended not only on argon gas pressure but also bias voltage ; i.e., the effect of increasing bias voltage was similar to that of decreasing argon gas pressure. The influences of argon gas pressure and bias voltage were explained by applying the adsorption inhibitor theory and the sputter theory. And also, this showed that the corrosion resistance of the Mg thin films can be changed by controlling the crystal orientaton and morphology.

• Textile Coloration and Finishing
• /
• v.27 no.4
• /
• pp.245-260
• /
• 2015

The effect of salt milling process on the crystal size, morphology, and color characteristics of C.I. Pigment Red 57:1 was studied. The primitive morphology and color properties of the pigment after synthesis were studied in the former series work. The size and morphology of primary particles and the second aggregation features should be considered because they are very important to determine pigment quality. We compared the primary morphology of pigment particles before drying with the secondary aggregated morphology of pigment particles after drying and salt milling process. Morphological properties were investigated by particle size analysis, X-ray diffraction, and scanning electron microscopy and color measurement was carried out. Significant reduction in particle size as well as enhanced crystallite size after salt milling process was observed. This result might give a difference in color of the pigment, turning into brighter and more blue-toned red color. It was revealed that synthesis condition affect the morphology and color of the pigment even after milling. Increase in HCl concentration in the synthesis process enhanced crystal size and quality forming bluer-red pigments but an increase in $CaCl_2$ concentration resulted in more amorphous crystals forming darker-red pigments after salt milling.

• Korean Journal of Crystallography
• /
• v.5 no.2
• /
• pp.93-99
• /
• 1994

Growth form and surface morphology of NYAB single crystal grown by TSSG technique using a K2O/3MoOS/0.5B203 flux was investigated. In the crystal grown from <100> or <120> seed, prismatic and (101) faces were well developed with different size each other. (001) face was also developed in the crystal grown from <001> seed. While growth hillocks were observed on the prismatic face of the crystal grown from <100> seed, surface striations parallel to neighbor (101) faces were formed on that face of the crystal grown from <001> seed. The (101) faces were grown by two dimensional nucleation growth. (001) face which was developed at slow growth velocity of [001] direction was grown by screw dislocation Anisotropy of growth velocity as to seed orientation affected on crystal morphology and surface morphology.

• Corrosion Science and Technology
• /
• v.3 no.4
• /
• pp.148-153
• /
• 2004

Magnesium thin flims were prepared on cold-rolled steel substrates by RF magnetron sputtering technique. The influence of argon gas pressure and substrate bias voltage on their crystal orientation and morphology of the coated films were investigated by scanning electron microscopy (SEM) and X-ray diffraction, respectively. And the effect of crystal orientation and morphology of magnesium films on corrosion behaviors was estimated by measuring anodic polarization curves in deaerated 3%NaCl solution. From the experimental results, all the sputtered magnesium films showed obviously good corrosion resistance to compare with 99.99% magnesium target of the sputter-evaporation metal. Finally it was shown that the Corrosion-resistance of magnesium films can be improved greatly by controlling the crystal orientation and morphology with effective use of the plasma sputtering technique.

• Macromolecular Research
• /
• v.14 no.6
• /
• pp.640-645
• /
• 2006

Polyethylene of bimodal molecular weight distribution was irradiated with an electron beam. The thermal and mechanical properties were examined by DSC, small and wide angle X-ray scattering and static tensile test according to the crystal morphology of the irradiated samples. The crystal morphology change upon irradiation, as revealed by wide angle X-ray scattering, correlated well with the changes in melting enthalpy, whereas the lamellar thickness and the amorphous gap thickness remained virtually unchanged at irradiation doses up to 500 kGy. Crosslinks in the crystal domains became evident at an energy level of 250 kGy, resulting in reduced crystallinity and crystal size of the (110) and (200) planes. The samples became stiff and brittle with increased irradiation dose, which seem to be more relevant to the amount of cross links than the crystal morphology changes.

• Journal of the Korean Chemical Society
• /
• v.65 no.1
• /
• pp.58-61
• /
• 2021

• Journal of Advanced Marine Engineering and Technology
• /
• v.20 no.5
• /
• pp.103-113
• /
• 1996

The properties of the deposited film depend on the deposition condition and these, in turn depend critically on the morphology and crystal orientation of the films. Therefore, it is important to clarify the nucleation occurrence and growth stage of the morphology and orientation of the film affected by deposition parameters, e.g. the gas pressure and bias voltage etc. In this work, magnesium thin flims were prepared on cold-rolled steel substrates by a thermo-eletron activation ion plating technique. The influence of nitrogen gas pressure and substrate bias voltage on their crystal orientation and morphology of the coated films were investigated by scanning electron microscopy (SEM) and X-ray diffraction, respectively. The diffraction peaks of magnesium film became less sharp and broadened with the increase of nitrogen gas pressure. With an increase in nitrogen gas pressure, flim morphology changed from colum nar to granular structure, and surface crystal grain-size decreased. The morphology of films depended not only on gas pressure but also on bias voltage, i.e., the effect of increasing bias voltage was similar to that of decreasing gas pressure. The effect of crystal orientation and morphology of magnesium films on corrosion behaviors was estimated by measuring anodic polarization curves in deaerated 3%NaCl solution. Magnesium, in general, has not a good corrosion resistance in all environments. However, these magnesium films prepared by changing nitrogen gas pressure showed good corrosion resistance. Among the films, magnesium films which exhibited granular structure had the highest corrosion resistance. The above phenomena can be explained by applying the effects of adsorption, occlusion and ion sputter of nitrogen gas.

• Journal of the Korean Society of Marine Environment & Safety
• /
• v.17 no.2
• /
• pp.155-160
• /
• 2011

In these days, there are increasing demands for weight reduction in many industrial fields including marine industries. Therefore, magnesium thin films for lightweight materials were prepared on magnesium alloy substrate. The influence of gas pressure and substrate bias voltages on the crystal orientation and morphology of the films was determined by using X-ray diffraction and FE-SEM, respectively. And the effect of crystal orientation and morphology of the magnesium thin films on corrosion behavior was estimated by measuring electro-chemical anodic polarization curves in deaerated 3% NaCl solution. From the results, corrosion resistance of Mg thin films was improved by controlling the crystal orientation and morphology of the films with effective use of plasma ion plating technique.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.18 no.5
• /
• pp.184-190
• /
• 2008

$CaMoO_4$ crystals with ellipsoid, peanut, dumbbell, and notched sphere shapes were synthesized using a simple precipitation reaction. The morphology of $CaMoO_4$ crystals evolved from ellipsoids, through peanut-like structures and dumbbells, to notched spheres with increasing the concentration of $Ca^{2+}$ and $MoO_4^{2-}$ ions. This morphology evolution of $CaMoO_4$ crystals is attributed to a fractal mechanism. Branched crystal growth started at both ends of the ellipsoids. The peanut-like and dumbbell morphologies were formed by the first and second fractal growths, respectively. Finally, the notched spheres were formed by further fractal growth of dumbbells.