This study was performed to evaluate the efficacy of 0.8% sodium hyaluronic acid solution and crosslinked hyaluronic acid mixture for the prevention of postoperative intraperitoneal adhesion in rats. Forty-five animals were divided into three groups ; 0.9% saline treated control group, 1% sodium carboxymethyl cellulose treated group (SCMC), and 0.8% sodium hyaluronic acid solution and crosslinked hyaluronic acid mixture treated group (SHCH). Adhesions were induced by suturing both the ileal serosa and peritoneum abrased until petechial bleeding occurred. Fourteen days later, adhesions were evaluated clinically and histopathologically. The mean tensile strength was significantly decreased in the SCMC and SHCH groups compared to the control group (p < 0.05), and the SHCH group had the lowest tensile strength. The distance of adhesion site was highest in the control group and significantly decreased in the SHCH group comparing control group (p < 0.05). The inflammatory cell infiltration, collagen hyperplasia and neovascularization of the SCMC and SHCH groups were significantly lower than the control group (p < 0.05). Therefore, it was concluded that the SHCH may be useful to prevent postoperative intraperitoneal adhesion in rats.

• 폴리머
• /
• 제29권5호
• /
• pp.445-450
• /
• 2005

인체 보형물의 생체 재료로 사용할 목적으로 히아루론산 비드를 제조하였다. 히아루론산 수용액과 콩기름을 섞어서 얻어진 현탁상태에서 히아루론산을 1,3-butadiene diepoxide로 가교시켰다. 제조된 비드의 물성을 살펴보기 위해 직경, 표면적과 팽윤도를 측정하였고 전자현미경으로 표면상태를 관찰하였다. 가교제의 농도가 $5-12\;vol\%$ 범위에서 비드가 형성되었으며 제조된 비드는 단순분산성을 보였다. 히아루론산 농도 혹은 가교제 농도가 증가할수록, 가교 온도가 감소할수록, BET표면적과 팽윤도가 감소하였다. 혼합속도의 변화에 의해 비드의 물성은 거의 변하지 않았으나 비드의 크기는 효과적으로 조절되었다.

• 대한의용생체공학회:의공학회지
• /
• 제42권6호
• /
• pp.251-258
• /
• 2021

Hyaluronic acid (HA) microspheres (MSs) crosslinked with polyethylene glycol diglycidyl ether (PEGDE) are prepared using a simple fluidic device (SFD) to investigate the optimized parameters. A solution mixture of PEGDE in 2-methyl-1-propanol was prepared as a continuous phase in SFD. HA solutions of 1 wt% concentration were introduced into SFD as a discontinuous phase. The HA solution prepared by stirring for more than 48 h exhibited spherical MSs at the needle tip inside the ring cap. As the flow rate of the continuous phase increased from 0.7 to 1.9 mL/min, the diameter of the MS decreased from 173±36 ㎛ to 129±13 ㎛. Although the PEGDE concentration in the range of 0.2 to 1.8 vol% did not affect the diameter of the MS, the microstructure of MS, consisting of inner hollow void and wall, was changed. The inner void and wall size decreased and increased from 79.5 ㎛ to 57.2 ㎛ and from 10.3 ㎛ to 21.4 ㎛, respectively, with increasing PEGDE concentration from 0.2 vol% to 1.8 vol%. FT-IR peaks located around 2867 cm^-1 and 1088 cm^-1 indicated that the HA MS prepared at different PEGDE concentrations were chemically crosslinked. The HA MSs containing different PEGDE concentrations exhibited quantitative cell viability of more than 98%. L-929 cells adhered well to the HA MSs and proliferated continuously with increasing culture time to 48 h regardless of PEGDE concentration, implying that the HA MSs are clinically safe and effective.

• 센서학회지
• /
• 제21권4호
• /
• pp.256-262
• /
• 2012

Hyaluronic acid(HA) hydrogels were synthesized by immersing HA microbeads in phosphate buffered saline solutions having different pH levels to assess the effect of pH on the swelling ratio of HA hydrogels for smart drug delivery systems. No beads were formed when the HA solution(below pH 9) was crosslinked with divinyl sulfone(DVS) because DVS is a basic solution. The variation regarding the size of the microbead was not significant, suggesting that the bead size is not a function of pH(10 ~ 14). However, the pore size of the microbeads decreased with increasing pH from 10 to 14, leading to the surface smoothness and dense network as a result of higher crosslinking. The swelling ratio of hydrogels increased when the pH rose from 2(acidic) to 6(neutral). Afterwards, it decreased with further increasing pH(basic). The lower swelling ratio may be due to the lack of ionization of the carboxyl groups. On the other hand, a higher swelling ratio is likely due to the increased electrostatic repulsions between negatively charged carboxyl groups on different chains. Experimental results suggested that pH-responsive HA hydrogels can be applicable to the controlled drug delivery systems.

• 한국세라믹학회지
• /
• 제49권6호
• /
• pp.518-522
• /
• 2012

Hyaluronic acid (HA) microbeads were synthesized by dropping 0.5 wt% of sodium hyaluronate dissolved in NaOH into 0.2 vol% of divinyl sulfone dissolved in 2-methyl-1propanol at a speed of 0.005 ml/min. HA microbeads were collected from a divinyl sulfone crosslinker solution stirred at 200 to 400 rpm for 5 h at temperatures from room temperature to $60^{\circ}C$ at intervals of $10^{\circ}C$. The crosslinked microbeads were then cleaned thoroughly using distilled water and ethanol. SEM results revealed that the microbeads were white-colored spheres. The 3-D porous network structure of the microbeads became dense with an increase in the crosslinking temperature; however, no dependence of the crosslinking temperature on the microbead size was detected. The extent of swelling decreased from 970% to 670% with an increase in the crosslinking temperature from room temperature to $60^{\circ}C$, most likely due to the increase in the degree of crosslinking.

• 폴리머
• /
• 제32권5호
• /
• pp.415-420
• /
• 2008

면역 거부반응이 없는 돼지 소장점막하조직(small intestinal submucosa, SIS)과 천연보습제인 히알루론산(hyaluronic acid, HA)은 생체재료로 널리 사용되고 있다. 본 연구에서는 이를 이용하여 스폰지를 제조하고 이들의 특성을 분석하였다. SIS-HA 스폰지는 완성된 SIS 스폰지에 1w%의 HA겔을 첨가하여 동결건조법으로 제조하고 100mM의 가교제를 통해 가교하여 이를 전자주사현미경, 적외선분광기, 물흡수성 실험을 하였다. 초기 세포부착률을 확인하고자 NIH/3T3를 분주하여 MTT 분석법을 수행하였다. FT-IR 분석을 통해 C-O관능기가 관찰되어 SIS-HA 스폰지 내부의 HA가 빠져나가지 않고 고르게 분포되어 있음을 확인하였고, MTT분석을 통하여 제조된 스폰지에서의 높은 세포생존율을 확인하였다. 즉, 본 연구에서 제조한 SIS-HA 스폰지는 SIS와 HA 각각의 특성을 모두 내재하고 있어 조직공학적 담체로 적합할 것이다.