• Journal of Advanced Marine Engineering and Technology
• /
• 제29권4호
• /
• pp.426-435
• /
• 2005

The lightness of components required in automobile and machinery industries is requiring high strength of components. Therefore this requirement is accomplished as the process of shot-peening method that the compressive residual stress is made on the metal surface as one of various improvement methods. Special research is, therefore, needed about compressive residual stress on the metal surface in the process of shot-peening method. Therefore, in this paper the effect of compressive residual stress of spring steel(JISG SUP-9) by shot-peening on fatigue crack growth characteristics in environmental condition(temperature) and mechanical condition(shot velocity, stress ratio) was investigated with considering fracture mechanics. By using the methods mentioned above, the following conclusions have been drawn. (1) The fatigue crack growth rate(da/dN) of the shot-peened material was lower than that of the un-peened one. In high temperature range. fatigue crack growth rate decreased with increasing temperature range, while fatigue crack growth rate increased by decreasing temperature in low temperature. (2) Fatigue life shows more improvement in the shot-peened material than in the un-peened material. And compressive residual stress of surface on the shot-peen processed operate resistance force of fatigue crack propagation.

• Journal of Mechanical Science and Technology
• /
• 제16권10호
• /
• pp.1246-1252
• /
• 2002

Ultrafine grained (UFG) low carbon (0.15 wt.% C) steel produced by equal channel angula. pressing (ECAP) was tested for investigating the effect of load ratio on the fatigue crack growth rate. Fatigue crack growth resistance and threshold of UFG steel were lower than that of asreceived coarse grained steel. It was attributed to the less tortuous crack path. The UFG steel exhibited slightly higher crack growth rates and a lower △Kth with an increase of R ratio. The R ratio effect on crack growth rates and △Kth was basically indistinguishable at lower load ratio (R >0.3), compared to other alloys, which indicates that contribution of the crack closure vanishes. The crack growth rate curve for UFG steel exhibited a longer linear extension to the lower growth rate regime than that for the coarse grained as-received steel.

• 대한금속재료학회지
• /
• 제50권4호
• /
• pp.271-279
• /
• 2012

9-12% Cr steels have been used in thermal power plants which repeat start and stop operations. Major factors of fatigue life are temperature, frequency, stress ratio, holding time, microstructure, and environment. Normally, fatigue life decreases at high temperature, low frequency, high stress ratio, and long holding time conditions. A Mod.9Cr-1Mo steel, called G91, was developed at ORNL (Oak Ridge National Laboratory, USA) and was adopted as a high-temperature structural material in the ASME Code in 2004. However, its low-cycle fatigue and fatigue crack growth characteristics have been rarely studied. In this work, we have investigated the low-cycle fatigue crack growth behaviors of G91 steel under various test conditions in terms of temperature and stress ratio. As temperature and stress ratio increase, the crack growth rate becomes faster and striation distance also increases. On the other hand, the number of branch cracks decreases.

• 한국공작기계학회:학술대회논문집
• /
• 한국공작기계학회 1997년도 추계학술대회 논문집
• /
• pp.120-126
• /
• 1997

This paper examines the crack growth behavior of 7075-T651 aluminum alloy under high-low block loading condition. The cantilever beam type specimen with a chevron notch is used in this study. The crack growth and closure are investgated by compliance method. The applied initial stress ratios are R=-0.5, R=0.0 and R=0.25 Crack length($\alpha$), effective stress intensity factor range(ΔKeff), ratio of effective stress intensity factor range(U) and crack growth rate(d$\alpha$/dN) etc. are inspected fracture mechanics estimate.

• 한국해양공학회지
• /
• 제1권1호
• /
• pp.104-110
• /
• 1987

Fatigue tests by axial loading (R = 0.05) were carried out to investigate fatigue crack growth characteristics of small surface cracks in 2 1/4 Cr-1 Mo steel at room temperature by using flat specimens with a small artificial pit. All the data of the fatigue crack growth rate obtained in the present test are determined as a function of the stress intensity factor range about a semi-elliptical crack, so that the application of linear fracture mechanics to the surface fatigue crack growth and to the fatigue crack growth into depth, and all the data obtained from tests were discussed in comparison with the data of Type 304 stainless steel and two type of mild steel under the same test conditions. The obtained results are as follows: 1)When the cycle ratios are same, surface fatigue crack length and its depth are almost same and fall within a narrow scatter band in spite of different stress levels. 2)Relations of the surface fatigue crack growth rate (da/dN) and fatigue crack growth rate into depth (db/dN) to its stress intensity factor range ($\Delta K_{Ia}, \Delta K_{Ib}$) can be plotted as a straight line at log-log diagram without dependence of stress level and coincide with the data of part-through crack in various steels.

• 한국생산제조학회지
• /
• 제6권4호
• /
• pp.80-88
• /
• 1997

An experimental investigation of the fatigue through crack growth behavior under simple stepped variable loading condition has been performed using Al7075-T651. Experiments were carried out by using cantilever bending type specimens, with chevron notches on a small electro-magnetic test machine. Tensile overloads have a retarding effect on the fatigue crack growth rates, therefore tensile overloads were used for the beneficial effect on the fatigue life. While in most cases compressive overloads have only a vanishing effect on crack growth rates, some experiments with single edge crack tension specimens reveal a marked growth retardation. The stress ratios used in this investigations varies from R=0.32 to 0.81, from R=0.04 to 0.76, from R=-0.15 to 0.73, and from R=-0.33 to 0.68 and the peak load for each case was not varied. The crack growth and crack closure were measured by Kikukawa's compliance method with a strain gauge mounted on the backside of each specimens. The results obtained are as follows. When the stepped variable load was applied, the smaller the stress ration was, the larger the delayed retardation of the crack growth rate was. The fatigue crack growh rate data obtained for through cracks were plotted well against the effective stress intensity factor range from 4.0 to 20.0MP{a^{SQRT}m}. It was found that the effective stress intensity factor range ratio was related well to the opening stress intensity factor, the maximum stress intensity factor, and crack length.

• 한국안전학회지
• /
• 제17권1호
• /
• pp.33-38
• /
• 2002

SS41 material is welded automatically and is investigated some effects of the welding residual stress on the growth and propagation of fatigue crack, so as to study the fatigue behaviour in the welding residual stress field. The summarized results are as follows; 1) In case of the load amplitude is constant, as the stress ration is changing to 0.1, 0.33 and 0.5 the propagation life is constant but the initiation life decreases. And than, when maximum load or minimum load is constant, s the stress ration increases the initiation life and propagation life. 2) It was shown that the fatigue crack propagation ratio da/dn was almost constant regardless of the stress ratio change at constant load amplitude and that the larger stress ratio, the slower was the fatigue crack propagation ratio. 3) The opening ratio U is influenced by $K_{max}$ but it isn't only the function of $K_{max}$ because data range is very large. 4) The fatigue life of the specimens on tensile compressive residual stress field was decreased and increased respectably more than that of the base metal.

• 한국자동차공학회논문집
• /
• 제12권4호
• /
• pp.58-64
• /
• 2004

The purpose of this study is to predict the behavior of fatigue crack propagation as one of fracture mechanics on the compressive residual stress. We got the following characteristics from fatigue crack growth test carried out in the environment of room temperature and low temperature at $25^{\circ}C$, -6$0^{\circ}C$, -8$0^{\circ}C$, and -10$0^{\circ}C$ in the range of stress ratio of 0.3 by means of opening mode displacement. There is a difference between shot peened specimen and unpeened specimen. Fatigue crack growth rate of shot peened specimen was lower than that of unpeened specimen. Shot peening is improve the resistance of crack growth by fatigue that make a compressive residual stress on surface. That is the constrained force about plasticity deformation was strengthened by resultant stress, which resulted from plasticity deformation and compressive residual stress in the process of fatigue crack propagation. Temperature goes down, fatigue crack growth rate decreased.

• 한국해양공학회지
• /
• 제4권2호
• /
• pp.250-250
• /
• 1990

In this paper, fatigue tests were carried out at stress test levels of 461 MPa, 441 MPa, and 431 MPa by using smooth specimen of$2_{1/4}$ Cr-1 Mo steel with the stress ratio(R) of 0.05. The initiation, growth and coalescense process of the major cracks and sub-cracks among the fatigue cracks on the smooth specimen are investigated and measured under each stress level at a constant cycle ratio by the replica technique with optical microscope. Some of the important results are as follows: In spite of the difference of stress levels, the major crack data gather into a small band in the curve of surface crack length and crack depth against cycle ratio N/Nf. The sub-crack data, however, deviate from the band of the major crack. The growth rates, da/dN, of major and sub-crack plotted against the stress intensity factor range, ${\Delta}K$, have the tendency to be compressed on a relatively small band. But it is more effective to predict fatigue life through major cracks. The propagation behavior of surface microcracks on the smooth specimens coincides with that of the specimen having an artificial small surface defect or through crack.

• 대한기계학회논문집A
• /
• 제29권6호
• /
• pp.822-827
• /
• 2005

The characteristics of elastic waves emanating from crack initiation and propagation in 6061 aluminum alloy subjected to fatigue loading with different stress ratio was investigated. The objective of this study is to determine the properties of the signals generated from each stage of fatigue crack growth. AS a crack propagates, substantial elastic wave occurred just prior to penetration. Then it decreased and the crack penetrated. The waveforms and their power spectra were found to be dependent on the different stress ratio associated with the signals. It is determined that high-frequency signal $0.5{\sim}0.75$ MHz is most likely emitted during crack propagation at peak load of fatigue cycle which release the highest energy. It is determined that 0.3 MHz is closely related to crack closure effect. The frequency peaks below 0.25 MHz may be attributed to fretting or hydraulic noise.