• Nuclear Engineering and Technology
• /
• v.27 no.6
• /
• pp.825-832
• /
• 1995

The effect of loading variables and temperature on fatigue crack growth rate in SA508 Cl.3 nuclear pressure vessel steel was investigated in air environment Crack growth rate tests on compact tension specimen of thickness 12mm were conducted by using sinusoidal waveform. The crack length was monitored by compliance method. Test conditions were at 0.1 and 0.5 of load ratio, at 1 and 10 Hz of loading frequency, and at room temperature to 40$0^{\circ}C$. At the lower temperatures, the fatigue crack propagation was not affected by the frequency and temperature, while at the higher temperatures above 12$0^{\circ}C$, fatigue crack growth rate increased with decreasing loading frequency and increasing temperature. This accelerated fatigue crack propagation was associated with the increase of oxidation rate at the ahead of crack tip. Fatigue crack growth rate increased with in-creasing the load ratio. The effect of load ratio was more significant at the lower temperature, while the dependence on load ratio decreased with increasing temperature. The sensitivity of load ratio to temperature can be explained by crack closure with the oxidation process.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.29 no.1
• /
• pp.43-48
• /
• 2009

The fatigue crack growth behavior of high strength X80 pipeline steel was investigated with compact tension specimens that crack growth directions were aligned either parallel or normal to the rolling direction of the pipeline. Also, the fatigue crack growth rates for welded joint of X80 pipeline steel were investigated with compact tension specimens that crack growth directions were aligned either parallel or normal to the welding line. The experimental results indicated the fatigue crack growth behavior was markedly different in three zones, weld metal, heat affected zone and base metal of welded joints. There was a trend toward increment in the fatigue life of weld metal and heat affected zone as compared with the X80 pipeline steel.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2001.10a
• /
• pp.263-268
• /
• 2001

The constant .DELTA. K fatigue tests are performed in SS41 and its weldment. The LASER ISDG method is used in determination of crack opening ratio. This method is more precise than indirect measurement method, faster and easier than other direct measurement method. And obtained results are followed 1) Crack opening ratio U is proportional to fatigue crack growth rate da/dN at constant .DELTA. K 2) Fatigue crack growth rate da/dN in weldment increases in weld metal and heat affected zone, decreases in base metal as crack grows.

• Journal of Welding and Joining
• /
• v.7 no.1
• /
• pp.28-35
• /
• 1989

The fatigue crack growth behavior in GTA butt welded joints of Al-Alloy 5052-H38 was examined using Single Edge Notched(SEN) specimens. It is well known that welding residual stress has marked influence on fatigue crack growth rate in welded structure. In the general area of fatigue crack growth in the presence of residual stress, it is noted that the correction of stress intensity factor (K) to account for residual stress is important for the determination of both stress intensity factor range(.DELTA.K) and stress ratio(R) during a loading cycle. The crack growth rate(da/dN) in welded joints were correlated with the effective stress intensity factor range(.DELTA.Keff) which was estimated by superposition of the respective stress intensity factors for the residual stress field and for the applied stress. However, redistribution of residual stress occurs during crack growth and its effect is not negligible. In this study, fatigue crack growth characteristics of the welded joints were examined by using superposition of redistributed residual stress and discussed in comparison with the results of the initial welding residual stress superposition.

• Journal of the Korean Society of Safety
• /
• v.12 no.4
• /
• pp.15-20
• /
• 1997

This study is to investigate the behavior of fatigue crack growth with ATOS 55 steel which can be applied to the commercial car Dump Frame. It is to obtain the material coefficients after tensile and fatigue crack growth test with the variation of thickness or heat treatment. Also, that is proved the Pari's law by experiment. The summarized results are as follows ; 1) Increasing thickness, tensile and yield strength measured highly regardless to heat treatment and measured lowly as variation of heat treatment temperature. 2) Specimen of thickness 8.0㎜ measured the faster of crack growth rate than another thickness according to the results of experiment. It was the different of stress conditions in crack tip. 3) It was found that the experimental constant m was range of 2∼5 to the relationship between fatigue crack growth rate and stress intensity factor range. Also, it was to prove the Paris's law by the experiment.

• Journal of Korea Foundry Society
• /
• v.15 no.4
• /
• pp.388-396
• /
• 1995

This study has been conducted with the purpose of examining the fatigue crack growth characteristics of $Al_2O_3$ short fiber reinforced aluminum matrix composites made by squeeze casting process with different applied pressure and binder amount. Fatigue crack growth experiments have been performed under constant load amplitude method with a fixed load ratio. The rate of crack propagation was decreased with binder amount as well as applied pressure. Also fatigue crack growth path in matrix was changed from flat to rough mode with an increase of applied pressure. In the composites, fatigue crack was propagated to interface between matrix and reinforcement at 10MPa, but it was propagated to reinforcement at 20MPa. The major reason of thee result was considered that interfacial bonding force and microstructure of matrix were improved due to an increase of applied pressure. Localized ductile striation in the composites was observed at low growth rate region and such a phenominon was remarkable with an increase of applied pressure. At high growth rate region, the propensity of fracture appearance was changed from interfacial debonding to reinforcement fracture with an increase of applied pressure.

• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.167-172
• /
• 2008

This study is to evaluate the fatigue crack growth characteristics for base metals and welded metal of 9% Ni steels. Since this material has very excellent fracture toughness at low temperature, it has been widely used for inner walls of LNG storage tank. These materials to compare fatigue crack growth (FCG) behaviour are treated with heat by the method of quenching and tempering (QT), and quenching, lamellarizing and tempering (QLT). FCG tests using compact temsion (CT) specimen under stress ratio R=0.1, 0.5, and constant load are carried out. K-increasing tests are conducted by the standard test method described in ASTM E 647. To investigate the effect of welded metal on the crack growth rate, the locations of notch tip were chosen at the center of welded metal and heat affected zone (HAZ). Form the results, FCG rate has almost same tendency according to stress ratio, base and welded metal, the locations of welded metal. FCG rate of welded metal is somewhat faster than base metal. Also scanning electron microscope (SEM) is used to observe the striation of the fractured surface after fatigue crack tests.

• Journal of Welding and Joining
• /
• v.19 no.3
• /
• pp.278-284
• /
• 2001

Both creep deformation and creep crack growth experiments have been conducted on 2.25Cr-1Mo steel weldment in order to provided an information on residual life prediction of structural component weldment containing a crack. The stress exponent of creep deformation equation for the base metal and weldment at 823k were found to be 10.2 and 7.3, respectively. These two values could be assumed that dislocation climb processes are controlling the creep deformation of both materials. The creep rate of the weldment was very low, compared with that of base metal under the same applied stress. Whereas the creep crack growth rate of the weldment was almost twice higher than that of base metal under the fixed value of $C^*$. This may indicate that the weldment is stronger than the base metal in view of creep deformation and is brittle during creep crack growth due to the intrinsic microstructure of banite and relatively higher and Mn contents.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.37 no.9
• /
• pp.1109-1116
• /
• 2013

This study aims to investigate the spatial randomness of fatigue crack growth rate for the friction stir welded (FSWed) 7075-T651 aluminum alloy joints. Our previous fatigue crack growth test data are adopted in this investigation. To clearly understand the spatial randomness of fatigue crack growth rate, fatigue crack growth tests were conducted under constant stress intensity factor range (SIFR) control testing. The experimental data were analyzed for two different materials-base metal (BM) and weld metal (WM)-to investigate the effects of spatial randomness of fatigue crack growth rate and material properties, the friction stir welded (FSWed) 7075-T651 aluminum alloy joints, namely weld metal (WM) and base metal (BM). The results showed that the variability, as evaluated by Weibull statistical analysis, of the WM is higher than that of the BM.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.27 no.2
• /
• pp.317-326
• /
• 2003

The influence of cyclic bending moment on the delamination and the fatigue crack propagation behavior in Al/GFRP laminate such as the wing section was investigated. The main objective of this study was to evaluate the relationship between crack profile and delamination behavior. And a propose parameter on the delamination growth rate(d $A_{D}$/da) of Al/GFRP laminates with a saw-cut using relationship between delamination area( $A_{D}$) and cycles(N), crack length(a), stress intensity factor range($\Delta$K). Also, the fiber bridging effect factor( $F_{BE}$ ) was propose that the fiber bridging modification factor($\beta$$_{fb}$ ) to evaluate using the delamination growth rate(d $A_{D}$/da). The shape and size of the delamination zone formed along the fatigue crack between aluminum alloy sheet. Class fiber-adhesive layer were measured by an ultrasonic C-scan image. The shape of delamination zone turns out to be semi-elliptic with the contour decreased non-linearly toward the crack tip. It represents that relationship between crack length and delamination growth rate(d $A_{D}$/da) were interdependent by reciprocal action, therefore it's applicable present a model for the delamination growth rate(dA/sib D//da) in Al/GFRP laminates.minates.s.