• 한국농공학회지
• /
• 제25권2호
• /
• pp.67-75
• /
• 1983

The objectives of this paper were to measure the bond strengths of reinforced concrete in which the steel rods were coated with five different kinds of anticorrosion paints, and to compare their prevention effects in salt water. The paints used in the study were epoxy resin I . II . III, Z.R. P., and silicone resin, which were applied at rates recommended by the manufacturers. The bond strengths were measured on the 7-, 14-, and 28-th days after molding. Corrosion conditions of coated steel plate under fresh water, seawater, 10 % salt water, and 20% salt water, were inspected every month during four months test peoriods, respectively. The results obtained from tests are summarized as follows: 1. Paint-coating may reduce the bond strengths of reinforced concrete. Silicone resin paint showed some 20% reduction in the strength compared to those without the paint. However, the other paints seemed not to significantly affect the strength. 2. Picture analyses showed that epoxy resin I and II significantly prevented corrosion steel plates in seawater. Epoxy resin I and silicone resin coating did not do a good job in corrosion prevention. Z.R. P. paint was found to be moderate as preventive coating paint. 3. Varying soluble salt contents had little effects on the corrosion prevention of tested paints. 4. Epoxy resin I and II were found to be appropriate as a coating material to prevent the corrosion of steel rods in seawater. Z.R.P. may also be used for the purpose.

• 도시과학
• /
• 제7권1호
• /
• pp.23-27
• /
• 2018

This research was carried out to investigate the corrosion prevention effect in the water distribution system by galvanized zinc-brass pipe which is using potential between brass and zinc. As a result of this study, pH and conductivity of influent were constant in spite of its installation, and it was difficult to estimate the effect of the installation with temporary increased and reduced concentration of Zn and Fe ions, respectively. However, since the corrosion rate of the steel coupon with galvanized zinc-brass pipe was relatively low, it has an effect of inhibiting corrosion.

• 한국재난정보학회 논문집
• /
• 제4권1호
• /
• pp.138-152
• /
• 2008

The most important factor in the maintenance of chemical industry facilities is related with deterioration and corrosion. Leakage of hazardous materials is likely to occur because the confirmation and maintenance of bottom plates are very difficult while the bottom corrosion of the massive hazmat-storage facilities is most dangerous especially. As a result of the analysis of the corrosion locations, areas, usage condition of 287 hazmat-storage tanks on this syudy, it is concluded that the main external corrosion factors are the inflow of moisture and the materials inducing corrosion in the air such as sodium chloride and the main internal corrosion factors are corrosion react caused by stay of seawater, sulfur and moisture in hazmat for a long time without appropriate discharges. It is anticipated that the corrosion of bottom plates can be restrained effectively by establishing the proper measures for the each corrosion cause.

• 한국조명전기설비학회:학술대회논문집
• /
• 한국조명전기설비학회 2009년도 추계학술대회 논문집
• /
• pp.379-382
• /
• 2009

최근 KTX의 등장으로 기존에 조금씩 논의 되어오던 누설전류에 의한 전기부식이 전면적으로 등장하고 있다. 대전류를 필요로하는 KTX의 주변 지하매설물의 부식이 심각한 수준에 이르렀다. 따라서 이에 대한 대책이 시급한 상황이다. 전기부식을 방지하는 방법에는 몇 가지가 대두되고 있으나 경제성과 효율성을 고려하여 희생양극법을 이용하는 방법이 가장 알맞다고 판단한 바 본 논문에서는 이에 대해 기술하였다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2006년도 추계 학술발표회 논문집
• /
• pp.581-584
• /
• 2006

The durability of reinforced concrete structures is severely degraded by mainly corrosion due to seawater attack and chloride ion diffusion in concrete. The deterioration of durability causes high repair cost for maintenance of marine concrete structure. In this paper, high-durability materials for prevention of rebar corrosion are investigated to promote the durability in marine concrete structures. For these, the effect of the mineral materials addition(SF, FA and BFS), the modified steel(stainless and coating steel). and corrosion inhibitors are compared.

• 한국마린엔지니어링학회:학술대회논문집
• /
• 한국마린엔지니어링학회 2001년도 춘계학술대회 논문집
• /
• pp.152-157
• /
• 2001

This paper was studied on the characteristics of crevice corrosion prevention of SS 400 in marine environment. In NaCl solution, polarization behavior under the crevice corrosion was investigated. And Weight loss rate of SS 400 applied cathodic protection and non cathodic protection was measured according to the NaCl concentration. The main results obtained are as follows : The weight loss rate of Al-alloy galvanic anode was increased as the concentration of NaCl solution increased by 3.5% but the concentration increased over 3.5%, that of Al-alloy galvanic anode become decreased. The protective potential of SS 400 used Al-alloy galvanic anode becomes more cathodic polarization with increasing concentration of NaCl solution. Effects of oxygen on the weight loss rate of Al-alloy sacrificial anode for cathodic protection as the concentration of 3.5% NaCl solution become sensitive than that of 0% NaCl solution.

• Corrosion Science and Technology
• /
• 제10권3호
• /
• pp.87-94
• /
• 2011

The typical corrosion prevention method inside the steel upper box girder in a suspension bridge involves the use of paints. However, in an effort to reduce environmental impact and cost, the suspension portion of the Yeongjong Bridge, Korea utilizes dehumidification systems to control humidity and prevent corrosion inside its box girder. Maintaining a uniform humidity distribution at the proper level inside the box girder is critical to the successful corrosion control. In this study, the humidity and the resultant atmospheric corrosivity inside the box girder of the Yeongjong Bridge was monitored. The corrosion rate of the steel inside the box girder was obtained using thin-film electrical resistance (TFER) corrosion sensors. Time-of-wetness (TOW) measurements and the deposition rates of atmospheric pollutants such as $Cl^{-}$ and $SO_{x}$ were also obtained. Classification of the atmospheric corrosivity inside the box girder was evaluated according to ISO 9223. As a result, no corrosion was found in the upper box girder, indicating that the dehumidification system used in the Yeongjong Bridge is an effective corrosion control method.

• 월간 기계설비
• /
• 통권13호
• /
• pp.128-130
• /
• 1991

• 월간 기계설비
• /
• 통권14호
• /
• pp.114-119
• /
• 1991

• 수산해양기술연구
• /
• 제37권1호
• /
• pp.65-70
• /
• 2001

바다모래에 의해 뒷채움된 지하연료저장탱크용 연강재의 부식전류밀도, 개로전위, 전식거동 및 연간부식률에 관하여 연구한 결과 다음과 같은 결론을 얻었다. 1) 습바다모래 중에서 비저항이 감소할수록 개로전위는 비전위화되고, 부식전류밀도는 높게 배류된다. 2) 습바다모래의 비저항이 감소할수록 인가전위 부가에 의한 부식전류밀도는 자연전위에서의 부식전류밀도보다 급격히 증가한다. 3) 습바다모래 중에서 비저항이 감소할수록 연간부식률은 선형적으로 증가함으로 지하연료저장탱크에 바다모래로 뒷채움하는 경우 습기가 유입하면 지하연료저장탱크의 부식성은 민감할 것으로 판단된다.