• Transactions of the Korean Society of Mechanical Engineers
• /
• v.11 no.6
• /
• pp.867-876
• /
• 1987

Corrosion fatigue fracture with change in the grain size of M.E.F. dual phase steel is investigated in 3.5% NaCI aqueous solution at pH 2, 4, 6, 9, and 11. Generally speaking, decrease in corrosion fatigue life is strongly dependent on decrease in pH and slightly on the grain size. For the B material with the big grain size, the fatigue life is small due to its large reduction ratio of corrosion fatigue life. The influence of grain size on the reduction ratio of corrosion fatigue life is large at pH 11-6. Whi9le at pH 4-2 the reduction ratio of corrosion fatigue life only depends on the corrosion effect. The larger grain size and the lass pH result in the greater influence on corrosion fatigue crack propagation rate. As pH decreases, the plateau portion in the crack propagation rate curves of the B material are distinct. Crack propagation rate curves become slow down at high .DELTA.K range because crack closure effect by minute corrosion products inside crack causes the oxidation corrosion action less effective for a certain period of time. In A material with small grain size, fatigue life is increased in proportion with increase of martensite intergranular which brings forth restraining the crack propagation decreases crack propagation rate. Corrosion pit which is created in the surface of specimen is found at pH 6,4 and 2 which is noticeable and the unevenness of the surface of the specimen becomes severe as pH decreases. The unevenness of corrosion fatigue fracture surface is severe as the effect of pH increases i.e. as pH decreases. In proportion with increase in the grain size and decrease in pH, the aspect of brittle fracture becomes evident.

• Journal of Ocean Engineering and Technology
• /
• v.2 no.2
• /
• pp.122-129
• /
• 1988

Recently with the rapid development in marine and shipbuliding industries such as marine structures, ship and chemical plants, there occurs much interest in the study of corrosion fatigue characteristics which was closed up an important role in mechanical design. In this study, the 5086 Al-alloy was tested by use of rotary bending fatigue tester. The retardation effect of overload on the corrosion fatigue crack propagation in sea environment was quantitatively studied. 1) Retardation effect of corrosion fatigue crack propagation is most eminent when overload ratio is 1.52, overload magnitude corresponds to about 77% and 55% of yield strength and tensile strength respectively. 2) After overload ratio 1.52 was used, retardation of corrosion fatigue crack growth rate is largely retarded and quasi-threshold stress intensity factor range($\Delta\textrm{K}_{th}$) appears. 3) According to m of experimental constant, retardation effect of corrosion fatigue crack propagation corresponds to about 25% of constant stress amplitude when overload ratio is 1.52. 4) When overload ratio 1.52 was used, retardation parameter (RP) decreases to about 0.43 and corrosion sensitivity (S)decreses to about 2.1.

• The Journal of the Convergence on Culture Technology
• /
• v.10 no.1
• /
• pp.363-368
• /
• 2024

Steel structures used in marine environments, such as ships, offshore structures or sub-structures in wind power generation facilities are prone to corrosion. In this study, the corrosion fatigue crack propagation characteristics due to the environmental load are examined by experiment at -1050 mV vs. SCE, which is equivalent to the anti-corrosion potential of zinc anodes that are widely used as sacrificial anodes. In this study, for this purpose, an experimental study is conducted on the effect of cathodic protection on the propagation of fatigue cracks in the seawater environment under the condition of -1050 mV vs. SCE, considering the wave period in synthetic seawater. Cathodic protection prevents corrosion; however, excessive protection generates hydrogen through chemical reactions as well as calcareous deposits. The fatigue crack propagation rate appeared to be faster than the rate in a seawater corrosion environment at the early stages of the experiment. As the crack length and stress intensity factor K increased, the crack propagation rate became slower than the fatigue crack propagation rate in seawater. However, the crack growth rate was faster than that in the atmosphere.

• Journal of Fisheries and Marine Sciences Education
• /
• v.9 no.2
• /
• pp.198-208
• /
• 1997

Recently, with rapid increase of gas demand, there occurs much interest their security of safety in the gas storage tanks and pressure vessels etc. In order to solve the problems, the occurrence of corrosion fatigue crack and the propagation behavior must be investigated. Especially the occurrence of corrosion fatigue crack and the propagation behavior in the part which has concentrated stress or defects, must be studied more carefully. In this paper, the high-tensile steel of SPV 50 which is much used for building the LPG storage tanks was tested by the use of a plane bending corrosion fatigue tester under the various marine environment and in the air. These experiments were carried out to investigate the surface crack propagation behavior, the value of experimental constant for Paris' rule(da/dN=$C(K)^m$), the crack depth propagation rate and the accelerative factor of the surface crack propagation rate. The main results obtained are as follows ; 1) As the specific resistances of marine environment decreases, the exponential value of slope m of Paris' rule(da/dN=$C(K)^m$) decreases and the value of intercept C increases. 2) The surface crack propagation rate and the crack depth propagation rate are delayed, as the specific resistances of marine environment is increased. 3) The accelerative factor of the surface crack propagation rate by corrosion fatigue is higher, according as the stress intensity factor range ${\Delta}K_A$ is small.

• Journal of the Society of Naval Architects of Korea
• /
• v.44 no.4
• /
• pp.417-424
• /
• 2007

With regard to corrosion fatigue crack initiation life (Nc), it has been treated ambiguously for the member which doesn't have stress concentration area. In this research, in order to clarify the corrosion fatigue crack initiation life (Nc), corrosion fatigue tests were carried out. Reasonable and universal corrosion fatigue crack initiation life (Nc) was defined and corrosion fatigue crack initiation/propagation model was suggested also. As the fatigue crack which emanates from the pit is usually small, accordingly it is treated as a small crack. In addition, the observation of the corrosion fatigue fracture surfaces using SEM was conducted. And the fracture mechanics analysis using an intrinsic crack model was conducted for the treatment of the small crack. Finally, the followings were obtained. When there is no clear stress concentration point which seems to fall into a corrosion fatigue crack initiation life, the significance of the definition and suggestion of the moment of the reasonable and universal corrosion fatigue crack initiation life (Nc), at which the fatigue crack propagation rate becomes faster than the corrosion pit growth rate so that the fatigue crack initiates from the pit and propagates in earnest, has been clarified.

• Journal of Ocean Engineering and Technology
• /
• v.1 no.1
• /
• pp.111-119
• /
• 1987

The corrosion fatigue crack propagation characteristics of SS41 steel in 3.5% NaCl solution have been evaluated for loading frequencies of 1Hz and 0.2Hz. A sine wave loading profile was used for fatigue testing. Each test was carried out at a constant stress ratio, R(0.1). The main results are summarized as follows; 1. Fatigue crack propagation rate was higher in 3.5% NaCl solution than in air, higher in the base metal than in the weld metal, and higher at f =0.2Hz than at f =1Hz. 2. The crack closure level of the base metal was not influenced by cyclic frequencies, but that of the weld metal was much influenced. 3. When the crack closure effect was eliminated in the evaluation of crack propagation characteristics by using $\Delta K_{eff}$, the envirommental influence was distinctly observed. At the base metal, crack propagation rate was enhanced by the hydrogen embrittlement, and the weld metal was reduced by the crac closure. 4. There was clearly observed hydrogen embrittlement and severely corroded aspect at fracture surface of lower frequency than that of higher frequency, and at that of base metal than that of the weld metal.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.28 no.3
• /
• pp.286-294
• /
• 1992

In this paper, the corrosion fatigue crack propagation behavior of structure rolled steel (SWS 41C) was investigated by changing the thickness, and this experiment was done by the three point bending corrosion fatigue tester. The main results obtained are as follows: 1) As the thickness of specimen becomes thicker, the corrosion sensitivity to initial stage crack becomes some sensitive, and that the fatigue life becomes more sensitive. 2) The crack growth rate to initial stage crack (da/dN) was retarded as the thickness of specimen becomes thicker. But after initial stage crack, as the thickness of specimen is more thicker, da/dN is more rapid. 3) As the corrosion fatigue crack length grows, the accelerative factor of thick specimen (t=12mm) is more higher than that of thin specimen (t=6mm). 4) As the corrosion fatigue crack length grows, the corroson potential of both thick specimen and thin specimen becomes more less noble potential, however thick specimen (t=12mm) tends to more less noble potential than that of thin specimen(t=6mm).

• Journal of Ocean Engineering and Technology
• /
• v.6 no.1
• /
• pp.140-147
• /
• 1992

Corrsion fatigue test was performed under rotated bending in 3.5% NaCl aqueous solution having a temperature from 278.deg.K in order to investigate the effects of aqueous solution remperature on the corrosion fatigue fracture of raw material steel(SS41) and dual phase steel that was produced from SS41 by a series of heat treatment. Corrosion fatigue life decreases remarkably with increase in solution temperature or with decrease in stress level. The corrosion fatigue life and the crack propagation rate at 303.deg.K show the similar behaviors with those at 318.deg.K, which is assumed to be caused by concentration polarization phenamena. The number and the lengths of microcracks increase with increase in solution temperature, so they lead to the decrease in corrosion fatigue life.

• Journal of Ocean Engineering and Technology
• /
• v.1 no.2
• /
• pp.123-129
• /
• 1987

Corrosion fatigue fracture of dual phase steel(SS41) and raw material steel(SS41) were investigated in 3.5% NaCl aqueous solution at PH 4,6,9 and 11. The fatigue limit of dual phase steel is increased approximately 1.8 times larger than that of raw material in air. The corrosion fatigue life of dual phase steel is about 5-10 times larger than that of raw material in 3.5% NaCl aqueous solution. The reduction of fatigue life is larger for the acidsalt solution than for the alkali salt solution. The reduction of stress level on the reduction ratio of corrosion fatigue life is large as pH 6-11. The reduction ratio of corrosion fatigue life of dual phase steel and raw material is nearly coincided at pH 2. While at pH4-2 the reduction ratio of corrosion fatigue life only depends on the corrosion effect. It has been found that the corrosion resistance effect of dual phase steel is smaller than that of raw material in corrosion fatigue crack propagation rate. As pH below 6 is changed, it can be clearly observed from raw material that the brittle intergranular fracture is characterized, and from the above result, the influence of corrosion of dual phase steel is small.

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2005.11a
• /
• pp.228-229
• /
• 2005

The compressive residual stress, which is induced by shot peening process, has the effect of increasing the intrinsic fatigue strength of surface and therefore would be beneficial in reducing the probability of fatigue damage. However, it was not known that the effect of shot peening in corrosion environment. In this study, the effect of shot peening on corrosion fatigue crack growth of sping steel immersed in 6% $FeCl_3$ solution and corrosion characteristics with considering fracture mechanics. The results of the experimental study corrosion fatigue characteristics of spring steel are as follows; the fatigue crack growth rate of the shot peening material was lower than of the un peening material. And fatigue life shows more improvement in the shot peening material than un peening material. This is because the compressive residual stress of surface operate resistance of corrosion fatigue crack propagation. It is assumed that the shot peening process improve corrosive resistance and mechanical property.